CN102321834A - 一种新型的用于加工铝钢复合带的铝合金 - Google Patents

一种新型的用于加工铝钢复合带的铝合金 Download PDF

Info

Publication number
CN102321834A
CN102321834A CN 201110320679 CN201110320679A CN102321834A CN 102321834 A CN102321834 A CN 102321834A CN 201110320679 CN201110320679 CN 201110320679 CN 201110320679 A CN201110320679 A CN 201110320679A CN 102321834 A CN102321834 A CN 102321834A
Authority
CN
China
Prior art keywords
aluminum
novel
steel composite
aluminum alloy
composite belt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110320679
Other languages
English (en)
Inventor
吕金明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yinbang Clad Material Co Ltd
Original Assignee
Yinbang Clad Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yinbang Clad Material Co Ltd filed Critical Yinbang Clad Material Co Ltd
Priority to CN 201110320679 priority Critical patent/CN102321834A/zh
Publication of CN102321834A publication Critical patent/CN102321834A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种新型的用于加工铝钢复合带的铝合金，其能有效解决目前采用普通1050铝合金生产的钢铝复合带复合强度低的问题。其技术方案是这样的，其特征在于：其包含以下重量份数的材料：硅（Si）0.7份～0.9份、铁（Fe）0.2份～0.4份、铜（Cu）0份～0.05份、锰（Mn）0份～0.05份、镁（Mg）0份～0.05份、锌（Zn）0份～0.05份、钛（Ti）0份～0.03份、其它杂质微量元素0份～0.15份，其余为铝（Al）98.32份～99.1份。

Description

一种新型的用于加工铝钢复合带的铝合金
技术领域
本发明涉及铝合金材料技术领域，具体为一种新型的用于加工铝钢复合带的铝合金。
背景技术
目前用于加工铝钢复合带的铝合金基体多是采用普通1050铝合金，其成分按重量份数主要包括硅（Si）0份～0.25份、铁（Fe）0份～0.4份、铜（Cu）0份～0.05份、锰（Mn）0份～0.05份、镁（Mg）0份～0.05份、锌（Zn）0份～0.05份、钛（Ti）0份～0.03份、其它杂质微量元素0份～0.15份，其余为铝（Al），其缺点在于：普通1050铝合金与钢带进行复合时、在高温下铝钢复合界面易生成FeAl3、Fe3Al5等脆性化合物，从而降低了铝钢复合带的复合强度。
发明内容
针对上述问题，本发明提供了一种新型的用于加工铝钢复合带的铝合金，其能有效解决目前采用普通1050铝合金生产的钢铝复合带复合强度低的问题。
其技术方案是这样的，其特征在于：其包含以下重量份数的材料：硅（Si）0.7份～0.9份、铁（Fe）0.2份～0.4份、铜（Cu）0份～0.05份、锰（Mn）0份～0.05份、镁（Mg）0份～0.05份、锌（Zn）0份～0.05份、钛（Ti）0份～0.03份、其它杂质微量元素0份～0.15份，其余为铝（Al）98.32份～99.1份。
与普通1050铝合金相比较，采用本发明铝合金加工钢铝复合带的有益效果在于：其成分中提高了硅（Si）含量，由于Si可以阻碍高温下钢铝复合介面FeAl3、Fe3Al5等脆性化合物的生成，因而能有效解决高温热脆性的问题，提高复合强度。
具体实施方式
实施例一：一种新型的用于加工铝钢复合带的铝合金，其包含以下重量份数的材料：硅（Si）0.7份、铁（Fe）0.4份、铜（Cu）0.025份、镁（Mg）0.05份、锌（Zn）0.05份、钛（Ti）0.015份，其余为铝（Al）98.32份。
实施例二：一种新型的用于加工铝钢复合带的铝合金，其包含以下重量份数的材料：硅（Si）0.9份、铁（Fe）0.3份、锰（Mn）0.05份、镁（Mg）0.025份、其它杂质微量元素0.15份，其余为铝（Al）98.71份。
实施例三：一种新型的用于加工铝钢复合带的铝合金，其包含以下重量份数的材料：硅（Si）0.8份、铁（Fe）0.2份、铜（Cu）0.05份、锰（Mn）0.025份、锌（Zn）0.025份、钛（Ti）0.03份、其它杂质微量元素0.075份，其余为铝（Al）99.1份。
下面描述一下本发明新型的用于加工铝钢复合带的铝合金的加工过程，将铝锭放入熔炼炉内待铝锭完全熔化后充分搅拌，按重量份数的要求向熔炼炉内依次加入硅（Si）、铁（Fe）、铜（Cu）、锰（Mn）、锌（Zn）、钛（Ti）后进一步熔炼，充分搅拌后检验成分合格，再转炉精炼，最后进行铸造。 

Claims (1)

1.一种新型的用于加工铝钢复合带的铝合金，其特征在于：其包含以下重量份数的材料：硅（Si）0.7份～0.9份、铁（Fe）0.2份～0.4份、铜（Cu）0份～0.05份、锰（Mn）0份～0.05份、镁（Mg）0份～0.05份、锌（Zn）0份～0.05份、钛（Ti）0份～0.03份、其它杂质微量元素0份～0.15份，其余为铝（Al）98.32份～99.1份。
CN 201110320679 2011-10-20 2011-10-20 一种新型的用于加工铝钢复合带的铝合金 Pending CN102321834A (zh)