CN102283547B - Method for manufacturing attapulgite multifunctional paper cup outer sleeve - Google Patents
Method for manufacturing attapulgite multifunctional paper cup outer sleeve Download PDFInfo
- Publication number
- CN102283547B CN102283547B CN 201110157536 CN201110157536A CN102283547B CN 102283547 B CN102283547 B CN 102283547B CN 201110157536 CN201110157536 CN 201110157536 CN 201110157536 A CN201110157536 A CN 201110157536A CN 102283547 B CN102283547 B CN 102283547B
- Authority
- CN
- China
- Prior art keywords
- attapulgite
- paper cup
- outer sleeve
- acidifying
- cup outer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for manufacturing an attapulgite multifunctional paper cup outer sleeve. According to the key point of the technical scheme, the method comprises the following steps of: manufacturing a blank boy of the attapulgite multifunctional paper cup outer sleeve by using attapulgite ceramic mud with an air purification function, wherein the blank body is a cylindrical shell, the lower part of the blank body is provided with a sealed bottom plate, the upper part of the blank body is opened, and the right side of the blank body is adhered with a handle; drying, baking, sintering at a medium temperature, cooling, cleanly polishing, and thus obtaining a semi-finished product; adhering a magnetic sheet onto the bottom plate of the semi-finished product; covering the magnetic sheet by using a flexible plastic bubble pad; and packaging, and thus obtaining a finished product of the attapulgite multifunctional paper cup outer sleeve. The attapulgite multifunctional paper cup outer sleeve can achieve the effects of heat preservation, heat insulation and water magnetization, can adsorb tea water which overflows or is scattered outside a paper cup, has the air purification function and the function of a drying agent, and is suitable for accommodating a disposable paper cup, a disposable plastic cup and a handle-free glass.
Description
Technical field
The present invention relates to the environment-friendly insulating material, be specifically related to a kind of preparation method of attapulgite multifunctional paper cup outer sleeve.
Background technology
The characteristics such as dixie cup has, and waterproof, grease proofing, heat-resisting, non-leakage, pollution-free, free from extraneous odour, intensity are good, but the good natural degradation of texture and recovery value are large.
The people that drinks tea often pours the boiling water of getting away in the dixie cup into and makes tea, and the external temperature of dixie cup is higher, dixie cup be do not have handled, often someone is burned, the dixie cup overcoat that burn prevention has therefore just been arranged adds the overcoat of a double layer design in the outside of cup, play insulation and heat insulation effect.
Overcoat adopts plastics or cotton goods to make mostly, although be novel in a measure in moulding, the smooth feel of plastic wrapper is relatively poor, and frosty sensation is particularly arranged winter, cotton goods have insulation and heat insulation effect, but it is unhygienic easily to be stained with tea in the process of making tea.
Many people like drinking magnetized water, and Disposable paper cup, plastic cup and glass do not have the function of magnetized drinking water.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, a kind of preparation method of attapulgite multifunctional paper cup outer sleeve is provided.
The preparation method of attapulgite multifunctional paper cup outer sleeve: the base substrate that is made into attapulgite multifunctional paper cup outer sleeve with the Attapulgite ceramic mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom, top is opened wide, the right side handles that bonds, then enter drying, oven dry, the middle high temperature clean semi-finished product that are that burn till, cool off and polish, magnetic sheet is sticked on half-finished base plate, a topped soft foam pad on the magnetic sheet is packaged as the finished product of attapulgite multifunctional paper cup outer sleeve.
Attapulgite ceramic mud with air purification function is comprised of paste attapulgite clay, attapulite constant humidity amendment, natural-minerals adsorptive filter medium, cacumen biotae, alumina silicate fibre, polyacrylamide and water.
Described paste attapulgite clay is to use Concare convex rod ore pul making production technology, the screening of the mineral such as the hydromica in the Concave-convex clay rod, quartz, opal and carbonate is got rid of, obtain a kind of paste attapulgite clay, paste attapulgite clay is through the high speed strong stirring, become the special good natural gelinite of a kind of thixotropy and gumminess, viscosity is up to more than the 10000mPas, be conducive to the bonding between the raw material, have ultrafine dust, friction hardness little, without the characteristics of sand feeling and soft fine and smooth free from extraneous odour.The dry after-contraction of paste attapulgite clay is little, does not produce be full of cracks, and has good, the high temperature resistant and anti-good character such as saline and alkaline of thixotropy.
Rice hulls, quick dissolved sodium silicate and the zeolite powder of attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying forms.Attapulite constant humidity amendment not only hydroscopicity is good, and after ambient humidity descends, has been adsorbed on the moisture in its duct, will outwards discharge slowly, remains a more stable hydroscopicity, is a kind of constant humidity conditioner of superior performance.The harmful substances such as formaldehyde, ammonia and benzene reduce the infringement healthy to people in the effective absorbed air of attapulite constant humidity amendment energy.
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of natural-minerals adsorptive filter medium after by acidifying forms.Natural-minerals adsorptive filter medium rough, inside have a large amount of micropores, have light specific gravity, specific area is large and absorption property is good characteristics.
Cacumen biotae is spray and the leaf of Cupressaceae plant arbor-vitae
,Summer, autumn gather, and the clip sprig is dried.The cacumen biotae multi-branched, sprig is flat, and the tiny flakey of leaf alternately to life, is pasted and is lied prostrate on branch, bottle green or yellow green, matter is crisp, frangibility, gas delicate fragrance, bitter and puckery flavor, little suffering.It is the charred CACUMEN PLATYCLADI that cacumen biotae is generated pitchy after anoxycausis that cacumen biotae is used for the present invention, has the characteristic of active carbon, has not only increased the porosity of pottery mud product, has also improved the adsorption capacity of pottery mud product.
The characteristics such as alumina silicate fibre is again ceramic fibre, and this material has that thermal capacitance is little, fiber long, lightweight, tensile strength large, the slag ball is few, heat endurance is high, anti-erosion and sound absorption qualities are good.Be used for cracking and improving when the present invention is conducive to avoid making base substrate the intensity of pottery mud product.
Polyacrylamide has good water-soluble and thickening property, the plasticity when being conducive to improve pottery mud making base substrate for the present invention.
The present invention is achieved by following technical proposals:
1, the preparation method of attapulgite multifunctional paper cup outer sleeve is: ⑴ is made into the base substrate of attapulgite multifunctional paper cup outer sleeve with the Attapulgite ceramic mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom in the cylinder shell, the groove of a circle of top reservation of base plate, top in the cylinder shell is opened wide, be the crude green body of attapulgite multifunctional paper cup outer sleeve at the right outside side of the cylinder shell handles that bonds, and with crude green body change over to carry out in the base substrate shed natural drying; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 60～120 ℃, and drying time is controlled at 1～4 hour; ⑶ the crude green body after will dry changes in the kiln, is introduced into middle temperature and burns till the stage, and firing temperature is controlled at 120～250 ℃, firing time is controlled at 1～6 hour, enter middle high temperature again and burn till the stage, firing temperature is controlled at 250～850 ℃, and firing time is controlled at 1～4 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to the clean glossy rear semi-finished product of attapulgite multifunctional paper cup outer sleeve that are of room temperature and polishing; ⑸ stick on a magnetic sheet in the groove above the base plate, and a topped soft foam pad on the magnetic sheet is packaged as the finished product of attapulgite multifunctional paper cup outer sleeve.
Described production method with Attapulgite ceramic mud of air purification function is: ⑴ will have rear the input in the mixer of batching mixing of the Attapulgite ceramic mud of air purification function and stir; ⑵ carry out wet ball grinding in the mixture input ball mill after stir, the grain fineness of ball milling disposed slurry is less than 0.044 millimeter; ⑶ carry out the old semi-finished product that are treated in the slurry input sedimentation basin after with ball milling, half-finished water content is less than 45%, and the old time is controlled at 3～30 days; ⑷ input semi-finished product and push and cut into rectangular block in the vacuum-extruder, and the thickness of the block thing of rectangle is less than 50 millimeters, for having the Attapulgite ceramic mud of air purification function;
Batching with Attapulgite ceramic mud of air purification function is comprised of following component by weight percentage: paste attapulgite clay 45～75%, attapulite constant humidity amendment 5～30%, natural-minerals adsorptive filter medium 5～15%, cacumen biotae 2～10%, alumina silicate fibre 1～5%, polyacrylamide 0.1～3% and water 1～35%.
Attapulgite ceramic mud with air purification function has been applied for patent of invention by the applicant on February 25th, 2011, and number of patent application is: 201110044982.0.
The production technology of described paste attapulgite clay: will stir in the concave convex rod ore deposit input mixer, after extruder is squeezed into sheet, again input in the mixer and stir, natural drying after extruder is squeezed into sheet, the concave convex rod ore deposit of drying is transported in the feed reservoir soaks, turn over the air pump punching, emit immersion water after the precipitation, the sieve decontamination in the input semi-finished product pond, is soaked again, turn over the air pump punching, emit immersion water after the precipitation, and the slurry transportation after will precipitating is paste attapulgite clay in end product pool.
Described paste attapulgite clay is comprised of following component by weight percentage: Concave-convex clay rod 25～60%, water 40～75%.
This production technology is to adopt " Concare convex rod ore pul making production technology " in application on January 6th, 2004 by the inventor, and the Chinese patent Granted publication number is: CN1287965C, Granted publication day: on December 6th, 2006.
Rice hulls, quick dissolved sodium silicate and the zeolite powder of described attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying forms; The production method of attapulite constant humidity amendment is: the rice hulls after the acidifying and Concave-convex clay rod and montmorillonite are mixed by batching, extrusion modification slabbing mixture, abrasive dust after airing mixes by batching with quick dissolved sodium silicate and zeolite powder and is attapulite constant humidity amendment;
The batching of attapulite constant humidity amendment is comprised of following component by weight percentage: the semi-finished product 55～90% of attapulite constant humidity amendment, quick dissolved sodium silicate 2～8% and zeolite powder 5～40%; The half-finished batching of attapulite constant humidity amendment is comprised of following component by weight percentage: the rice hulls 5～15% after the acidifying, Concave-convex clay rod 35～55%, montmorillonite 5～15% and water 35～55%;
Aforementioned production method is to adopt " production method of attapulite constant humidity amendment " in application on August 30th, 2007 by the inventor, and the Chinese patent Granted publication number is: CN100528337C, Granted publication day: on August 19th, 2009.
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of described natural-minerals adsorptive filter medium after by acidifying forms; The preparation method of natural-minerals adsorptive filter medium is: the batching of natural-minerals adsorptive filter medium is natural-minerals adsorptive filter medium through mixing, pulverizing, screening.
The batching of natural-minerals adsorptive filter medium is comprised of following component by weight percentage: the zeolite 15～35% after the acidifying, the Concave-convex clay rod 15～35% after the acidifying, the bentonite 15～25% after the acidifying, the diatomite 10～20% after the acidifying, volcanic rock 5～10% and alumine 5～10%.
Natural-minerals adsorptive filter medium adopts " natural-minerals adsorptive filter medium " in application on May 30th, 2006 by the inventor, and the Chinese patent Granted publication number is: CN100502999C, Granted publication day: on June 24th, 2009.
Using method: dixie cup is directly put into attapulgite multifunctional paper cup outer sleeve, the bottom of dixie cup is a kind of soft contact with the soft foam pad, can guarantee that dixie cup is placed in the attapulgite multifunctional paper cup outer sleeve stably, can normally make tea, can use the handle end of attapulgite multifunctional paper cup outer sleeve to play dixie cup, also can directly hold attapulgite multifunctional paper cup outer sleeve to drink tea.
With boiling water pour into make tea in the dixie cup after, attapulgite multifunctional paper cup outer sleeve not only can play insulation and heat insulation effect, the tea that overflows or trickle down in dixie cup outside can also be adsorbed the dried sanitary of maintenance dixie cup.
A magnetic sheet is arranged at the bottom of attapulgite multifunctional paper cup outer sleeve, can magnetize processing to the tea in the dixie cup, and magnetized drinking water can improve the health.
A large amount of micropores and active carbon are arranged in the attapulgite multifunctional paper cup outer sleeve; function with drier; the harmful substances such as formaldehyde, ammonia and benzene in the effective absorbed air of energy; protection of the environment and enhancement people's is healthy; attapulgite multifunctional paper cup outer sleeve is elegant in appearance, and being placed on indoor is again a handicraft.
The present invention is used for making attapulgite multifunctional paper cup outer sleeve, is applicable to place Disposable paper cup, disposal plastic cup in the attapulgite multifunctional paper cup outer sleeve and does not have handled glass.
Description of drawings
Fig. 1 is the schematic diagram of attapulgite multifunctional paper cup outer sleeve, and Fig. 2 is that the A-A of Fig. 1 is to view.
As shown in the figure: the 1st, cylinder shell, the 2nd, magnetic sheet, the 3rd, soft foam pad, the 4th, groove, the 5th, base plate, the 6th, dixie cup, the 7th, handle.
The specific embodiment
The invention will be further described below in conjunction with embodiment:
1, the preparation method of attapulgite multifunctional paper cup outer sleeve is: ⑴ is made into the base substrate of attapulgite multifunctional paper cup outer sleeve with the Attapulgite ceramic mud with air purification function, base substrate is a cylinder shell 1, the base plate 5 of a sealing is arranged at the bottom in the cylinder shell 1, the groove 4 of a circle of top reservation of base plate 5, top in the cylinder shell 1 is opened wide, be the crude green body of attapulgite multifunctional paper cup outer sleeve at the right outside side of cylinder shell 1 handles 7 that bonds, and with crude green body change over to carry out in the base substrate shed natural drying; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 80～100 ℃, and drying time is controlled at 3 hours; ⑶ the crude green body after will dry changes in the kiln, is introduced into middle temperature and burns till the stage, and firing temperature is controlled at 200～220 ℃, and firing time is controlled at 2 hours, enters middle high temperature again and burns till the stage, and firing temperature is controlled at 500～550 ℃, and firing time is controlled at 1 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to the clean glossy rear semi-finished product of attapulgite multifunctional paper cup outer sleeve that are of room temperature and polishing; ⑸ stick on a magnetic sheet 2 in the groove 4 above the base plate 5, and a topped soft foam pad 3 on the magnetic sheet 2 is packaged as the finished product of attapulgite multifunctional paper cup outer sleeve.
Using method: dixie cup 6 is directly put into attapulgite multifunctional paper cup outer sleeve, the bottom of dixie cup is a kind of soft contacts with soft foam pad 3, can guarantee that dixie cup is placed in the attapulgite multifunctional paper cup outer sleeve stably, can normally make tea, can use handle 7 ends of attapulgite multifunctional paper cup outer sleeve to play dixie cup, also can directly hold attapulgite multifunctional paper cup outer sleeve to drink tea.
Claims (1)
1. the preparation method of an attapulgite multifunctional paper cup outer sleeve, it is characterized in that, ⑴ be made into the base substrate of attapulgite multifunctional paper cup outer sleeve with the Attapulgite ceramic mud with air purification function, base substrate is a cylinder shell, the base plate of a sealing is arranged at the bottom in the cylinder shell, the groove of a circle of top reservation of base plate, top in the cylinder shell is opened wide, be the crude green body of attapulgite multifunctional paper cup outer sleeve at the right outside side of the cylinder shell handles that bonds, and with crude green body change over to carry out in the base substrate shed natural drying; ⑵ change in the low temperature oven and slowly dry after the water content of crude green body is less than 15%, and bake out temperature is controlled at 60～120 ℃, and drying time is controlled at 1～4 hour; ⑶ the crude green body after will dry changes in the kiln, is introduced into middle temperature and burns till the stage, and firing temperature is controlled at 120～250 ℃, firing time is controlled at 1～6 hour, enter middle high temperature again and burn till the stage, firing temperature is controlled at 250～850 ℃, and firing time is controlled at 1～4 hour; ⑷ the crude green body after burn till slowly cools off, and is cooled to the clean glossy rear semi-finished product of attapulgite multifunctional paper cup outer sleeve that are of room temperature and polishing; ⑸ stick on a magnetic sheet in the groove above the base plate, covers a soft foam pad on the magnetic sheet, is packaged as the finished product of attapulgite multifunctional paper cup outer sleeve;
Described production method with Attapulgite ceramic mud of air purification function is: ⑴ will have rear the input in the mixer of batching mixing of the Attapulgite ceramic mud of air purification function and stir; ⑵ carry out wet ball grinding in the mixture input ball mill after stir, the grain fineness of ball milling disposed slurry is less than 0.044 millimeter; ⑶ carry out the old semi-finished product that are treated in the slurry input sedimentation basin after with ball milling, half-finished water content is less than 45%, and the old time is controlled at 3～30 days; ⑷ input semi-finished product and push and cut into rectangular block in the vacuum-extruder, and the thickness of the block thing of rectangle is less than 50 millimeters, for having the Attapulgite ceramic mud of air purification function;
Batching with Attapulgite ceramic mud of air purification function is comprised of following component by weight percentage: paste attapulgite clay 45～75%, attapulite constant humidity amendment 5～30%, natural-minerals adsorptive filter medium 5～15%, cacumen biotae 2～10%, alumina silicate fibre 1～5%, polyacrylamide 0.1～3% and water 1～35%;
The production technology of described paste attapulgite clay: will stir in the concave convex rod ore deposit input mixer, after extruder is squeezed into sheet, again input in the mixer and stir, natural drying after extruder is squeezed into sheet, the concave convex rod ore deposit of drying is transported in the feed reservoir soaks, turn over the air pump punching, emit immersion water after the precipitation, the sieve decontamination in the input semi-finished product pond, is soaked again, turn over the air pump punching, emit immersion water after the precipitation, and the slurry transportation after will precipitating is paste attapulgite clay in end product pool;
Described paste attapulgite clay is comprised of following component by weight percentage: Concave-convex clay rod 25～60%, water 40～75%;
Rice hulls, quick dissolved sodium silicate, zeolite powder and the water of described attapulite constant humidity amendment after by Concave-convex clay rod, montmorillonite, acidifying forms; The production method of attapulite constant humidity amendment is: the rice hulls after the acidifying and Concave-convex clay rod and montmorillonite are mixed by batching, extrusion modification slabbing mixture, abrasive dust after airing mixes by batching with quick dissolved sodium silicate and zeolite powder and is attapulite constant humidity amendment;
The batching of attapulite constant humidity amendment is comprised of following component by weight percentage: the semi-finished product 55～90% of attapulite constant humidity amendment, quick dissolved sodium silicate 2～8% and zeolite powder 5～40%; The half-finished batching of attapulite constant humidity amendment is comprised of following component by weight percentage: the rice hulls 5～15% after the acidifying, Concave-convex clay rod 35～55%, montmorillonite 5～15% and water 35～55%;
Zeolite, Concave-convex clay rod acidifying after, bentonite acidifying after, diatomite acidifying after, volcanic rock and the alumine of the batching of described natural-minerals adsorptive filter medium after by acidifying forms; The preparation method of natural-minerals adsorptive filter medium is: the batching of natural-minerals adsorptive filter medium is natural-minerals adsorptive filter medium through mixing, pulverizing, screening;
The batching of natural-minerals adsorptive filter medium is comprised of following component by weight percentage: the zeolite 15～35% after the acidifying, the Concave-convex clay rod 15～35% after the acidifying, the bentonite 15～25% after the acidifying, the diatomite 10～20% after the acidifying, volcanic rock 5～10% and alumine 5～10%.