CN102285779B - 水溶性丙烯酸树脂混凝土及其施工方法 - Google Patents
水溶性丙烯酸树脂混凝土及其施工方法 Download PDFInfo
- Publication number
- CN102285779B CN102285779B CN 201110157179 CN201110157179A CN102285779B CN 102285779 B CN102285779 B CN 102285779B CN 201110157179 CN201110157179 CN 201110157179 CN 201110157179 A CN201110157179 A CN 201110157179A CN 102285779 B CN102285779 B CN 102285779B
- Authority
- CN
- China
- Prior art keywords
- acrylic resin
- water soluble
- soluble acrylic
- concrete
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种水溶性丙烯酸树脂混凝土及其施工方法,该水溶性丙烯酸树脂混凝土包括组分及其重量份如下:水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份。本发明的水溶性丙烯酸树脂混凝土,通过水溶性丙烯酸树脂的加入,可提高混凝土硬化速度,特别在用于公路补修后快速提高强度,加快交通开放,便于行车;本发明施工简单方便,通过水溶性丙烯酸树脂的加入,快速提高混凝土的强度,通过3天时间即可达到现有混凝土所需15天的强度;此外,水溶性丙烯酸树脂在混凝土表面形成一层硬膜,可防止水分的流失,因此不需要现有加水养护。
Description
技术领域
本发明涉及一种混凝土,尤其涉及一种水溶性丙烯酸树脂混凝土及其施工方法。
背景技术
混凝土一般由胶凝材料(如水泥)、水、砂、石等材料按一定比例配合,经搅拌、成型、养护而得,广泛应用于土木工程。混凝土作为一种路面材料,具有施工简单、路面强度高、稳定性好、耐久性好,养护维修简单等优点。建设公路使用的混凝土主要有水泥混凝土和沥青混凝土,这两种各有其优缺点,而现有的水泥混凝土施工或路面修补施工之后凝固速度慢,需要养护15天,强度才达70%,这使得对公路路面进行修补之后,要封闭修补区域15天,才可开放交通,这对行车造成很大不便。
发明内容
本发明的一目的在于,提供一种水溶性丙烯酸树脂混凝土,通过加入水溶性丙烯酸树脂,可提高混凝土硬化速度,特别在用于公路补修后快速提高强度,加快交通开放,便于行车。
本发明的另一目的在于提供上述水溶性丙烯酸树脂混凝土的施工方法,简单方便,通过水溶性丙烯酸树脂的加入,快速提高混凝土的强度,此外,水溶性丙烯酸树脂在混凝土表面形成一层硬膜,可防止水分的流失,不需要现有加水养护。
为实现上述目的,本发明提供一种水溶性丙烯酸树脂混凝土,其包括组分及其重量份如下:水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份。
水溶性丙烯酸树脂溶液的质量浓度是5%-50%。
本发明还提供一种水溶性丙烯酸树脂混凝土的施工方法,包括如下步骤:
步骤1,施工准备:准备施工所需机械设备、计量器具、材料,选择符合规范要求的水溶性丙烯酸树脂混凝土原料组分;
步骤2,制备所述水溶性丙烯酸树脂混凝土:按重量份称取各组分,其中水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份,将水溶性丙烯酸树脂溶液与水泥、砂、石一起拌和均匀;
步骤3,浇筑:将制备好的水溶性丙烯酸树脂混凝土浇筑于待浇筑区,浇筑至所需厚度,然后进行振捣。
水溶性丙烯酸树脂溶液的质量浓度是5%-50%。
本发明的有益效果:本发明的水溶性丙烯酸树脂混凝土,通过水溶性丙烯酸树脂的加入,可提高混凝土硬化速度,特别在用于公路补修后快速提高强度,加快交通开放,便于行车;本发明施工简单方便,通过水溶性丙烯酸树脂的加入,快速提高混凝土的强度,通过3天时间即可达到现有混凝土所需15天的强度;此外,水溶性丙烯酸树脂在混凝土表面形成一层硬膜,可防止水分的流失,因此不需要现有加水养护。
为了能更进一步了解本发明的特征以及技术内容,请参阅以下有关本发明的详细说明。
具体实施方式
本发明提供一种水溶性丙烯酸树脂混凝土,其包括组分及其重量份如下:水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份。水溶性丙烯酸树脂溶液的质量浓度是5%-50%。
其中,所述砂为河砂或机制砂,或其混合物,所述砂、水泥、石及水等原料组分可采用现有技术中所选择的各组分种类,如水泥可采用硅酸盐水泥。本发明中还可包括减水剂、抗冻剂等助剂。所述水溶性丙烯酸树脂具有高光泽性及干燥快等特点,该组分的加入可加快混凝土硬化速度的同时还可一定程度上提高混凝土的光泽性。
进一步地,本发明提供上述水溶性丙烯酸树脂混凝土一实施例的施工方法,其包括如下步骤:
步骤1,施工准备:准备施工所需机械设备(如搅拌机、运输车、振捣棒、压纹器等)、计量器具、材料,选择符合规范要求的水溶性丙烯酸树脂混凝土原料组分并进行检验,各组分根据季节和具体原料选择最佳配比。
步骤2,制备所述水溶性丙烯酸树脂混凝土:按重量份称取各组分,其中水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份,将水溶性丙烯酸树脂溶液与水泥、砂、石一起拌和均匀,形成符合施工指标的混凝土;根据不同施工要求和条件,所述水溶性丙烯酸树脂混凝土可在施工现场或搅拌站集中搅拌制备。水溶性丙烯酸树脂溶液的制备可先将水溶性丙烯酸树脂溶解于适量水中,并将水溶性丙烯酸树脂溶液的质量浓度调节至5%-50%。
步骤3,浇筑:将制备好的水溶性丙烯酸树脂混凝土浇筑于施工现场的待浇筑区,可人工浇筑或采用机械进行浇筑,浇筑至所需厚度,然后进行振捣,使浇筑后的混凝土达到一定的密实性。该步骤可采用现有技术实行。其中,水溶性丙烯酸树脂在混凝土表面形成一硬膜,可防止水分流失,因此可不需要后续养护。另外,由于水溶性丙烯酸树脂的加入,当和水泥、砂、石等组分搅拌混合后,水溶性丙烯酸树脂的水分被水泥反应所吸收而失水,失水的水溶性丙烯酸树脂快速变硬使得浇筑的混凝土整体快速变硬,通过3天时间其强度即可达到现有混凝土所需15天的强度,从而利于交通开放,便于行车。
综上所述,本发明的水溶性丙烯酸树脂混凝土,通过水溶性丙烯酸树脂的加入,可提高混凝土硬化速度,特别在用于公路补修后快速提高强度,加快交通开放,便于行车;本发明施工简单方便,通过水溶性丙烯酸树脂的加入,快速提高混凝土的强度,通过3天时间即可达到现有混凝土所需15天的强度;此外,水溶性丙烯酸树脂在混凝土表面形成一层硬膜,可防止混凝土内的水分因蒸发的流失,因此不需要现有加水养护,节省养护成本。
以上所述,对于本领域的普通技术人员来说,可以根据本发明的技术方案和技术构思作出其他各种相应的改变和变形,而所有这些改变和变形都应属于本发明后附的权利要求的保护范围。
Claims (2)
1.一种水溶性丙烯酸树脂混凝土,其特征在于,其包括组分及其重量份如下:水泥100份、砂150~300份、碎石350~500份、水溶性丙烯酸树脂溶液40~80份;
水溶性丙烯酸树脂溶液的质量浓度是5%-50%。
2.一种如权利要求1所述的水溶性丙烯酸树脂混凝土的施工方法,其特征在于,包括如下步骤:
步骤1,施工准备:准备施工所需机械设备、计量器具、材料,选择符合规范要求的水溶性丙烯酸树脂混凝土原料组分;
步骤2,制备所述水溶性丙烯酸树脂混凝土:按重量份称取各组分,将水溶性丙烯酸树脂溶液与水泥、砂、石一起拌和均匀;
步骤3,浇筑:将制备好的水溶性丙烯酸树脂混凝土浇筑于待浇筑区,浇筑至所需厚度,然后进行振捣。