CN102321431A - 一种uv色漆 - Google Patents
一种uv色漆 Download PDFInfo
- Publication number
- CN102321431A CN102321431A CN 201110231765 CN201110231765A CN102321431A CN 102321431 A CN102321431 A CN 102321431A CN 201110231765 CN201110231765 CN 201110231765 CN 201110231765 A CN201110231765 A CN 201110231765A CN 102321431 A CN102321431 A CN 102321431A
- Authority
- CN
- China
- Prior art keywords
- colored paint
- mixture
- resin
- monomer
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种UV色漆,该色漆的组分及其重量配比为:100%的UV树脂45%-65%、消泡剂0.1%-0.5%、分散剂3%-8%、引发剂3%-8%、颜料5%-20%,余量为单体;100%的UV-树脂为聚氨酯丙烯酸树脂或改性环氧丙烯酸树脂或聚酯丙烯酸酯或它们的混合物;单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物。分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物。本发明遮盖好,附着力佳,采用该色漆生产工艺简单、生产成本低、提高了生产效率,适用于家具、地板等家居型材上。
Description
技术领域
本发明涉及一种UV光固化色漆,具体地说是一种遮盖好,附着力佳的UV色漆。
背景技术
家具、地板等实木、非实木制品在加工中会产生很多瑕疵,由于这些瑕疵无法进行修复,目前绝大多数这些瑕疵基材被丢弃,因此产生资源浪费。
发明内容
为了解决瑕疵基材被丢弃所产生资源浪费的问题,本发明的目的是提供一种UV色漆,采用该色漆遮盖好,附着力佳。该色漆配合UV转印油墨在实木、非实木制品表面涂布,可以形成很好的遮盖的涂膜,减少了资源浪费,节约了生产成本。
本发明的目的是通过以下技术方案来实现的:
一种UV色漆,其特征在于:该色漆的组分及其重量配比为:100%的UV树脂 45 %- 65 %、消泡剂 0 . 1 %- 0 . 5 %、分散剂 3%- 8%、引发剂 3%- 8%、颜料5%-20%,余量为单体;所述100%的UV-树脂为聚氨酯丙烯酸树脂或改性环氧丙烯酸树脂或聚酯丙烯酸酯或它们的混合物;所述单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物。
本发明中,所述分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物;所述引发剂为酰基膦化合物、苯偶姻及其衍生物或它们的混合物;所述消泡剂为聚硅氧烷、聚丙烯酸高聚物或它们的混合物。所述颜料为有机颜料或无机颜料或它们的混合物。
本发明中,该色漆的组分及其重量配比优选为:100%的UV树脂 50 %、单体25%、消泡剂0 . 5 %、分散剂5%、颜料15%、引发剂 4 . 5%。
本发明采用特殊的树脂和单体来提高漆膜的流平性和柔韧性。与现有技术相比,本发明遮盖好、柔韧性佳、附着力佳。采用该色漆配合UV转印油墨在实木、非实木制品表面涂布,可以形成很好的遮盖的涂膜。使用该UV色漆能改变现有的地板、家具等实木,非实木制品中加工过程中产生瑕疵而丢弃浪费,符合节约资源的环保生产要求。
本发明生产工艺简单、生产成本低、提高了生产效率,适用于家具、地板等家居型材上。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例1
一种本发明所述的UV色漆,该色漆的组分及其重量配比为:100%的UV树脂 50%、单体25%、消泡剂0 . 5 %、分散剂5%、颜料12. 5%、引发剂 7%。上述组分中:所述UV-树脂可采用CYTEC公司、SARTOMER公司、长兴公司、三木公司或它们的混合物;所述单体为:丙烯酸酯类、改性丙烯酸酯类或它们的混合物,如 CYTEC、SARTOMER、长兴、三木或它们的混合物;所述消泡剂为聚硅氧烷、聚丙烯酸高聚物或它们的混合物,如迪高公司生产的tego920、tego931或它们的混合物;所述分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物,如迪高公司生产的tego685、tego655或它们的混合物;所述引发剂为酰基膦化合物、苯偶姻及其衍生物或它们的混合物,如BASF生产的TPO、CIBA的184、1173或它们的混合物;所述颜料为金红石型二氧化钛,如HUNTSMAN的TR92。
配制时,将UV-树脂和部分单体、消泡剂、分散剂、引发剂分散后,加入颜料充分分散后研磨至一定细度,再加入余量单体高速分散均匀即可。
涂装施工时,可根据具体情况控制涂料温度来调节粘度,通过辊涂的方式将漆涂于家具、地板等实木与非实木制品基材上。
经检测,本发明的UV色漆的主要技术指标如表1:
表1
序号 | 检验项目 | 检验结果 | 检验标准 |
1 | 涂膜外观 | 表面平整、光滑 | 目测 |
2 | 附着力 | 0-1 | EN ISO 2409 |
3 | 遮盖率 | 95%以上 | - |
本发明形成的漆膜遮盖好、附着力佳,应用在家具、地板等实木与非实木制品基材上,对一些有瑕疵无法进行修复的基材进行修改,因此节约材料资源,减少浪费。
实施例2
又一种本发明所述的UV色漆,与实施例1相比,实施例2仅仅将色漆成分改变,该色漆的组分及其重量配比为:100%的UV树脂 45%、单体37%、消泡剂 0 . 5 %、分散剂 3%、引发剂 7%,颜料7.5%。经检测,得到的UV色漆满足要求。
实施例3
又一种本发明所述的UV色漆,与实施例1相比,实施例3仅仅将色漆成分改变,该色漆的组分及其重量配比为:100%的UV树脂60%、单体20%、消泡剂0 . 5 %、分散剂7%、引发剂 6.5%,颜料6%。经检测,得到的UV色漆满足要求。
实施例4
又一种本发明所述的UV色漆,与实施例1相比,实施例4仅仅将色漆成分改变,该色漆的组分及其重量配比为:100%的UV树脂65%、单体19%、消泡剂0 . 2 %、分散剂4%、引发剂 6.8%,颜料5%。经检测,得到的UV色漆满足要求。
Claims (6)
1.一种UV色漆,其特征在于:该色漆的组分及其重量配比为:100%的UV树脂 45 %- 65 %、消泡剂 0 . 1 %- 0 . 5 %、分散剂 3%- 8%、引发剂 3%- 8%、颜料5%-20%,余量为单体;所述100%的UV-树脂为聚氨酯丙烯酸树脂或改性环氧丙烯酸树脂或聚酯丙烯酸酯或它们的混合物;所述单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物。
2.根据权利要求1所述的UV色漆,其特征在于:所述消泡剂为聚硅氧烷、聚丙烯酸高聚物或它们的混合物。
3.根据权利要求1所述的UV色漆,其特征在于:所述分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物。
4.根据权利要求1所述的UV色漆,其特征在于:所述引发剂为酰基膦化合物、苯偶姻及其衍生物或它们的混合物。
5.根据权利要求1所述的UV色漆,其特征在于:所述颜料为有机颜料或无机颜料或它们的混合物。
6.根据权利要求1所述的UV色漆,其特征在于:该色漆的组分及其重量配比为:100%的UV树脂 50 %、单体25%、消泡剂0 . 5 %、分散剂5%、颜料15%、引发剂 4 . 5%。