CN102336961A - 一种pp纺粘无纺布可降解复合材料及其制备工艺 - Google Patents
一种pp纺粘无纺布可降解复合材料及其制备工艺 Download PDFInfo
- Publication number
- CN102336961A CN102336961A CN2011102070787A CN201110207078A CN102336961A CN 102336961 A CN102336961 A CN 102336961A CN 2011102070787 A CN2011102070787 A CN 2011102070787A CN 201110207078 A CN201110207078 A CN 201110207078A CN 102336961 A CN102336961 A CN 102336961A
- Authority
- CN
- China
- Prior art keywords
- spun
- composite material
- bonded non
- polyisobutene
- poe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种PP纺粘无纺布可降解复合材料及其制备工艺,其特征在于,它主要由重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯制成,重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比为(70-85):(15-25):(1-2):(3-7):(55-65):(1-3)。本发明在纺粘无纺布机器上,按原有聚丙烯生产工艺,完全正常生产,过滤性能好、可纺性好、不滴浆、着色性能好、铺网均匀、克重正常、拉伸强度、柔软性能好、表面光泽度好。
Description
技术领域
本发明涉及PP纺粘无纺布技术领域,更具体的说是涉及一种PP纺粘无纺布复合材料及工艺。
背景技术
目前,PP纺粘法无纺布系采用PP聚丙烯原料,经设备高温喷丝梳理粘结成网后,由物理方法使纤维间形成透气而非透水的纤维结构,达到物理的防潮、防霉、防蛀的理想效果。它主要用于妇女卫生巾、尿布、餐巾、服装衬布、鞋帽衬布、及一次性手术衣、手术帽、手术台罩,并广泛应用于人造革、家私、化工、印刷、装饰、包装、汽车、建材服务、工矿土工布、以及工业过滤布吸油布、旅游用品、生活用品等行业。但目前的PP纺粘法无纺布系普遍不能降解,不符合环保要求,而且抗拉,抗撕裂,抗顶破等性能差,难以满足人们的生活需求。
发明内容
本发明的目的就是为了解决现有技术之不足而提供的一种不仅制备工艺简单,过滤性能好、可纺性好、不滴浆、着色性能好、铺网均匀、克重正常、拉伸强度、柔软性能好、表面光泽度好,而且达到环保降解功能的PP纺粘无纺布可降解复合材料。
本发明的另一目的是提供一种PP纺粘无纺布可降解复合材料的制备工艺。
本发明是采用如下技术解决方案来实现上述目的:一种PP纺粘无纺布可降解复合材料,其特征在于,它主要由重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯制成,重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比为(70-85):(15-25):(1-2):(3-7):(55-65):(1-3)。
作为上述方案的进一步说明:所述重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比优选80:20:1.5:5:60:2。
所述重质碳酸钙的粒径为2300-2600目,玉米淀粉的粒径为1300-1600目。
一种PP纺粘无纺布可降解复合材料的制备工艺,其特征在于,它包括如下步骤:
a、先将重质碳酸钙和玉米淀粉加在卧式双螺带混合机,加热中速混合25-35分钟,含水量<2%;
b、 加表面处理剂,高速混合10-20分钟;
c、加POE和聚丙烯,高速混合5-15分钟;
d、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐;
e、通过粉体计量喂料机,喂料到连续密炼机;
f、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机;
g、挤出造粒;
h、成品包装。
在所述工艺步骤b的高速混合过程中,处理剂要完全包覆粉体。
本发明采用上述技术解决方案所能达到的有益效果是:
1、本发明的本复合材料在纺粘无纺布机器上,按原有聚丙烯生产工艺,完全正常生产。
2、过滤性能好、可纺性好、不滴浆、着色性能好、铺网均匀、克重正常、拉伸强度、柔软性能好、表面光泽度好。
3、达到环保降解功能。
具体实施方式
本发明一种PP纺粘无纺布可降解复合材料,它是由重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯制成,重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比为(70-85):(15-25):(1-2):(3-7):(55-65):(1-3)。本实施例中,重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比优选80:20:1.5:5:60:2。
PP纺粘无纺布可降解复合材料,其制备工艺如下:
1、先将重质碳酸钙和玉米淀粉加在卧式双螺带混合机,加热中速混合30分钟,达到混合干燥效果,含水量<2%;
2、加表面处理剂,高速混合15分钟, 处理剂完全包覆粉体;
3、加POE和聚丙烯,高速混合10分钟,各组份分布混合均匀;
4、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐;
5、通过粉体计量喂料机,喂料到连续密炼机;
6、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机;
7、挤出造粒;
8、成品包装。
以上所述的仅是本发明的优选实施方式,应当指出,对于本领域的普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。
Claims (5)
1.一种PP纺粘无纺布可降解复合材料,其特征在于,它主要由重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯制成,组分中重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比为(70-85):(15-25):(1-2):(3-7):(55-65):(1-3)。
2.根据权利要求1所述的PP纺粘无纺布可降解复合材料,其特征在于,所述重质碳酸钙、玉米淀粉、表面处理剂、POE、聚丙烯和聚异丁烯的重量比优选80:20:1.5:5:60:2。
3.根据权利要求1或2所述的PP纺粘无纺布可降解复合材料,其特征在于,所述重质碳酸钙的粒径为2300-2600目,玉米淀粉的粒径为1300-1600目。
4.一种PP纺粘无纺布可降解复合材料的制备工艺,其特征在于,它包括如下步骤:
a、先将重质碳酸钙和玉米淀粉加在卧式双螺带混合机,加热中速混合25-35分钟,含水量<2%;
b、 加表面处理剂,高速混合10-20分钟;
c、加POE和聚丙烯,高速混合5-15分钟;
d、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐;
e、通过粉体计量喂料机,喂料到连续密炼机;
f、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机;
g、挤出造粒;
h、成品包装。
5.根据权利要求4所述的PP纺粘无纺布可降解复合材料的制备工艺,其特征在于,在所述工艺步骤b的高速混合过程中,处理剂要完全包覆粉体。