CN102531810B - 一种防返粉改性铵油炸药 - Google Patents
一种防返粉改性铵油炸药 Download PDFInfo
- Publication number
- CN102531810B CN102531810B CN 201210062306 CN201210062306A CN102531810B CN 102531810 B CN102531810 B CN 102531810B CN 201210062306 CN201210062306 CN 201210062306 CN 201210062306 A CN201210062306 A CN 201210062306A CN 102531810 B CN102531810 B CN 102531810B
- Authority
- CN
- China
- Prior art keywords
- ammonium nitrate
- explosive
- percent
- kilogram
- fuel oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及民用爆破器材,是一种防返粉改性铵油炸药,其组分重量百分比为硝酸铵89~93%、木粉3.5~5.0%、复合油相3.5~6.0%,且外加有改性剂0.3~0.5%,其特征是:还外加有柴油1.0%~3.0%、分散剂CNF0.1%~0.4%;本发明解决了现有同类炸药返粉严重、爆破效果差,作业环境差等问题,广泛适用于无沼气及无矿尘爆炸危险的爆破工程。
Description
(一)技术领域:本发明涉及民用爆破器材,尤其是一种防返粉改性铵油炸药。
(二)背景技术:改性铵油炸药是以硝酸铵(硝酸铵可以是粉状硝酸铵、粒状硝酸铵)为主要成份,与油相和木粉(或者不加木粉)所组成的混合炸药,通过添加一种改性剂,对硝酸铵进行改性和自敏化,并有效控制硝酸铵吸湿速度,很大程度上提高了改性铵油炸药的产品质量。改性铵油炸药作为一种新型粉状无梯工业炸药,是近几年国内开发研制的新产品,也是产业政策重点推广的工业炸药的更新换代产品,属我国目前主要的露天矿爆破用药,也广泛应用于地下矿山开采。
主要技术原理:
在工业炸药制造中引入了机械力化学有关原理,加入以阳离子型表面活性剂为主要成份的WT(无梯)型复合改性剂,利用硝酸铵连续改性机对炸药组份中的主要原料硝酸铵进行复合改性,制得平均粒径小于50μm、颗粒外观近似球形的改性硝铵粉体。通过这种方法制得的改性硝铵,其晶形结构已经发生了变化,为不定晶形;比表面积大大增加,提高了硝酸铵颗粒承载油相的能力。由此制得的改性铵油炸药,具有装药密度高、爆轰感度高、重量威力高、体积威力高等四高特征,其防潮抗水性能以及贮存稳定性也相应得到大幅提高。
改性铵油炸药的制备方法是:首先把硝酸铵和改性剂进行粗碎、混合,然后进行干燥、改性,再加入木粉和复合油相,混合均匀后制得成品。
但是,现有的改性铵油炸药在地下矿山使用过程中存在如下问题:
1、返粉严重
在地下矿山开采爆破作业中,常采用风动机械装药的方式进行装填炸药。而改性铵油炸药为粉状炸药,由于药粉没有粘性,返药现象严重,特别是现场填装上向孔时,一般返药掉药率高达30%~40%,炸药浪费严重,作业效率低。
2、爆破效果差
由于返粉严重,直接导致炮孔中炸药的实际填装量远小于预定值,进而降低了爆炸威力,爆破效果差。
3、作业环境差
炮孔中返掉下来药粉严重污染作业环境,工作面一般都是粉尘飞扬,环境恶劣,十分损害人员身心健康。
(三)发明内容:本发明的目的就是要解决现有改性铵油炸药返粉严重、爆破效果差,影响作业环境的问题,提供一种防返粉改性铵油炸药。
本发明的具体方案是:一种防返粉改性铵油炸药,其组分重量百分比为硝酸铵89~93%、木粉3.5~5.0%、复合油相3.5~6.0%,且外加有改性剂0.3~0.5%,其特征是:还外加有柴油1.0%~3.0%、分散剂CNF 0.1%~0.4%。
本发明中所述复合油相组分重量百分比为:石蜡40%~60%,工业凡士林35~55%,斯本-80 2~6%,硬脂酸2~6%。
本发明中所述改性剂组分重量百分比为:十八伯胺25~40%,微晶蜡10~25%,十二烷基胺醋酸盐8~20%,十二烷基胺硫酸钠6~17%,多烷基化合物2~8%。
本发明通过在现有粉状改性铵油炸药中外加柴油和分散剂CNF,达到增加产品流散性和粘着性的目的。柴油可以增加药粉的粘度,使其更易附着在炮孔内;分散剂CNF具有良好的分散性能,使柴油与药粉均匀混合,增加炸药药粉体粘性的同时,又使其确保一定的流散性。通过调整添加比例,使药粉既具有一定粘性,减少返粉;同时又具有一定流散性,便于井下上向炮孔压气装药的装填施工。经过不断试制和检测,发现柴油1%~3%(外加),分散剂CNF0.1%~0.4%(外加)的添加比例较为合适。既保证产品性能质量,同时最大限度降低装药返粉率。
本发明炸药经井下装药现场试验,返粉率由以往的30%~40%下降为5%~12%,不但提高了作业效率和爆破效果,减少浪费,同时极大改善了作业环境。
(四)具体实施方式:
例1:备料:取硝酸铵89公斤、木粉5公斤、复合油相6公斤、改性剂0.3公斤、柴油1公斤、分散剂CNF 0.1公斤(其化学组分为苄基萘磺酸甲醛缩合物)。
本实施例中所述的复合油相是由2.4公斤石蜡,3.3公斤工业凡士林,0.12公斤斯本-80,0.18公斤硬脂酸组成。
本实施例中所述的改性剂是由0.075公斤十八伯胺,0.075公斤微晶蜡,0.075公斤十二烷基胺醋酸盐,0.051公斤十二烷基胺硫酸钠, 0.024公斤多烷基化合物组成。
制备方法如下:首先把硝酸铵和改性剂进行粗碎、混合,然后进行干燥、改性,再加入木粉和复合油相,最后加入柴油和分散剂CNF,混合均匀后制得成品。
例2:备料:取硝酸铵91公斤、木粉4公斤、复合油相5公斤、改性剂0.4公斤、柴油2公斤、分散剂CNF0.3公斤。
本实施例中所述的复合油相是由2.5公斤石蜡,2.2公斤工业凡士林,0.18公斤斯本-80,0.12公斤硬脂酸组成。
本实施例中所述的改性剂是由0.12公斤十八佰胺,0.10公斤微晶蜡,0.08公斤十二烷基胺醋酸盐,0.068 公斤十二烷基胺硫酸钠,0.032 公斤多烷基化合物组成。
制备方法如下:首先把硝酸铵和改性剂进行粗碎、混合,然后进行干燥、改性,再加入木粉和复合油相,最后加入柴油和分散剂CNF,混合均匀后制得成品。
例3:备料:取硝酸铵93公斤、木粉3.5公斤、复合油相3.5公斤、改性剂0.5公斤、柴油3公斤、分散剂CNF 0.4公斤。
本实施例中所述的复合油相是由2.1公斤石蜡,1.25 公斤工业凡士林,0.08公斤斯本-80,0.07 公斤硬脂酸组成。
本实施例中所述的改性剂是由 0.2公斤十八伯胺,0.1 公斤微晶蜡,0.1 公斤十二烷基胺醋酸盐,0.07公斤十二烷基胺硫酸钠,0.03公斤多烷基化合物组成。
制备方法如下:首先把硝酸铵和改性剂进行粗碎、混合,然后进行干燥、改性,再加入木粉和复合油相,最后加入柴油和分散剂CNF,混合均匀后制得成品。
Claims (3)
1.一种防返粉改性铵油炸药,其组分重量百分比为硝酸铵89~93%、木粉3.5~5.0%、复合油相3.5~6.0%,且外加有改性剂0.3~0.5%,其特征是:还外加有柴油1.0%~3.0%、分散剂CNF 0.1%~0.4%。
2.根据权利要求1所述的一种防返粉改性铵油炸药,其特征是:所述复合油相组分重量百分比为:石蜡40%~60%,工业凡士林35~55%,斯本-80 2~6%,硬脂酸2~6%。
3.根据权利要求1所述的一种防返粉改性铵油炸药,其特征是:所述改性剂组分重量百分比为:十八伯胺25~40%,微晶蜡10~25%,十二烷基胺醋酸盐8~20%,十二烷基胺硫酸钠6~17%,多烷基化合物2~8%,以上组份的百分比之和为百分之百。