CN102262018A - 内衬pvc钢筋混凝土排水管pvc焊接接头水压试验方法及所用的试验装置 - Google Patents
内衬pvc钢筋混凝土排水管pvc焊接接头水压试验方法及所用的试验装置 Download PDFInfo
- Publication number
- CN102262018A CN102262018A CN2011101618436A CN201110161843A CN102262018A CN 102262018 A CN102262018 A CN 102262018A CN 2011101618436 A CN2011101618436 A CN 2011101618436A CN 201110161843 A CN201110161843 A CN 201110161843A CN 102262018 A CN102262018 A CN 102262018A
- Authority
- CN
- China
- Prior art keywords
- pvc
- welding
- lining
- tank
- reinforced concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法，依照下列步骤完成：(1)焊制PVC接头试件：将焊接工艺确定以后依据焊接工艺将两块PVC衬里焊接牢固；(2)用电火花监测仪检测PVC衬里及焊缝在常压状态下有无漏点后将焊好的试件安装在试验装置上；(3)加压检测：将试验装置充满水后以0.02MPa/min的速度缓慢加压，待压力升至设计压力后恒压5min后观察焊缝有无开裂。该试验方法是采用等效内压法不仅能直接检测PVC衬里接头耐水压的能力，而且还能模拟实际的工况条件直观的检测PVC衬里接头的耐压值。
Description
技术领域：
本发明涉及一种排水管接头水压试验方法，特别涉及一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法。
背景技术：
随着内衬PVC防腐蚀钢筋混凝土排水管在我国的建筑市场中的逐步应用，这种产品的各种试验方法开始受到使用者和生产厂家的重视。目前各种地方性的标准相继出台，为规范这种产品起到了很好的作用。但是各种标准在制定过程中主要参照现行的国家标准(GB/T11836-2009《混凝土和钢筋混凝土排水管》)来制定的，产品的试验方法一般还是采用混凝土和钢筋混凝土排水管的试验方法，内水压力检测采用闭水试验法检测。
而内衬PVC防腐蚀钢筋混凝土排水管作为一种特殊结构的排水管，其管道内壁镶衬了一层耐腐蚀的PVC衬里，使管道内部的腐蚀介质与管道内壁混凝土隔开，从而有效地保护了管子内壁的混凝土和埋入混凝土内的钢筋。在管道生产的过程中PVC衬里需要焊接，在管道的安装过程中管与管接头处的PVC衬里也需要焊接，这样可以使管道内壁PVC衬里连为一体，以确保制作管道的混凝土不予腐蚀介质侵蚀接触，达到管线整体防腐蚀的效果(见图1)。但是用单纯的闭水试验法却只能检测出这每一根管子的混凝土抗渗情况，而不能检测管道内PVC衬里的密封耐水压效果，因为普通混凝土排水管自身就具有很强耐水压能力，即使PVC衬里的焊缝开裂，水压试验时也无法检测PVC衬里的开裂情况。一旦焊缝达不到设计的耐水压能力，水压试验时焊缝将压破，介质将直接与混凝土接触，但是试验人员从管道外侧根本无法观察到焊缝的渗漏情况，而无法判断接头的焊接后密封性能，从而使其防腐效果丧失。
发明内容：
本发明的目的就在于提供一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法，该试验方法是采用等效内压法不仅能直接检测PVC衬里接头耐水压的能力，而且还能模拟实际的工况条件直观的检测PVC衬里接头的耐压值。
本发明的另一个目的是提供一种上述试验方法所用的试验装置，该装置结构简单、操作方便，可检测PVC防腐蚀钢筋混凝土排水管内的PVC衬里的密封 耐水压效果。
如上构思，本发明的技术方案是：一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法，其特征在于：依照下列步骤完成：
(1)焊制PVC接头试件：将焊接工艺确定以后依据焊接工艺将两块PVC衬里焊接牢固；
(2)组装：用电火花监测仪检测PVC衬里及焊缝在常压状态下有无漏点后将焊好的试件安装在试验装置上；
(3)加压检测：将试验装置充满水后以0.02MPa/min的速度缓慢加压，待压力升至设计压力后恒压5min后观察焊缝有无开裂。如果在设计压力值以内焊缝或PVC衬里开裂则应调整焊接参数或更换PVC衬里重新焊制试件，重新检测；如果在设计压力值下焊缝或PVC衬里未开裂，则表明焊接参数合理而且PVC衬里合格，则可以进行现场施工。
上述试验装置由水槽、带有长孔的水槽压盖、进水管、排气管、压力表、进水阀和排气止水阀组成；水槽的两侧分别安装有进水管和出水管，进水管和出水管上分别安装有进水阀和排气止水阀，进水管上装有压力表；水槽压盖和水槽紧固安装。
上述水槽压盖上带有1200*25mm长孔。
上述水槽压盖和水槽通过紧固螺栓连接，并在连接处装有橡胶密封圈。
本发明具有如下的优点和积极效果：
1、该试验方法是采用等效内压法不仅能直接检测PVC衬里接头耐水压的能力，而且还能模拟实际的工况条件直观的检测PVC衬里接头的耐压值。
2、所用的试验装置结构紧凑、重量轻、试验用水量小，整个试验仅需40kg水即可，远远小于管道试验用水量；试验操作简单；试验效果直观，通过试验可以直接发现渗漏部位，直观的判定是焊缝漏水还是PVC衬里漏水，对制定和调整焊接工艺有非常好的指导意义。
附图说明：
图1是内衬PVC钢筋混凝土排水管的结构示意图。
图2是试验装置的结构示意图。
具体实施方式：
一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法，依照下列步骤完成：
1、制作试验装置。该装置由水槽、带有1200*25mm长孔的水槽压盖、进水管、排气管、压力表、进水阀和排气止水阀组成；水槽的两侧分别安装有进水管和出水管，进水管和出水管上分别安装有进水阀和排气止水阀，进水管上装有压力表；水槽压盖和水槽紧固安装。
2、焊制PVC接头试件：将焊接工艺确定以后依据焊接工艺将两块400x1200mm的PVC衬里焊接牢固。将焊接后的PVC衬里放置在试验装置的水槽上，并用紧固螺栓将PVC衬里、水槽压盖和水槽按图3所示方式连接并用橡胶密封圈进行密封，然后从进水管向密封腔内注水打压直至达到试验压力，然后根据渗漏与否进行焊接工艺的评定。
3、用电火花监测仪检测PVC衬里及焊缝在常压状态下有无漏点后将焊好的试件安装在试验装置上。
4、加压检测：将试验装置充满水后以0.02MPa/min的速度缓慢加压，待压力升至设计压力后恒压5min后观察焊缝有无开裂。如果在设计压力值以内焊缝或PVC衬里开裂则应调整焊接参数或更换PVC衬里重新焊制试件，重新检测；如果在设计压力值下焊缝或PVC衬里未开裂，则表明焊接参数合理而且PVC衬里合格，则可以进行现场施工。
Claims (4)
1.一种内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法，其特征在于：依照下列步骤完成：
(1)焊制PVC接头试件：将焊接工艺确定以后依据焊接工艺将两块PVC衬里焊接牢固；
(2)组装：用电火花监测仪检测PVC衬里及焊缝在常压状态下有无漏点后将焊好的试件安装在试验装置上；
(3)加压检测：将试验装置充满水后以0.02MPa/min的速度缓慢加压，待压力升至设计压力后恒压5min后观察焊缝有无开裂。如果在设计压力值以内焊缝或PVC衬里开裂则应调整焊接参数或更换PVC衬里重新焊制试件，重新检测；如果在设计压力值下焊缝或PVC衬里未开裂，则表明焊接参数合理而且PVC衬里合格，则可以进行现场施工。
2.一种根据权利要求1所述的内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法所用的试验装置，其特征在于：上述试验装置由水槽、带有长孔的水槽压盖、进水管、排气管、压力表、进水阀和排气止水阀组成；水槽的两侧分别安装有进水管和出水管，进水管和出水管上分别安装有进水阀和排气止水阀，进水管上装有压力表；水槽压盖和水槽紧固安装。
3.根据权利要求2所述的内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法所用的试验装置，其特征在于：上述水槽压盖上带有1200*25mm长孔。
4.根据权利要求2所述的内衬PVC钢筋混凝土排水管PVC焊接接头水压试验方法所用的试验装置，其特征在于：上述水槽压盖和水槽通过紧固螺栓连接，并在连接处装有橡胶密封圈。