CN102473017B - 用于层压光伏模块的方法和系统 - Google Patents
用于层压光伏模块的方法和系统 Download PDFInfo
- Publication number
- CN102473017B CN102473017B CN201080035774.8A CN201080035774A CN102473017B CN 102473017 B CN102473017 B CN 102473017B CN 201080035774 A CN201080035774 A CN 201080035774A CN 102473017 B CN102473017 B CN 102473017B
- Authority
- CN
- China
- Prior art keywords
- intermediate layer
- substrate
- roll
- systems
- infrared radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
用于层压光伏模块的方法可以包括以下步骤：将中间层放置成与基底接触；用红外辐射源加热中间层；以及在真空层压机中将中间层和基底按压到一起。
Description
要求优先权
本申请要求按照35 U.S.C.§119(e)于2009年8月10日提交的序列号为61/232,766的美国临时专利申请的优先权，该申请通过引用包含于此。
技术领域
本发明涉及光伏模块及制造方法。
背景技术
光伏模块可以包括沉积在基底上的半导体材料，例如，具有用作窗口层的第一层和用作吸收层的第二层。半导体窗口层可以允许太阳辐射穿透到诸如碲化镉层的吸收层，吸收层将太阳能转换成电。光伏模块也可以包含一个或多个透明导电氧化物层，该一个或多个透明导电氧化物层通常也是电荷的导体。
发明内容
本发明的一方面提供了一种用于层压光伏模块的方法，该方法包括以下步骤：将中间层放置成与基底接触；用红外辐射源加热中间层和基底；以及将中间层和基底按压到一起。
本发明的另一方面提供给了一种用于层压光伏模块的系统，该系统包括：中间层，与基底接触；红外辐射加热器，被构造成加热与基底接触的中间层；以及按压机，被构造成促使中间层和基底在一起。
附图说明
图1是光伏模块的示意图。
图2是光伏模块的示意图。
图3是光伏模块的示意图。
图4是用于层压光伏模块的系统的示意图。
图5是用于层压光伏模块的系统的示意图。
图6是用于层压光伏模块的系统的示意图。
具体实施方式
光伏模块可以包括与基底相邻的透明导电氧化物层和半导体材料层。半导体材料层可以包括双层，所述双层可以包括n型半导体窗口层和p型半导体吸收层。n型窗口层和p型吸收层可以彼此接触地定位以产生电场。光子在与n型窗口层接触时可以使电子-空穴对自由，将电子输送至n侧并将空穴输送至p侧。电子可以通过外部电流通路流回至p侧。得到的电子流提供电流，与由电场导致的电压结合产生电力。结果是光子能向电能的转换。为了保持并提高装置性能，除半导体窗口层和吸收层之外，还可以将许多层设置在基底上方。
光伏模块可以形成在诸如玻璃的光学透明基底上。由于玻璃不导电，所以通常在基底和半导体双层之间沉积透明导电氧化物(TCO)层。锡酸镉的该性能优异，这是由于锡酸镉表现出高的光传输和低的薄层电阻。可以在TCO层和半导体窗口层之间沉积平坦的缓冲层，以减少在半导体窗口层的形成过程中发生不规则的可能。此外，在基底和TCO层之间可以包括阻挡层，以减少会导致劣化和分层的钠或其他污染物从基底向半导体层的扩散。阻挡层可以是透明、热稳定、具有较少的针孔和具有高的钠阻挡性能以及优异的粘附性能。因此，TCO可以是可以包括例如二氧化硅阻挡层、锡酸镉TCO层和缓冲层(例如，氧化锡(Ⅳ))的三层堆叠的一部分。缓冲层可以包括各种合适的材料，包括氧化锡、氧化锌锡、氧化锌和氧化镁锌。光伏模块可以包括沉积在TCO堆叠上的硫化镉窗口层和沉积在硫化镉层上的碲化镉吸收层。碲化镉光伏模块与其他光伏技术相比提供了若干优点。在这些优点中包括在阴天和光扩散条件下的优异光吸收性能以及易于制造。
可以通过被设计成在各种条件下将模块密封并包裹在一起长达多年的材料来将碲化镉薄膜层包封在模块内。包封材料可以通过形成将镉和/或其他重金属固定、螯合、吸收和/或稳固在模块的结构内以助于处理和解决的低溶解性化合物来帮助保留存在于模块内的重金属。
在一个方面，一种用于层压光伏模块的方法可以包括以下步骤：将中间层放置成与基底接触；用红外辐射源加热中间层和基底；以及将中间层和基底按压到一起。
该方法可以包括各种可选特征。例如，基底可以包括玻璃。玻璃可以是钠钙玻璃。将中间层和基底按压到一起的步骤可以包括使用真空层压机。可以在用红外辐射源加热中间层和基底的步骤发生之前将中间层放置成与基底接触。可以在用红外辐射源加热中间层和基底的步骤发生之后将中间层放置成与基底接触。用红外辐射源加热中间层和基底的步骤可以发生在将中间层放置成与基底接触之前和之后。中间层可以包括热塑性中间层。热塑性中间层可以包括丙烯腈-丁二烯-苯乙烯(ABS)、丙烯酸化物(PMMA)、赛璐珞、醋酸纤维素、环烯烃共聚物(COC)、聚乙烯醇缩丁醛(PVB)、硅树脂、环氧树脂、乙烯乙酸乙烯酯(EVA)、乙烯乙烯醇(EVOH)、氟塑料(PTFE)、离子交联聚合物、KYDEX、液晶聚合物(LCP)、聚甲醛(POM)、聚丙烯酸酯、聚丙烯腈(PAN)、聚酰胺(PA)、聚酰胺-酰亚胺(PAI)、聚芳醚酮(PAEK)、聚丁二烯(PBD)、聚丁烯(PB)、聚对苯二甲酸丁二酯(PBT)、聚己酸内酯(PCL)、聚三氟氯乙烯(PCTFE)、聚对苯二甲酸乙二酯(PET)、聚对苯二甲酸二甲基环己酯(PCT)、聚碳酸酯(PC)、聚羟基烷基酸酯(PHA)、聚酮(PK)、聚酯、聚乙烯(PE)、聚醚醚酮(PEEK)、聚醚酮酮(PEKK)、聚醚酰亚胺(PEI)、聚醚砜(PES)、氯化聚乙烯(PEC)、聚酰亚胺(PI)、聚乳酸(PLA)、聚甲基戊烯(PMP)、聚苯醚(PPO)、聚苯硫醚(PPS)、聚邻苯二甲酰胺(PPA)、聚丙烯(PP)、聚苯乙烯(PS)、聚砜(PSU)、聚对苯二甲酸丙二醇酯(PTT)、聚氨酯(PU)、聚醋酸乙烯酯(PVA)、聚氯乙烯(PVA)、聚偏二氯乙烯(PVDC)或苯乙烯-丙烯腈(SAN)或任何其他合适材料或它们的任何组合。在某些实施例中，热塑性中间层可以包括乙烯乙酸乙烯酯(EVA)、聚乙烯醇缩丁醛(PVB)、硅树脂或环氧树脂。
在某些实施例中，该方法可以包括发生在将中间层和基底按压到一起的步骤之前的用红外辐射源加热中间层和基底的步骤。在某些实施例中，该方法可以包括发生在将中间层和基底按压到一起的步骤之后的用红外辐射源加热中间层和基底的步骤。在某些实施例中，该方法可以包括发生在将中间层和基底按压到一起的步骤之前和之后的用红外辐射源加热中间层和基底的步骤。该方法还可以包括使中间层和基底经历至少一个轧辊。在某些实施例中，该方法可以包括在将中间层和基底按压到一起的步骤之前使中间层和基底经历至少一个轧辊的步骤。在某些实施例中，该方法可以包括在将中间层和基底按压到一起的步骤之后使中间层和基底经历至少一个轧辊的步骤。该方法可以包括在将中间层和基底按压到一起的步骤之前和之后使基底的层经历至少一个轧辊的步骤。在某些实施例中，该方法可以包括在用红外辐射源加热中间层和基底的步骤之前使中间层和基底经历至少一个轧辊的步骤。在某些实施例中，该方法可以包括在用红外辐射源加热中间层和基底的步骤之后使中间层和基底经历至少一个轧辊的步骤。在某些实施例中，该方法可以包括在用红外辐射源加热中间层和基底的步骤之前和之后使中间层和基底经历至少一个轧辊的步骤。在某些实施例中，该方法可以包括在使中间层和基底经历至少一个轧辊的步骤之前和之后发生的用红外辐射源加热中间层和基底的步骤。该方法可以包括用红外辐射源加热中间层和基底的步骤、将中间层和基底按压到一起的步骤以及使中间层和基底经历至少一个轧辊的步骤的任何组合。
在另一方面，一种用于层压光伏模块的系统可以包括：IR加热器，被构造成加热与基底接触的中间层；以及按压机，被构造成促使中间层和基底在一起。
该系统可以包括各种可选特征。例如，基底可以包括玻璃。玻璃可以是钠钙玻璃。被构造成促使中间层和基底在一起的按压机可以包括真空层压机。可以在使用被构造成加热中间层和基底的IR加热器之前将中间层放置成与基底接触。可以在使用被构造成加热中间层和基底的IR加热器之后将中间层放置成与基底接触。可以在将中间层放置成与基底接触之前和之后使用被构造成加热中间层和基底的IR加热器。中间层可以包括热塑性中间层。热塑性中间层可以包括丙烯腈-丁二烯-苯乙烯(ABS)、丙烯酸化物(PMMA)、赛璐珞、醋酸纤维素、环烯烃共聚物(COC)、聚乙烯醇缩丁醛(PVB)、硅树脂、环氧树脂、乙烯乙酸乙烯酯(EVA)、乙烯乙烯醇(EVOH)、氟塑料(PTFE)、离子交联聚合物、KYDEX、液晶聚合物(LCP)、聚甲醛(POM)、聚丙烯酸酯、聚丙烯腈(PAN)、聚酰胺(PA)、聚酰胺-酰亚胺(PAI)、聚芳醚酮(PAEK)、聚丁二烯(PBD)、聚丁烯(PB)、聚对苯二甲酸丁二酯(PBT)、聚己酸内酯(PCL)、聚三氟氯乙烯(PCTFE)、聚对苯二甲酸乙二酯(PET)、聚对苯二甲酸二甲基环己酯(PCT)、聚碳酸酯(PC)、聚羟基烷基酸酯(PHA)、聚酮(PK)、聚酯、聚乙烯(PE)、聚醚醚酮(PEEK)、聚醚酮酮(PEKK)、聚醚酰亚胺(PEI)、聚醚砜(PES)、氯化聚乙烯(PEC)、聚酰亚胺(PI)、聚乳酸(PLA)、聚甲基戊烯(PMP)、聚苯醚(PPO)、聚苯硫醚(PPS)、聚邻苯二甲酰胺(PPA)、聚丙烯(PP)、聚苯乙烯(PS)、聚砜(PSU)、聚对苯二甲酸丙二醇酯(PTT)、聚氨酯(PU)、聚醋酸乙烯酯(PVA)、聚氯乙烯(PVA)、聚偏二氯乙烯(PVDC)或苯乙烯-丙烯腈(SAN)或任何其他合适材料或它们的任何组合。在某些实施例中，热塑性中间层可以包括乙烯乙酸乙烯酯(EVA)、聚乙烯醇缩丁醛(PVB)、硅树脂或环氧树脂。
在某些实施例中，系统可以包括在中间层接触基底之前使用被构造成加热中间层的IR加热器。在某些实施例中，系统可以包括在中间层接触基底之后使用被构造成加热中间层的IR加热器。在某些实施例中，系统可以包括在中间层接触基底之前和之后使用被构造成加热中间层的IR加热器。在某些实施例中，系统可以包括被构造成在按压之前促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括被构造成在按压之后促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括被构造成在按压之前和之后促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括被构造成在IR加热器之前促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括被构造成在IR加热器之后促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括被构造成在IR加热器之前和之后促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊。在某些实施例中，系统可以包括在被构造成促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊之前和之后的IR加热器。系统可以包括被构造成加热与基底接触的中间层的IR加热器、被构造成促使中间层和基底在一起的按压机和被构造成促使中间层和基底在一起的用来处理中间层和基底的至少一个轧辊中的任何组合。
参照图1，自修复光伏模块101可以包括前基底100。前基底100可以包括任何合适的材料，合适的材料包括例如钠钙玻璃的玻璃。可以与前基底100相邻地沉积一个或多个层110，前基底100可以用作在其顶部上可以添加各种层的第一基底。层110可以包括一个或多个装置层。例如，层110可以包括与硫化镉窗口层相邻的碲化镉吸收层。层110可以包括与碲化镉吸收层相邻的附加金属层。可以与层110相邻地沉积一层或多层金属固定剂。例如，可以与层110相邻地沉积金属固定剂120。
可以从光伏模块的边缘将半导体材料和其他涂层的一部分除去，光伏模块可以包括一串连接的光伏装置。例如，工业上的需求要求光伏模块在它们的周围附近保持最小的不导电宽度。将涂层从光伏模块除去的传统方法需要使用机械刷。虽然刷子足以将不想要的材料除去，但刷子易于磨损，导致许多问题，包括涂层除去工艺中的不均匀、用于维修的停工期和重复产生替换成本。可选择的是，完全放弃使用机械刷而使用激光刻划来光学除去不期望的材料。由于光学模块可以包含玻璃基底，所以激光能够透过基底层穿透光伏结构，从而将另一侧上的不期望的涂层除去。参照图2，已通过机械方法将层110和层120的一部分从光伏装置101除去，机械方法可以包括激光刻划。
参照图3，光伏模块101可以包括与层110和层120接触的一个或多个中间层138。光伏模块101还可以包括背基底130。背基底130可以包括任何合适的材料，合适的材料包括例如钠钙玻璃的玻璃。可以在设置中间层138之后将背基底130设置到光伏模块101。可选择地，可以在设置中间层138之前将背基底130设置到光伏模块101。
可以通过层压工艺将光伏模块101的层对准、加热并结合到一起。层压将光伏模块101的半导体层、TCO、金属导体和任何其他层包封，使光伏装置密封而与环境隔离。可以通过层压工艺将前基底100和背基底130与中间层138结合到一起。中间层可以包括热塑性中间层。热塑性中间层可以包括丙烯腈-丁二烯-苯乙烯(ABS)、丙烯酸化物(PMMA)、赛璐珞、醋酸纤维素、环烯烃共聚物(COC)、聚乙烯醇缩丁醛(PVB)、硅树脂、环氧树脂、乙烯乙酸乙烯酯(EVA)、乙烯乙烯醇(EVOH)、氟塑料(PTFE)、离子交联聚合物、KYDEX、液晶聚合物(LCP)、聚甲醛(POM)、聚丙烯酸酯、聚丙烯腈(PAN)、聚酰胺(PA)、聚酰胺-酰亚胺(PAI)、聚芳醚酮(PAEK)、聚丁二烯(PBD)、聚丁烯(PB)、聚对苯二甲酸丁二酯(PBT)、聚己酸内酯(PCL)、聚三氟氯乙烯(PCTFE)、聚对苯二甲酸乙二酯(PET)、聚对苯二甲酸二甲基环己酯(PCT)、聚碳酸酯(PC)、聚羟基烷基酸酯(PHA)、聚酮(PK)、聚酯、聚乙烯(PE)、聚醚醚酮(PEEK)、聚醚酮酮(PEKK)、聚醚酰亚胺(PEI)、聚醚砜(PES)、氯化聚乙烯(PEC)、聚酰亚胺(PI)、聚乳酸(PLA)、聚甲基戊烯(PMP)、聚苯醚(PPO)、聚苯硫醚(PPS)、聚邻苯二甲酰胺(PPA)、聚丙烯(PP)、聚苯乙烯(PS)、聚砜(PSU)、聚对苯二甲酸丙二醇酯(PTT)、聚氨酯(PU)、聚醋酸乙烯酯(PVA)、聚氯乙烯(PVA)、聚偏二氯乙烯(PVDC)或苯乙烯-丙烯腈(SAN)或任何其他合适材料或它们的任何组合。在某些实施例中，热塑性中间层可以包括乙烯乙酸乙烯酯(EVA)、聚乙烯醇缩丁醛(PVB)、硅树脂或环氧树脂。
参照图4，可以将光伏模块101的前基底100、背基底130和中间层138按压到一起。按压前基底100、背基底130和中间层138的工具可以包括真空层压机。真空层压机通过由真空层压机的面对前基底100的底部加热板220加热来处理真空室内的光伏模块，同时真空层压机的顶部板210和底部板220将前基底100和背基底130按压到一起。通过该工艺，中间层138会熔化，从而流动、填充在间隙内并固化。
参照图5，除了在层压工艺中在真空层压机200内进行处理之外，可以用红外辐射(IR)源300来加热光伏模块101。可以在将中间层138设置到光伏装置101之前使用IR加热器300。可以在将中间层138设置到光伏装置101之后使用IR加热器300。可以在将中间层138设置到光伏装置101之前和之后使用IR加热器300。可以在真空层压机200内对光伏模块101处理之前使用IR加热器300对光伏模块进行预加热。可以在层压机200内对光伏模块101处理之后使用IR加热器300对光伏模块的中间层进行连续加热和固化。可以在层压机200内对光伏模块101处理之前和之后都使用IR加热器300对模块进行预加热并对中间层进行连续加热和固化。在光伏模块101的层压过程中可以多次使用IR加热器。
参照图6，除了IR加热器300和在真空层压机200内对光伏模块101进行处理之外，还可以使光伏模块101经历被构造成促使中间层和基底在一起的至少一个轧辊400。可以在真空层压机200内对光伏模块101处理之前使用轧辊400对光伏模块101除气。可以在真空层压机200内对光伏模块101处理之后使用轧辊400来将压力施加到光伏模块101上并改善中间层138的流动。可以在真空层压机200内对光伏模块101处理之前和之后都使用轧辊400来对光伏模块101除气以及将压力施加到光伏模块101上并改善中间层138的流动。也可以在使用IR加热器300之前使用、在使用IR加热器300之后使用或者在使用IR加热器300之前和之后都使用轧辊400。可以在使用轧辊400之前使用、在使用轧辊400之后使用或者在使用轧辊400之前和之后都使用IR加热器300。在光伏模块101的层压过程中可以多次使用轧辊400。可以以任何可能的组合和排列使用轧辊、IR加热器和真空层压机内处理来用于光伏模块的层压。
使用在此公开的方法制造的光伏模块可以包括在一个或多个光伏阵列中。该阵列可以包括在用于发电的各种系统中。例如，可以用光束照射光伏模块来产生光电流。可以收集光电流，将光电流从直流(DC)转换成交流(AC)并分配到电网。可以将任何合适波长的光引导到模块来产生光电流，包括例如大于400nm的光或小于700nm的光(例如，紫外光)。由一个光伏模块产生的光电流可以与由其他光伏模块产生的光电流结合。例如，光伏模块可以是光伏阵列的一部分，可以管理并分配来自光伏阵列的汇总电流。
通过解释和示例的方式给出了上述实施例。应该理解的是，可以在某些方面改变上面提供的示例，并且改变的示例仍在权利要求的范围内。应该意识到，虽然已参照上面优选实施例描述了本发明，但其他实施例在权利要求的范围内。
Claims (26)
1.一种用于层压光伏模块的方法，所述方法包括以下步骤：
将中间层放置成与基底接触；
用位于真空层压机内的红外辐射源加热中间层和基底；以及
在加热的同时，使用真空层压机将中间层和基底按压到一起。
2.如权利要求1所述的方法，其中，基底包括玻璃。
3.如权利要求2所述的方法，其中，玻璃是钠钙玻璃。
4.如权利要求1所述的方法，其中，所述将中间层放置成与基底接触的步骤发生在所述用红外辐射源加热中间层和基底的步骤之前。
5.如权利要求1所述的方法，其中，中间层包括热塑性中间层。
6.如权利要求5所述的方法，其中，热塑性中间层包括丙烯腈-丁二烯-苯乙烯、丙烯酸化物、赛璐珞、醋酸纤维素、环烯烃共聚物、聚乙烯醇缩丁醛、硅树脂、环氧树脂、乙烯乙酸乙烯酯、乙烯乙烯醇、氟塑料、离子交联聚合物、液晶聚合物、聚甲醛、聚丙烯酸酯、聚丙烯腈、聚酰胺、聚酰胺-酰亚胺、聚芳醚酮、聚丁二烯、聚丁烯、聚对苯二甲酸丁二酯、聚己酸内酯、聚三氟氯乙烯、聚对苯二甲酸乙二酯、聚对苯二甲酸二甲基环己酯、聚碳酸酯、聚羟基烷基酸酯、聚酮、聚酯、聚乙烯、聚醚醚酮、聚醚酮酮、聚醚酰亚胺、聚醚砜、氯化聚乙烯、聚酰亚胺、聚乳酸、聚甲基戊烯、聚苯醚、聚苯硫醚、聚邻苯二甲酰胺、聚丙烯、聚苯乙烯、聚砜、聚对苯二甲酸丙二醇酯、聚氨酯、聚醋酸乙烯酯、聚氯乙烯、聚偏二氯乙烯或苯乙烯-丙烯腈或它们的任何组合。
7.如权利要求6所述的方法，其中，所述热塑性中间层包括乙烯乙酸乙烯酯、聚乙烯醇缩丁醛、硅树脂或环氧树脂。
8.如权利要求1所述的方法，所述方法还包括使中间层和基底经历至少一个轧辊。
9.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述将中间层和基底按压到一起的步骤之前。
10.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述将中间层和基底按压到一起的步骤之后。
11.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述将中间层和基底按压到一起的步骤之前和之后。
12.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述用红外辐射源加热中间层和基底的步骤之前。
13.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述用红外辐射源加热中间层和基底的步骤之后。
14.如权利要求8所述的方法，其中，所述使中间层和基底经历至少一个轧辊的步骤发生在所述用红外辐射源加热中间层和基底的步骤之前和之后。
15.如权利要求8所述的方法，其中，所述用红外辐射源加热中间层和基底的步骤以及将中间层和基底按压到一起的步骤发生在所述使中间层和基底经历至少一个轧辊的步骤之前和之后。
16.一种用于层压光伏模块的系统，所述系统包括：
中间层，与基底接触；
红外辐射加热器，位于真空层压机内并被构造成加热与基底接触的中间层；以及
真空层压机，被构造成在加热的同时促使中间层和基底在一起。
17.如权利要求16所述的系统，其中，基底包括玻璃。
18.如权利要求17所述的系统，其中，玻璃是钠钙玻璃。
19.如权利要求16所述的系统，其中，红外辐射加热器被构造成在中间层接触基底之后加热中间层。
20.如权利要求16所述的系统，其中，中间层包括热塑性中间层。
21.如权利要求20所述的系统，其中，热塑性中间层包括丙烯腈-丁二烯-苯乙烯、丙烯酸化物、赛璐珞、醋酸纤维素、环烯烃共聚物、聚乙烯醇缩丁醛、硅树脂、环氧树脂、乙烯乙酸乙烯酯、乙烯乙烯醇、氟塑料、离子交联聚合物、液晶聚合物、聚甲醛、聚丙烯酸酯、聚丙烯腈、聚酰胺、聚酰胺-酰亚胺、聚芳醚酮、聚丁二烯、聚丁烯、聚对苯二甲酸丁二酯、聚己酸内酯、聚三氟氯乙烯、聚对苯二甲酸乙二酯、聚对苯二甲酸二甲基环己酯、聚碳酸酯、聚羟基烷基酸酯、聚酮、聚酯、聚乙烯、聚醚醚酮、聚醚酮酮、聚醚酰亚胺、聚醚砜、氯化聚乙烯、聚酰亚胺、聚乳酸、聚甲基戊烯、聚苯醚、聚苯硫醚、聚邻苯二甲酰胺、聚丙烯、聚苯乙烯、聚砜、聚对苯二甲酸丙二醇酯、聚氨酯、聚醋酸乙烯酯、聚氯乙烯、聚偏二氯乙烯或苯乙烯-丙烯腈或它们的任何组合。
22.如权利要求21所述的系统，其中，所述热塑性中间层包括乙烯乙酸乙烯酯、聚乙烯醇缩丁醛、硅树脂或环氧树脂。
23.如权利要求16所述的系统，所述系统还包括处理中间层和基底的至少一个轧辊。
24.如权利要求23所述的系统，其中，处理中间层和基底的至少一个轧辊被构造成在真空层压机之前促使中间层和基底在一起。
25.如权利要求23所述的系统，其中，处理中间层和基底的至少一个轧辊被构造成在真空层压机之后促使中间层和基底在一起。
26.如权利要求23所述的系统，其中，处理中间层和基底的至少一个轧辊被构造成在真空层压机之前和之后促使中间层和基底在一起。