CN102531702A - High-quality bone china glaze - Google Patents
High-quality bone china glaze Download PDFInfo
- Publication number
- CN102531702A CN102531702A CN2011104178207A CN201110417820A CN102531702A CN 102531702 A CN102531702 A CN 102531702A CN 2011104178207 A CN2011104178207 A CN 2011104178207A CN 201110417820 A CN201110417820 A CN 201110417820A CN 102531702 A CN102531702 A CN 102531702A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- quality
- sclerotin
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-quality bone chain glaze which consists of the following raw materials in parts by weight: 30-40 parts of potash feldspar, 10-20 parts of kaolin, 15-28 parts of zirconium silicate, 5-15 parts of quartz, 5-10 parts of calcite, 2-5 parts of zinc oxide, 1-3 parts of talc, 5-15 parts of barium carbonate and 2-6 parts of borax. The high-quality bone chain glaze of the invention is simple in formula, reasonable in proportioning, high in purify of glaze, and few in impurities; the bone china prepared by the high-quality bone chain glaze is excellent in product translucency of a product, soft in color of glaze, and few in defects; the flowability of the glaze in the baking process is strong, and the quality of the glaze and the quality of the product are excellent.
Description
Technical field
The present invention relates to a kind of ceramic glaze, particularly a kind of high quality sclerotin enamel material.
Background technology
The sclerotin porcelain is the high-grade porcelain of generally acknowledging in the world, and 18th century were risen in Britain, is at first to imitate the hard-paste of China and a kind of soft porcelain of being developed out by French frit china.Through the development in surplus 200 years, the sclerotin porcelain is a kind of high-grade daily-use fine that receives the countries in the world welcome deeply because of its distinctive texture and performance become, and enjoys the highest reputation on the market at home and abroad.
The sclerotin porcelain be a kind of be main with bone meal (calcination processing), add raw mineral materialss such as part clay, feldspar, quartz simultaneously, the soft porcelain that adopts high temperature biscuiting, low temperature glaze firing double-firing process to fire.The phase composite of porcelain base thing mainly is the glassy phase of tricalcium phosphate, lime feldspar and certain content.Just because of the distinctive thing phase composite of sclerotin porcelain characteristics, make that its porcelain is pure white, gloss is gentle, have transparence preferably, higher intensity and relatively poor thermostability etc.The sclerotin porcelain successively passes to America and Europe and Japan by Britain.Our province has also carried out trial production to it in succession from the sixties; The seventies has been test-manufactured part sclerotin porcelain products, and to Tangshan of the eighties China, Zibo etc. successively produces in batches, output enlarges year by year; Product quality level improves day by day; And created the china brand of controlling oneself, and progress into domestic high-grade hotel, restaurant and part common people family, won the approval and the praise of home market.
Sclerotin porcelain products translucency is good; The glaze color and luster is soft, receives client's favor, mainly is because the sclerotin porcelain products have the good surface appearance image; Be most critical with regard to the glaze quality that has determined it like this; Its glaze quality is the key link, generation of defects such as pin hole, glaze, aberration, dirty point, ripple, all with glaze in impurity relevant; The purity of glaze directly affects the overglaze quality, reduce the glaze plane defect, and key is the purity of control glaze.
Summary of the invention
The object of the invention is to provide a kind of high quality sclerotin enamel material.
For addressing the above problem; The technical scheme that the present invention adopted is: a kind of high quality sclerotin enamel material according to the invention, form by the raw material of following parts by weight: 30 ~ 40 parts of potassium felspar sands, 10 ~ 20 parts of kaolin, 15 ~ 28 parts of zirconium silicates, 5 ~ 15 parts in quartz, 5 ~ 10 parts in calcite, 2 ~ 5 parts in zinc oxide, 1 ~ 3 part in talcum, 5 ~ 15 parts of barium carbonates, 2 ~ 6 parts of boraxs.
The present invention with respect to the beneficial effect of prior art is: high quality sclerotin enamel material formula according to the invention is simple, reasonable ratio, and glaze purity is high, impurity is few; Adopt the prepared sclerotin porcelain that goes out of high quality sclerotin enamel material of the present invention; The product translucency is good, and the glaze color and luster is soft, and defective is few; Glaze is mobile strong in sintering process, and glaze quality and quality product are high.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1Adopt following formulation high quality sclerotin according to the invention enamel material: in the raw material of parts by weight: 30 parts of potassium felspar sands, 15 parts of kaolin, 15 parts of zirconium silicates, quartzy 15 parts, 10 parts in calcite, 5 parts in zinc oxide, 2 parts in talcum, 15 parts of barium carbonates, 4 parts of boraxs.
Embodiment 2Adopt following formulation high quality sclerotin according to the invention enamel material: in the raw material of parts by weight: 35 parts of potassium felspar sands, 20 parts of kaolin, 22 parts of zirconium silicates, quartzy 10 parts, 8 parts in calcite, 4 parts in zinc oxide, 3 parts in talcum, 11 parts of barium carbonates, 2 parts of boraxs.
Embodiment 3Adopt following formulation high quality sclerotin according to the invention enamel material: 40 parts of potassium felspar sands, 20 parts of kaolin, 28 parts of zirconium silicates, 5 parts in quartz, 5 parts in calcite, 2 parts in zinc oxide, 1 part in talcum, 15 parts of barium carbonates, 6 parts of boraxs.
Claims (1)
1. high quality sclerotin enamel material, it is characterized in that: the raw material by following parts by weight is formed: 30 ~ 40 parts of potassium felspar sands, 10 ~ 20 parts of kaolin, 15 ~ 28 parts of zirconium silicates, quartzy 5 ~ 15 parts, 5 ~ 10 parts in calcite, 2 ~ 5 parts in zinc oxide, 1 ~ 3 part in talcum, 5 ~ 15 parts of barium carbonates, 2 ~ 6 parts of boraxs.