CN103572130A - 高强度铸造铝合金 - Google Patents

高强度铸造铝合金 Download PDF

Info

Publication number
CN103572130A
CN103572130A CN201310581917.0A CN201310581917A CN103572130A CN 103572130 A CN103572130 A CN 103572130A CN 201310581917 A CN201310581917 A CN 201310581917A CN 103572130 A CN103572130 A CN 103572130A
Authority
CN
China
Prior art keywords
titanium
cast aluminum
rare earth
strength cast
boron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310581917.0A
Other languages
English (en)
Inventor
潘敏
徐军
赵金生
徐伟
侯文洪
盛积
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jiangxu Casting Group Co Ltd
Original Assignee
Jiangsu Jiangxu Casting Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jiangxu Casting Group Co Ltd filed Critical Jiangsu Jiangxu Casting Group Co Ltd
Priority to CN201310581917.0A priority Critical patent/CN103572130A/zh
Publication of CN103572130A publication Critical patent/CN103572130A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种高强度铸造铝合金，用于航空、航天、航海、高速列车等交通运输业的高强度结构，其成分按重量百分比为：铜2.8—3.2wt%、锰2.8—3.2wt%、钛0.1-0.2wt%、铝稀土合金2.2—2.9wt%、六氯乙烷0.2—0.7wt%、铝钛硼1.4—1.8wt%、余量为铝。本发明高强度铝合金经时效处理，其室温抗拉强度为440-470MPa，伸长率为5.8-6.8％。

Description

高强度铸造铝合金
技术领域
本发明属于一种铝合金，具体是一种高强度铸造铝合金。
背景技术
随着现代科技和工业的发展, 航空、航天、航海、高速列车等交通运输业对高强度结构材料的需求日益迫切, 要求在保证强度的前提下尽量减轻重量与成本, 以提高运载能力和速度, 高强度铸造铝合金成为首选。
发明内容
本发明的目的在于提供一种高强度铸造铝合金材料，本发明所采取的技术方案为：
其成分按重量百分比为：铜2.8—3.2wt%、锰2.8—3.2wt%、钛0.1-0.2wt%、铝稀土合金2.2—2.9wt%、六氯乙烷0.2—0.7wt%、铝钛硼1.4—1.8wt%、余量为铝。
所述铝稀土合金中的稀土含量为10wt%。
所述铝钛硼中钛含量为5wt%，硼含量为1wt%。
其制造方法包括以下步骤：
（1）首先熔化铝；
（2）720℃时加入铜、锰进行熔化；
（3）加入钛和铝稀土合金，均匀搅拌；
（4）用六氯乙烷进行精炼处理；
（5）出炉前加入铝钛硼搅拌均匀；
（6）浇注，模具温度280℃-360℃；
（7）150℃保温10小时。
本发明提供的高强度铸造铝合金，其室温抗拉强度为440-470MPa，伸长率为5.8-6.8％。
具体实施方式
实施例1
高强度铸造铝合金，其成分按重量百分比为：铜2.8wt%、锰2.8wt%、钛0.1wt%、铝稀土合金2.2wt%、六氯乙烷0.2wt%、铝钛硼1.4wt%、余量为铝。
所述铝稀土合金中的稀土含量为10wt%。
所述铝钛硼中钛含量为5wt%，硼含量为1wt%。
其制造方法包括以下步骤：
（1）首先熔化铝；
（2）720℃时加入铜、锰进行熔化；
（3）加入钛和铝稀土合金，均匀搅拌；
（4）用六氯乙烷进行精炼处理；
（5）出炉前加入铝钛硼搅拌均匀；
（6）浇注，模具温度280℃-360℃；
（7）150℃保温10小时。
实施例2
高强度铸造铝合金，其成分按重量百分比为：铜3.2wt%、锰3.2wt%、钛0.2wt%、铝稀土合金2.9wt%、六氯乙烷0.7wt%、铝钛硼1.8wt%、余量为铝。
所述铝稀土合金中的稀土含量为10wt%。
所述铝钛硼中钛含量为5wt%，硼含量为1wt%。
其制造方法包括以下步骤：
（1）首先熔化铝；
（2）720℃时加入铜、锰进行熔化；
（3）加入钛和铝稀土合金，均匀搅拌；
（4）用六氯乙烷进行精炼处理；
（5）出炉前加入铝钛硼搅拌均匀；
（6）浇注，模具温度280℃-360℃；
（7）150℃保温10小时实施例2。

Claims (4)

1.一种高强度铸造铝合金，其特征在于：其成分按重量百分比，铜2.8—3.2wt%、锰2.8—3.2wt%、钛0.1-0.2wt%、铝稀土合金2.2—2.9wt%、六氯乙烷0.2—0.7wt%、铝钛硼1.4—1.8wt%、余量为铝。
2.根据权利要求1所述的一种高强度铸造铝合金，其特征在于，所述铝稀土合金中的稀土含量为10wt%。
3.根据权利要求1所述的一种高强度铸造铝合金，其特征在于，所述铝钛硼中钛含量为5wt%，硼含量为1wt%。
4.根据权利要求1所述的一种高强度铸造铝合金，其特征在于，其制造方法包括以下步骤：
（1）首先熔化铝；
（2）720℃时加入铜、锰进行熔化；
（3）加入钛和铝稀土合金，均匀搅拌；
（4）用六氯乙烷进行精炼处理；
（5）出炉前加入铝钛硼搅拌均匀；
（6）浇注，模具温度280℃-360℃；
（7）150℃保温10小时。
CN201310581917.0A 2013-11-20 2013-11-20 高强度铸造铝合金 Pending CN103572130A (zh)