CN102282200B - 由包含环己烷-1,2-二羧酸酯作为增塑剂的聚乙烯醇缩醛制成的含增塑剂的膜 - Google Patents
由包含环己烷-1,2-二羧酸酯作为增塑剂的聚乙烯醇缩醛制成的含增塑剂的膜 Download PDFInfo
- Publication number
- CN102282200B CN102282200B CN200980116478.8A CN200980116478A CN102282200B CN 102282200 B CN102282200 B CN 102282200B CN 200980116478 A CN200980116478 A CN 200980116478A CN 102282200 B CN102282200 B CN 102282200B
- Authority
- CN
- China
- Prior art keywords
- film
- plasticizer
- weight
- polyvinyl acetal
- softening agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及含增塑剂的膜,其包含:具有小于74℃的软化温度Tg的聚乙烯醇缩醛,和至少一种环己烷二羧酸酯作为增塑剂。该含增塑剂的膜具有低的增塑剂渗出趋势并且可以将它们用于制造复合安全玻璃和光电模块。
Description
技术领域
本发明涉及适用作复合安全玻璃中的中间层并且基于部分缩醛化的聚乙烯醇、使用氢化邻苯二甲酸酯作为增塑剂的含增塑剂的膜,以及该中间层在复合玻璃层压物和光电模块中的用途。
现有技术
复合安全玻璃通常由两个玻璃板和连接所述玻璃板的中间膜组成。主要使用含增塑剂的部分缩醛化聚乙烯醇(聚乙烯醇缩醛),特别是聚乙烯醇缩丁醛(PVB)作为膜材料。复合安全玻璃(VSG)例如用作汽车工业中的挡风玻璃或侧窗玻璃和建筑工业中的安全玻璃。
同时,已经确立的是三甘醇或四甘醇的脂族二酯作为用于这类PVB膜的增塑剂。特别常见的是使用3G7、3G8或4G7作为增塑剂,第一个数字表示乙二醇单元的数目并且最后一个数字表示化合物的羧酸部分中碳原子的数目。因此3G8代表三甘醇-双-(2-乙基己酸酯),即式C4H9CH(CH2CH3)CO(OCH2CH2)3O2CCH(CH2CH3)C4H9的化合物。
在VSG中间层膜中提供膜的高透明性、低吸水性、好的玻璃粘结性和足够低温柔性的化合物优选用作部分缩醛化聚乙烯醇用的增塑剂。此外,这些化合物必须展现出与部分缩醛化聚乙烯醇足够的相容性,即它们必须可以以足够的量与其混合,不会再次渗出。
增塑剂和部分缩醛化的聚乙烯醇的相容性通常随着增塑剂的极性降低而降低。因此较高极性的增塑剂比较低极性的那些更好地与聚乙烯醇缩醛相容。备选地,低极性增塑剂的相容性随着缩醛化程度,即随着羟基数目减少和因此聚乙烯醇缩醛的极性降低而增加。
在EP 0877 665 B1中,低极性的3G8被推荐作为用于PVB膜的增塑剂,因为其使得膜产品更耐水。由于水分可能永久性损坏粘结膜与玻璃之间的粘结性,在极端情形中导致膜可见地从玻璃上脱离,因此希望在使用PVB膜制造复合安全玻璃(VSG)期间膜展现出尽可能高的耐水性。
用3G8增塑的PVB膜改进的耐水性由该增塑剂与例如4G7或3G7 增塑剂相比较强的非极性产生,因为由辛酸残基代替了庚酸基化学构成增塑剂分子。使用3G8的另一个优点是其的相对低挥发性,这一方面抵抗在VSG的自由边缘增塑剂消耗,和另一方面导致当加工膜形成VSG时仅产生些微讨厌的气味。
出于这些原因,增塑剂3G8在短时间内在PVB膜生产商中得以确立。
一方面,与在其它工业分支中广泛流传的标准增塑剂例如用于增塑PVC的邻苯二甲酸酯相比,该产品的优异技术性能补偿了显著更高的准备或生产成本。另外,希望增塑的PVB膜的吸水性进一步降低,因为复合安全玻璃的寿命可以因此进一步增加。然而在3G8的情形中,吸水性进一步降低受到高度亲水性三甘醇的比例限制。
从EP 0 877 665 B1获知具有大于19.5重量%的聚乙烯醇含量的PVB类型不能容易地用3G8增塑,因为预期增塑剂将渗出。正如其它含增塑剂的塑料产品的情形,在用于VSG的中间层膜的情形中增塑剂渗出也是不希望的,因为增塑剂的释放,尤其是沿着PVB的自由边缘,可能导致在复合物边缘过早脱层。在EP 0877 665 B1中,由于3G8的相容性低或渗出趋势,因此3G8的使用受限于具有17-19.5重量%的聚乙烯醇含量的PVB类型。
原则上,增塑剂/PVB混合物的差相容性还适用于其它非极性增塑剂,例如在酯醇中具有多于6个碳原子的己二酸二烷基酯、在酯醇中具有多于4个碳原子的癸二酸二烷基酯,或者邻苯二甲酸酯增塑剂,例如邻苯二甲酸二辛酯或邻苯二甲酸二异壬酯。在差的相容性情形中,特别在潮湿和/或低温环境中储存期间观察到增塑剂渗出。当在实践中使用PVB膜时两种条件均盛行,并且因此对于增塑剂相容性的评价关系重大。
PVB膜的卷通常在低于8℃的温度下储存和运输,以避免相邻的膜层粘结。在该情形中,自然不希望在储存期间液体增塑剂从膜中排出。
另外,取决于气候条件,使用PVB膜制造的复合安全玻璃当安装时经受低温和高大气湿度,这可能导致增塑剂的渐进损耗和因此形成小气泡形式的可见缺陷或者膜从玻璃上脱离,特别是在PVB膜暴露的VSG边缘下相容性不充足的话。
除了低相容性,与较强极性增塑剂相比低极性的增塑剂例如3G7与 给定的PVB组合展现出导致PVB膜低温柔性降低的性能。如果增塑剂含量设置为小于25重量%和/或如果使用的聚乙烯醇缩丁醛本身具有低缩醛化程度和因此高的聚乙烯醇基团残余含量,尤其是这种情况。如果,即缩醛化程度过低,则PVB的软化温度(Tg)将增加,这对在由此制得的含增塑剂的膜的低温柔性有负面影响。
DE 101 16812 A1推荐使用环己烷多羧酸酯的衍生物增塑PVC和PVB。在该情形中,公开了包含聚乙烯醇缩丁醛的混合物,其中游离羟基的份额为5-50%。取决于环状缩醛基团、羟基和乙酸酯基团的类型和分布,这些聚乙烯醇缩丁醛展现出至少80℃的软化温度Tg。
整个混合物的聚乙烯醇缩醛含量指定为5-95重量%,特别为20-55重量%。基于增塑剂含量,这对应于5-95重量%或45-80重量%的值范围,假定不加入另外的组分。
当使用具有多于80℃的软化温度的PVB时,伴随着较高的增塑剂份额出现不相容。如果增塑剂含量减少,则导致膜的低温柔性降低。
技术目的
需要使用增塑剂的PVB膜制剂,该增塑剂以更低成本获得,与3G8相比在膜中导致降低的吸水性,和与展现出足够高的缩醛化程度的部分缩醛化聚乙烯醇的组合是相容的,并且制得具有好的低温柔性的膜。
技术解决方案
发现包含具有低软化温度(Tg)的聚乙烯醇缩丁醛并且用1,2-环己烷二羧酸二酯软化的膜与包含3G8作为增塑剂的膜相比展现出降低的吸水性。该组成的膜具有好的增塑剂相容性水平和好的低温柔性。
发明描述
因此本发明涉及含增塑剂的膜,其包含:60-90%的具有小于74℃的软化温度Tg的聚乙烯醇缩醛,和10-40重量%(基于膜的总配方)的至少一种在酯基中具有4-17个C原子的环己烷二羧酸酯。
DE 101 16 812中公开的所有化合物均可用作环己烷二羧酸酯。
由于它们容易的获得性,因此氢化的邻苯二甲酸即1,2-环己烷二羧酸的二酯是本发明的优选增塑剂。
特别地,具有9-17个碳原子的酯醇被用作酯醇,并且特别优选使用具有9、13或17个碳原子的那些(人们所说的羰基合成醇(Oxoalkohol))。这些醇可以以支化或未支化的形式使用,其中主要未支 化的酯醇的使用产生更好的增塑效果。
根据本发明使用的环己烷二羧酸酯增塑剂可以与至少一种另外的也适合作为另外的增塑剂的非极性或极性增塑剂组合使用,其份额为1-40%。
膜优选具有10-40重量%、14-32重量%、16-30重量%、18-28重量%,特别为22-26重量%的总增塑剂含量,即膜中全部增塑剂的份额。基于该混合物,根据本发明使用的环己烷二羧酸酯增塑剂的份额可以为多于10%、多于20%、多于30%、多于40%、多于50%、多于60%、多于70%、多于80%或多于90%。
膜原则上可以包含得自提及的环己烷二羧酸酯的增塑剂的增塑剂混合物,该增塑剂混合物包含至少一种以下已知用于PVB膜的增塑剂:
●多价脂族或芳族酸的酯,例如己二酸二烷基酯例如己二酸二己酯、己二酸二辛酯、己二酸己基环己酯、己二酸庚酯和壬酯的混合物、己二酸庚基壬酯,和己二酸与脂环族酯醇或者含醚键的酯醇的酯,癸二酸二烷基酯例如癸二酸二丁酯,以及癸二酸与脂环族酯醇或含醚键的酯醇的酯,邻苯二甲酸酯例如邻苯二甲酸丁基苄酯或双-2-丁氧基乙基邻苯二甲酸酯,
●具有一个或多个未支化或支化的脂族或芳族取代基的多元脂族或芳族醇或者低聚醚乙二醇的酯或醚,例如具有线型或支化脂族或脂环族羧酸的二、三或四乙二醇的酯;后一类的例子可以包括二甘醇-双-(2-乙基己酸酯)、三甘醇-双-(2-乙基己酸酯)、三甘醇-双-(2-乙基丁酸酯)、四甘醇-双-正庚酸酯、三甘醇-双-正庚酸酯、三甘醇-双-正己酸酯、四甘醇二甲醚和/或二丙二醇苯甲酸酯。
合适的另外高极性增塑剂类包括,例如二-(2-丁氧基乙基)-己二酸酯(DBEA)、二-(2-丁氧基乙基)-癸二酸酯(DBES)、二-(2-丁氧基乙基)-壬二酸酯、二-(2-丁氧基乙基)-戊二酸酯、二-(2-丁氧基乙氧基乙基)-己二酸酯(DBEEA)、二-(2-丁氧基乙氧基乙基)-癸二酸酯(DBEES)、二-(2-丁氧基乙氧基乙基)-壬二酸酯、二-(2-丁氧基乙氧基乙基)-戊二酸酯、二-(2-己氧基乙基)-己二酸酯、二-(2-己氧基乙基)-癸二酸酯、二-(2-己氧基乙基)-壬二酸酯、二-(2-己氧基乙基)-戊二酸酯、二-(2-己氧基乙氧基乙基)-己二酸酯、二-(2-己氧基乙氧基乙基)-癸二酸酯、二-(2-己氧基乙氧基乙基)-壬二酸酯、二-(2-己氧基乙氧基乙基)-戊二酸酯、二-(2-丁氧基乙基)-邻苯二甲 酸酯和/或二-(2-丁氧基乙氧基乙基)-邻苯二甲酸酯。也可以使用非离子表面活性剂。
为了不会不必要地通过使用在混合物中过度极性的增塑剂而削弱膜的耐水性,特别地可以将低极性的增塑剂与根据本发明使用的环己烷二羧酸酯组合。低极性的增塑剂合适的是根据公式100x(O原子数)/(C原子数+H原子数)计算,具有小于/等于9.4的极性的增塑剂。包含具有多于6个碳原子的烷基残基的己二酸二烷基酯和包含具有多于7个碳原子的羧酸残基的低聚乙醇酸酯被优选用作低极性增塑剂。特别地,以下化合物是合适的:
表1
名称 | 极性值 |
二-2-乙基己基癸二酸酯(DOS) | 5.3 |
二-2-乙基己基己二酸酯(DOA) | 6.3 |
二-2-乙基己基邻苯二甲酸酯(DOP) | 6.5 |
三甘醇-双-2-丙基己酸酯 | 7.9 |
三甘醇-双-异壬酸酯 | 8.6 |
二-2-丁氧基乙基癸二酸酯(DBES) | 9.4 |
三甘醇-双-2-乙基己酸酯(3G8) | 9.4 |
根据本发明的膜也可以包含本领域技术人员已知的另外的添加剂,例如剩余量的水、UV吸收剂、抗氧化剂、粘结调节剂、荧光增白剂、稳定剂、着色剂、加工助剂、有机或无机纳米颗粒、热解硅酸 和/或表面活性物质。
通过使用提及的增塑剂或增塑剂组合,可以制造展现出特别低的增塑剂排出的膜,这造成在加工期间产生降低的讨厌气味或减少增塑剂气溶胶的排出可能性的优点,并且造成最终VSG增加的寿命的优点。
根据本发明的膜的增塑剂排出(如下文定义)优选为少于4重量%,优选3重量%,特别优选少于2重量%并且最优选少于1重量%,在每一情形下基于整个膜。
具有等于或大于81重量%,优选82,特别优选83,特别为84重量%的聚乙酸乙烯酯含量(缩醛化程度)的部分乙缩醛化或部分丁缩醛化的聚乙烯醇(聚乙烯醇缩丁醛)优选用作部分缩醛化的聚乙烯醇,因为这些 部分缩醛化的聚乙烯醇具有足够低的软化温度和极性,并且制得与环己烷二羧酸酯增塑剂相容并具有好的低温柔性的制剂。然而,不应该超过87重量%的缩醛化程度,因为膜的机械性能通常不再充足。在本发明的特别优选的变型中,在1重量%残余乙酸酯下,缩醛化程度约为81-87、82-86和83-85.5重量%。在高于1重量%的较高残余乙酸酯含量下,给出的缩醛化程度的数值相应降低。
缩醛化程度和残余乙酸酯的总和可以由根据ASTM D 1396确定的聚乙烯醇含量(即聚乙烯醇缩醛的游离羟基的含量)产生至100所需的剩余部分计算。缩醛化程度也可以通过高分辨率NMR谱直接确定。
为了使根据本发明的膜具有足够的低温柔性,同时在升高的温度下也具有足够的机械强度,可用于本发明的聚乙烯醇缩醛通常具有小于/等于74℃,优选64-74℃,优选65-73℃,特别优选66-72℃并且特别为61-71℃的软化温度(Tg)。
为了制备聚乙烯醇缩醛,将聚乙烯醇溶于水并且伴随着加入酸催化剂用醛例如丁醛缩醛化。将制得的聚乙烯醇缩醛分离出来、中性清洗、任选地悬浮于碱性含水介质中并且然后再次中性清洗,并且干燥。
可以通过在缩醛化期间使用的醛的量调节聚乙烯醇缩醛的聚乙烯醇含量。也可以使用其它或另外的具有2-10个碳原子的醛(例如戊醛)进行缩醛化。
基于含增塑剂的聚乙烯醇缩醛的膜优选包含通过用丁醛将聚乙烯醇缩醛化获得的未交联聚乙烯醇缩丁醛(PVB)。
交联聚乙烯醇缩醛,特别是交联聚乙烯醇缩丁醛(PVB)的使用也是可能的。合适的交联聚乙烯醇缩醛描述于例如EP 1527107 B1和WO2004/063231 A1(含羧基的聚乙烯醇缩醛的热自交联)、EP 1606325 A1(与聚醛交联的聚乙烯醇缩醛),和WO 03/020776 A1(与乙醛酸交联的聚乙烯醇缩醛)。这些专利申请的公开内容全部作为参考引入本文。
水解乙酸乙烯酯/乙烯共聚物的三聚物也可用作本发明范围内的聚乙烯醇。这些化合物通常水解至超过98mol%并且含有1-10重量%基于乙烯的单元(例如得自Kuraray Europe GmbH的″Exceval″类型)。
此外,由乙酸乙烯酯和至少一种另外的烯属不饱和单体的水解共聚物也可用作本发明范围内的聚乙烯醇。
在本发明的范围内,聚乙烯醇可以纯的形式或者作为具有不同的聚 合度或水解度的聚乙烯醇混合物使用。
除了缩醛单元,聚乙烯醇缩醛还包含由乙酸乙烯酯和乙烯醇产生的单元。使用的部分缩醛化聚乙烯醇的聚乙烯醇含量通常为12-18%,优选13-16%并且最优选14-16%。
根据本发明使用的聚乙烯醇缩醛的残余乙酸酯含量通常为低于5重量%,优选低于3重量%,特别优选低于2重量%并且特别低于1.5重量%或1重量%。
基于聚乙烯醇缩醛的膜的原理性制备和组成描述于例如EP 185 863B1、EP 1 118 258 B1、WO 02/102591 A1、EP 1 118 258 B1或EP 387 148 B1中。
工业应用
根据本发明的膜可以特别地以本领域技术人员已知的方式通过与一个或多个玻璃板层压制造复合安全玻璃。该复合安全玻璃可在汽车工业中使用例如作为挡风玻璃,和在建筑领域中作为透明建筑部件,或者在家具构造中。由于它们的低吸水性和增塑剂排出,因此根据本发明的膜还非常适用于制造玻璃/膜/塑料层压物,例如用于在玻璃板与PET层之间提供持续的粘结性。也可以使用根据本发明的膜粘结例如由聚碳酸酯或PMMA制成的两个塑料板。
根据本发明的膜可用于粘结光电模块。
因此本发明进一步涉及包括以下部件的层压物的光电模块:
a)透明前覆盖层,
b)一个或多个光敏半导体层,
c)至少一个基于聚乙烯醇缩醛的含增塑剂的膜,和
d)后覆盖层,
该含增塑剂的膜包含:60-90%的具有小于74℃的软化温度Tg的聚乙烯醇缩醛,和10-40重量%的至少一种在酯基中具有4-17个C原子的环己烷二羧酸酯作为增塑剂。
所有所述的含增塑剂的膜的变型或者所述的环己烷二羧酸酯的变型可用于根据本发明的光电模块。
根据本发明使用的膜优选在85%相对湿度环境湿度下在23℃展现出至少5E+11 ohm*cm,或至少1E+12 ohm*cm,特别优选至少5E+12ohm*cm,或至少1E+13 ohm*cm,或特别为至少1E+14 ohm*cm的电阻 率。这些值将在膜的任何位置,特别在模块的边缘区域实现。
此外,离子迁移率-其可能取决于膜的水含量,和因此电阻率可能受到SiO2,特别是热解硅酸加入的影响。基于聚乙烯醇缩醛的根据本发明使用的含增塑剂的膜优选包含0.001-15重量%,优选2-5重量%的SiO2。
当制备膜材料时避免酸痕迹 可以减少与光敏半导体层相比根据本发明使用的膜的腐蚀易受性。这类膜通常通过在升高的温度挤出含增塑剂的聚乙烯醇缩醛制备,其中聚合物材料或增塑剂可以进行热分解。此外,聚乙烯醇的残余乙酸酯基团可能被扩散进入的水分解,由此释放乙酸。在两种情形中产生酸痕迹,其可能侵蚀光敏半导体层。
因此按照碱滴定度表示,根据本发明使用的膜优选展现出将超过5或10,优选超过15并且特别超过20、30或40的特定碱度。应该不超过100的最大碱滴定度。
如下文所述,碱滴定度通过膜返滴定确定并且可以通过加入碱性物质例如具有1-15个碳原子的有机羧酸的金属盐,特别是碱金属盐或碱土金属盐例如乙酸镁或乙酸钾调节。基于整个混合物,碱性化合物通常以0.005-2重量%,特别为0.05-1重量%的浓度使用。
通过使膜熔化进行光电模块的层压,使得用膜实现光敏半导体层的无气泡和无波纹封装。
在根据本发明的光电模块的一个变型中,光敏半导体层施加于覆盖层d)(例如通过蒸镀、气相沉积、溅射或湿沉积)并且借助于膜c)与透明前覆盖层a)粘结。
在另一个变型中,光敏半导体层施加于透明前覆盖层a)并且借助于膜c)与后覆盖层d)粘结。
备选地,光敏半导体层可以嵌入两个膜c)之间并且以该方式与覆盖层a)和d)粘结。
在用于光电模块的情形中,基于含增塑剂的聚乙烯醇缩醛的膜的厚度通常为0.38、0.51、0.76、1.14、1.52或2.28mm。
在层压过程期间,根据本发明使用的膜填充存在于光敏半导体层或其的电连接的空隙。
透明前覆盖层a)通常由玻璃或PMMA组成。根据本发明的光电模块的后覆盖层d)(所谓的后板)可由玻璃、塑料或金属或者其的复合物组成,其 中载体之一可以是透明的。还可以将一个或两个覆盖层设计为复合玻璃(即由至少两个玻璃板和至少一个PVB膜制成的层压物)或者具有气隙的绝缘玻璃。自然地,这些措施的组合也是可能的。
用于模块的光敏半导体层不需要具有任何特殊性能。可以使用单晶、多晶或非晶态体系。
在薄膜太阳能模块的情形中,将光敏半导体层直接施加于载体。这里不可能包封。因此,由载体(例如后覆盖层)与光敏半导体层和透明前覆盖层通过至少一个置于其间的基于含增塑剂的聚乙烯醇缩醛的本发明的膜组装层体,并藉此在升高的温度粘结。备选地,光敏半导体层可以施加于作为载体的透明前覆盖层,并且借助于至少一个置于其间的根据本发明的基于含增塑剂的聚乙烯醇缩醛的膜与后覆盖层粘结。
为了层压由此获得的层体 可以使用本领域那些技术人员已知的方法,预先或不预先制备预复合物(Vorverbund)。
所谓的高压釜工艺在约10-15巴的升高压力和130-145℃的温度下在约2小时内进行。例如根据EP 1 235 683 B1,真空袋或真空环方法在约200毫巴和130-145℃的温度工作。
真空层压机优选用于制造根据本发明的光电模块。它们由可加热并且可抽真空的室组成,在其中复合玻璃可以在30-60分钟内层压。0.01-300毫巴的降低压力和100-200℃,特别是130-160℃的温度在实践中证明有价值。
备选地,可以在至少一对辊子之间在60-150℃温度将如上所述组装的层体压制成根据本发明的模块。这类装置被已知用于制造复合玻璃并且通常在具有两个压制设备的装置中在第一压制设备的上游或下游具有至少一个加热通道。
根据本发明的光电模块可用作正面元件(Fassadenbauteil)、屋顶面、温室覆盖物、隔音墙、阳台或胸墙元件,或者作为窗口区域构件。
测量方法
为了测定碱滴定度,在磁性搅拌机中将3-4g含增塑剂的聚乙烯醇缩醛膜溶于100ml乙醇/THF(80∶20)的混合物中过夜。出于该目的,加入10ml稀盐酸(c=0.01mol/升)并且然后使用滴定处理器相对于空白样品用氢氧化四丁铵(TBAH)于2-丙醇中的溶液(c=0.01mol/升)电位滴定。碱滴 定度如下计算:
碱滴定度=ml HCl/100g样品=(TBAH空白样品的消耗量-TBAH样品x以g计的100样品重量)
在膜于下面条件下调节至少24h后,根据DIN IEC 60093在规定的温度和环境湿度(23℃和85%空气相对湿度)下进行膜的体积电阻率测量。为了完成测量,使用得自Fetronic GmbH公司的型号302 132的板电极,和得自Amprobe公司的电阻测量仪器ISO-Digi 5kV。试验电压为2.5kV,施加试验电压后直到获得测量数据的等待时间为60秒。为了保证测量电极的平板与膜之间充分接触,当根据DIN EN ISO 4287测量时膜的表面粗糙度Rz应该不大于10mm;即如果需要,在电阻测量前必须通过热重新压印使PVB膜的原始表面光滑。
聚乙烯醇缩醛的聚乙烯醇和聚乙烯醇乙酸酯含量根据ASTM D1396-92测量。金属离子含量的分析借助于原子吸收光谱(AAS)进行。膜的水或水分含量通过卡尔费歇尔(Karl Fischer)方法确定。
为了测定PVB膜在高湿度下的渗出性能,将测试条在用水蒸气饱和的气氛中储存30天。由于吸水性和因此伴随着极性增加,因此增塑剂可以使得其在膜表面作为高度可见的膜或以液滴的形式随着时间排出的方式代替较少相容的体系。在相容制剂的情形中,在30天后在测试条上没能验证到增塑剂排出,而在不相容制剂情形中仅在24h后通常已经出现这种情形。为了调节较大相对空气湿度(相对湿度)的气氛,在密闭容器例如玻璃干燥器中伴随着沉淀制备五水合硫酸铜的饱和水溶液。在23℃下通过该溶液调节约98%相对湿度的平衡湿度。
为了测定PVB膜在低温环境中的渗出性能,首先便规格为30x10cm的膜部分在23℃/23相对湿度气候下调节24h并且然后卷绕成卷,密封入在不透水蒸气的Alu-PE袋中并且在5℃温度下储存1星期。一旦这一星期过去,取出膜并且检查排出的增塑剂。
例如,为了生产塑化的PVB膜,可以例如在滚筒架上或通过挤出使膜物质均匀以检验其的渗出性能。
在实验中在基于如用于制造光电模块那样在真空层压机中进行加工的条件下测定来自PVB膜的增塑剂排出。为了该目的,由0.76mm厚的膜/样品切割或制造具有60mm直径的圆片坯料,并且以底座上的平面方式插入具有65mm直径的配衡的铝壳(neoLab铝壳,光滑,65mm,产 品号2-1605,重量约2.5g)。将样品在壳中在23℃/25%相对湿度气候下调节过夜,并且然后在真空干燥箱(Heraeus,型号VTR 5022)中在150℃和1毫巴下保持30分钟。在重新称重前,将壳再次在23℃/25%相对湿度下调节过夜。以%计基于膜原始重量确定的重量减少被定义为增塑剂排出。
根据DIN 53765在-50℃至150℃的温度间隔中使用10K/min的加热速率借助于差示扫描量热法(DSC)进行部分缩醛化聚乙烯醇的软化温度Tg的测量。采用第一次加热爬坡,随后冷却下坡,随后第二次加热爬坡。根据DIN51007由归于第二次加热爬坡的测量曲线确定玻璃化转变温度的位置。DIN中点(Tg DIN)被定义为水平线在半梯段高度与测量曲线的交点。梯段高度由与玻璃化转变之前和之后测量曲线的基线的中间切线的两个交叉点的垂直距离定义。
膜的水含量或湿含量通过卡尔费歇尔(Karl Fischer)方法测量,根据该方法,将膜在23℃和85%相对湿度下调节至少24h。
膜的低温柔性以简单的方式通过在5℃储存温度下人工比较DINA4大小的膜部分而评价。
实施例
在实施例的根据本发明的膜符合通常放在用于复合安全玻璃或光电模块的PVB膜上的要求,更具体地:高透明性或没有浑浊,低固有颜色,特别是低黄度,足够的机械强度,低固有气味,通过加入常规抗粘结剂减小粘结性的可能,对玻璃好且均匀的粘结作用,和高体积电阻。
制备表2-4中所示的组成的膜并且检验它们在复合安全玻璃或光电模块中的适用性。除非另外说明,所有数据以基于总的膜的重量%计,例外的是:PVOH含量基于PVB树脂的量。Hexamoll DINCH代表得自BASF SE的二异壬基环己烷-1,2-二羧酸,AEROSIL 130是得自EvonikDegussa GmbH的商业产品。
参考比较例1,其证实在潮湿气氛(30天后)或在低温环境中(1星期后),具有79重量%缩醛化程度、20.0重量%PVA含量和75℃软化温度的聚乙烯醇缩丁醛在PVB膜常用的混合比(74重量%PVB、26重量%DINCH)下使DINCH再次部分排出,即其展现出渗出。另外,这类膜仅展现出平均的低温柔性。
比较例8表明,在潮湿气氛(30天后)或在低温环境中(1星期后)伴随 着使用相对少量的DINCH作为增塑剂(80重量%PVB、20重量%DINCH),具有72.5重量%缩醛化程度、26.4重量%PVA含量和81℃软化温度的聚乙烯醇缩丁醛再次部分排出,即展现出渗出。另外,这类膜具有差的低温柔性。
根据本发明的实施例2和4与比较例3和5(非根据本发明进行)的比较表明,与使用3G8制备的试验膜相比,当使用DINCH时吸湿性和增塑剂排出可以进一步减少。
根据本发明的实施例6表明,当在包含26重量%Hexamoll DINCH的混合物中使用具有86重量%缩醛化程度、13.0重量%PVA含量和67℃软化温度的聚乙烯醇缩丁醛,制得展现出特别低的吸湿性和低增塑剂排出的足够相容的膜。
根据本发明的实施例7表明,当伴随着使用四水合乙酸镁在包含24重量%Hexamoll DINCH的混合物中使用具有84.7重量%缩醛化程度、14.3重量%PVA含量和68℃软化温度的聚乙烯醇缩丁醛,可以设置增加的碱滴定度,而不会削弱体积电阻并且不会影响所述的足够相容性以及特别低的吸湿性和增塑剂排出的特征。
根据本发明的实施例8表明,当通过加入热解SiO2和使用四水合乙酸镁在包含24重量%Hexamoll DINCH的混合物中使用具有84.7重量%缩醛化程度、14.3重量%PVA含量和68℃软化温度的聚乙烯醇缩丁醛,可以设置增加的碱滴定度并且同时可以进一步增加体积电阻,不会显著影响所述的足够相容性以及特别低的吸湿性和增塑剂排出的特征。
根据本发明的实施例9表明,当通过加入热解SiO2在包含24重量% Hexamoll DINCH的混合物中使用具有84.7重量%缩醛化程度、14.3重量%PVA含量和68℃软化温度的聚乙烯醇缩丁醛,可以进一步增加体积电阻,不会显著影响所述的足够相容性以及特别低的吸湿性和增塑剂排出的特征。
由于它们好的绝缘性能,根据本发明的膜非常适合于制造光电模块。另外,由于它们增加的碱性和/或热解SiO2的存在,因此根据本发明的实施例7-9的膜与光电模块的敏感功能层相比展现出特别低的腐蚀性。
表2
表3
表4
Claims (14)
1.含增塑剂的膜,其包含:60-90%的聚乙烯醇缩醛,和10-40重量%的至少一种在酯基中具有4-17个C原子的环己烷二羧酸酯作为增塑剂,
其中所述聚乙烯醇缩醛具有小于74℃的软化温度Tg,该软化温度Tg根据DIN53765在-50℃至150℃的温度间隔中使用10K/min的加热速率借助于差示扫描量热法进行测量,并且所述膜展现出少于4重量%的增塑剂排出。
2.根据权利要求1的含增塑剂的膜,特征在于该膜还包含1-40重量%的至少一种另外的增塑剂。
3.根据权利要求1或2的含增塑剂的膜,特征在于该膜还包含1-40重量%的至少一种选自以下的高极性增塑剂:二-(2-丁氧基乙基)-己二酸酯、二-(2-丁氧基乙基)-癸二酸酯、二-(2-丁氧基乙基)-壬二酸酯、二-(2-丁氧基乙基)-戊二酸酯、二-(2-丁氧基乙氧基乙基)-己二酸酯、二-(2-丁氧基乙氧基乙基)-癸二酸酯、二-(2-丁氧基乙氧基乙基)-壬二酸酯、二-(2-丁氧基乙氧基乙基)-戊二酸酯、二-(2-己氧基乙基)-己二酸酯、二-(2-己氧基乙基)-癸二酸酯、二-(2-己氧基乙基)-壬二酸酯、二-(2-己氧基乙基)-戊二酸酯、二-(2-己氧基乙氧基乙基)-己二酸酯、二-(2-己氧基乙氧基乙基)-癸二酸酯、二-(2-己氧基乙氧基乙基)-壬二酸酯、二-(2-己氧基乙氧基乙基)-戊二酸酯、二-(2-丁氧基乙基)-邻苯二甲酸酯和二-(2-丁氧基乙氧基乙基)-邻苯二甲酸酯。
4.根据权利要求1或2的含增塑剂的膜,特征在于,该膜还包含1-40重量%的至少一种具有小于/等于9.4的极性的化合物作为增塑剂,所述极性根据公式100x(O原子数)/(C原子数+H原子数)计算。
5.根据权利要求1或2的含增塑剂的膜,特征在于聚乙酸乙烯酯的缩醛化程度为大于/等于81重量%。
6.根据权利要求1或2的含增塑剂的膜,特征在于聚乙烯醇缩醛的乙酸酯含量为小于5重量%。
7.根据权利要求1或2的含增塑剂的膜,特征在于所述膜具有20-30重量%的环己烷二羧酸酯含量。
8.根据权利要求1或2的含增塑剂的膜,特征在于使用聚乙烯醇缩丁醛作为聚乙烯醇缩醛。
9.根据权利要求1-8任一项的含增塑剂的膜用于制造复合玻璃、挡风玻璃或光电模块的用途。
10.光电模块,包括以下组件的层压物:
a)透明前覆盖层,
b)一个或多个光敏半导体层,
c)至少一个基于聚乙烯醇缩醛的含增塑剂的膜,和
d)后覆盖层,特征在于该含增塑剂的膜包含:60-90%的具有小于74℃的软化温度Tg的聚乙烯醇缩醛,和10-40重量%的至少一种在酯基中具有4-17个C原子的环己烷二羧酸酯作为增塑剂,其中根据DIN53765在-50℃至150℃的温度间隔中使用10K/min的加热速率借助于差示扫描量热法进行部分缩醛化聚乙烯醇的软化温度Tg的测量。
11.根据权利要求10的光电模块,特征在于基于聚乙烯醇缩醛的含增塑剂的膜c)包含具有1-15个碳原子的羧酸金属盐作为碱性化合物。
12.根据权利要求10或11的光电模块,特征在于基于聚乙烯醇缩醛的含增塑剂的膜包含0.001-5重量%的SiO2。
13.根据权利要求10或11的光电模块,特征在于将一个或多个光敏半导体层b)施加于透明前覆盖层a)或后覆盖层d),并且通过至少一个基于聚乙烯醇缩醛的含增塑剂的膜c)彼此粘结。
14.根据权利要求10-12任一项的光电模块,特征在于将光敏半导体层b)嵌入两个膜c)之间并且与覆盖层a)和d)相粘结。