CN102283547A - Method for manufacturing attapulgite multifunctional paper cup outer sleeve - Google Patents
Method for manufacturing attapulgite multifunctional paper cup outer sleeve Download PDFInfo
- Publication number
- CN102283547A CN102283547A CN2011101575360A CN201110157536A CN102283547A CN 102283547 A CN102283547 A CN 102283547A CN 2011101575360 A CN2011101575360 A CN 2011101575360A CN 201110157536 A CN201110157536 A CN 201110157536A CN 102283547 A CN102283547 A CN 102283547A
- Authority
- CN
- China
- Prior art keywords
- concavo
- convex
- acidifying
- finished product
- dixie cup
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for manufacturing an attapulgite multifunctional paper cup outer sleeve. According to the key point of the technical scheme, the method comprises the following steps of: manufacturing a blank boy of the attapulgite multifunctional paper cup outer sleeve by using attapulgite ceramic mud with an air purification function, wherein the blank body is a cylindrical shell, the lower part of the blank body is provided with a sealed bottom plate, the upper part of the blank body is opened, and the right side of the blank body is adhered with a handle; drying, baking, sintering at a medium temperature, cooling, cleanly polishing, and thus obtaining a semi-finished product; adhering a magnetic sheet onto the bottom plate of the semi-finished product; covering the magnetic sheet by using a flexible plastic bubble pad; and packaging, and thus obtaining a finished product of the attapulgite multifunctional paper cup outer sleeve. The attapulgite multifunctional paper cup outer sleeve can achieve the effects of heat preservation, heat insulation and water magnetization, can adsorb tea water which overflows or is scattered outside a paper cup, has the air purification function and the function of a drying agent, and is suitable for accommodating a disposable paper cup, a disposable plastic cup and a handle-free glass.
Description
Technical field
The present invention relates to the environment-friendly insulating material, be specifically related to the preparation method of the multi-functional dixie cup overcoat of a kind of concavo-convex rod.
Background technology
Characteristics such as dixie cup has, and waterproof, grease proofing, heat-resisting, non-leakage, pollution-free, free from extraneous odour, intensity are good, but the good natural degradation of texture and recovery value are big.
The people that drinks tea often pours the boiling water of getting away in the dixie cup into and makes tea, and the external temperature of dixie cup is higher, and dixie cup does not have handle, often there is the people to be scalded, therefore the anti-dixie cup overcoat that scalds one's hand has just been arranged, added the overcoat of a double layer design in the outside of cup, played insulation and heat insulation effect.
Overcoat adopts plastics or cotton goods to make mostly, though be novel in a measure in moulding, the smooth feel of plastic wrapper is relatively poor, and frosty sensation is particularly arranged winter, cotton goods have insulation and heat insulation effect, but it is unhygienic to be stained with tea in the process of making tea easily.
Many people like drinking magnetized water, and Disposable paper cup, plastic cup and glass do not have the function of magnetized drinking water.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, the preparation method of the multi-functional dixie cup overcoat of a kind of concavo-convex rod is provided.
The preparation method of the multi-functional dixie cup overcoat of concavo-convex rod: the base substrate that is made into the multi-functional dixie cup overcoat of concavo-convex rod with concavo-convex excellent pottery mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom, top is opened wide, handle of right side bonding, enter drying, oven dry, the middle high temperature clean semi-finished product that are that burn till, cool off and polish then, magnetic sheet is sticked on half-finished base plate, a topped soft foam pad on the magnetic sheet is packaged as the finished product of the multi-functional dixie cup overcoat of concavo-convex rod.
Concavo-convex excellent pottery mud with air purification function is made up of paste attapulgite clay, attapulite constant humidity amendment, natural-minerals adsorptive filter medium, cacumen biotae, alumina silicate fibre, polyacrylamide and water.
Described paste attapulgite clay is to use concavo-convex excellent ore pul making production technology, the screening of mineral such as the hydromica in the Concave-convex clay rod, quartz, opal and carbonate is got rid of, obtain a kind of paste attapulgite clay, paste attapulgite clay is through powerful stirring at a high speed, become the special good natural gelinite of a kind of thixotropy and gumminess, viscosity is up to more than the 10000mPas, help the bonding between the raw material, have the characteristics of ultrafine dust, friction little, the no sand feeling of hardness and soft fine and smooth free from extraneous odour.The dry after-contraction of paste attapulgite clay is little, does not produce be full of cracks, and has good, the high temperature resistant and anti-good properties such as saline and alkaline of thixotropy.
Rice hulls, quick dissolved sodium silicate and the zeolite powder of attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying formed.Attapulite constant humidity amendment not only hydroscopicity is good, and after ambient humidity descends, has been adsorbed on the moisture in its duct, will outwards discharge slowly, remains a more stable hydroscopicity, is a kind of constant humidity conditioner of superior performance.Harmful substances such as formaldehyde, ammonia and benzene reduce the infringement healthy to people in the effective absorbed air of attapulite constant humidity amendment energy.
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of natural-minerals adsorptive filter medium after by acidifying formed.The natural-minerals adsorptive filter medium particle surface is coarse, and there is a large amount of micropores inside, has light specific gravity, specific area is big and absorption property is good characteristics.
Cacumen biotae is spray and the leaf of Cupressaceae plant arbor-vitae
,Summer, autumn gather, and the clip sprig is dried.The cacumen biotae multi-branched, sprig is flat, and the tiny flakey of leaf alternately to life, is pasted and is lied prostrate on branch, bottle green or yellow green, matter is crisp, frangibility, gas delicate fragrance, bitter and puckery flavor, little suffering.It is the charred CACUMEN PLATYCLADI that cacumen biotae is generated pitchy after anoxycausis that cacumen biotae is used for the present invention, has the characteristic of active carbon, has not only increased the porosity of pottery mud product, has also improved the adsorption capacity of pottery mud product.
Alumina silicate fibre is ceramic fibre again, and this material has that thermal capacitance is little, fiber long, in light weight, characteristics such as tensile strength big, the slag ball is few, heat endurance is high, anti-erosion and sound absorption qualities are good.Be used for cracking and improving when the present invention helps avoiding making base substrate the intensity of pottery mud product.
Polyacrylamide has good water-solubility and thickening property, the plasticity when being used for the present invention and helping improving pottery mud and make base substrate.
The present invention is achieved by following technical proposals:
1, the preparation method of the multi-functional dixie cup overcoat of concavo-convex rod is: ⑴ is made into the base substrate of the multi-functional dixie cup overcoat of concavo-convex rod with the concavo-convex excellent pottery mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom in the cylinder shell, the groove of a circle of top reservation of base plate, top in the cylinder shell is opened wide, at crude green body that handle is the multi-functional dixie cup overcoat of concavo-convex rod of right outside bonding of cylinder shell, and crude green body changed over to carry out air dry in the base substrate shed; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 60～120 ℃, and drying time was controlled at 1～4 hour; ⑶ the crude green body after will dry changes in the kiln, and temperature is burnt till the stage in being introduced into, and firing temperature is controlled at 120～250 ℃, firing time was controlled at 1～6 hour, high temperature burns till the stage in entering again, and firing temperature is controlled at 250～850 ℃, and firing time was controlled at 1～4 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to room temperature and polishes the clean glossy back semi-finished product of the multi-functional dixie cup overcoat of concavo-convex rod that are; ⑸ stick on a magnetic sheet in the groove above the base plate, and a topped soft foam pad on the magnetic sheet is packaged as the finished product of the multi-functional dixie cup overcoat of concavo-convex rod.
Described production method with concavo-convex excellent pottery mud of air purification function is, and: ⑴ will have after the batch mixes of concavo-convex excellent pottery mud of air purification function and stir in the input mixer; ⑵ carry out wet ball grinding in the mixture after being mixed input ball mill, the grain fineness of ball milling disposed slurry is less than 0.044 millimeter; ⑶ carry out the old semi-finished product that are treated in the slurry input sedimentation basin after with ball milling, half-finished water content is less than 45%, and the old time was controlled at 3～30 days; ⑷ import semi-finished product and push and cut into rectangular block in the vacuum-extruder, and the thickness of the block thing of rectangle is less than 50 millimeters, for having the concavo-convex excellent pottery mud of air purification function;
Batching with concavo-convex excellent pottery mud of air purification function is made up of following component by weight percentage: paste attapulgite clay 45～75%, attapulite constant humidity amendment 5～30%, natural-minerals adsorptive filter medium 5～15%, cacumen biotae 2～10%, alumina silicate fibre 1～5%, polyacrylamide 0.1～3% and water 1～35%.
Concavo-convex excellent pottery mud with air purification function has been applied for patent of invention by the applicant on February 25th, 2011, and number of patent application is: 201110044982.0.
The production technology of described paste attapulgite clay: will stir in the concavo-convex excellent ore deposit input mixer, after extruder is squeezed into sheet, import once more in the mixer and stir, natural drying after extruder is squeezed into sheet, the concavo-convex excellent ore deposit of drying is transported in the feed reservoir soaks, dash with air pump and to turn over, post precipitation is emitted immersion water, the sieve decontamination in the input semi-finished product pond, is soaked again, dash with air pump and to turn over, post precipitation is emitted immersion water, and the slurry transportation of post precipitation is arrived in the finished product pond, is paste attapulgite clay.
Described paste attapulgite clay is made up of following component by weight percentage: Concave-convex clay rod 25～60%, water 40～75%.
This production technology is to adopt " the concavo-convex excellent ore pul making production technology " in application on January 6th, 2004 by the inventor, and the Chinese patent Granted publication number is: CN1287965C, Granted publication day: on December 6th, 2006.
Rice hulls, quick dissolved sodium silicate and the zeolite powder of described attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying formed; The production method of attapulite constant humidity amendment is: the rice hulls after the acidifying and Concave-convex clay rod and montmorillonite are mixed by batching, extrusion modification slabbing mixture, abrasive dust after airing mixes by batching with quick dissolved sodium silicate and zeolite powder and is attapulite constant humidity amendment;
The batching of attapulite constant humidity amendment is made up of following component by weight percentage: the semi-finished product 55～90% of attapulite constant humidity amendment, quick dissolved sodium silicate 2～8% and zeolite powder 5～40%; The half-finished batching of attapulite constant humidity amendment is made up of following component: the rice hulls 5～15% after the acidifying, Concave-convex clay rod 35～55%, montmorillonite 5～15% and water 35～55% by weight percentage;
Aforementioned production method is to adopt " production method of attapulite constant humidity amendment " in application on August 30th, 2007 by the inventor, and the Chinese patent Granted publication number is: CN100528337C, Granted publication day: on August 19th, 2009.
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of described natural-minerals adsorptive filter medium after by acidifying formed; The preparation method of natural-minerals adsorptive filter medium is: is natural-minerals adsorptive filter medium with the batching of natural-minerals adsorptive filter medium through mixing, pulverize, sieving.
The batching of natural-minerals adsorptive filter medium is made up of following component by weight percentage: the zeolite 15～35% after the acidifying, the Concave-convex clay rod 15～35% after the acidifying, the bentonite 15～25% after the acidifying, the diatomite 10～20% after the acidifying, volcanic rock 5～10% and alumine 5～10%.
Natural-minerals adsorptive filter medium adopts " natural-minerals adsorptive filter medium " in application on May 30th, 2006 by the inventor, and the Chinese patent Granted publication number is: CN100502999C, Granted publication day: on June 24th, 2009.
Using method: dixie cup is directly put into the multi-functional dixie cup overcoat of concavo-convex rod, the bottom of dixie cup is a kind of soft contact with the soft foam pad, can guarantee that dixie cup is placed in the multi-functional dixie cup overcoat of concavo-convex rod stably, can normally make tea, can use the handle end of the multi-functional dixie cup overcoat of concavo-convex rod to play dixie cup, also can directly hold the multi-functional dixie cup overcoat of concavo-convex rod to drink tea.
With boiling water pour into make tea in the dixie cup after, the multi-functional dixie cup overcoat of concavo-convex rod not only can play insulation and heat insulation effect, the tea that overflows or trickle down in dixie cup outside can also be adsorbed the dry health of maintenance dixie cup.
A magnetic sheet is arranged at the bottom of the multi-functional dixie cup overcoat of concavo-convex rod, can magnetize processing to the tea in the dixie cup, and magnetized drinking water can improve the health.
In the multi-functional dixie cup overcoat of concavo-convex rod a large amount of micropores and active carbon are arranged; function with drier; harmful substances such as formaldehyde, ammonia and benzene in the effective absorbed air of energy; protection environment and enhancement people's is healthy; the multi-functional dixie cup overcoat of concavo-convex rod is elegant in appearance, and being placed on indoor is again a handicraft.
The present invention is used to make the multi-functional dixie cup overcoat of concavo-convex rod, is applicable to the glass of placing Disposable paper cup, disposal plastic cup and not having handle in the multi-functional dixie cup overcoat of concavo-convex rod.
Description of drawings
Fig. 1 is the schematic diagram of the multi-functional dixie cup overcoat of concavo-convex rod, and Fig. 2 is that the A-A of Fig. 1 is to view.
As shown in the figure: the 1st, cylinder shell, the 2nd, magnetic sheet, the 3rd, soft foam pad, the 4th, groove, the 5th, base plate, the 6th, dixie cup, the 7th, handle.
The specific embodiment
The invention will be further described below in conjunction with embodiment:
1, the preparation method of the multi-functional dixie cup overcoat of concavo-convex rod is: ⑴ is made into the base substrate of the multi-functional dixie cup overcoat of concavo-convex rod with the concavo-convex excellent pottery mud with air purification function, base substrate is a cylinder shell 1, the base plate 5 of a sealing is arranged at the bottom in the cylinder shell 1, the groove 4 of a circle of top reservation of base plate 5, top in the cylinder shell 1 is opened wide, handle 7 of right outside bonding at cylinder shell 1 is the crude green body of the multi-functional dixie cup overcoat of concavo-convex rod, and crude green body changed over to carries out air dry in the base substrate shed; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 80～100 ℃, and drying time was controlled at 3 hours; ⑶ the crude green body after will dry changes in the kiln, and temperature is burnt till the stage in being introduced into, and firing temperature is controlled at 200～220 ℃, and firing time was controlled at 2 hours, and high temperature burns till the stage in entering again, and firing temperature is controlled at 500～550 ℃, and firing time was controlled at 1 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to room temperature and polishes the clean glossy back semi-finished product of the multi-functional dixie cup overcoat of concavo-convex rod that are; ⑸ stick on a magnetic sheet 2 in the groove 4 above the base plate 5, and a topped soft foam pad 3 on the magnetic sheet 2 is packaged as the finished product of the multi-functional dixie cup overcoat of concavo-convex rod.
Using method: dixie cup 6 is directly put into the multi-functional dixie cup overcoat of concavo-convex rod, the bottom of dixie cup is a kind of soft contacts with soft foam pad 3, can guarantee that dixie cup is placed in the multi-functional dixie cup overcoat of concavo-convex rod stably, can normally make tea, can use handle 7 ends of the multi-functional dixie cup overcoat of concavo-convex rod to play dixie cup, also can directly hold the multi-functional dixie cup overcoat of concavo-convex rod to drink tea.
Claims (1)
1. the preparation method of the multi-functional dixie cup overcoat of concavo-convex rod, it is characterized in that, ⑴ be made into the base substrate of the multi-functional dixie cup overcoat of concavo-convex rod with the concavo-convex excellent pottery mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom in the cylinder shell, the groove of a circle of top reservation of base plate, top in the cylinder shell is opened wide, at crude green body that handle is the multi-functional dixie cup overcoat of concavo-convex rod of right outside bonding of cylinder shell, and crude green body changed over to carry out air dry in the base substrate shed; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 60～120 ℃, and drying time was controlled at 1～4 hour; ⑶ the crude green body after will dry changes in the kiln, and temperature is burnt till the stage in being introduced into, and firing temperature is controlled at 120～250 ℃, firing time was controlled at 1～6 hour, high temperature burns till the stage in entering again, and firing temperature is controlled at 250～850 ℃, and firing time was controlled at 1～4 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to room temperature and polishes the clean glossy back semi-finished product of the multi-functional dixie cup overcoat of concavo-convex rod that are; ⑸ stick on a magnetic sheet in the groove above the base plate, and a topped soft foam pad on the magnetic sheet is packaged as the finished product of the multi-functional dixie cup overcoat of concavo-convex rod;
Described production method with concavo-convex excellent pottery mud of air purification function is, and: ⑴ will have after the batch mixes of concavo-convex excellent pottery mud of air purification function and stir in the input mixer; ⑵ carry out wet ball grinding in the mixture after being mixed input ball mill, the grain fineness of ball milling disposed slurry is less than 0.044 millimeter; ⑶ carry out the old semi-finished product that are treated in the slurry input sedimentation basin after with ball milling, half-finished water content is less than 45%, and the old time was controlled at 3～30 days; ⑷ import semi-finished product and push and cut into rectangular block in the vacuum-extruder, and the thickness of the block thing of rectangle is less than 50 millimeters, for having the concavo-convex excellent pottery mud of air purification function;
Batching with concavo-convex excellent pottery mud of air purification function is made up of following component by weight percentage: paste attapulgite clay 45～75%, attapulite constant humidity amendment 5～30%, natural-minerals adsorptive filter medium 5～15%, cacumen biotae 2～10%, alumina silicate fibre 1～5%, polyacrylamide 0.1～3% and water 1～35%;
The production technology of described paste attapulgite clay: will stir in the concavo-convex excellent ore deposit input mixer, after extruder is squeezed into sheet, import once more in the mixer and stir, natural drying after extruder is squeezed into sheet, the concavo-convex excellent ore deposit of drying is transported in the feed reservoir soaks, dash with air pump and to turn over, post precipitation is emitted immersion water, the sieve decontamination in the input semi-finished product pond, is soaked again, dash with air pump and to turn over, post precipitation is emitted immersion water, and the slurry transportation of post precipitation is arrived in the finished product pond, is paste attapulgite clay;
Described paste attapulgite clay is made up of following component by weight percentage: Concave-convex clay rod 25～60%, water 40～75%;
Rice hulls, quick dissolved sodium silicate and the zeolite powder of described attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying formed; The production method of attapulite constant humidity amendment is: the rice hulls after the acidifying and Concave-convex clay rod and montmorillonite are mixed by batching, extrusion modification slabbing mixture, abrasive dust after airing mixes by batching with quick dissolved sodium silicate and zeolite powder and is attapulite constant humidity amendment;
The batching of attapulite constant humidity amendment is made up of following component by weight percentage: the semi-finished product 55～90% of attapulite constant humidity amendment, quick dissolved sodium silicate 2～8% and zeolite powder 5～40%; The half-finished batching of attapulite constant humidity amendment is made up of following component: the rice hulls 5～15% after the acidifying, Concave-convex clay rod 35～55%, montmorillonite 5～15% and water 35～55% by weight percentage;
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of described natural-minerals adsorptive filter medium after by acidifying formed; The preparation method of natural-minerals adsorptive filter medium is: is natural-minerals adsorptive filter medium with the batching of natural-minerals adsorptive filter medium through mixing, pulverize, sieving;
The batching of natural-minerals adsorptive filter medium is made up of following component by weight percentage: the zeolite 15～35% after the acidifying, the Concave-convex clay rod 15～35% after the acidifying, the bentonite 15～25% after the acidifying, the diatomite 10～20% after the acidifying, volcanic rock 5～10% and alumine 5～10%.