CN102432269A - 一种ffc泥浆料及其加工方法 - Google Patents
一种ffc泥浆料及其加工方法 Download PDFInfo
- Publication number
- CN102432269A CN102432269A CN2011102753045A CN201110275304A CN102432269A CN 102432269 A CN102432269 A CN 102432269A CN 2011102753045 A CN2011102753045 A CN 2011102753045A CN 201110275304 A CN201110275304 A CN 201110275304A CN 102432269 A CN102432269 A CN 102432269A
- Authority
- CN
- China
- Prior art keywords
- parts
- clay
- mud
- ffc
- rhombspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种FFC泥浆料，它由以下重量份的原料组成：章村土4-5份，煅烧高岭土9-11份，彰武粘土6-8份，山西木节5-7份，沁阳土5-7份，石英14-16份，广东球土13-16份，广东黑泥5-7份，白云石2-4份，围场粘土1.5-3份，丰润砂岩3-5份，滦县长石5-7份，瓷粉3-4.5份，湛江B瓷土8.5-9.5份，宣化瓷石2.5-4.5份。将白云石研磨，加工成白云石浆；将白云石浆和其他原料一起入球磨机研磨，其料球水的重量比例为1:1.8:0.35，即得到FFC泥浆料。本发明所公开的FFC泥浆料，其原料全部为国产原料，成本低，增加经济效益；泥浆料热稳定性好，适合生产现场的环境，工作效率高。
Description
技术领域
本发明涉及一种陶瓷生产领域中使用的FFC泥浆料，具体地说是一种生产卫生陶瓷过程中应用的FFC泥浆料及其加工方法。
背景技术
目前，在卫生陶瓷的生产过程中，所采用的FFC泥浆料中，一般都包括3A原料和3B原料，而且这种FFC泥浆料主要来源是国外进口，费用高，这样就大大的增大了陶瓷产品的成本。另外，现有的FFC泥浆料的烧成温度为1230℃-1250℃，烧成周期为18-24个小时，不能满足现场的烧成温度，生产效率较低，不能实现大批量的生产要求。
发明内容
本发明是针对现有技术中FFC泥浆料进口费用高、不适合现场烧成温度等缺陷，一是提供一种完全国产化、原料易取、成本低、热稳定性好的FFC泥浆料；二是提供这种泥浆料的加工方法。
实现上述发明目的采用的技术方案是：一种FFC泥浆料，它由以下重量份的原料组成：章村土4-5份，煅烧高岭土9-11份，彰武粘土6-8份，山西木节5-7份，沁阳土5-7份，石英14-16份，广东球土13-16份，广东黑泥5-7份，白云石2-4份，围场粘土1.5-3份，丰润砂岩3-5份，滦县长石5-7份，瓷粉3-4.5份，湛江B瓷土8.5-9.5份，宣化瓷石2.5-4.5份。
组成所述FFC泥浆料的各原料的最佳重量份是：章村土4.5份，煅烧高岭土10份，彰武粘土7份，山西木节6份，沁阳土6份，石英15份，广东球土15份，广东黑泥6份，白云石3份，围场粘土2份，丰润砂岩3.8份，滦县长石5.7份，瓷粉4份，湛江B瓷土9份，宣化瓷石3份。
泥浆料中各化学成分的重量百分比是：I.L 7.55，SiO2 61.40，Al2O3 24.51，Fe2O3 1.23，TiO2 0.79，CaO 1.24，MgO 0.90，K2O 1.81，Na2O 0.58。
加工方法是：先将白云石研磨，加工成白云石浆，该白云石浆的细度在325目筛余0.2-0.3%；然后将白云石浆和其他原料一起入球磨机研磨，其料球水的重量比例为1:1.8:0.35，即得到FFC泥浆料。
与现有技术相比，本发明所公开的FFC泥浆料，其原料全部为国产原料，原料易取，且成本低，适合各种规模的生产，大大增加经济效益；泥浆料热稳定性好，烧成温度为1185℃，完全适合生产现场的环境，烧成周期为14-16小时，工作效率高。
具体实施方式
下面结合实施例对本发明做进一步说明。
本发明所公开的这种FFC泥浆料，它由以下重量份的原料组成：章村土4-5份，煅烧高岭土9-11份，彰武粘土6-8份，山西木节5-7份，沁阳土5-7份，石英14-16份，广东球土13-16份，广东黑泥5-7份，白云石2-4份，围场粘土1.5-3份，丰润砂岩3-5份，滦县长石5-7份，瓷粉3-4.5份，湛江B瓷土8.5-9.5份，宣化瓷石2.5-4.5份。这些原料全部是国内各地区的产品，全部为国产产品，与进口原料相比，其成本低，且容易获取。
组成该FFC泥浆料的各原料的最佳重量份是：章村土4.5份，煅烧高岭土10份，彰武粘土7份，山西木节6份，沁阳土6份，石英15份，广东球土15份，广东黑泥6份，白云石3份，围场粘土2份，丰润砂岩3.8份，滦县长石5.7份，瓷粉4份，湛江B瓷土9份，宣化瓷石3份。
泥浆料中各化学成分的重量百分比是：I.L 7.55，SiO2 61.40，Al2O3 24.51，Fe2O3 1.23，TiO2 0.79，CaO 1.24，MgO 0.90，K2O 1.81，Na2O 0.58。这里所说的泥浆料中各化学成分的重量百分比，是指最佳组分的泥浆料中化学成本的重量百分比，原料为其他重量份的泥浆料的化学成分的重量百分比也会随着原料多少的改变而变化，其变化范围在原料重量份的变化范围之内。
这种FFC泥浆料的加工方法是：先将白云石研磨，加工成白云石浆，该白云石浆的细度在325目筛余0.2-0.3%；然后将白云石浆和其他原料一起入球磨机研磨，其料球水的重量比例为1:1.8:0.35，即得到FFC泥浆料。
该注浆泥的参数控制为：
比重（g/ml）：1.80-1.90
筛余（325目）：5-7%
流动性V0（秒/100ml）：35-45
流动性V30（秒/100ml）：50-90
屈服值：20-35
吸浆速度（mm/30min）：5.5-6.5
总收缩（%）：7-9
变形度（mm）：≤10
吸水率（1185℃）%：8-10
在生产过程中，使用时保证泥浆温度是30-35℃，室内工作环境的温度是28-33℃。
对此泥浆进行热稳定性的测试：将用该泥浆制作的瓷片先放入110℃的热水中煮沸90min，然后捞出后马上放入0℃的冰水混合物中静置10min，再放入红墨水中浸泡1小时，拿出洗净后查看坯料表面无炸裂现象，即热稳定性良好。
在进行压力测试时，其蒸压釜内的压强为0.35MPa 10小时，然后1MPa 1小时，拿出浸泡墨水后无炸裂现象。
Claims (4)
1. 一种FFC泥浆料，其特征在于，它由以下重量份的原料组成：章村土4-5份，煅烧高岭土9-11份，彰武粘土6-8份，山西木节5-7份，沁阳土5-7份，石英14-16份，广东球土13-16份，广东黑泥5-7份，白云石2-4份，围场粘土1.5-3份，丰润砂岩3-5份，滦县长石5-7份，瓷粉3-4.5份，湛江B瓷土8.5-9.5份，宣化瓷石2.5-4.5份。
2.根据权利要求1所述的FFC泥浆料，其特征在于，组成所述FFC泥浆料的各原料的最佳重量份是：章村土4.5份，煅烧高岭土10份，彰武粘土7份，山西木节6份，沁阳土6份，石英15份，广东球土15份，广东黑泥6份，白云石3份，围场粘土2份，丰润砂岩3.8份，滦县长石5.7份，瓷粉4份，湛江B瓷土9份，宣化瓷石3份。
3.根据权利要求2所述的FFC泥浆料，其特征在于，所述泥浆料中各化学成分的重量百分比是：I.L 7.55，SiO2 61.40，Al2O3 24.51，Fe2O3 1.23，TiO2 0.79，CaO 1.24，MgO 0.90，K2O 1.81，Na2O 0.58。
4.一种权利要求1所述的FFC泥浆料的加工方法，其特征在于，所述加工方法是：先将白云石研磨，加工成白云石浆，该白云石浆的细度在325目筛余0.2-0.3%；然后将白云石浆和其他原料一起入球磨机研磨，其料球水的重量比例为1:1.8:0.35，即得到FFC泥浆料。