CN102241035A - Wood protectant - Google Patents

Wood protectant Download PDF

Info

Publication number
CN102241035A
CN102241035A CN2011102070522A CN201110207052A CN102241035A CN 102241035 A CN102241035 A CN 102241035A CN 2011102070522 A CN2011102070522 A CN 2011102070522A CN 201110207052 A CN201110207052 A CN 201110207052A CN 102241035 A CN102241035 A CN 102241035A
Authority
CN
China
Prior art keywords
wood
wood protecting
protecting agent
agent according
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102070522A
Other languages
Chinese (zh)
Other versions
CN102241035B (en
Inventor
李艳丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201110207052.2A priority Critical patent/CN102241035B/en
Publication of CN102241035A publication Critical patent/CN102241035A/en
Application granted granted Critical
Publication of CN102241035B publication Critical patent/CN102241035B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a wood protectant. The wood protectant is characterized by being a composition prepared from acrylic emulsion, borax, boric acid, propylene glycol, absolute alcohol, an azole bactericide, an isothiazoline bactericide, salicylanilide, a defoaming agent, a flatting agent, a surfactant and deionized water, wherein the chemical formula of the acrylic emulsion is CH2=CHCOOH; the azole bactericide is chlorothalonil; the isothiazoline bactericide is Kathon; the defoaming agent is organic modified polyether or mineral oil; the flatting agent is modified polyether or acrylic polymer; and the surfactant belongs to quaternary ammonium salt. The wood protectant can resist mold, corrosion and moth and have leachability resistance; and the wood protectant is convenient to construct and operate and does not require special equipment and professional protection.

Description

A kind of Wood protecting agent
Technical field
The present invention relates to the timber additive agent field, more particularly, relate to a kind of Wood protecting agents of wood mould corrosion-resistant such as being used in wooden plaque, thick china, wood strip bar, rough ground, density board, circuit board, fiberboard, ceiling in the indoor decorating process.
Background technology
Along with the raising day by day and the science and technology development of people's living standard, the consumer is more and more higher to the performance requirement of timber, and is also more and clearer and more definite.The protection of woodworks such as the wooden plaque of a large amount of uses in the modern house finishing, thick china, wood strip bar, rough ground, density board, circuit board, fiberboard, ceiling also seems particularly important.So, to the mildew-resistant of timber, anticorrosion, the insect protected performance demands is also just more outstanding.
Present industrial employing CCA timber preservative, ACQ timber preservative and borate compounds carry out preservative treatment to timber; but; CCA timber preservative and ACQ timber preservative product also are not suitable for civilian (must use professional tool to use by the professional); and; these two kinds of Wood protecting agents all can make the color of timber change, though after treatment, timber can present green; but, still influence attractive in appearance.
The CCA timber preservative is cooked raw material production with arsenic acid and chromic acid and is prepared into, arsenic acid and chromic acid all have huge toxicity, after using the CCA timber preservative that timber is carried out preservative treatment, timber need solidify about 20 days or dry 4 hours (temperature need remain 90-100 ℃) and could use, otherwise, anticorrisive agent leakage will occur not and before chemistry reflection curing takes place wood-fibred, and also very big to workmen's harm.
The ACQ timber preservative is to use liquefied ammonia as solvent, and penetrating odor is very big.
More than two kinds of anticorrisive agents all need the equipment and the protective garment of specialty, by practitioner's operation of specialty, otherwise can the grievous injury workmen healthy.
It is also more to adopt borate compounds to do the technical scheme of Wood protecting agent, as the patent No. is that 200710144325.7 " a kind of Wood protecting agent and preparation method thereof " and the patent No. are 200410047075.1 " Wood protecting agent ", though boride all has very strong inhibition and killing action to wood-decaying fungus, termite etc.; Very low to mammiferous toxicity, safe in utilization; The timber of handling through it is clean, keeps true qualities; Permeability to timber is fine.But, but boride is invalid substantially to mould, and use borate compounds to need the equipment of specialty, and the operating personnel of specialty could use, so also only suitable at present industrial production field.
Summary of the invention
Technical problem to be solved by this invention is: existing Wood protecting agent does not possess fungicidal properties; and can not be applied to the protection of interior decoration with timber; and needing the professional to be equipped with professional equipment could operate; the construction cost height; mould contamination for indoor woodwork can not be removed, for the very limited problem of the protection of indoor woodwork.
It is as described below that the present invention solves the technical scheme that its technical problem adopts: a kind of Wood protecting agent; it is characterized in that; it is the composition that is prepared into by acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol, azoles fungicide, isothiazoline series bactericidal agent, salicylanilide, defoamer, levelling agent, surfactant, deionized water, and wherein the quality proportioning of each component is:
Acrylic emulsion 5-60kg/L borax 5-20kg/L boric acid 5-15kg/L
Propane diols 1-10kg/L absolute ethyl alcohol 1-10kg/L azoles fungicide 0.1-5kg/L
Isothiazoline series bactericidal agent 0.1-5kg/L salicylanilide 0.1-5kg/L defoamer 0.05-0.2kg/L
Levelling agent 0.05-0.2kg/L surfactant 0.05-5kg/L surplus is an ionized water.
The chemical formula of described acrylic emulsion is CH2=CHCOOH.
As optimization, described azoles fungicide is a Bravo.
As optimization, described isothiazoline series bactericidal agent is the card pine.
As optimization, described defoamer is organically-modified polyethers or mineral oil.
As optimization, described levelling agent is modified polyether or acrylate copolymer.
As optimization, described surfactant is a quaternary ammonium salt.
According to above-mentioned the present invention, its beneficial effect is: the present invention is to be carrier with the acrylic emulsion, and is composite with multiple mould inhibitor.Good water solubility of the present invention, good film-forming property, do the back to wood performance without any influence, do not influence the technologies such as paint, gummed of timber, timber is played effective mildew-resistant, anticorrosion, anti-effect of damaging by worms.
1, the dry solidification time fast, drying time is short, rate of drying is fast, need not to heat, and is normal temperature solidified.To the protection of timber more comprehensively, especially more targeted with the protection of woodwork to indoor decorating.
2, seepage velocity is fast; can be penetrated in the timber that needs protection rapidly and uniformly; and formation one deck waterproofing protection film; fungicidal properties excellence of the present invention; inhibition to common mould is effective; detect through national building materials inspection center, Wood protecting agent fungicidal properties of the present invention reaches more than 1 grade, and excellent performances such as wet-hot aging performance and adhesive force.
3, do not have waste gas, waste water, waste residue in the production process of the present invention and produce, use and use the back security performance good detects through national building materials inspection center and not to contain toxic pollutants such as formaldehyde, toluene, dimethylbenzene, environmental protection more.
4, simple to operate, the use crowd is extensive, and constructing operation is convenient in the present invention, need not the protection of special equipment and specialty, and operating personnel can adopt the mode of brushing or roller coat to construct.
The specific embodiment
Below in conjunction with embodiment the present invention is further described:
Embodiment one
A kind of Wood protecting agent; it is characterized in that; it is the composition that is prepared into by acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol, Bravo, card pine, salicylanilide, organically-modified polyethers, modified polyether, quaternary ammonium salt surface active agent, deionized water, and wherein the quality proportioning of each component is:
Acrylic emulsion 40kg borax 10kg boric acid 7kg
Propane diols 10kg absolute ethyl alcohol 5kg Bravo 0.5kg
Block the organically-modified polyethers 0.1kg of loose 0.6kg salicylanilide 0.5kg
Modified polyether 0.1kg quaternary ammonium salt surface active agent 2kg ionized water 26.2kg
The preparation method is as described below:
A, according to above-mentioned quality proportion relation, put acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol into high speed dispersor and stir;
Add card pine, Bravo, salicylanilide, organically-modified polyethers, modified polyether, quaternary ammonium salt surface active agent behind b, the stirring some hrs, put high speed dispersor more together into and stir;
C, add deionized water again after having stirred, mix and get final product.
The present invention of this embodiment can be used for location of moisture such as toilet and rough ground, will play the termite-proof protective effect of fungus-proof antisepsis.
Embodiment two
A kind of Wood protecting agent; it is characterized in that; it is the composition that is prepared into by acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol, Bravo, card pine, salicylanilide, mineral oil, acrylate copolymer, quaternary surfactant, deionized water, and wherein the quality proportioning of each component is:
Acrylic emulsion 20kg borax 15kg boric acid 10kg
Propane diols 5kg absolute ethyl alcohol 5kg Bravo 0.5kg
Block loose 1kg salicylanilide 0.5kg mineral oil 0.1kg
Acrylate copolymer 0.1kg quaternary ammonium salt surface active agent 3kg deionized water 40.8
The preparation method is as described below:
A, according to above-mentioned quality proportion relation, put acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol into high speed dispersor and stir;
Add card pine, Bravo, salicylanilide, mineral oil, acrylate copolymer, quaternary surfactant behind b, the stirring some hrs, put high speed dispersor more together into and stir;
C, add deionized water again after having stirred, mix and get final product.
The present invention of present embodiment can be used for conventional wood strip bar, on the timber such as rough ground, thick china, plays the termite-proof protective effect of fungus-proof antisepsis.
Though the present invention describes with reference to the above embodiments; but those of ordinary skill in the art can recognize very clearly that fully above embodiment is used to illustrate the present invention; wherein can make variations and modifications and not break away from the present invention in a broad sense; so be not as limitation of the invention; as long as in connotation scope of the present invention, all will fall within the protection domain that the present invention requires the variation of above-described embodiment.

Claims (9)

1. Wood protecting agent; it is characterized in that; it is the composition that is prepared into by acrylic emulsion, borax, boric acid, propane diols, absolute ethyl alcohol, azoles fungicide, isothiazoline series bactericidal agent, salicylanilide, defoamer, levelling agent, surfactant, deionized water, and wherein the quality proportioning of each component is:
Acrylic emulsion 5-60kg/L borax 5-20kg/L boric acid 5-15kg/L
Propane diols 1-10kg/L absolute ethyl alcohol 1-10kg/L azoles fungicide 0.1-5kg/L
Isothiazoline series bactericidal agent 0.1-5kg/L salicylanilide 0.1-5kg/L defoamer 0.05-0.2kg/L
Levelling agent 0.05-0.2kg/L surfactant 0.05-5kg/L surplus is an ionized water.
2. a kind of Wood protecting agent according to claim 1 is characterized in that: the chemical formula of described acrylic emulsion is CH2=CHCOOH.
3. a kind of Wood protecting agent according to claim 1 is characterized in that: described azoles fungicide is a Bravo.
4. a kind of Wood protecting agent according to claim 1 is characterized in that: described isothiazoline series bactericidal agent is the card pine.
5. a kind of Wood protecting agent according to claim 1 is characterized in that: described defoamer is organically-modified polyethers.
6. a kind of Wood protecting agent according to claim 1 is characterized in that: described defoamer is a mineral oil.
7. a kind of Wood protecting agent according to claim 1 is characterized in that: described levelling agent is a modified polyether.
8. a kind of Wood protecting agent according to claim 1 is characterized in that: described levelling agent is an acrylate copolymer.
9. a kind of Wood protecting agent according to claim 1 is characterized in that: described surfactant is a quaternary ammonium salt.
CN201110207052.2A 2011-07-23 2011-07-23 A kind of Wood protecting agent Expired - Fee Related CN102241035B (en)