CN106738179A - A kind of Fibreboard Production additive - Google Patents
A kind of Fibreboard Production additive Download PDFInfo
- Publication number
- CN106738179A CN106738179A CN201611135280.2A CN201611135280A CN106738179A CN 106738179 A CN106738179 A CN 106738179A CN 201611135280 A CN201611135280 A CN 201611135280A CN 106738179 A CN106738179 A CN 106738179A
- Authority
- CN
- China
- Prior art keywords
- parts
- fibreboard production
- fine powder
- agent
- production additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to industrial circle, specially a kind of Fibreboard Production additive, its component for including following parts by weight：10 ~ 20 parts of adhesive, 5 ~ 15 parts of metallic oxide fine powder, 3 ~ 8 parts of string, 5 ~ 10 parts of alumina silicate fibre, 2 ~ 6 parts of paraffin, 1 ~ 5 part of rosin.Fiberboard additive steady quality of the invention, by adding adhesive and metallic oxide fine powder, can avoid it is rotten, the problems such as damage by worms, by adding string, alumina silicate fibre, paraffin and rosin, fiberboard swell-shrink characteristic can be made small, be easy to processing, by adding levelling agent fibreboard surface can be made smooth, it is easy to paste various facings, the furniture that can be made fiberboard is more attractive in appearance.
Description
Technical field
The present invention relates to industrial circle, specially a kind of Fibreboard Production additive.
Background technology
Fiberboard also known as density board, be with wood fibre or other plant cellulose fiber as raw material, apply Lauxite or its
The wood-based plate that the adhesive that he is applicable is made, can apply in manufacturing process adhesive and（Or）Additive.Fiberboard has material
Matter is uniform, in length and breadth intensity difference it is small, it is not easy to crack the advantages of, widely used, development Fibreboard Production is timber resources comprehensive utilization
Effective way.The shortcoming of fiberboard is that the back side has reticulate pattern, causes sheet material two sides surface area, because producing expansive force after moisture absorption
Difference and deform bow warping, hard plate material surface is hard, and nail nail is difficult, poor water resistance.
The content of the invention
In view of this, a kind of Fibreboard Production additive of present invention offer, fiberboard additive steady quality of the invention,
When fiberboard is produced by adding additive of the invention, fiberboard swell-shrink characteristic can be made small, processing of being more convenient for.
To achieve these goals, the present invention uses following technical scheme：
A kind of Fibreboard Production additive, its component for including following parts by weight：10 ~ 20 parts of adhesive, metal oxide are thin
5 ~ 15 parts of powder, 3 ~ 8 parts of string, 5 ~ 10 parts of alumina silicate fibre, 2 ~ 6 parts of paraffin, 1 ~ 5 part of rosin.
As of the invention a kind of preferred, a kind of Fibreboard Production additive, its component for including following parts by weight：Glue
10 parts of stick, 5 parts of metallic oxide fine powder, 3 parts of string, 5 parts of alumina silicate fibre, 3 parts of paraffin, 2 parts of rosin.
As of the invention another preferred, a kind of Fibreboard Production additive, its component for including following parts by weight：
20 parts of adhesive, 8 parts of metallic oxide fine powder, 6 parts of string, 6 parts of alumina silicate fibre, 4 parts of paraffin, 3 parts of rosin.
Further, the adhesive is made up of host and auxiliary agent, and the host is plant sizing, synthetic resin, rubber
One or more any mixing in glue or inorganic sizing, the auxiliary agent is curing agent, solvent, plasticizer, filler, toughness reinforcing
One or more any mixing in agent, coupling agent.
Further, the plant sizing includes but is not limited to starch, cellulose, tannin, gum arabic and sea
One or more in mosanom, the synthetic resin includes but is not limited to epoxy, phenolic aldehyde, unsaturated polyester (UP), polyurethane, organic
Silicon, polyimides, BMI, allyl resin, furane resins, amino resins, alkyd resin, polyethylene, polypropylene,
It is polyvinyl chloride, polystyrene, acrylic resin, nylon, makrolon, polyformaldehyde, thermoplastic polyester, polyphenylene oxide, fluororesin, poly-
One or more in diphenyl sulfide, polysulfones, polyketone class, polybenzoate, liquid crystal polymer, polymer alloy, the rubber include but
It is not limited to neoprene, butyl nitrile EP rubbers, fluorubber, polyisobutene, polysulfide rubber, natural rubber, chlorosulfonated polyethylene
One or more in rubber, the inorganic sizing includes but is not limited to the one kind in silicate, phosphate and Phosphoric Acid-Copper Oxide
Or it is various.
Further, the metallic oxide fine powder is aluminum oxide fine powder, iron oxide fines, magnesium oxide powder, barium monoxide
One kind in fine powder, sodium oxide molybdena fine powder.
Further, 0.5 ~ 2 part of activating agent is also included in a kind of Fibreboard Production additive.
Further, the activating agent is the one kind in fatty acid, amine, soaps, polyalcohol and amino alcohol.
Further, 1 ~ 5 part of levelling agent is also included in a kind of Fibreboard Production additive.
Further, the levelling agent be alkyl-modified organosiloxane, terminal groups modification organosilicon, acrylic resin,
One kind in Lauxite, melamine resin.
The beneficial effects of the invention are as follows：Fiberboard additive steady quality of the invention, by adding adhesive and metal
Oxide fine powder, can avoid it is rotten, the problems such as damage by worms, by adding string, alumina silicate fibre, paraffin and rosin, can make
Fiberboard swell-shrink characteristic is small, is easy to processing, by adding levelling agent fibreboard surface can be made smooth, it is easy to paste various facings, can
So that the furniture that fiberboard is made is more attractive in appearance.
Specific embodiment
The present invention provides a kind of Fibreboard Production additive, fiberboard additive steady quality of the invention, in production fiberboard
When by adding additive of the invention, fiberboard swell-shrink characteristic can be made small, be more convenient for processing.
To achieve these goals, the present invention uses following technical scheme：
A kind of Fibreboard Production additive, its component for including following parts by weight：10 ~ 20 parts of adhesive, metal oxide are thin
5 ~ 15 parts of powder, 3 ~ 8 parts of string, 5 ~ 10 parts of alumina silicate fibre, 2 ~ 6 parts of paraffin, 1 ~ 5 part of rosin.
As of the invention a kind of preferred, a kind of Fibreboard Production additive, its component for including following parts by weight：Glue
10 parts of stick, 5 parts of metallic oxide fine powder, 3 parts of string, 5 parts of alumina silicate fibre, 3 parts of paraffin, 2 parts of rosin.
As of the invention another preferred, a kind of Fibreboard Production additive, its component for including following parts by weight：
20 parts of adhesive, 8 parts of metallic oxide fine powder, 6 parts of string, 6 parts of alumina silicate fibre, 4 parts of paraffin, 3 parts of rosin.
Further, the adhesive is made up of host and auxiliary agent, and the host is plant sizing, synthetic resin, rubber
One or more any mixing in glue or inorganic sizing, the auxiliary agent is curing agent, solvent, plasticizer, filler, toughness reinforcing
One or more any mixing in agent, coupling agent.
Further, the plant sizing includes but is not limited to starch, cellulose, tannin, gum arabic and sea
One or more in mosanom, the synthetic resin includes but is not limited to epoxy, phenolic aldehyde, unsaturated polyester (UP), polyurethane, organic
Silicon, polyimides, BMI, allyl resin, furane resins, amino resins, alkyd resin, polyethylene, polypropylene,
It is polyvinyl chloride, polystyrene, acrylic resin, nylon, makrolon, polyformaldehyde, thermoplastic polyester, polyphenylene oxide, fluororesin, poly-
One or more in diphenyl sulfide, polysulfones, polyketone class, polybenzoate, liquid crystal polymer, polymer alloy, the rubber include but
It is not limited to neoprene, butyl nitrile EP rubbers, fluorubber, polyisobutene, polysulfide rubber, natural rubber, chlorosulfonated polyethylene
One or more in rubber, the inorganic sizing includes but is not limited to the one kind in silicate, phosphate and Phosphoric Acid-Copper Oxide
Or it is various.
Further, the metallic oxide fine powder is aluminum oxide fine powder, iron oxide fines, magnesium oxide powder, barium monoxide
One kind in fine powder, sodium oxide molybdena fine powder.
Further, 0.5 ~ 2 part of activating agent is also included in a kind of Fibreboard Production additive.
Further, the activating agent is the one kind in fatty acid, amine, soaps, polyalcohol and amino alcohol.
Further, 1 ~ 5 part of levelling agent is also included in a kind of Fibreboard Production additive.
Further, the levelling agent be alkyl-modified organosiloxane, terminal groups modification organosilicon, acrylic resin,
One kind in Lauxite, melamine resin.
In order that those skilled in the art are better understood from the technical scheme in the application, come below in conjunction with embodiment
Technical scheme is clearly and completely described, it is clear that described embodiment is only the part of the application
Embodiment, based on the embodiment in the application, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment for obtaining, should all belong to the scope of the application protection.
Embodiment 1
A kind of Fibreboard Production additive, its component for including following parts by weight：15 parts of adhesive, metallic oxide fine powder 10
Part, 5 parts of string, 6 parts of alumina silicate fibre, 3 parts of paraffin, 2 parts of rosin.
In embodiment 1, the adhesive is made up of host and auxiliary agent, the host be plant sizing, synthetic resin,
One or more any mixing in rubber or inorganic sizing, the auxiliary agent is curing agent, solvent, plasticizer, filler, toughness reinforcing
One or more any mixing in agent, coupling agent.
In embodiment 1, the plant sizing includes but is not limited to starch, cellulose, tannin, gum arabic and sea
One or more in mosanom, the synthetic resin includes but is not limited to epoxy, phenolic aldehyde, unsaturated polyester (UP), polyurethane, organic
Silicon, polyimides, BMI, allyl resin, furane resins, amino resins, alkyd resin, polyethylene, polypropylene,
It is polyvinyl chloride, polystyrene, acrylic resin, nylon, makrolon, polyformaldehyde, thermoplastic polyester, polyphenylene oxide, fluororesin, poly-
One or more in diphenyl sulfide, polysulfones, polyketone class, polybenzoate, liquid crystal polymer, polymer alloy, the rubber include but
It is not limited to neoprene, butyl nitrile EP rubbers, fluorubber, polyisobutene, polysulfide rubber, natural rubber, chlorosulfonated polyethylene
One or more in rubber, the inorganic sizing includes but is not limited to the one kind in silicate, phosphate and Phosphoric Acid-Copper Oxide
Or it is various.
In embodiment 1, the metallic oxide fine powder is aluminum oxide fine powder, iron oxide fines, magnesium oxide powder, oxidation
One kind in barium fine powder, sodium oxide molybdena fine powder.
In embodiment 1,1 part of activating agent is also included in a kind of Fibreboard Production additive.
In embodiment 1, the activating agent is the one kind in fatty acid, amine, soaps, polyalcohol and amino alcohol.
In embodiment 1,3 parts of levelling agent is also included in a kind of Fibreboard Production additive.
In embodiment 1, the levelling agent be alkyl-modified organosiloxane, terminal groups modification organosilicon, acrylic resin,
One kind in Lauxite, melamine resin.
Embodiment 2
A kind of Fibreboard Production additive, its component for including following parts by weight：20 parts of adhesive, metallic oxide fine powder 5
Part, 5 parts of string, 6 parts of alumina silicate fibre, 4 parts of paraffin, 3 parts of rosin.
In example 2, the adhesive is made up of host and auxiliary agent, the host be plant sizing, synthetic resin,
One or more any mixing in rubber or inorganic sizing, the auxiliary agent is curing agent, solvent, plasticizer, filler, toughness reinforcing
One or more any mixing in agent, coupling agent.
In example 2, the plant sizing includes but is not limited to starch, cellulose, tannin, gum arabic and sea
One or more in mosanom, the synthetic resin includes but is not limited to epoxy, phenolic aldehyde, unsaturated polyester (UP), polyurethane, organic
Silicon, polyimides, BMI, allyl resin, furane resins, amino resins, alkyd resin, polyethylene, polypropylene,
It is polyvinyl chloride, polystyrene, acrylic resin, nylon, makrolon, polyformaldehyde, thermoplastic polyester, polyphenylene oxide, fluororesin, poly-
One or more in diphenyl sulfide, polysulfones, polyketone class, polybenzoate, liquid crystal polymer, polymer alloy, the rubber include but
It is not limited to neoprene, butyl nitrile EP rubbers, fluorubber, polyisobutene, polysulfide rubber, natural rubber, chlorosulfonated polyethylene
One or more in rubber, the inorganic sizing includes but is not limited to the one kind in silicate, phosphate and Phosphoric Acid-Copper Oxide
Or it is various.
In example 2, the metallic oxide fine powder is aluminum oxide fine powder, iron oxide fines, magnesium oxide powder, oxidation
One kind in barium fine powder, sodium oxide molybdena fine powder.
In example 2,1 part of activating agent is also included in a kind of Fibreboard Production additive.
In example 2, the activating agent is the one kind in fatty acid, amine, soaps, polyalcohol and amino alcohol.
In example 2,5 parts of levelling agent is also included in a kind of Fibreboard Production additive.
In example 2, the levelling agent be alkyl-modified organosiloxane, terminal groups modification organosilicon, acrylic resin,
One kind in Lauxite, melamine resin.
The invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing substantially from spirit or essential attributes of the invention
In the case of, can in other specific forms realize the present invention.Which point therefore, no matter from the point of view of, embodiment all should be seen
Work is exemplary, and is nonrestrictive, and those skilled in the art should be using specification an as entirety, each embodiment
In technical scheme can also through appropriately combined, formed it will be appreciated by those skilled in the art that other embodiment, the present invention
Scope limited rather than described above by appended claims, it is intended that the implication that will fall in the equivalency of claim
Included in the present invention with all changes in scope.
Claims (9)
1. a kind of Fibreboard Production additive, it is characterised in that its component for including following parts by weight：10 ~ 20 parts of adhesive,
5 ~ 15 parts of metallic oxide fine powder, 3 ~ 8 parts of string, 5 ~ 10 parts of alumina silicate fibre, 2 ~ 6 parts of paraffin, 1 ~ 5 part of rosin.
2. a kind of Fibreboard Production additive according to claim 1, it is characterised in that it includes following parts by weight
Component：10 parts of adhesive, 5 parts of metallic oxide fine powder, 3 parts of string, 5 parts of alumina silicate fibre, 3 parts of paraffin, 2 parts of rosin.
3. a kind of Fibreboard Production additive according to claim 1, it is characterised in that it includes following parts by weight
Component：20 parts of adhesive, 8 parts of metallic oxide fine powder, 6 parts of string, 6 parts of alumina silicate fibre, 4 parts of paraffin, 3 parts of rosin.
4. a kind of Fibreboard Production additive according to claim 1, it is characterised in that the adhesive is by host and helps
Agent is constituted, and the host is one or more any mixing in plant sizing, synthetic resin, rubber or inorganic sizing, institute
It is one or more any mixing in curing agent, solvent, plasticizer, filler, toughener, coupling agent to state auxiliary agent.
5. a kind of Fibreboard Production additive according to claim 1, it is characterised in that the metallic oxide fine powder is
One kind in aluminum oxide fine powder, iron oxide fines, magnesium oxide powder, barium monoxide fine powder, sodium oxide molybdena fine powder.
6. a kind of Fibreboard Production additive according to claim 1, it is characterised in that a kind of Fibreboard Production adds
Plus 0.5 ~ 2 part of activating agent is also included in agent.
7. a kind of Fibreboard Production additive according to claim 6, it is characterised in that the activating agent is aliphatic acid
One kind in class, amine, soaps, polyalcohol and amino alcohol.
8. a kind of Fibreboard Production additive according to claim 1, it is characterised in that a kind of Fibreboard Production adds
Plus 1 ~ 5 part of levelling agent is also included in agent.
9. a kind of Fibreboard Production additive according to claim 8, it is characterised in that the levelling agent is alkyl-modified
Organosiloxane, terminal groups modification organosilicon, acrylic resin, the one kind in Lauxite, melamine resin.