CN102464905A - Workpiece antirust emulsion - Google Patents
Workpiece antirust emulsion Download PDFInfo
- Publication number
- CN102464905A CN102464905A CN2010105417287A CN201010541728A CN102464905A CN 102464905 A CN102464905 A CN 102464905A CN 2010105417287 A CN2010105417287 A CN 2010105417287A CN 201010541728 A CN201010541728 A CN 201010541728A CN 102464905 A CN102464905 A CN 102464905A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- paraffin
- oleic acid
- trolamine
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a workpiece antirust emulsion, comprising the following ingredients: 14-18 wt% of oleic acid, 3-8 wt% of polyvinyl alcohol, 4-8 wt% of barium petroleum sulfonate, 2-5 wt% of paraffin, 2-4 wt% of triethanolamine, 1-2 wt% of alkylphenol polyoxyethylene, and the balance consisting of water. The workpiece antirust emulsion has the advantages of no toxicity, no smell, no oil stain leakage, and good cleaning effect.
Description
Technical field:
The present invention relates to a kind of field of chemicals, particularly a kind of workpiece rust preventing emulsion.
Background technology:
Generally all need remove paint, immersion oil behind the workpiece bonderizing, but after the immersion oil processing, the very easy absorption dust of the oil film of surface attachment forms uneven stain, influences apparent mass.In addition, oil film is difficult for dry, even if dispose unnecessary oil droplet by hand, also has oil later on and oozes out.For example, the clutch component of automobile-use is handled through the phosphatization immersion oil, though wipe surperficial oil stain by hand, after the assembling, still has oil stain around the rivet, and oil is as being seeped on the asbestos friction sheet, and during use, the rule of can skidding resemble.Therefore the existence of oil stain directly influences the functional quality of product.
Summary of the invention:
Be to solve the deficiency of prior art, the invention provides a kind of nontoxicly, tasteless, adopt the oiliness inhibiter that rust inhibition is arranged, the workpiece that makes immersion liquid is because moisture evaporation and very fast dry, the workpiece rust preventing emulsion that no oil stain oozes out.
The present invention is achieved in that the workpiece rust preventing emulsion, its prescription (weight percent) as follows: oleic acid 14-18%, Z 150PH, 3-8%; Barium mahogany sulfonate, 4-8%; Paraffin, 2-5%; Trolamine, 2-4%; TX10,1-2%; Surplus is a water.
A kind of workpiece rust preventing emulsion, its prescription (weight percent) be as follows: oleic acid 15.5%, Z 150PH, 5.0%; Barium mahogany sulfonate, 6.0%; Paraffin, 3.0%; Trolamine, 2.5%; TX10,1.2%; Surplus is a water.
A kind of workpiece rust preventing emulsion, its prescription (weight percent) be as follows: oleic acid 14.0%, Z 150PH, 3.0%; Barium mahogany sulfonate, 4.0%; Paraffin, 2.0%; Trolamine, 2.0%; TX10,1.0%; Surplus is a water.
A kind of workpiece rust preventing emulsion, its prescription (weight percent) be as follows: oleic acid 18.0%, Z 150PH, 8.0%; Barium mahogany sulfonate, 8.0%; Paraffin, 5.0%; Trolamine, 4.0%; TX10,2.0%; Surplus is a water.
The effect of major ingredient is following among the present invention:
TX10 is in the present invention as emulsifying agent; Trolamine is in the present invention as emulsifying agent; Z 150PH is in the present invention as tackiness agent; Paraffin is used as the solubility promoter of oleic acid and barium mahogany sulfonate in the present invention; Oleic acid is effective constituent of the present invention; Barium mahogany sulfonate is in the present invention as the oiliness inhibiter.
Preparation of the present invention and method of use are:
One, materials such as paraffin, oleic acid and barium mahogany sulfonate are placed container, constantly stirring is fully dissolved each other material under 70 ℃ of temperature.Add trolamine and TX10 then, continue to be stirred to the even dope of formation.
Two, Z 150PH is added in the entry constantly to stir down in 90 ℃ make it be dissolved into clear solution.After being cooled to 40～50 ℃, this solution is added in the above-mentioned material under constantly stirring, just can make milky emulsion.
During use with this emulsion dip-coating, brush or be sprayed on the workpiece and get final product.
The present invention is nontoxic, tasteless, adopts the oiliness inhibiter that rust inhibition is arranged, make immersion liquid workpiece since moisture evaporation and very fast dry, no oil stain oozes out phenomenon, makes the workpiece after the immersion liquid can meet the dipping lacquer requirement.
The present invention compared with prior art has the following advantages: nontoxic, tasteless, no oil stain oozes out, cleaning performance is good.
Embodiment:
Below in conjunction with embodiment, the present invention is made further detailed description, but does not constitute any restriction of the present invention:
Embodiment one: a kind of workpiece rust preventing emulsion, its prescription (weight percent) as follows: oleic acid 15.5%, Z 150PH, 5.0%; Barium mahogany sulfonate, 6.0%; Paraffin, 3.0%; Trolamine, 2.5%; TX10,1.2%; Surplus is a water.
Embodiment two: a kind of workpiece rust preventing emulsion, its prescription (weight percent) as follows: oleic acid 14.0%, Z 150PH, 3.0%; Barium mahogany sulfonate, 4.0%; Paraffin, 2.0%; Trolamine, 2.0%; TX10,1.0%; Surplus is a water.
Embodiment three: a kind of workpiece rust preventing emulsion, its prescription (weight percent) as follows: oleic acid 18.0%, Z 150PH, 8.0%; Barium mahogany sulfonate, 8.0%; Paraffin, 5.0%; Trolamine, 4.0%; TX10,2.0%; Surplus is a water.
Claims (4)
1. the workpiece rust preventing emulsion is characterized in that, its prescription (weight percent) as follows: oleic acid 14-18%, Z 150PH, 3-8%; Barium mahogany sulfonate, 4-8%; Paraffin, 2-5%; Trolamine, 2-4%; TX10,1-2%; Surplus is a water.
2. a kind of workpiece rust preventing emulsion according to claim 1 is characterized in that, its prescription (weight percent) as follows: oleic acid 15.5%, Z 150PH, 5.0%; Barium mahogany sulfonate, 6.0%; Paraffin, 3.0%; Trolamine, 2.5%; TX10,1.2%; Surplus is a water.
3. a kind of workpiece rust preventing emulsion according to claim 1 is characterized in that, its prescription (weight percent) as follows: oleic acid 14.0%, Z 150PH, 3.0%; Barium mahogany sulfonate, 4.0%; Paraffin, 2.0%; Trolamine, 2.0%; TX10,1.0%; Surplus is a water.
4. a kind of workpiece rust preventing emulsion according to claim 1 is characterized in that, its prescription (weight percent) as follows: oleic acid 18.0%, Z 150PH, 8.0%; Barium mahogany sulfonate, 8.0%; Paraffin, 5.0%; Trolamine, 4.0%; TX10,2.0%; Surplus is a water.