CN102453418A - 一种水包水多彩乳胶漆及其加工工艺 - Google Patents
一种水包水多彩乳胶漆及其加工工艺 Download PDFInfo
- Publication number
- CN102453418A CN102453418A CN2010105304927A CN201010530492A CN102453418A CN 102453418 A CN102453418 A CN 102453418A CN 2010105304927 A CN2010105304927 A CN 2010105304927A CN 201010530492 A CN201010530492 A CN 201010530492A CN 102453418 A CN102453418 A CN 102453418A
- Authority
- CN
- China
- Prior art keywords
- water
- pigment
- kaolin
- wetting agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水包水多彩乳胶漆及其加工工艺。由去离子水、高岭土、助剂AMP95、分散剂金红石钛白粉、成膜物质硅丙乳液、阴离子润湿剂和颜料组成，各成分占总质量的重量百分比例分别为：去离子水30-40％，高岭土25-35％，AMP95助剂0.1-0.2％，钛白粉5-10％，硅丙乳液15-25％，阴离子润湿剂3-7％，颜料少量。本发明既没有水包油型涂料对环境、墙体的侵害和使用寿命期短的缺陷，又没有全水性型涂料的仿真度差、施工难度大的问题，克服了其它花岗彩涂料的各种病灶，成为一种使用寿命长、仿真性极强、各种性能均为优异的涂料。本发明工艺操作简单，对设备的要求低，生产效率高。
Description
技术领域
本发明涉及一种花岗彩涂料及其加工工艺，尤其涉及一种水包水多彩乳胶漆及其加工工艺。
背景技术
花岗彩涂料目前在国内具有水包油型、水包水型和全水性型三类，水包油型花岗彩涂料由于它无法克服环保的要求，而且极容易使饰面基层受到伤害，使保温隔热效果严重降低，而且其使用寿命较短；全水性型涂料生成的涂膜外观明显无自然感，仿真度差，施工难度大。既没有“水包油型”对环境、墙体的侵害和使用寿命期短的缺陷，又没有“全水性型”的仿真度差、施工难度大的问题，克服了其它花岗彩涂料的各种病灶，成为一款耐候性超长、仿真性极强、各种性能均为优异的涂料，由于它特性它成为了一款极有市场竞争力的产品。
发明内容
本发明为了解决以上问题提供了一种使用寿命长、仿真性强、生产简单的水包水多彩乳胶漆及其加工工艺。
本发明的技术方案是：由去离子水、高岭土、助剂AMP95、分散剂金红石钛白粉、成膜物质硅丙乳液、阴离子润湿剂和颜料组成，各成分占总质量的重量百分比例分别为：去离子水30-40％，高岭土25-35％，AMP95助剂0.1-0.2％，钛白粉5-10％，硅丙乳液15-25％，阴离子润湿剂3-7％，颜料少量。
一种水包水多彩乳胶漆的加工工艺，将上述原料按以下步骤加工：
1)、先将去离子水加入容器内，再加入高岭土、分散剂钛白粉、助剂AMP95充分混合，搅拌均匀；
2)、向上述溶液中再加入成膜物质硅丙乳液、阴离子润湿剂和颜料，充分搅拌分散，形成彩色颗粒；
3)、将上述溶液过滤，向溶液内加入少量消泡剂，得到成品。
本发明既没有水包油型涂料对环境、墙体的侵害和使用寿命期短的缺陷，又没有全水性型涂料的仿真度差、施工难度大的问题，克服了其它花岗彩涂料的各种病灶，成为一种使用寿命长、仿真性极强、各种性能均为优异的涂料。
本发明工艺操作简单，对设备的要求低，生产效率高。
具体实施方式
一种水包水多彩乳胶漆，由去离子水、高岭土、助剂AMP95、分散剂金红石钛白粉、成膜物质硅丙乳液、阴离子润湿剂和颜料组成，各成分占总质量的重量百分比例分别为：去离子水30-40％，高岭土25-35％，AMP95助剂0.1-0.2％，钛白粉5-10％，硅丙乳液15-25％，阴离子润湿剂3-7％，颜料少量。
一种水包水多彩乳胶漆的加工工艺，将上述原料按以下步骤加工：
实施例1
1)、先将去离子水30％加入容器内，再加入高岭土25％、分散剂钛白粉5％、助剂AMP950.1％充分混合，搅拌均匀；
2)、向上述溶液中再加入成膜物质硅丙乳液15％、阴离子润湿剂3％和颜料，充分搅拌分散，形成彩色颗粒；
3)、将上述溶液过滤，向溶液内加入少量消泡剂，得到成品。
实施例2
1)、先将去离子水35％加入容器内，再加入高岭土20％、分散剂钛白粉8％、助剂AMP950.15％充分混合，搅拌均匀；
2)、向上述溶液中再加入成膜物质硅丙乳液20％、阴离子润湿剂5％和颜料，充分搅拌分散，形成彩色颗粒；
3)、将上述溶液过滤，向溶液内加入少量消泡剂，得到成品。
实施例3
1)、先将去离子水40％加入容器内，再加入高岭土35％、分散剂钛白粉10％、助剂AMP950.2％充分混合，搅拌均匀；
2)、向上述溶液中再加入成膜物质硅丙乳液25％、阴离子润湿剂7％和颜料，充分搅拌分散，形成彩色颗粒；
3)、将上述溶液过滤，向溶液内加入少量消泡剂，得到成品。
Claims (2)
1.一种水包水多彩乳胶漆，其特征在于：由去离子水、高岭土、助剂AMP95、分散剂金红石钛白粉、成膜物质硅丙乳液、阴离子润湿剂和颜料组成，各成分占总质量的重量百分比例分别为：去离子水30-40％，高岭土25-35％，AMP95助剂0.1-0.2％，钛白粉5-10％，硅丙乳液15-25％，阴离子润湿剂3-7％，颜料少量。
2.一种水包水多彩乳胶漆的加工工艺，其特征在于：将上述原料按以下步骤加工：
1)、先将去离子水加入容器内，再加入高岭土、分散剂钛白粉、助剂AMP95充分混合，搅拌均匀；
2)、向上述溶液中再加入成膜物质硅丙乳液、阴离子润湿剂和颜料，充分搅拌分散，形成彩色颗粒；
3)、将上述溶液过滤，向溶液内加入少量消泡剂，得到成品。