CN102516861A - 一种木器用聚氨酯涂料的制备方法 - Google Patents
一种木器用聚氨酯涂料的制备方法 Download PDFInfo
- Publication number
- CN102516861A CN102516861A CN2011104192238A CN201110419223A CN102516861A CN 102516861 A CN102516861 A CN 102516861A CN 2011104192238 A CN2011104192238 A CN 2011104192238A CN 201110419223 A CN201110419223 A CN 201110419223A CN 102516861 A CN102516861 A CN 102516861A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyurethane coating
- emulsion
- mixing
- woodenware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种木器用聚氨酯涂料的制备方法，该方法的制备步骤如下：将540-560质量份聚丁二烯、100-140份氢氧化钙、58份辛基化二苯胺、10份消泡剂和40-44份乳化液混合搅拌均匀，形成粘度为5-6Pa·s的乳液，将该乳液与150-158份烷基苯磺酸钠、70份二甲苯烷异氰酸酯和20-25份邻苯二甲酸二辛酯混合、研磨、过滤，即得。本发明方法生产出的产品经工业试验证明，该涂料具有良好的耐水性、耐洗涤性、流平性、再涂性、耐摩擦性和耐久性。
Description
技术领域
本发明涉及一种木器用聚氨酯涂料的制备方法，属于化工涂料技术领域。
技术背景
聚氨酯全称为聚氨基甲酸酯 ,是主链上含有重复氨基甲酸酯基团的大分子化合物的统称。它是由有机二异氰酸酯或多异氰酸酯与二羟基或多羟基化合物加聚而成。聚氨酯涂层剂是当今发展的主要种类，它的优势在于：涂层柔软并有弹性；涂层强度好，可用于很薄的涂层；涂层多孔，具有透湿和通气性能；耐磨，耐湿，耐干洗。所以在木器的表面涂饰聚氨酯涂料，这样可以很好的保护木器。但是聚氨酯涂料在遇水、热、油要水解。
发明内容
本发明目的是提供一种木器用聚氨酯涂料的制备方法，该方法制备出的聚氨酯涂料用于涂饰木器表面，具有光泽高,耐水性和耐油性好的。
为了达到上述目的，本发明采用的技术方案是：一种木器用聚氨酯涂料的制备方法, 其特征在于该方法的制备步骤如下：将540-560质量份聚丁二烯、100-140份氢氧化钙、58份辛基化二苯胺、10份消泡剂和40-44份乳化液混合搅拌均匀，形成粘度为5-6Pa·s的乳液，将该乳液与150-158份烷基苯磺酸钠、70份二甲苯烷异氰酸酯和20-25份邻苯二甲酸二辛酯混合、研磨、过滤，即得。
有益效果：本发明方法生产出的产品经工业试验证明，该涂料具有良好的光泽高,耐水、耐油、耐切割液、耐沾污性能好。
具体实施方式
实施例1
一种木器用聚氨酯涂料的制备方法, 其特征在于该方法的制备步骤如下：将540-560质量份聚丁二烯、100-140份氢氧化钙、58份辛基化二苯胺、10份消泡剂和40-44份乳化液混合搅拌均匀，形成粘度为5-6Pa·s的乳液，将该乳液与150-158份烷基苯磺酸钠、70份二甲苯烷异氰酸酯和20-25份邻苯二甲酸二辛酯混合、研磨、过滤，即得。
Claims (1)
1.一种木器用聚氨酯涂料的制备方法，其特征在于该方法的制备步骤如下：将540-560质量份聚丁二烯、100-140份氢氧化钙、58份辛基化二苯胺、10份消泡剂和40-44份乳化液混合搅拌均匀，形成粘度为5-6Pa·s的乳液，将该乳液与150-158份烷基苯磺酸钠、70份二甲苯烷异氰酸酯和20-25份邻苯二甲酸二辛酯混合、研磨、过滤，即得。