CN102477165A - 一种非均匀介质基板的制备方法 - Google Patents

一种非均匀介质基板的制备方法 Download PDF

Info

Publication number
CN102477165A
CN102477165A CN2011102969726A CN201110296972A CN102477165A CN 102477165 A CN102477165 A CN 102477165A CN 2011102969726 A CN2011102969726 A CN 2011102969726A CN 201110296972 A CN201110296972 A CN 201110296972A CN 102477165 A CN102477165 A CN 102477165A
Authority
CN
China
Prior art keywords
preparation
liquid film
cold
head
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102969726A
Other languages
English (en)
Other versions
CN102477165B (zh
Inventor
刘若鹏
金曦
张影
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Guangqi Metamaterials Microelectronics Technology Co.,Ltd.
Original Assignee
Kuang Chi Institute of Advanced Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuang Chi Institute of Advanced Technology filed Critical Kuang Chi Institute of Advanced Technology
Priority to CN 201110296972 priority Critical patent/CN102477165B/zh
Publication of CN102477165A publication Critical patent/CN102477165A/zh
Application granted granted Critical
Publication of CN102477165B publication Critical patent/CN102477165B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明实施例提供了一种非均匀介质基板的制备方法，该制备方法包括：配置预设浓度的树脂溶液；将所述树脂溶液涂敷在无纺布的上表面，形成一层液膜；将上表面具有液膜的无纺布垂直悬挂在两个冷、热喷射头中间；开启冷、热喷射头，通过水蒸气带走所述液膜中可溶于水的有机溶剂；取下所述液膜，置于干燥烘箱干燥后获得非均匀介质基板。以降低非均匀介质基板的制备难度。

Description

一种非均匀介质基板的制备方法
【技术领域】
本发明涉及超材料基板的制造加工技术领域，特别涉及一种非均匀介质基板的制备方法。
【背景技术】
近年来，随着雷达探测、卫星通信、航空航天等高新技术的快速发展，以及抗电磁干扰、隐形技术、微波暗室等研究领域的兴起，微波吸收材料的研究越来越受到人们的重视。超材料可以现出非常奇妙的电磁效应，可用于吸波材料和隐形材料等领域，成为吸波材料领域研究的热点。
超材料的性质和功能主要来自于其内部的结构，如何精确制备具有周期排列的三维精细结构成为超材料制备技术的关键。超材料的加工过程主要是将带有金属微结构阵列的PCB基板叠层在一起，各层基板之间填充其他介质。但是传统的PCB基板大多为均匀介质基板，难以满足对介质基板电磁特性的需求。
【发明内容】
本发明所要解决的技术问题是提供一种非均匀多孔介质基板的制备方法，能够降低制备非均匀介质基板工艺流程的复杂度，提高制备效率。
为解决上述技术问题，本发明一实施例提供了一种非均匀介质基板的制备方法，其特征在于，该制备方法包括：
配置预设浓度的树脂溶液；
将所述树脂溶液涂敷在无纺布的上表面，形成一层液膜；
将上表面具有液膜的无纺布垂直悬挂在两个冷、热喷射头中间；
开启冷、热喷射头，通过水蒸气带走所述液膜中可溶于水的有机溶剂；
取下所述液膜，置于干燥烘箱干燥后获得非均匀介质基板。
与现有技术相比，上述技术方案具有以下优点：以无纺布作为支撑，将树脂溶液涂敷在表面形成液膜，然后在悬挂的液膜两侧同时用冷、热喷射头喷水，通过水蒸气带走液膜中可溶于水的有机溶剂，从而在液膜上形成孔，将该液膜干燥后获得具有多孔的非均匀介质基板，制备工艺简单。并且能够满足对介质基板电磁特性的需求。
【附图说明】
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其它的附图。
图1是本发明实施例一提供的一种非均匀介质基板的制备方法流程图；
图2是本发明实施例一提供的一种非均匀介质基板的制备方法流程图；
图3是本发明实施例一提供的一种非均匀介质基板的制备方法流程图；
图4是本发明实施例提供的一种非均匀介质基板的结构示意图。
【具体实施方式】
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例一、
参见图1，是本发明实施例一提供的一种非均匀介质基板的制备方法流程图，该制备方法包括：
S11：配置预设浓度的树脂溶液。
其中，该预设浓度的树脂溶液为聚砜(PSF/PSU)溶液；或者聚偏氟乙烯(PVDF)溶液。聚砜溶液的浓度为15-20％；聚偏氟乙烯溶液的浓度为20-25％。
S12：将树脂溶液涂敷在无纺布的上表面，形成一层液膜。
其中，该无纺布的形状为正方形或者长方形。
S13：将上表面具有液膜的无纺布垂直悬挂在两个冷、热喷射头中间。
S14：开启冷、热喷射头，通过水蒸气带走所述液膜中可溶于水的有机溶剂。一般情况下，冷、热喷射头的开启时间为5-10分钟。
S15：取下液膜，置于干燥烘箱干燥后获得非均匀介质基板。
其中，干燥烘箱的温度为40-60℃。
其中，获得的非均匀介质基板的介电常数在0.9-1.5之间；液膜的厚度在0.06-0.2mm之间；孔径的大小在60-900nm之间，在具体的实施过程中，根据对介质基板电磁特性的要求，选择对应的液膜厚度和孔径大小。
本实施例中，通过以无纺布作为支撑，将树脂溶液涂敷在表面形成液膜，然后通过水蒸气带走液膜中可溶于水的有机溶剂，从而在液膜上形成孔，将该液膜干燥后获得具有多孔的非均匀介质基板，制备工艺简单。并且能够满足对介质基板电磁特性的需求。
实施例二、
参见图2，是本发明实施例二提供的一种非均匀介质基板的制备方法流程图，该制备方法包括：
S21：配置浓度为17％的聚砜溶液。
S22：将浓度为17％的聚砜溶液涂敷在正方形无纺布的上表面，形成一层液膜。
S23：将上表面具有液膜的正方形无纺布垂直悬挂在两个冷、热喷射头中间。
S24：开启冷、热喷射头，调整冷、热喷射头的水蒸气喷出量，直到最后达到恒定喷速，喷淋10分钟。
其中，冷喷射头水蒸气喷出量大于热喷射头水蒸气喷射量。
S25：取下聚砜液膜，放入温度为60℃的鼓风干燥烘箱中进行烘干获得非均匀介质基板。
相对于实施例一，本实施例通过具体实例对本发明技术方案进行了详细描述。
实施例三、
参见图3，是本发明实施例三提供的一种非均匀介质基板的制备方法流程图，该制备方法包括：
S31：配置浓度为23％的聚偏氟乙烯溶液。
S32：将浓度为23％的聚偏氟乙烯溶液涂敷在长方形无纺布的上表面，形成一层液膜。
S33：将上表面具有液膜的长方形无纺布垂直悬挂在两个冷、热喷射头中间。
S34：开启冷、热喷射头，调整冷、热喷射头的水蒸气喷出量，直到最后达到恒定喷速，喷淋8分钟。在此过程中，水蒸气带走了液膜中的可溶于水的有机溶剂。
其中，冷喷射头水蒸气喷出量大于热喷射头水蒸气喷射量。
S35：取下聚偏氟乙烯液膜，放入温度为40℃的鼓风干燥烘箱中进行烘干获得非均匀介质基板。
相对于实施例一，本实施例通过具体实例对本发明技术方案进行了详细描述。在具体的实施过程中，根据实施一中列举的参数范围，还可以得出其他实施例，此处不再赘述。
采用上述实施例一至实施例三制备的非均匀介质基板如图4所示，非均匀介质基板41为两表面具有不同孔径的贯穿孔的多孔介质基板。
以上对本发明实施例进行了详细介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (10)

1.一种非均匀介质基板的制备方法，其特征在于，该制备方法包括：
配置预设浓度的树脂溶液；
将所述树脂溶液涂敷在无纺布的上表面，形成一层液膜；
将上表面具有液膜的无纺布垂直悬挂在两个冷、热喷射头中间；
开启冷、热喷射头，通过水蒸气带走所述液膜中可溶于水的有机溶剂；
取下所述液膜，置于干燥烘箱干燥后获得非均匀介质基板。
2.根据权利要求1所述的制备方法，其特征在于，所述树脂溶液为聚砜溶液或者聚偏氟乙烯溶液。
3.根据权利要求2所述的制备方法，其特征在于，所述聚砜溶液的浓度为15-20％。
4.根据权利要求2所述的制备方法，其特征在于，所述聚偏氟乙烯溶液的浓度为20-25％。
5.根据权利要求1所述的制备方法，其特征在于，所述无纺布的形状为正方形或者长方形。
6.根据权利要求1所述的制备方法，其特征在于，所述冷、热喷射头的开启时间为5-10分钟。
7.根据权利要求1所述的制备方法，其特征在于，所述干燥烘箱为鼓风干燥烘箱。
8.根据权利要求1或者7所述的制备方法，其特征在于，所述干燥烘箱的温度为40-60℃。
9.根据权利要求1所述的制备方法，其特征在于，开启冷、热喷射头之后，还包括：调整冷、热喷射头的水蒸气喷出量。
10.根据权利要求1或者9所述的制备方法，其特征在于，所述冷喷射头水蒸气喷出量大于热喷射头水蒸气喷射量。
CN 201110296972 2011-09-30 2011-09-30 一种非均匀介质基板的制备方法 Active CN102477165B (zh)