CN102454106B - 硬挺剂及其生产方法 - Google Patents

硬挺剂及其生产方法 Download PDF

Info

Publication number
CN102454106B
CN102454106B CN201010511287.6A CN201010511287A CN102454106B CN 102454106 B CN102454106 B CN 102454106B CN 201010511287 A CN201010511287 A CN 201010511287A CN 102454106 B CN102454106 B CN 102454106B
Authority
CN
China
Prior art keywords
add
stiffening agent
acetate emulsion
adds
total amount
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201010511287.6A
Other languages
English (en)
Other versions
CN102454106A (zh
Inventor
朱国华
王海峰
管永华
施达本
卢海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong C&T Textile Technology Co., Ltd.
Original Assignee
NANTONG C&T TEXTILE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG C&T TEXTILE TECHNOLOGY Co Ltd filed Critical NANTONG C&T TEXTILE TECHNOLOGY Co Ltd
Priority to CN201010511287.6A priority Critical patent/CN102454106B/zh
Publication of CN102454106A publication Critical patent/CN102454106A/zh
Application granted granted Critical
Publication of CN102454106B publication Critical patent/CN102454106B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种硬挺剂及其生产方法，产品由40％聚醋酸乙烯乳液、可溶性淀粉、明胶、去离子水组成。本发明的优点：赋予织物挺括、厚实的手感，并可防止针织物卷曲；整理织物不易发生吸湿回软，且具一定的耐洗性能；能最大限度地保持纺织物的强力；可防止织物的滑移现象发生；能与绝大多数整理药剂同浴使用。

Description

硬挺剂及其生产方法
技术领域：
本发明涉及一种硬挺剂及其生产方法。
背景技术：
现有的硬挺剂配方不合理，工作效果不理想。
发明内容：
本发明的目的在于提供一种配方合理，工作效果好的硬挺剂及其生产方法。
本发明的技术解决方案是：
一种硬挺剂，其特征是：由下列重量百分比的成分组成：
40％聚醋酸乙烯乳液50-60％
可溶性淀粉：3-5％
明胶：5-10％
去离子水：余量；
其中醋酸乙烯乳液由下列重量百分比的成分组成：
醋酸乙烯：15～25
苯乙烯：3-5
乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂：0.5～3
过硫酸钾：0.05～0.5
聚乙烯醇(1799)：10～30
水：余量。
所述的硬挺剂的生产方法，其特征是：包括：
(1)醋酸乙烯乳液的制备：
聚乙烯醇的溶解及过滤：将聚乙烯醇加入到水中，升温至85-90℃搅拌2小时以上至溶解；过滤后加入到反应釜中，然后加入乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂，搅拌5分钟，加入醋酸乙烯和苯乙烯总量的15％和过硫酸钾水溶液总量的45％，其中过硫酸钾事先用冷的蒸馏水溶解；加热升温，待温度升至60-65℃时停止加热，在66℃时开始回流，待温度自升至80-83℃且回流减少时，开始滴加醋酸乙烯单体，单体以每小时加入其总量的10-15％左右速度均匀加入，控制6-8小时加完；与此同时，引发剂过硫酸钾水溶液以每小时加入总量4-5％的速度加入，反应温度控制t＝78-82℃。加完单体后，加入剩余的引发剂；因放热反应而使体系温度升至90-95℃，保温90-95℃反应30分钟，加入剩余量的水，搅拌降温，降温至40℃以下，关搅拌，过滤出料；得醋酸乙烯乳液；
(2)将醋酸乙烯乳液稀释成45％质量浓度，然后与可溶性淀粉、明胶、去离子水混合得到硬挺剂。
本发明特点：
(1)高分子聚合物，优异的成膜性
(2)大分子中不含有水溶性基团
(3)极佳的增加强力效果
(4)优良的纱线抱合性能
(5)极佳的相容性，且不影响整理织物的色光
本发明的优点还在于：
(1)赋予织物挺括、厚实的手感，并可防止针织物卷曲
(2)整理织物不易发生吸湿回软，且具一定的耐洗性能
(3)能最大限度地保持纺织物的强力
(4)可防止织物的滑移现象发生
(5)能与绝大多数整理药剂同浴使用
下面结合实施例对本发明作进一步说明。
具体实施方式：
一种硬挺剂，由下列重量百分比的成分组成：
40％聚醋酸乙烯乳液50-60％(例50％、55％、60％)
可溶性淀粉：3-5％(例3％、4％、5％)
明胶：5-10％(例5％、8％、10％)
去离子水：余量；
其中醋酸乙烯乳液由下列重量百分比的成分组成：
醋酸乙烯：15～25(例15％、20％、25％)
苯乙烯：3-5(例3％、4％、5％)
乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂：0.5～3(例1％、2％、3％)
过硫酸钾：0.05～0.5(例0.05％、0.1％、0.5％)
聚乙烯醇(1799)：10～30(例10％、20％、30％)
水：余量。
上述硬挺剂的生产方法，包括：
(1)醋酸乙烯乳液的制备：
聚乙烯醇的溶解及过滤：将聚乙烯醇加入到水中，升温至85-90℃搅拌2小时以上至溶解；过滤后加入到反应釜中，然后加入乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂，搅拌5分钟，加入醋酸乙烯和苯乙烯总量的15％和过硫酸钾水溶液总量的45％，其中过硫酸钾事先用冷的蒸馏水溶解；加热升温，待温度升至60-65℃时停止加热，在66℃时开始回流，待温度自升至80-83℃且回流减少时，开始滴加醋酸乙烯单体，单体以每小时加入其总量的10-15％左右速度均匀加入，控制6-8小时加完；与此同时，引发剂过硫酸钾水溶液以每小时加入总量4-5％的速度加入，反应温度控制t＝78-82℃。加完单体后，加入剩余的引发剂；因放热反应而使体系温度升至90-95℃，保温90-95℃反应30分钟，加入剩余量的水，搅拌降温，降温至40℃以下，关搅拌，过滤出料；得醋酸乙烯乳液；
(2)将醋酸乙烯乳液稀释成45％质量浓度，然后与可溶性淀粉、明胶、去离子水混合得到硬挺剂GH-100。

Claims (1)

1.一种硬挺剂，其特征是：由下列重量百分比的成分组成：
40%聚醋酸乙烯乳液 50—60%
可溶性淀粉：3-5%
明胶：5-10%
去离子水：余量；
其中聚醋酸乙烯乳液由下列重量百分比的成分组成：
醋酸乙烯：15～25
苯乙烯：3-5
乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂：0.5～3
过硫酸钾：0.05～0.5
聚乙烯醇1799：10～30
水：余量；
其制备方法：
（1）聚醋酸乙烯乳液的制备：
聚乙烯醇的溶解及过滤：将聚乙烯醇加入到水中，升温至85-90℃搅拌2小时以上至溶解；过滤后加入到反应釜中，然后加入乙二醇双琥珀酸正辛醇双酯磺酸钠乳化剂，搅拌5分钟，加入醋酸乙烯和苯乙烯总量的15%和过硫酸钾水溶液总量的45%，其中过硫酸钾事先用冷的蒸馏水溶解；加热升温，待温度升至60-65℃时停止加热，在66℃时开始回流，待温度自升至80-83℃且回流减少时，开始滴加醋酸乙烯单体，单体以每小时加入其总量的10-15%速度均匀加入，控制6-8小时加完；与此同时，引发剂过硫酸钾水溶液以每小时加入总量4-5%的速度加入，反应温度控制t=78-82℃；加完单体后，加入剩余的引发剂；因放热反应而使体系温度升至90-95℃，保温90-95℃反应30分钟，加入剩余量的水，搅拌降温，降温至40℃以下，关搅拌，过滤出料；得聚醋酸乙烯乳液；
（2）将聚醋酸乙烯乳液稀释成45%质量浓度，然后与可溶性淀粉、明胶、去离子水混合得到硬挺剂。
CN201010511287.6A 2010-10-18 2010-10-18 硬挺剂及其生产方法 Expired - Fee Related CN102454106B (zh)