CN102500952B - 镍基高温合金钎料及其制备方法 - Google Patents
镍基高温合金钎料及其制备方法 Download PDFInfo
- Publication number
- CN102500952B CN102500952B CN2011103474400A CN201110347440A CN102500952B CN 102500952 B CN102500952 B CN 102500952B CN 2011103474400 A CN2011103474400 A CN 2011103474400A CN 201110347440 A CN201110347440 A CN 201110347440A CN 102500952 B CN102500952 B CN 102500952B
- Authority
- CN
- China
- Prior art keywords
- filler metal
- brazing filler
- brazing
- preparation
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种镍基高温合金钎料及其制备方法,由下述重量百分比的组分组成:Cr 5.0%~20.0%,Si 4.0%~10.0%,Fe 0.1%~3.0%,Cu 0.1%~10.0%,P 0.1%~3.0%,余量Ni;其制备方法,包括如下步骤:将以下组分Cr、Si、Fe、Cu、P、Ni按比例混合,采用真空熔炼及气雾化、超声波筛分,将钎料制成240~600目的球形粉末状,最后用有机粘结剂将钎料粉末调制成膏状钎料。优点:本发明具有焊接接缝强度高,因熔点高具有良好的耐高温性,添加的Cu、Fe有效地抑制了钎料的流淌;适用于不锈钢的钎焊,特别是对汽车EGR不锈钢冷却器的钎焊具有优良的润湿性和间隙填充性,其钎焊构件的气密性、耐腐蚀性能、接缝强度均达到EGR不锈钢冷却器的技术要求。
Description
技术领域
本发明涉及一种镍基高温合金钎料及其制备方法。
背景技术
废气再循环技术(EGR)是目前控制汽车NOX排放的最有效的措施。在冷却的EGR技术中,关键的总成是EGR冷却器。EGR废气工作在高温、高压下,且排放物中含有较多的硫氮氧化物,废气冷却时可形成强氧化物,对冷却器产生腐蚀。此种工作条件就要求冷却器耐高温、耐腐蚀。在诸多钎料中,之所以选择镍基钎料,是因为其具有极好的抗氧化和耐腐蚀性能,有良好的塑性及中等的强度。
传统上,不锈钢真空钎焊采用BNi-2、BNi-5钎料或铜基钎料,但钎焊后形成的接头对稀硫酸腐蚀比较敏感,导致EGR冷却器可靠性下降。世界各国对镍基钎料的研究较多,历史也比较悠久,但很少适合用在EGR冷却器系统上。这是因为基于EGR冷却器的特殊结构,对镍基焊料的性能要求非常苛刻,不仅要求浸润性好,但又不能出现流淌的现象。因EGR冷却器为多管壳结构和镍基钎料的不易成型性,镍基钎料主要以粉体的形式参与焊接,通常也就是将粉体与粘合剂混合制成膏体使用。因此对焊料的氧含量、粒度范围、球形度及微量元素等方面要求甚严,所以需对EGR冷却器系统开发新型专用的镍基钎料,以满足该焊接领域的需要。
国内目前生产的镍基钎料均存在一个弊端:焊接时发生流淌现象。随着汽车这一关系国计民生的交通工具在生活中的普及,EGR冷却器生产市场势必会增加规模和产量。
发明内容
本发明的目的就是为了解决已知技术中的镍基钎料钎焊汽车EGR不锈钢冷却器钎焊过程中存在的流淌、接头外观质量差、可靠性低和耐腐蚀性能不佳等问题,提供一种镍基高温合金钎料及其制备方法。
为达到上述目的,本发明采用如下技术方案:一种镍基高温合金钎料,由下述重量百分比的组分组成:Cr 5.0%~20.0%,Si 4.0%~10.0%,Fe 0.1%~3.0%,Cu 0.1%~10.0%,P 0.1%~3.0%,余量Ni。
所述镍基高温合金钎料的制备方法,包括如下步骤:将以下组分Cr、Si、Fe、Cu、P、Ni按比例混合,采用真空熔炼及气雾化、超声波筛分,将钎料制成240~600目的球形粉末状,最后用有机粘结剂将钎料粉末调制成膏状钎料。
对于本发明的一种优化,P是以Ni-P合金的形式与Cr、Si、Fe、Cu、Ni混合。
其中上述Cr的质量纯度为99.0.0%~99.9%,Si的质量纯度为99.0.0%~99.9%,Fe的质量纯度为99.0.0%~99.9%,Cu的质量纯度为99.0.0%~99.9%,Ni的质量纯度为99.0.0%~99.9%,P的质量纯度为99.0.0%~99.9%。
本发明与背景技术相比,具有焊接接缝强度高,因熔点高具有良好的耐高温性,添加的Cu、Fe有效地抑制了钎料的流淌;适用于不锈钢的钎焊,特别是对汽车EGR不锈钢冷却器的钎焊具有优良的润湿性和间隙填充性,其钎焊构件的气密性、耐腐蚀性能、接缝强度均达到EGR不锈钢冷却器的技术要求。
附图说明
图1是传统的镍基钎料的XRD示意图。
图2是本发明镍基高温合金钎料的XRD示意图。
具体实施方式
下面通过实施例对本发明作进一步具体的说明,但本发明的保护范围并不限于此。
实施例1:一种镍基高温合金钎料,由下述重量百分比的组分组成:Cr5.0%~20.0%,Si 4.0%~10.0%,Fe 0.1%~3.0%,Cu 0.1%~10.0%,P 0.1%~3.0%,余量Ni。
所述镍基高温合金钎料的制备方法,包括如下步骤:将以下组分Cr、Si、Fe、Cu、P、Ni按比例混合,采用真空熔炼及气雾化、超声波筛分,将钎料制成240~600目的球形粉末状,最后用有机粘结剂将钎料粉末调制成膏状钎料。其中P是以Ni-P合金的形式与Cr、Si、Fe、Cu、Ni混合。
其中上述Cr的质量纯度为99.0.0%~99.9%,Si的质量纯度为99.0.0%~99.9%,Fe的质量纯度为99.0.0%~99.9%,Cu的质量纯度为99.0.0%~99.9%,Ni的质量纯度为99.0.0%~99.9%,P的质量纯度为99.0.0%~99.9%。
实施例2:本发明采用添加Cu和Fe元素来控制非需要结构Ni5P2和Ni2P的产生。因为Cu和Fe会与Ni进行竞争反应,形成相应的磷化物,进而减少Ni5P2和Ni2P的产生。实践表明,Cu和Fe含量低于0.1%达不到上述预期的作用,当Cu含量超过10.0%、Fe含量含量超过3.0%时,过多的Cu和Fe会导致其它问题的产生,如抗腐蚀性能的下降或者更容易被腐蚀。添加P元素可提高镍基钎料的抗氧化性能,降低钎料的产渣量。P含量低于0.1%时作用不明显,当P含量超过3.0%时,钎料的脆性增加,塑性降低。
本发明镍基高温合金钎料的综合焊接性能与传统的BNi-2、BNi-5的焊接性能对比如下表所示。
实施例3:参照图1和2。从XRD图中可以看出添加Cu、Fe元素后本发明制备的钎料中的Ni5P2和Ni2P相明显减少。
需要理解到的是:本实施例虽然对本发明作了比较详细的说明,但是这些说明,只是对本发明的简单说明,而不是对本发明的限制,任何不超出本发明实质精神内的发明创造,均落入本发明的保护范围内。
Claims (1)
1.一种镍基高温合金钎料,其特征是:所述镍基高温合金钎料由下述重量百分比的组分组成:Cr 5.0%~20.0%,Si 4.0%~10.0%,Fe 0.1%~3.0%,Cu 0.1%~10.0%,P 0.1%~3.0%,余量Ni。