CN102517441A - 含铅复合球团的生产方法 - Google Patents
含铅复合球团的生产方法 Download PDFInfo
- Publication number
- CN102517441A CN102517441A CN2011104260396A CN201110426039A CN102517441A CN 102517441 A CN102517441 A CN 102517441A CN 2011104260396 A CN2011104260396 A CN 2011104260396A CN 201110426039 A CN201110426039 A CN 201110426039A CN 102517441 A CN102517441 A CN 102517441A
- Authority
- CN
- China
- Prior art keywords
- lead
- compound
- semicoke
- leaded
- pellet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种含铅复合球团的生产方法,选用市售的炭粉球团粘结剂MY,将混碾后的半焦、低品位氧化铅矿和含铅粉料搅拌均匀得到混合料,在混合料中加入MY粘结剂溶液,搅拌均匀;将混合料送入成型机进行冷压成型制成直径为50mm~100mm的椭圆形含铅复合球团,即可投入铅还原炉进行熔炼。本发明使褐煤资源和低品位氧化铅矿得到进一步的开发利用;褐煤干馏的颗粒状半焦合理有效的配入含铅氧化矿中成型,既能发热产生热量供铅冶炼之用,又能使碳更好地分散与整个球团中;真正实现褐煤半焦及铅氧化矿粉状物料的合理开发利用。
Description
技术领域
本发明涉及一种用半焦、含铅粉料和低品位氧化铅矿冷压成型的含铅复合球团生产方法。
背景技术
申请人地处边疆,是一个铅锌生产企业,具有年产万吨的铅还原炉生产线。在铅冶炼生产过程中产生大量的含铅粉料,如大量的烟尘,这部分含铅粉料烟尘不能直接使用,需要进行处理后使用,此外公司有年产10万吨的褐煤生产矿山和储存有上百万吨的地表与井下氧化铅矿资源,地表与井下氧化铅矿为含铅10%以下的低品位氧化铅矿。同时,拥有碳化炉一座,可生产粒度<3mm占20~40%,含碳量70%左右的半焦。目前铅还原炉多年的燃料靠运距千里的焦炭产地通过公路运来,半焦外售价仅700元/吨左右,而焦炭价格至2010年上半年已过突破1900元/吨,且仍有上涨的趋势。如何找到一种合理有效降低铅生产成本的途径,又能将本地资源合理开发利用,实质降低粗铅生产成本,乃是本发明人的根本目的。
发明内容
本发明的目的是充分开发利用半焦、含铅粉料及低品位氧化铅矿不能综合利用的不足,提供一种含铅复合球团的生产方法,本发明采用半焦、含铅粉料、低品位氧化铅矿混合料,加入MY粘结剂,冷压生产工艺将混合料制成直径为50mm~100mm的椭圆形球团产品,风干后进入还原炉进行冶炼。本发明的目的通过以下技术方案实现:
一种含铅复合球团的生产方法,包括如下步骤:
(一)制备MY粘结剂溶液
选用市售的炭粉球团粘结剂MY,先往容器里加一定量水并快速搅拌,同时按质量比例1:50缓慢地加入所述MY粘结剂,注意尽量不要使之结成较大团块,等到水分完全浸润MY粘结剂,再搅拌均匀就得到MY粘结剂溶液;
(二)成型
(1)、将含碳68~70%的半焦和含铅10%以下的低品位氧化铅矿分别混碾到粒度<5mm占70~80%,混碾后的半焦、低品位氧化铅矿和含铅粉料搅拌均匀得到混合料,在混合料中按重量计加入3~4‰的MY粘结剂溶液,搅拌2~5分钟,当混合料湿度不足时通过补加自来水来调整混合料水份,混合料湿度以搅拌均匀手握成团不散为宜;
(2)、将上一步骤得到的混合料均匀送入成型机进行冷压成型制成直径为50mm~100mm的椭圆形含铅复合球团,冷压成型机压强控制在14~16Mpa,将生产出来的球团进行自然干燥至水分≤5%、抗压强度不低于80kg/cm2,即可投入铅还原炉进行熔炼;
上述的%均为质量百分比例。
本发明将企业内自产资源有机结合进行充分利用,一是使褐煤资源得到进一步的开发利用,减少运距离焦炭运输使用的成本;二是解决了低品位氧化矿外销价格低的问题,将氧化矿资源更好的利用;三是将褐煤干馏的颗粒状半焦合理有效的配入含铅氧化矿中成型,既能发热产生热量供铅冶炼之用,又能使碳更好地分散与整个球团中;另外,由于其分散性,加速了铅还原反应的进行。既改善了还原反应的条件,改善了炉内的透气性,又能使生产成本降低,炉况稳定,弃渣含铅降低,渣含铅≤2%,真正实现褐煤半焦及铅氧化矿粉状物料的合理开发利用。
具体实施方式
实施例
本发明中采用的物料均按质量百分比例:
半焦20%、低品位氧化铅矿60%、含铅粉料20%;
MY粘结剂配成溶液加入:占混合料3±1‰
含铅复合球团的生产方法,步骤如下:
(一)制备MY粘结剂溶液
MY粘结剂溶于水后具有一定的粘度,如溶解方法不当会造成较大结团,影响正常使用,正确的溶解方法为:MY粘结剂和水按质量比例1:50溶解,需先往容器里加一定量水并用搅拌棍或搅拌机快速搅拌,同时缓慢、均匀分散地加入MY粘结剂,注意尽量不要使之结成较大团块,等到水分完全浸润MY粘结剂,再搅拌均匀就可以做成MY粘结剂溶液。
MY粘结剂是市场有售的炭粉球团粘结剂。例如:河北铭泰化工有限公司产生的铭泰牌PAC-HVHS高粘度粘接剂。
(二)成型
1、将含碳68~70%的半焦和含铅10%以下的低品位氧化铅矿混碾到粒度<5mm占70~80%,将半焦、含铅粉料、低品位氧化铅矿搅拌均匀得到混合料,按混合料重量计称取3~4‰的MY粘结剂制成MY粘结剂溶液。在混合料加入MY粘结剂溶液搅拌2~5分钟,当混合料湿度不足时通过补加自来水来调整混合料水份,混合料湿度以搅拌均匀手握成团不散为宜。
2、将搅拌好的混合料均匀送入成型机进行冷压成型,冷压成型机压强控制在14~16Mpa。制成的直径为50mm~100mm的椭圆形产品,将生产出来的球团进行自然干燥,干燥后水分≤5%,含铅复合球团抗压强度>80kg/cm2,风干后入铅还原炉进行熔炼。
Claims (1)
1.一种含铅复合球团的生产方法,其特征在于:包括如下步骤:
(一)制备MY粘结剂溶液
选用市售的炭粉球团粘结剂MY,先往容器里加一定量水并快速搅拌,同时按质量比例1:50缓慢地加入所述MY粘结剂,注意尽量不要使之结成较大团块,等到水分完全浸润MY粘结剂,再搅拌均匀就得到MY粘结剂溶液;
(二)成型
(1)、将含碳68~70%的半焦和含铅10%以下的低品位氧化铅矿分别混碾到粒度<5mm占70~80%,混碾后的半焦、低品位氧化铅矿和含铅粉料搅拌均匀得到混合料,在混合料中按重量计加入3~4‰的MY粘结剂溶液,搅拌2~5分钟,当混合料湿度不足时通过补加自来水来调整混合料水份,混合料湿度以搅拌均匀手握成团不散为宜;
(2)、将上一步骤得到的混合料均匀送入成型机进行冷压成型制成直径为50mm~100mm的椭圆形含铅复合球团,冷压成型机压强控制在14~16Mpa,将生产出来的球团进行自然干燥至水分≤5%、抗压强度不低于80kg/cm2,即可投入铅还原炉进行熔炼;
上述的%均为质量百分比例。