CN102241035B - A kind of Wood protecting agent - Google Patents
A kind of Wood protecting agent Download PDFInfo
- Publication number
- CN102241035B CN102241035B CN201110207052.2A CN201110207052A CN102241035B CN 102241035 B CN102241035 B CN 102241035B CN 201110207052 A CN201110207052 A CN 201110207052A CN 102241035 B CN102241035 B CN 102241035B
- Authority
- CN
- China
- Prior art keywords
- agent
- acrylic emulsion
- timber
- borax
- kazon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Wood protecting agent, it is characterized in that, it is by acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol, azoles fungicide, isothiazoline series bactericidal agent, N-phenylsalicylamide, defoamer, levelling agent, surfactant, the compositions that deionized water is prepared as, the chemical formula of described acrylic emulsion is CH2=CHCOOH, described azoles fungicide is Bravo, described isothiazoline series bactericidal agent is Kazon, described defoamer is organically-modified polyethers or mineral oil, described levelling agent is modified polyether or acrylate copolymer, described surfactant is quaternary ammonium salt.The present invention can mildew-resistant, anticorrosion, Anti-moth-eating, and there is resistance leachability, simultaneously, it is simple to constructing operation, it is not necessary to special equipment and the protection of specialty.
Description
Technical field
The present invention relates to timber additive agent field, more particularly, it relates to be used in wood decorations during indoor decorating
The wood mould antiseptical one timber such as plate, thick china, making wood twig, rough ground, density board, circuit board, fibre board, ceiling are protected
Protect agent.
Background technology
Along with day by day improving and the development of science and technology of people's living standard, the performance requirement of timber is more come by consumer
The highest, more and clearer and more definite.Wooden plaque that a large amount of in modern house is fitted up use, thick china, making wood twig, rough ground, close
The protection of the woodworks such as degree plate, circuit board, fibre board, ceiling is also particularly important.So, to the mildew-resistant of timber, anticorrosion,
The requirement of insect protected performance is the most prominent.
Current industrial employing CCA timber preservative, ACQ timber preservative and borate compounds carry out anticorrosion to timber
Process, but, CCA timber preservative and ACQ timber preservative product are not particularly suited for civilian (must use specially by professional
Industry instrument uses), and, both Wood protecting agents all can make the color of timber change, though after treatment, and timber
Green can be presented, but, still affect attractive in appearance.
CCA timber preservative is cooked raw material production with arsenic acid and chromic acid and is prepared as, and arsenic acid and chromic acid all have huge
Toxicity, uses after CCA timber preservative carries out preservative treatment to timber, timber need to solidify about 20 days or dry 4 little
Time (temperature need to remain 90-100 DEG C) could use, otherwise, preservative not and before the wood fiber occurs chemistry reflection to solidify,
Arise that leakage, and the harm to workmen is the biggest.
ACQ timber preservative is that penetrating odor is the biggest as solvent with liquefied ammonia.
Both the above preservative is required to equipment and the protective garment of specialty, the practitioner of specialty operate, otherwise can
Serious infringement workmen's is healthy.
The technical scheme that employing borate compounds does Wood protecting agent is the most more, such as Patent No. 200710144325.7
" a kind of Wood protecting agent and preparation method thereof " and " Wood protecting agent " of Patent No. 200410047075.1, although boride
Wood-decaying fungus, Coptotermes formosanus Shtrari. etc. are had the strongest suppression and killing action；The lowest to the toxicity of mammal, use safety；Warp
The timber that it processes is clean, keeps true qualities；Fine to the permeability of timber.But, but boride is the most invalid to mycete, and
Using borate compounds to need the equipment of specialty, professional operator could use, so it is raw to be currently also only suitable for industry
Product field.
Summary of the invention
The technical problem to be solved is: existing Wood protecting agent does not possess fungicidal properties, and can not apply
In the protection of interior decoration timber, and needing professional to be equipped with professional equipment could to operate, construction cost is high, for indoor
The mould contamination of woodwork can not remove, for the very limited amount of problem of protection of indoor woodwork.
The technical scheme that the present invention solves the employing of its technical problem is as described below: a kind of Wood protecting agent, it is characterized in that, its
It is by acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol, azoles fungicide, isothiazoline series bactericidal agent, salicyloyl benzene
The compositions that amine, defoamer, levelling agent, surfactant, deionized water are prepared as, the quality proportioning of the most each component is:
The chemical formula of described acrylic emulsion is CH2=CHCOOH.
As optimization, described azoles fungicide is Bravo.
As optimization, described isothiazoline series bactericidal agent is Kazon.
As optimization, described defoamer is organically-modified polyethers or mineral oil.
As optimization, described levelling agent is modified polyether or acrylate copolymer.
As optimization, described surfactant is quaternary ammonium salt.
According to the above-mentioned present invention, it has the beneficial effects that: the present invention is with acrylic emulsion as carrier, with multiple mildew-resistant
Agent compounds.Good water solubility of the present invention, good film-forming property, after doing, wood performance is not had any impact, do not affect the paint of timber, glue
The techniques such as conjunction, play the effect of effective mildew-resistant, anticorrosion, Anti-moth-eating to timber.
1, the dry solidification time is fast, and drying time is short, and rate of drying is fast, it is not necessary to heat, normal temperature solidified.Guarantor to timber
Protecting more comprehensively, the especially protection to indoor decorating woodwork is more targeted.
2, seepage velocity is fast, it is possible to penetrates into rapidly and uniformly and needs in timber to be protected, and forms one layer of waterproofing protection
Film, fungicidal properties of the present invention is excellent, good to the inhibition of common mycete, through country's building materials test Spot detection, the present invention's
Wood protecting agent fungicidal properties reaches more than 1 grade, and the excellent performance such as wet-hot aging performance and adhesive force.
3, producing without waste gas, waste water, waste residue in production process of the present invention, after using process and using, security performance is good, warp
Country's building materials test Spot detection is without toxic pollutants such as formaldehyde, toluene, dimethylbenzene, more environmentally-friendly.
4, simple to operate, use crowd extensive, the present invention is easy to constructing operation, it is not necessary to special equipment and professional preventing
Protecting, operator can construct in the way of using brushing or roller coat.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is conducted further description:
Embodiment one
A kind of Wood protecting agent, is characterized in that, its be by acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol, hundred
Bacterium is clear, Kazon, N-phenylsalicylamide, organically-modified polyethers, modified polyether, quaternary ammonium salt surface active agent, deionized water are prepared as
Compositions, the quality proportioning of the most each component is:
Preparation method is as described below:
A, according to above-mentioned quality proportion relation, acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol are put at a high speed
Dispersion machine stirs；
B, stir some hours after add Kazon, Bravo, N-phenylsalicylamide, organically-modified polyethers, modified polyether, quaternary ammonium
Type surfactant, then put high speed dispersor stirring together into；
C, stirred after add deionized water, mix homogeneously.
The present invention of this embodiment can be used for the location of moisture such as toilet and rough ground, termite-proof by playing fungus-proof antisepsis
Protective effect.
Embodiment two
A kind of Wood protecting agent, is characterized in that, its be by acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol, hundred
The group that bacterium is clear, Kazon, N-phenylsalicylamide, mineral oil, acrylate copolymer, quaternary surfactant, deionized water are prepared as
Compound, the quality proportioning of the most each component is:
Preparation method is as described below:
A, according to above-mentioned quality proportion relation, acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol are put at a high speed
Dispersion machine stirs；
B, stir some hours after add Kazon, Bravo, N-phenylsalicylamide, mineral oil, acrylate copolymer, quaternary ammonium salt
Surfactant, then put high speed dispersor stirring together into；
C, stirred after add deionized water, mix homogeneously.
The present invention of the present embodiment can be used for conventional making wood twig, on the timber such as rough ground, thick china, plays fungus-proof antisepsis and prevents
The protective effect of Coptotermes formosanus Shtrari..
Although the present invention describes with reference to the above embodiments, but those of ordinary skill in the art is entirely capable of
Enough will be apparent from recognize above embodiment be only for illustrate the present invention, wherein can make various changes and revise and in broad sense
On without departing from the present invention, so being not intended as limitation of the invention, as long as in the spirit of the present invention, right
Within the change of embodiment described above falls within the protection domain of application claims.
Claims (1)
1. a Wood protecting agent, is characterized in that, it is by acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol, hundred bacterium
Clearly, the combination that Kazon, N-phenylsalicylamide, mineral oil, acrylate copolymer, quaternary surfactant, deionized water are prepared as
Thing, the quality proportioning of the most each component is:
Its preparation method is:
A, according to above-mentioned quality proportion relation, put acrylic emulsion, Borax, boric acid, propylene glycol, dehydrated alcohol into high speed dispersion
Machine stirs；
B, stir some hours after add Kazon, Bravo, N-phenylsalicylamide, mineral oil, acrylate copolymer, quaternary ammonium salt surface
Activating agent, then put high speed dispersor stirring together into；
C, stirred after add deionized water, mix homogeneously.