CN102347116A - Bonding treatment method for aluminum foil polyester composite strip - Google Patents
Bonding treatment method for aluminum foil polyester composite strip Download PDFInfo
- Publication number
- CN102347116A CN102347116A CN2010102448512A CN201010244851A CN102347116A CN 102347116 A CN102347116 A CN 102347116A CN 2010102448512 A CN2010102448512 A CN 2010102448512A CN 201010244851 A CN201010244851 A CN 201010244851A CN 102347116 A CN102347116 A CN 102347116A
- Authority
- CN
- China
- Prior art keywords
- aluminium foil
- polyester composite
- aluminum foil
- composite band
- foil polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a bonding treatment method for an aluminum foil polyester composite strip. The method comprises the following steps of: (1) uniformly coating diluted aluminum foil polyvinyl chloride (PVC) glue on the surface of the aluminum foil polyester composite strip; and (2) drying the bonding treatment material at the temperature of between 50 and 100 DEG C. The method has the advantages that: the surface of an aluminum foil or a polyester film is treated, and the aluminum foil or the polyester film is bonded with a PVC sheath in a heating state, so that the sheath and an outer shielding layer (the aluminum foil polyester composite strip) can be conveniently peeled at the same time in the cable installation process, and the installation time is saved.
Description
Technical field
The present invention relates to a kind of cable processing method, specifically be meant the adhesion process method on its packaging material surface.
Background technology
Aluminium foil mark drawstring (aluminium foil polyester composite band) is mainly used in the shield pack coating of electric wire, mainly contains vertical bag and wrapped dual mode.Common aluminium foil mark drawstring (aluminium foil polyester composite band) can't be bonding with the PVC sheath of electric wire, and in carrying out electric wire installation process, PVC sheath and shielding aluminium foil layering have increased the intractability of electric wire joint, have reduced installation effectiveness.
Summary of the invention
The technical problem that the present invention will solve is the defective that remedies existing aluminium foil polyester composite band treatment process, and a kind of surperficial adhesion process method is provided, and temperature is and PVC sheath good bond a little.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
The adhesion process method of aluminium foil polyester composite band, it comprises the steps:
(1) the aluminium foil PVC glue after will diluting is uniformly coated on aluminium foil polyester composite band surface;
(2) with the material of above-mentioned adhesion process in 50 ℃～100 ℃ oven dry;
The volume proportion of said aluminium foil PVC glue and diluent is 1: 1～3.
Further, said diluent is ester class or ketones solvent, and particularly, said esters solvent is methyl acetate, ethyl acetate or propyl acetate; Said ketones solvent is acetone, espeleton or methylisobutylketone.
In the step (1), the method for said even coating is, through 60～80 lines/centimetre anilox roll evenly be applied to aluminium foil polyester composite band surface, operation of equipment speed is 40～150 meters/minute.
Beneficial effect of the present invention is: bonding with the PVC sheath under warm-up mode through surface treatment to aluminium foil or polyester film, in the cable installation process, can conveniently sheath and outer shielding layer (aluminium foil polyester composite band) be peeled off simultaneously, and save the set-up time.
Description of drawings
Accompanying drawing is used to provide further understanding of the present invention, and constitutes the part of specification, is used to explain the present invention with embodiments of the invention, is not construed as limiting the invention.In the accompanying drawings:
Fig. 1 is the equipment needed thereby structural representation of adhesion process method of the present invention;
Embodiment
Below in conjunction with accompanying drawing the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein only is used for explanation and explains the present invention, and be not used in qualification the present invention.
Embodiment 1
The lubricated method of aluminium foil polyester composite band, it comprises the steps:
(1) with PVC glue: diluent carries out proportioning in 1: 1～3 ratio; Through unreeling structure 1 blowing, aluminium foil PVC glue evenly is applied to aluminium foil polyester composite band surface (aluminium foil or plastic film surface) through the anilox roll (printing element 2) of 60～80 lines; Wherein, aluminium foil PVC glue outward appearance is weak yellow liquid, solid content 25 (+/-2) %, viscosity 70～75 seconds (being coated with-4 glasss, 23 ℃).
(2) material with above-mentioned adhesion process passes through three stage baking ovens, 3 dryings, and three sections baking oven 3 temperature controls are respectively 60 ℃, 100 ℃, 80 ℃; Operation of equipment speed is wound into coiled strip through rolling-up mechanism 4 then at 40～150 meters/minute.Final coating weight after the oven dry is controlled at 3～4g/m
2
Particularly, the coating weight of the product of certain proportioning raw materials, technological parameter preparation is as shown in the table:
Table 1: the coating scale of the product of certain proportioning raw materials, technological parameter preparation
| Group | PVC glue: diluent ratio | Anilox roll line number | Service speed rice/minute | Coating weight g/m 2 |
| 1 | 1: 1 ethyl acetate | 60 | 50 | 4 |
| 2 | 1: 2 propyl acetate | 80 | 75 | 3.8 |
| 3 | 1: 3 acetone | 73 | 100 | 3.5 |
| 4 | 1: 4 methylisobutylketone | 77 | 150 | 3 |
What should illustrate at last is: the above only is the preferred embodiments of the present invention; Be not limited to the present invention; Although the present invention has been carried out detailed explanation with reference to previous embodiment; For a person skilled in the art; It still can be made amendment to the technical scheme that aforementioned each embodiment put down in writing, and perhaps part technical characterictic wherein is equal to replacement.All within spirit of the present invention and principle, any modification of being done, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. the lubricated method of aluminium foil polyester composite band, it comprises the steps:
(1) the aluminium foil PVC glue after will diluting is uniformly coated on aluminium foil polyester composite band surface;
(2) with the material of above-mentioned adhesion process in 50 ℃～100 ℃ oven dry;
The volume proportion of said aluminium foil PVC glue and diluent is 1: 1～3.
2. the lubricated method of aluminium foil polyester composite band according to claim 1 is characterized in that: said diluent is ester class or ketones solvent.
3. the lubricated method of aluminium foil polyester composite band according to claim 2 is characterized in that: said esters solvent is methyl acetate, ethyl acetate or propyl acetate; Said ketones solvent is acetone, espeleton or methylisobutylketone.
4. the adhesion process method of aluminium foil polyester composite band according to claim 1; It is characterized in that: in the step (1); The method of said even coating is, through 60～80 lines/centimetre anilox roll evenly be applied to aluminium foil polyester composite band surface, operation of equipment speed is 40～150 meters/minute.