CN102241501A - 淤泥快速固化材料 - Google Patents

淤泥快速固化材料 Download PDF

Info

Publication number
CN102241501A
CN102241501A CN2011101293769A CN201110129376A CN102241501A CN 102241501 A CN102241501 A CN 102241501A CN 2011101293769 A CN2011101293769 A CN 2011101293769A CN 201110129376 A CN201110129376 A CN 201110129376A CN 102241501 A CN102241501 A CN 102241501A
Authority
CN
China
Prior art keywords
cement
mud
silt
parts
aluminum oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101293769A
Other languages
English (en)
Inventor
满志清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU JUHUI TECHNOLOGIES Co Ltd
Original Assignee
JIANGSU JUHUI TECHNOLOGIES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU JUHUI TECHNOLOGIES Co Ltd filed Critical JIANGSU JUHUI TECHNOLOGIES Co Ltd
Priority to CN2011101293769A priority Critical patent/CN102241501A/zh
Publication of CN102241501A publication Critical patent/CN102241501A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种淤泥快速固化材料。具体说，是用来对淤泥进行固化处理过程中加入到淤泥中的添加剂。其特点是由高分子材料、水泥、炉灰、铝氧熟料和石膏等重量份数的原料均匀混合而成。其中的高分子材料是聚丙烯酸钠或聚丙烯酸钾，水泥是325号水泥或425号水泥，炉灰是高炉矿渣粉或粉煤灰，铝氧熟料是铝酸钠为主要成分的烧结物。采用这种材料对淤泥进行固化处理，可提高固化速度和效率。

Description

淤泥快速固化材料
技术领域
本发明涉及一种淤泥固化剂。具体说，是用来对淤泥进行固化处理过程中加入到淤泥中的添加剂。
背景技术
为保持湖泊的生态环境，需定期对湖泊中的淤泥进行疏浚。而清理出来的淤泥含水率较高，如不进行固化处理，就无法直接利用。为了使清理出来的淤泥能够用作道路铺设、低洼区回填和绿化等场合，就需对从湖泊中清理出来的淤泥进行固化处理。而在对淤泥处理过程中需在淤泥中添加固化材料。目前，用作淤泥固化处理的固化材料由水泥、粉煤灰和石膏等原料均匀混合而成。这种固化材料是通过水泥的水化学反应来对淤泥起到固化作用，而水化学反应速度较慢，当将其加入到淤泥中与淤泥一起混合后，一般需要七天后才能使淤泥的强度慢慢提高。因此，采用这种固化材料对淤泥进行固化处理，固化速度慢，生产效率低。
发明内容
本发明要解决的问题是提供一种淤泥快速固化材料。采用这种材料对淤泥进行固化处理，可提高固化速度和效率。
为解决上述问题，采取以下技术方案：
本发明的淤泥快速固化材料特点是由以下重量份数的原料均匀混合而成：
高分子材料1～2份；
水泥30～40份；
炉灰60～70份；
铝氧熟料1.5～2份；
石膏3～6份。
其中的高分子材料是聚丙烯酸钠或聚丙烯酸钾，水泥是325号水泥或425号水泥，炉灰是高炉矿渣粉或粉煤灰，铝氧熟料是铝酸钠为主要成分的烧结物。
采取上述方案，具有以下优点：
由上述方案可以看出，由于本发明由高分子材料、水泥、炉灰、铝氧熟料和石膏等原料均匀混合而成。其中的高分子材料为吸水材料，当将高分子材料加入到淤泥中后，可瞬间吸收淤泥中的大量水分，只有余下的少量水分才由水泥进行水化学反应，使得淤泥很快变干。其中的铝氧熟料可促进水泥的水化学反应速度，提高处理后的淤泥的早期强度，经试验，利用传统固化材料需要28天才能使淤泥达到需要的强度，而采用本发明的固化材料只需14天时间即可使淤泥达到需要的强度。因此，采用本发明的淤泥快速固化材料来对淤泥进行固化处理，可大大提高固化速度和生产效率。
具体实施方式
以下结合实施例对本发明作进一步详细说明：
实施例一
先选取2重量份的高分子材料、40重量份的水泥、60重量份的炉灰、2重量份的铝氧熟料和6重量份的石膏，然后将上述原料一起投入搅拌器内混合均匀，制成混合物料即本发明的淤泥快速固化材料。
其中的高分子材料是聚丙烯酸钠，水泥是325号水泥，炉灰是高炉矿渣粉，铝氧熟料是铝酸钠为主要成分的烧结物。
实施例二
先选取1重量份的高分子材料、35重量份的水泥、65重量份的炉灰、1.8重量份的铝氧熟料和3重量份的石膏，然后将上述原料一起投入搅拌器内混合均匀，制成混合物料即本发明的淤泥快速固化材料。
其中的高分子材料是聚丙烯酸钾，水泥是425号水泥，炉灰是粉煤灰，铝氧熟料是铝酸钠为主要成分的烧结物。
实施例三
先选取1.5重量份的高分子材料、30重量份的水泥、70重量份的炉灰、1.5重量份的铝氧熟料和5重量份的石膏，然后将上述原料一起投入搅拌器内混合均匀，制成混合物料即本发明的淤泥快速固化材料。
其中的高分子材料是聚丙烯酸钠，水泥是325号水泥，炉灰是高炉矿渣粉，铝氧熟料是铝酸钠为主要成分的烧结物。

Claims (1)

1.淤泥快速固化材料，其特征在于由以下重量份数的原料均匀混合而成：
高分子材料1～2份；
水泥30～40份；
炉灰60～70份；
铝氧熟料1.5～2份；
石膏3～6份；
其中的高分子材料是聚丙烯酸钠或聚丙烯酸钾，水泥是325号水泥或425号水泥，炉灰是高炉矿渣粉或粉煤灰，铝氧熟料是铝酸钠为主要成分的烧结物。
CN2011101293769A 2011-05-19 2011-05-19 淤泥快速固化材料 Pending CN102241501A (zh)