KR20030077916A - Multipurpose, multifunctional coating composition - Google Patents
Multipurpose, multifunctional coating composition Download PDFInfo
- Publication number
- KR20030077916A KR20030077916A KR1020020030287A KR20020030287A KR20030077916A KR 20030077916 A KR20030077916 A KR 20030077916A KR 1020020030287 A KR1020020030287 A KR 1020020030287A KR 20020030287 A KR20020030287 A KR 20020030287A KR 20030077916 A KR20030077916 A KR 20030077916A
- Authority
- KR
- South Korea
- Prior art keywords
- coating composition
- weight
- wax
- parts
- present
- Prior art date
Abstract
Description
[산업상 이용 분야][Industrial use]
본 발명은 다목적, 다기능 코팅제 조성물에 관한 것으로서, 더욱 상세하게는 방수성, 발수성, 방염성, 방미성, 방부성, 방충성 및 목재, 콘크리트 등의 건축자재에 대한 접착성이 우수하고, 아름다운 색채를 나타내고, 코팅방법이 간단하고 코팅층의 두께를 자유로이 조절할 수 있고 환경친화적인 코팅제 조성물 및 코팅막 보존제에 관한 것이다.The present invention relates to a multi-purpose, multi-functional coating composition, more specifically, waterproof, water repellent, flame retardant, anti-fog, antiseptic, insect repellent and excellent adhesion to building materials, such as wood, concrete, exhibits a beautiful color, The coating method is simple and the thickness of the coating layer can be freely controlled, and it relates to an environmentally friendly coating composition and coating film preservative.
[종래 기술][Prior art]
목재는 건축, 가구, 집기 등의 제조에 널리 사용되는 재료이지만 재질의 특성상 화재, 미생물 또는 각종 곤충에 의한 열화에 매우 취약하다는 단점이 있다. 또한 장마철에는 수분을 많이 흡수하여 빨리 썩는 등의 문제점이 있다. 특히 목조 구조물의 경우 이러한 수분, 화재나 생물 열화에 의해 그 수명이 다하는 경우가 대부분임을 감안하면 목재에 방수, 발수, 방염, 방미, 방부 및 방충 등의 처리를 함으로써 목재로 만들어진 각종 구조물의 수명과 성능을 획기적으로 향상시킬 수 있음은 자명하다.Wood is a widely used material for manufacturing construction, furniture, appliances, etc., but due to the nature of the material, it is very vulnerable to deterioration by fire, microorganisms or various insects. In addition, there is a problem in the rainy season to absorb a lot of moisture and quickly decay. Particularly, in the case of wooden structures, most of them are at the end of their life due to moisture, fire, or biological deterioration. It is obvious that performance can be significantly improved.
우리나라는 예로부터 목조 문화재 국가로서 목조 문화재가 그간 각종 전란 등에 의하여 상당량 소실되었음에도 불구하고 아직도 많은 수가 남아 있으며 그 중 일부는 유네스코에 의하여 세계문화유산으로 지정되어 그 우수성을 인정받았다.Korea has been a country of wooden cultural heritage since ancient times, but a large number of wooden cultural assets have been lost due to various wars. Some of them have been designated as World Cultural Heritage by UNESCO.
현존하는 최고의 목조 문화재인 고려시대의 부석사의 무량수전(국보 제18호)과 봉정사의 극락전(국보 제15호), 조선초기의 건축물로는 무위사의 극락전, 관룡사의 약사전 등이 있으며, 조선 중기의 건축물로는 법주사의 팔상전(국보 제 55호) 등이 있다.The best wooden cultural assets of Korea, Buseoksa Temple of Goryeo Dynasty (National Treasure No. 18), Bongjeongsa's Paradise Exhibition (National Treasure No. 15) and early Joseon Dynasty include Muwisa's Paradise Exhibition and Gwanryongsa's Pharmacist Dictionary There are Palsangjeon (National Treasure No. 55) of Beopjusa.
현존하는 우리나라의 각종 목조 문화재에서도 알 수 있는 바와 같이, 적절한 목재의 보존방법만 강구된다면 목재의 수명은 1,000년 이상이 되는 것으로 확인되고 있으나 이러한 우수한 목조 문화재에 대한 보존기술은 현재까지 전무하다시피 하였다.As can be seen from the various wooden cultural assets in Korea, if the proper timber preservation methods are taken, the life span of the wood is confirmed to be over 1,000 years, but there are no preservation techniques for such excellent wooden cultural assets. .
최근에는 쌍봉사 대웅전이 화재로 소실되었고, 무위사 극락보전(국보 제13호) 등이 흰개미와 목재 부식의 피해를 입고 있다. 이처럼 목재는 수분, 화재, 미생물 등의 각종 천재지변에 매우 취약함을 알 수 있다.Recently, the Bongbong Daeungjeon has been destroyed by fires, and the warriors' paradise preservation (National Treasure No. 13) has been damaged by termites and wood decay. As such, the wood is very vulnerable to various natural disasters such as moisture, fire, microorganisms.
우리 나라의 목조 문화재의 재료로는 예로부터 소나무가 가장 많이 사용되어 오고 있다. 이는 소나무가 내강성, 내굴곡성, 내구성 등이 매우 우수하다는 점에 기인한다. 그러나 목질이 강하여 제재된 표면이 거칠고 건조시 균열되고 각종 충해 등을 받기 쉽다는 문제점이 있다. 따라서 예로부터 목재에는 단청을 칠하여 오고 있는 것이 관행이다.Pine wood has been the most used material in our country's wooden cultural assets since ancient times. This is due to the fact that pine has very good strength, flex resistance and durability. However, there is a problem in that the wood is strong and the surface being crushed is rough and cracks when dried and is susceptible to various kinds of damages. Therefore, it is common practice that wood has been painted monochromatic.
단청이란 용매에 용해되지 않는 유색 미립자상의 무기 또는 유기 화합물의 착색제로서 접착제와 혼합하여 해당 건물에 칠을 하여 사용하는 것을 말한다. 이와 같은 단청을 해당 건물에 칠하면 해당 건물의 표면에 도막이 형성되어 성형물에 아름다운 색채가 나타난다. 그러나 이와 같은 단청은 방수, 발수, 방염, 방미, 방부 및 방충 등의 기능은 가지고 있지 않다.Monochromate is a coloring agent of colored fine inorganic or organic compounds which are not soluble in a solvent, mixed with an adhesive, and painted on the building. When such monochromatic paint is applied to the building, a film is formed on the surface of the building, and beautiful colors appear on the molding. However, such mono has no functions such as waterproof, water repellent, flame retardant, anti-fog, antiseptic and insect repellent.
목재의 방염성을 향상시키기 위하여, 황산 암모늄, 황산나트륨과 같은 황산염 및 붕사나 붕산 등이 약제로 사용되어 오고 있다. 이들 약제는 뛰어난 방염 효과를 가지나 장기간 사용하면 이들 약제가 목재 표면에서 백화현상을 일으켜 단청의 외관을 손상시키고 방염성 또한 저하된다는 문제점이 있다.In order to improve the flame retardancy of wood, sulfates such as ammonium sulfate, sodium sulfate, borax and boric acid have been used as pharmaceuticals. These drugs have excellent flame retardant effect, but when used for a long time, these drugs cause bleaching on the surface of wood, which damages the appearance of monochromatic and also reduces the flame resistance.
또한, 목재의 방부성을 향상시키기 위하여, 펜타클로로페놀 및 이들의 유도체인 펜타클로로페놀-라우레이트, 펜타클로로페놀-디하이드로아비에틸아민 등이 알려져 있다. 그러나 이들 화합물은 환경에 유해한 페놀을 포함하고 있어 현재에는 사용이 금지되어 있는 물질이다.Moreover, pentachlorophenol and its derivatives, pentachlorophenol-laurate, pentachlorophenol-dihydroabiethylamine, etc. are known in order to improve the preservative property of wood. However, these compounds contain phenols that are harmful to the environment and are currently prohibited from use.
또한, 방충제로는 딜도린, 크롤텐, 스미치온 등의 화합물이 알려져 있다. 이 화합물 또한 환경에 유해한 독성 물질로서 그 사용이 금지되어 있는 물질이다.In addition, as insect repellents, compounds such as Dudlin, Crolthene, and Sumition are known. This compound is also a toxic substance that is harmful to the environment and its use is prohibited.
또한, 기존에 목재 구조물에 대하여 실시하던 방염, 방충, 방부 처리방법은 방염 성능을 갖는 약제를 먼저 함침시킨 다음 건조한 후에 방충, 방부성능을 갖는 약제를 함침시키는 방법 등이 사용되어 오고 있다. 그러나 이 방법은 여러 단계를 나누어 실시하여야 하므로 코팅방법이 번거롭다는 문제점이 있다.In addition, the conventional flame retardant, insect repellent, antiseptic treatment method for the wooden structure has been used to impregnate the agent having a flame retardant performance first, and then to impregnate the agent having insect repellent, antiseptic performance after drying. However, this method has a problem that the coating method is cumbersome because it must be carried out in several steps.
본 발명은 상술한 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 방수서, 발수성, 방염성, 방미성, 방부성, 방충성 및 목재, 콘크리트 등의 건축자재에 대한 접착성이 우수하고, 아름다운 색채를 나타내고, 코팅방법이 간단하고 코팅층의 두께를 자유로이 조절할 수 있고 환경친화적인 코팅제 조성물을 제공하는 것이다.The present invention is to solve the above-mentioned problems, the object of the present invention is waterproof, water repellent, flame retardant, anti-fog, antiseptic, insect repellent and excellent adhesion to building materials such as wood, concrete, beautiful colors The coating method is simple and the thickness of the coating layer can be freely controlled, and an environmentally friendly coating composition is provided.
본 발명의 목적은 또한 상기 코팅막 보존제를 제공하는 것이다.It is also an object of the present invention to provide such coating preservatives.
상기 목적을 달성하기 위하여, 본 발명은 (a) 담말 수지, 송진 및 로진으로 이루어진 군으로부터 선택되는 접착성분 70 내지 100 중량부; 및 (b) 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분 5 내지 100 중량부를 포함하는 코팅제 조성물을 제공한다.In order to achieve the above object, the present invention (a) 70 to 100 parts by weight of the adhesive component selected from the group consisting of dipped resin, rosin and rosin; And (b) 5 to 100 parts by weight of a wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax, and white lead.
본 발명은 또한 (a) 트리클로로에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물 10 내지 200 중량부; 및 (b) 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분 5 내지 100 중량부를 포함하는 코팅막 보존제를 제공한다.The invention also relates to (a) 10 to 200 parts by weight of trichloroethylene, methylene chloride or mixtures thereof; And (b) 5 to 100 parts by weight of a wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax and white lead.
이하 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 코팅제 조성물은 필수 성분으로 접착성분 및 왁스성분을 포함한다.The coating composition of the present invention includes an adhesive component and a wax component as essential components.
상기 접착성분으로는 담말 수지(dammar resin), 송진, 로진 또는 이들의 혼합물이 사용되고 왁스성분으로는 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스, 백납 또는 이들의 혼합물이 사용된다.As the adhesive component, a dammar resin, rosin, rosin or a mixture thereof is used, and as a wax component, polyethylene wax, paraffin wax, liquid paraffin, carbona wax, white lead or a mixture thereof is used.
본 발명의 코팅제 조성물에 포함되는 담말 수지(dammar resin)는 천연 수지의 일종으로 Dipterocarpceae과 나무의 분비물이 고체화된 것으로 담말 배니시(dammar vanish) 제조에 주로 사용된다. 담말 수지는 접착성이 우수하여 본 발명의 코팅제 조성물은 목재, 콘크리트 등의 건축자재에 접착성이 매우 우수하다.Dammar resin included in the coating composition of the present invention is a kind of natural resin and is mainly used for the production of dammar vanish as the secretion of Dipterocarpceae and wood is solidified. The adhesive resin is excellent in adhesiveness and the coating composition of the present invention is very excellent in adhesion to building materials such as wood and concrete.
본 발명의 코팅제 조성물에 포함되는 상기 담말 수지의 함량은 70 내지 100 중량부가 바람직하다. 담말 수지의 함량이 70 중량부 미만이면 본 발명의 코팅제 조성물이 목재, 콘크리트 등의 건축자재에의 접착력이 저하되고 상기 조성물이 코팅된 목재, 콘크리트 등의 건축자재 표면이 거칠어지는 문제점이 있고, 100 중량부를 초과하면 본 발명의 코팅제 조성물의 방수성 및 발수성이 저하되는 문제점이 있다.The content of the above-mentioned resin included in the coating composition of the present invention is preferably 70 to 100 parts by weight. If the content of the resin resin is less than 70 parts by weight of the coating composition of the present invention has a problem that the adhesive strength to the building materials, such as wood, concrete is reduced and the surface of the building material, such as wood, concrete coated with the composition is rough, 100 When it exceeds the weight part, there is a problem that the waterproofing and water repellency of the coating composition of the present invention is lowered.
본 발명의 코팅제 조성물은 또한 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분을 포함한다. 이 왁스성분은 분산제, 가공조제, 윤활제, 이형제, 계면 활성제, 플라스틱, 고무, 전선케이블 등 제조시 첨가제로 널리 사용되어 오고 있다.The coating composition of the present invention also includes a wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax and white lead. This wax component has been widely used as an additive in the manufacture of dispersants, processing aids, lubricants, mold release agents, surfactants, plastics, rubber, wire cables, and the like.
상기 왁스성분은 본 발명의 코팅제 조성물에 요변성(thixotropy)을 부여하고 방수 및 발수 기능을 부여한다. 각종 목재 등에 생육하는 미생물은 습도 15% 이하에서 번식이 중단된다. 이처럼 왁스성분은 방수 및 발수 기능이 우수하여 목재의 수분흡수를 차단하므로 본 발명의 코팅제 조성물이 코팅된 목재에서는 대부분의 미생물이 사멸하게 된다.The wax component imparts thixotropy to the coating composition of the present invention and imparts waterproofing and water repellency. Microorganisms growing on various woods, etc., stop breeding at 15% or less humidity. As such, the wax component is excellent in waterproofing and water repellency to block water absorption of the wood, so most of the microorganisms are killed in the wood coated with the coating composition of the present invention.
본 발명의 코팅제 조성물에 포함되는 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분의 함량은 5 내지 100 중량부가 바람직하다. 상기 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분의 함량이 5 중량부 미만이면 본 발명의 코팅제 조성물의 방수 및 발수 기능이 저하되고, 100 중량부를 초과하면 본 발명의 코팅제 조성물의 투과도가 지나치게 낮아져 목재, 콘크리트 등의 건축자재의 화려한 색채가 잘 나타나지 않는 문제점이 있다.The content of the wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax and white lead included in the coating composition of the present invention is preferably 5 to 100 parts by weight. When the content of the wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax and white lead is less than 5 parts by weight, the waterproofing and water repellency of the coating composition of the present invention is lowered, and if it exceeds 100 parts by weight. The transmittance of the coating composition of the present invention is too low, there is a problem that the colorful color of the building materials such as wood, concrete does not appear well.
본 발명의 코팅제 조성물은 또한 에틸렌 비닐 아세테이트 수지(ethylene vinyl acetate resin), 우레탄 수지(urethane resin) 또는 이들의 혼합물을 더욱 포함할 수 있다. 이 에틸렌 비닐 아세테이트 수지, 우레탄 수지 또는 이들의 혼합물은 본 발명의 코팅제 조성물의 온도 특성을 향상시키는 역할을 한다.The coating composition of the present invention may also further comprise ethylene vinyl acetate resin, urethane resin or mixtures thereof. This ethylene vinyl acetate resin, urethane resin, or mixtures thereof serves to improve the temperature characteristics of the coating composition of the present invention.
즉, 본 발명의 코팅제 조성물에 상기 에틸렌 비닐 아세테이트 수지(ethylene vinyl acetate resin), 우레탄 수지 또는 이들의 혼합물을 첨가하면 코팅제 조성물은 겨울철의 저온에서도 지나치게 경화되지 않는다. 이로 인하여 본 발명의 코팅제 조성물이 코팅된 코팅막이 저온에서도 갈라지지 않는 효과가 있다.That is, when the ethylene vinyl acetate resin, urethane resin, or a mixture thereof is added to the coating composition of the present invention, the coating composition does not cure excessively even at low temperatures in winter. Because of this, there is an effect that the coating film coated with the coating composition of the present invention does not crack even at low temperatures.
또한, 본 발명의 코팅제 조성물에 상기 에틸렌 비닐 아세테이트 수지, 우레탄 수지 또는 이들의 혼합물을 첨가하면 코팅제 조성물은 여름철의 고온에서도 지나치게 경도가 낮아지지 않는다. 이로 인하여 본 발명의 코팅제 조성물이 코팅된 코팅막이 고온에서도 유동성을 갖지 않는 효과가 있다.In addition, when the ethylene vinyl acetate resin, urethane resin, or a mixture thereof is added to the coating composition of the present invention, the coating composition does not become too low even at high temperatures in summer. This has the effect that the coating film coated with the coating composition of the present invention does not have fluidity even at high temperatures.
본 발명의 코팅제 조성물에 포함될 수 있는 에틸렌 비닐 아세테이트 수지,우레탄 수지 또는 이들의 혼합물의 함량은 10 내지 50 중량부가 바람직하다. 이 에틸렌 비닐 아세테이트 수지, 우레탄 수지 또는 이들의 혼합물의 함량이 10 중량부 미만이면 코팅제 조성물의 경도가 낮아서 내후성이 떨이지는 문제점이 있고, 50 중량부를 초과하면 코팅제 조성물이 지나치게 경화된다는 문제점이 있어 바람직하지 않다.The content of ethylene vinyl acetate resin, urethane resin or mixtures thereof that may be included in the coating composition of the present invention is preferably 10 to 50 parts by weight. If the content of the ethylene vinyl acetate resin, urethane resin, or mixture thereof is less than 10 parts by weight, the hardness of the coating composition is low, and thus the weatherability is reduced. If the content is more than 50 parts by weight, the coating composition is excessively cured. not.
본 발명의 코팅제 조성물은 들기름, 동유, 테레핀유, 파인류 또는 이들의 혼합물의 유지성분을 더욱 포함할 수 있다.The coating composition of the present invention may further comprise a fat or oil component of oil, tung oil, terepin oil, pine or mixtures thereof.
이 유지성분은 본 발명의 코팅제 조성물을 보호하고 온도의 변화에 따른 코팅제 조성물의 물성을 보호하는 기능을 한다.This fat and oil component serves to protect the coating composition of the present invention and to protect the physical properties of the coating composition with the change of temperature.
본 발명의 코팅제 조성물에 더욱 첨가될 수 있는 들기름, 동유, 테레핀유, 파인류 또는 이들의 혼합물인 유지성분의 함량은 0.1 내지 20 중량부가 바람직하다.The content of the oil or fat component which can be further added to the coating composition of the present invention is oil, tung oil, terepin oil, pine or mixtures thereof is preferably 0.1 to 20 parts by weight.
상기 들기름, 동유, 테레핀유, 파인류 또는 이들의 혼합물인 유지성분의 함량이 0.1 중량부 미만이면 코팅제 조성물의 온도에 따른 물성의 변화가 저하되고, 20 중량부를 초과하면 코팅제 조성물 코팅시 잘 건조되지 않는다는 문제점이 있다.When the content of the fat or oil of the oil, kerosene, terepine oil, pine or mixtures thereof is less than 0.1 parts by weight, the change in physical properties according to the temperature of the coating composition is lowered, and if it exceeds 20 parts by weight, the coating composition is not dried well There is a problem.
또한, 본 발명의 코팅제 조성물은 제1 인산 인산암모늄을 주성분으로 하는 분말소화기용 조성물, 황산암모늄 또는 이들의 혼합물인 방염성분을 더욱 포함할 수 있다.In addition, the coating composition of the present invention may further include a flame retardant component which is a composition for powder fire extinguishers, the ammonium sulphate or a mixture thereof, mainly comprising first ammonium phosphate.
상기 방염성분 중 제1인산 암모늄을 주성분으로 하는 분말소화기용 조성물은 소화 기능이 우수한 물질로서 분말 소화기에 일반적으로 사용되는 화합물이다. 본발명에 사용될 수 있는 제1 인산 암모늄을 주성분으로 하는 분말소화기용 조성물은 제1인산 암모늄 70 내지 97 중량%, 가소제 0.1 내지 0.5 중량%, 실리콘유 0.5 내지 1.0 중량%, 경화제 0.1 내지 0.5 중량%, 유동제 0.5 내지 1.0 중량%를 포함하고, 분말의 입경이 0.1 내지 75 ㎛인 것이 바람직하다.The composition for a powder fire extinguisher having a primary component of ammonium phosphate as the main component of the flame retardant is a compound generally used in powder fire extinguishers as a material having excellent extinguishing function. The composition for powder fire extinguishers based on the first ammonium phosphate which can be used in the present invention is 70 to 97% by weight of ammonium monophosphate, 0.1 to 0.5% by weight of plasticizer, 0.5 to 1.0% by weight of silicone oil, and 0.1 to 0.5% by weight of curing agent. And 0.5 to 1.0% by weight of a flow agent, and the particle size of the powder is preferably 0.1 to 75 µm.
상기 제1인산 암모늄을 주성분으로 하는 분말소화기용 조성물은 인체와 가축에 무해한 것으로 이 제1인산 암모늄을 주성분으로 하는 분말소화기용 조성물을 포함하는 본 발명의 코팅제 조성물은 환경친화적인 효과가 있다.The composition for powder fire extinguishers containing the first ammonium phosphate as a main component is harmless to humans and livestock, and the coating composition of the present invention comprising the composition for powder fire extinguishers containing the first ammonium phosphate as a main component has an environmentally friendly effect.
본 발명의 코팅제 조성물에 있어서, 제1 인산 인산암모늄을 주성분으로 하는 분말소화기용 조성물, 황산암모늄 또는 이들의 혼합물인 방염성분의 함량은 150 내지 200 중량부가 바람직하다. 상기 코팅제 조성물은 제1 인산 인산암모늄을 주성분으로 하는 분말소화기용 조성물, 황산암모늄 또는 이들의 혼합물인 방염성분의 함량이 150 중량부 미만이면 본 발명의 코팅제 조성물의 방염성이 저하되고, 200 중량부를 초과하면 코팅제 조성물의 점도가 너무 높아져 목재, 콘크리트 등의 건축자재에의 접착력이 저하되어 바람직하지 않다.In the coating composition of the present invention, the content of the flame retardant composition, which is a composition for a powder fire extinguisher having a primary ammonium phosphate as a main component, ammonium sulfate or a mixture thereof, is preferably 150 to 200 parts by weight. The coating composition has a flame retardancy of the coating composition of the present invention is lowered if the content of the flame retardant composition, which is the first component of ammonium phosphate, ammonium sulfate or a mixture thereof, is less than 150 parts by weight, and the coating composition of the present invention is less than 200 parts by weight. The viscosity of the coating composition becomes so high that adhesion to building materials such as wood and concrete is lowered, which is undesirable.
또한 본 발명의 코팅제 조성물은 상온에서도 우수한 코팅성을 가지고 백화현상을 제거하기 위하여 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물을 더욱 포함할 수 있다.In addition, the coating composition of the present invention may further include trichloroethylene, methylene chloride or a mixture thereof in order to remove the whitening phenomenon with excellent coating properties even at room temperature.
트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물은 휘발성이 우수하여 본 발명의 코팅제 조성물의 점도를 낮추어 준다. 따라서 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물을 포함할 경우 본 발명의 코팅제 조성물은상온에서도 쉽게 코팅제로 사용될 수 있다. 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물이 첨가되지 않은 본 발명의 코팅제 조성물은 일반적으로 50 내지 160 ℃의 온도에서 가열하여 사용하면 코팅성이 우수하다. 그러나 상기와 같은 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물이 첨가된 코팅제 조성물은 가열하지 않아도 우수한 코팅성을 나타낸다.Trichloro ethylene, methylene chloride or mixtures thereof are excellent in volatility to lower the viscosity of the coating composition of the present invention. Therefore, when including trichloro ethylene, methylene chloride or a mixture thereof, the coating composition of the present invention can be easily used as a coating agent even at room temperature. The coating composition of the present invention, to which trichloroethylene, methylene chloride or a mixture thereof is not added, generally has excellent coating properties when heated and used at a temperature of 50 to 160 ° C. However, the coating composition to which such trichloroethylene, methylene chloride or a mixture thereof is added shows excellent coating property even without heating.
또한, 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물은 폴리에틸렌 왁스 등과 반응하여 본 발명의 코팅제 조성물이 코팅된 코팅막 표면에 보호막을 형성한다. 이와 같이 형성된 보호막은 본 발명의 코팅제 조성물이 코팅된 코팅막의 백화 현상을 방지하는 기능을 한다.In addition, trichloroethylene, methylene chloride or a mixture thereof reacts with polyethylene wax or the like to form a protective film on the surface of the coating film coated with the coating composition of the present invention. The protective film formed as described above functions to prevent whitening of the coating film coated with the coating composition of the present invention.
본 발명의 코팅제 조성물에 상기 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물이 첨가될 경우에 바람직한 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물의 함량은 10 내지 200 중량부이다.When the trichloro ethylene, methylene chloride or a mixture thereof is added to the coating composition of the present invention, the preferred content of trichloro ethylene, methylene chloride or a mixture thereof is 10 to 200 parts by weight.
본 발명의 코팅제 조성물에 상기 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물이 첨가될 경우에 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물의 함량이 10 중량부 미만이면 본 발명의 코팅제 조성물의 점도가 지나치게 높아져 상온에서 코팅제로 사용될 수 없고 반드시 가열하여 사용하여야 한다는 문제점이 있다.When the trichloroethylene, methylene chloride or a mixture thereof is added to the coating composition of the present invention, if the content of trichloroethylene, methylene chloride or a mixture thereof is less than 10 parts by weight, the viscosity of the coating composition of the present invention becomes excessively high. There is a problem that can not be used as a coating agent at room temperature and must be used after heating.
또한, 본 발명의 코팅제 조성물에 상기 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물이 첨가될 경우에 트리클로로 에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물의 함량이 200 중량부를 초과하면 본 발명의 코팅제 조성물의 점도가 지나치게 낮아져 본 발명의 코팅제 조성물을 목재 등의 표면에 코팅한 경우 코팅제 조성물이 흘러내려 균일한 코팅층을 형성할 수 없다는 문제점이 있다.In addition, when the trichloro ethylene, methylene chloride or a mixture thereof is added to the coating composition of the present invention, if the content of trichloro ethylene, methylene chloride or a mixture thereof exceeds 200 parts by weight, the viscosity of the coating composition of the present invention may be When the coating composition of the present invention is coated on the surface of wood, such as too low, there is a problem that the coating composition flows down to form a uniform coating layer.
본 발명의 코팅제 조성물은 또한 아름다운 색채를 나타내기 하기 위하여 안료를 더욱 포함할 수 있다. 본 발명의 코팅제 조성물에 바람직하게 첨가될 수 있는 안료로는 크게 유기질 안료와 무기질 안료로 구분된다.The coating composition of the present invention may also further comprise a pigment in order to exhibit a beautiful color. Pigments that can be preferably added to the coating composition of the present invention are largely divided into organic pigments and inorganic pigments.
유기질 안료로는 뇌록색의 시아닌그린(cyanine green), 장단색의 퍼머넌트 오렌지(permanant orange), 석황색의 퍼머넌트 옐로(permanent yellow), 주홍색의 톨루이딘 레드(toluidine red), 먹색의 퍼머넌트 블랙(permanent black) 등이 바람직하게 사용될 수 있다.Organic pigments include cyanine green in cerebral green, permanant orange in short and short, permanent yellow in turquoise, scarlet toludine red, and permanent black in black. ) May be preferably used.
또한 무기질 안료로는 백분색의 티타늄 디옥사이드(titanium dioxide), 황토색의 아이언 옥사이드 옐로(iron oxide yellow), 호분, 양분색의 에머랄드 그린(emerald green), 장단색의 리드 레드(lead red), 군청색의 코발트 블루(cobalt blue), 석간주색의 아이언 옥사이드 레드(iron oxide red), 석황색의 크롬 옐로(chrome yellow), 하엽색의 크로미움 옥사이드 그린(chromium oxide green), 군청색의 울트라마린 블루(ultramarine blue) 등이 바람직하게 사용될 수 있다.Inorganic pigments include white titanium dioxide, yellow iron oxide yellow, whiskers, bicolor emerald green, long and short reddish red, ultramarine blue. Cobalt blue, lime-colored iron oxide red, tin-yellow chrome yellow, lower-color chromium oxide green, ultramarine ultramarine blue ) May be preferably used.
상기에서 예를 든 유기질 안료 및 무기질 안료는 모두 문화재관리국에서 지정하는 규격 안료로 단청에 일반적으로 사용되는 것이다. 본 발명의 코팅제 조성물의 용도에 따라 상기 안료 중 적절한 색을 선택하여 본 발명의 코팅제 조성물에 첨가할 수 있다.The organic pigments and inorganic pigments exemplified above are all commonly used in mono as a standard pigment designated by the Cultural Heritage Administration. According to the use of the coating composition of the present invention, an appropriate color among the pigments may be selected and added to the coating composition of the present invention.
본 발명의 코팅제 조성물에 포함되는 상기 안료의 함량은 0.1 내지 60 중량부가 바람직하다. 이 안료의 함량이 0.1 중량부 미만이면 본 발명의 코팅제 조성물이 단청에 가까운 아름다운 색을 나타 내지 못하고, 60 중량부를 초과하면 상기 코팅제 조성물의 경도 및 점도가 상승하여 목재, 콘크리트 등의 건축자재에 대한 접착력이 저하되어 바람직하지 않다.The content of the pigment included in the coating composition of the present invention is preferably 0.1 to 60 parts by weight. If the content of the pigment is less than 0.1 parts by weight, the coating composition of the present invention does not exhibit a beautiful color close to mono, and if it exceeds 60 parts by weight, the hardness and viscosity of the coating composition is increased to the construction materials such as wood, concrete, etc. It is unpreferable because adhesive force falls.
본 발명의 코팅제 조성물을 목재, 콘크리트 등의 건축자재에 코팅하는 방법으로는 스프레이 코팅, 딥 코팅 등 일반적으로 사용되는 코팅 방법은 모두 사용 가능하다. 또한 목재, 콘크리트 등의 건축자재에 직접 칠하여 사용할 수도 있다.As a method of coating the coating composition of the present invention on building materials such as wood and concrete, any coating method generally used, such as spray coating or dip coating, may be used. It can also be used by directly painting on building materials such as wood and concrete.
본 발명은 또한, (a) 트리클로로에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물 10 내지 200 중량부; 및 (b) 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분 0.1 내지 20 중량부를 포함하는 코팅막 보존제를 제공한다.The present invention also provides (a) 10 to 200 parts by weight of trichloroethylene, methylene chloride or a mixture thereof; And (b) 0.1 to 20 parts by weight of a wax component selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax, and white lead.
상기 코팅막 보존제를 본 발명의 코팅제 조성물이 코팅된 코팅막에 도포하면 코팅막의 표면에 막이 형성되어 코팅막 표면에 백화현상이 발생하지 않고 영하의 저온이나 열대지방의 고온에서도 코팅막이 안전하게 보존된다.When the coating film preservative is applied to the coating film coated with the coating composition of the present invention, a film is formed on the surface of the coating film so that whitening does not occur on the surface of the coating film, and the coating film is safely stored even at a low temperature below zero or a high temperature in the tropics.
이 코팅막 보존제는 트리클로로에틸렌, 메틸렌 클로라이드 또는 이들의 혼합물 및 폴리에틸렌 왁스, 파라핀 왁스, 유동파라핀, 카르보나 왁스 및 백납으로 이루어진 군으로부터 선택되는 왁스성분을 혼합하여 50 내지 160 ℃로 가열한 다음 상온으로 식혀 코팅막 표면에 도포할 수 있다.This coating film preservative is mixed with trichloroethylene, methylene chloride or a mixture thereof and wax components selected from the group consisting of polyethylene wax, paraffin wax, liquid paraffin, carbona wax and white lead, heated to 50 to 160 ℃ and then to room temperature It can cool and apply to the surface of a coating film.
이상 살펴본 바와 같이, 본 발명의 코팅제 조성물은 방수성, 발수성, 방염성, 방미성, 방부성, 방충성 및 목재, 콘크리트 등의 건축자재에 대한 접착성이 우수하고, 아름다운 색채를 나타내고, 코팅방법이 간단하고 코팅층의 두께를 자유로이 조절할 수 있고 환경친화적이다.As described above, the coating composition of the present invention is excellent in adhesion to building materials such as waterproof, water repellent, flame retardant, anti-fog, antiseptic, insect repellent and wood, concrete, exhibits a beautiful color, coating method is simple and The thickness of the coating layer can be freely adjusted and environmentally friendly.
이하 본 발명의 바람직한 실시예 및 비교예를 기재한다. 하기 실시예 및 비교예는 본 발명을 보다 명확히 표현하기 위한 목적으로 기재될 뿐 본 발명의 내용이 하기 실시예 및 비교예에 한정되는 것은 아니다.Hereinafter, preferred examples and comparative examples of the present invention are described. The following examples and comparative examples are described for the purpose of more clearly expressing the present invention, but the contents of the present invention are not limited to the following examples and comparative examples.
(실시예 1)(Example 1)
담말 수지 80 g, 폴리에틸렌 왁스 8 g, 파라핀 왁스 8 g 및 에틸렌 비닐 아세테이트 수지 27 g을 혼합하고 이 혼합물을 150 ℃에서 7 분 동안 가열하였다. 이 가열된 혼합물에 유동 파라핀 5 g을 첨가하고 150 ℃에서 3 분 동안 균일하게 혼합하여 코팅제 조성물을 제조하였다.80 g of the resin resin, 8 g of polyethylene wax, 8 g of paraffin wax and 27 g of ethylene vinyl acetate resin were mixed and the mixture was heated at 150 ° C. for 7 minutes. 5 g of liquid paraffin was added to this heated mixture and uniformly mixed at 150 ° C. for 3 minutes to prepare a coating composition.
(실시예 2)(Example 2)
트리클로로에틸렌 40 g을 더욱 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 실시하였다.The same procedure as in Example 1 was carried out except that 40 g of trichloroethylene was further added.
(실시예 3)(Example 3)
담말 수지 80 g, 폴리에틸렌 왁스 8 g, 유동 파라핀 5 g, 파라핀 왁스 8 g 및 에틸렌 비닐 아세테이트 수지 27 g을 혼합하고 이 혼합물을 160 ℃에서 7 분 동안 가열하였다. 상기 가열된 혼합물에 제1인산 암모늄을 주성분으로 하는 분말소화기용 조성물을 180 g 첨가한 후 3 분 동안 균일하게 혼합하여 코팅제 조성물을 제조하였다.80 g of the resin resin, 8 g of polyethylene wax, 5 g of liquid paraffin, 8 g of paraffin wax, and 27 g of ethylene vinyl acetate resin were mixed and the mixture was heated at 160 ° C. for 7 minutes. 180 g of a powder fire extinguisher composition mainly containing ammonium monophosphate was added to the heated mixture, and then uniformly mixed for 3 minutes to prepare a coating composition.
(실시예 4)(Example 4)
제1인산 암모늄을 주성분으로 하는 분말소화기용 조성물 첨가시 아이언 옥사이드 레드(iron oxide red) 20 g을 더욱 첨가한 후 트리클로로에틸렌 40 g을 더욱 첨가한 것을 제외하고는 실시예 3과 동일하게 실시하여 코팅제 조성물을 제조하였다.When adding the composition for the powder fire extinguisher mainly composed of ammonium phosphate, the same procedure as in Example 3 was performed except that 20 g of iron oxide red was further added, followed by 40 g of trichloroethylene. A coating composition was prepared.
방수성 시험Waterproof test
크기 13 ×2 ×1 ㎝의 미국산 소나무의 표면에 상기 실시예 1 내지 4에서 제조한 코팅제 조성물을 2 ㎜ 두께로 코팅한 후 상기 소나무를 10 ㎝ 깊이의 물속에침적시켰다. 그 다음 상기 소나무를 12 시간 간격으로 꺼내어 소나무의 표면을 닦고 무게를 측정하여 수분 흡수율을 계산하였다. 또한 비교예로는 상시 실시예 1 내지 4의 코팅제 조성물을 코팅하지 않은 크기 13 ×2 ×1 ㎝의 미국산 소나무를 사용하였다.After coating the coating composition prepared in Examples 1 to 4 with a thickness of 2 mm on the surface of American pines having a size of 13 x 2 x 1 cm, the pines were immersed in water of 10 cm depth. Then, the pines were taken out at 12 hour intervals, and the surface of the pines was wiped and weighed to calculate moisture absorption. In addition, as a comparative example, US pines having a size of 13 × 2 × 1 cm without coating the coating composition of Examples 1 to 4 were used.
방수성 평가는 코팅제 조성물을 처리하지 않은 소나무의 수분 흡수율 및 코팅제 조성물을 처리한 소나무의 수분 흡수율을 계산하여 하기 식에 대입하여 방수지수를 평가하였다.Water resistance evaluation was calculated by calculating the water absorption rate of the pine without the coating composition and the water absorption rate of the pine treated with the coating composition in the following formula to evaluate the waterproof index.
[식 1] [Equation 1]
방수지수가 높을수록 방수율이 높으며 수분을 전혀 흡수하지 않으면 방수지수가 100이된다.The higher the waterproof index, the higher the waterproofing rate, and if it does not absorb moisture at all, it becomes 100.
상기 식 1에 의하여 각 실시예의 코팅제 조성물의 방수지수를 계산하여 그 결과를 하기 표 1에 나타내었다.By calculating the waterproof index of the coating composition of each Example by the formula 1 shown in Table 1 below.
상기 표 1에 나타나 바와 같이, 본 발명의 코팅제 조성물을 처리한 소나무의 방수지수는 시간이 경과함에 따라 거의 변하지 않았으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무의 방수지수는 시간이 경과함에 따라 급속히 저하됨을 알 수 있었다. 따라서 본 발명의 코팅제 조성물은 방수성이 우수함을 알 수 있다.As shown in Table 1, the waterproof index of the pine treated with the coating composition of the present invention was almost unchanged over time, but the waterproof index of the pine without the coating composition of the present invention rapidly decreased with time. And it was found. Therefore, it can be seen that the coating composition of the present invention is excellent in water resistance.
발수성 시험Water repellency test
상기 실시예 1 내지 4의 코팅제 조성물을 처리한 소나무 시료 및 코팅제 조성물을 처리하지 않은 소나무 시료에 대한 발수성은 JISL-1005에 따른 분무방법으로 측정하여 그 결과를 하기 표 3에 나타내었다. 발수평가지수는 0 내지 100으로 하였다. 발수평가지수가 높을수록 발수도가 우수함을 나타낸다. 발수평가지수에 대한 평가를 하기 표 2에 나타내었다.The water repellency of the pine sample treated with the coating composition of Examples 1 to 4 and the pine sample not treated with the coating composition was measured by a spray method according to JISL-1005, and the results are shown in Table 3 below. The water repellency evaluation index was 0-100. Higher water repellency evaluation index indicates better water repellency. Evaluation of the water repellency evaluation index is shown in Table 2 below.
상기 표 3에 나타난 바와 같이, 본 발명의 코팅제 조성물을 처리한 소나무의 발수평가지수는 모두 100이었으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무의 발수평가지수는 모두 0이었다. 따라서 본 발명의 코팅제 조성물은 발수성도 우수함을 알 수 있다.As shown in Table 3, the water repellency evaluation index of the pine treated with the coating composition of the present invention was all 100, but the water repellency evaluation index of the pine without the coating composition of the present invention was all zero. Therefore, it can be seen that the coating composition of the present invention is also excellent in water repellency.
방염성 시험Flame retardant test
본 발명의 코팅제 조성물을 처리한 소나무 및 코팅제 조성물을 처리하지 않은 소나무 3 편의 시편을 준비하여 행정자치부/한국소방검정공사에서 발행한 방염성능의 기준 및 시험세칙(KOFEIS 1001) 제 7조 ‘함판 등의 방염성능측정기준 및 방법’에 따라 방염시험을 행한 뒤 평균값을 구하여 그 결과를 하기 표 4에 나타내었다. 소방법 시행령에 따라 각 시편에 메이커 버너로 2 분간 가열한 후 버너의 불꽃을 제거하고 나서 불꽃을 올리며 연소하는 상태가 그칠 때까지의 시간을 잔염시간, 불꽃을 올리지 아니하고 연소하는 상태가 그칠때까지의 시간을 잔신시간, 탄화한 길이를 탄화거리, 탄화한 면적을 탄화면적이라 정의한다. KOFEIS 1001의 합격기준은 잔염시간 10 초 이내, 잔신시간 30 초 이내, 탄화거리 20 ㎝ 이하, 탄화면적 50 ㎠ 이하이다.Preparation of pine wood treated with the coating composition of the present invention and three pieces of pine wood without the coating composition were prepared, and the standards and test regulations for flame-proof performance issued by the Ministry of Public Administration and Home Affairs / Korea Fire Protection Corporation (KOFEIS 1001) According to the flame resistance performance measurement standards and methods of 'to measure the average value of the flame resistance test is shown in Table 4 below. According to the Enforcement Decree, each specimen is heated with a maker burner for 2 minutes, after which the flame of the burner is removed, and then the time until the burning state is over with the flame is raised. Time is defined as remaining time, carbonized length is carbonized distance, and carbonized area is carbon screen. The acceptance criteria for KOFEIS 1001 are less than 10 seconds of residual flame time, less than 30 seconds of residual time, less than 20 cm of carbonization distance and less than 50 cm 2 of carbon screen area.
상기 표 4에 나타난 바와 같이, 본 발명의 실시예 3 및 4의 코팅제 조성물을 처리한 소나무는 방염성능 시험에 모두 합격하였으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무는 방염성능 시험에 모두 불합격하였다. 따라서 본 발명의 코팅제 조성물은 방염성 또한 우수함을 알 수 있다.As shown in Table 4, the pine treated with the coating composition of Examples 3 and 4 of the present invention passed all flame retardant performance test, but all of the pine without the coating composition of the present invention failed the flame retardant test. Therefore, it can be seen that the coating composition of the present invention is also excellent in flame resistance.
방미성 시험Anti-fog test
임업연구원 목재보존연구실 규격 제 2호(1997)에 정하는 방법에 따라 털곰팡이와 청변균을 사용하여 4 주일간 시험한 후 개개 시편에서의 균체발육상황을 관찰하여 평가치를 하기 표 6에 나타내었다. 하기 표 5에는 평가치에 대한 정의를 나태내었다.According to the Forest Conservation Research Institute Timber Preservation Laboratory Specification No. 2 (1997), after testing for 4 weeks using the fungus and blue bacteria, the growth status of the individual specimens was observed and shown in Table 6. Table 5 below shows the definition of the evaluation values.
상기 표 6에 나타난 바와 같이, 본 발명의 코팅제 조성물을 처리한 소나무는 방미성 시험에 모두 합격하였으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무는 방미성 시험에 모두 불합격하였다. 따라서 본 발명의 코팅제 조성물은 방미성 또한 우수함을 알 수 있다.As shown in Table 6, the pine treated with the coating composition of the present invention passed all the anti-fog test, but all of the pine without the coating composition of the present invention failed the anti-fog test. Therefore, it can be seen that the coating composition of the present invention is also excellent in odor.
방부성 시험Antiseptic test
KS M-1701 목재 방부제(1997)에서 정하는 시험방법에 따라 갈색 부후균인 부후개떡버섯균과 백색 부후균인 구름버섯균을 사용하여 3 주간 시험한 후에 시편의 평균 질량 감소율을 구하여 그 결과를 하기 표 7에 나타내었다. KS에서는 평균 질량감소율이 3% 이하를 방부성능 달성기준으로 정하고 있다.According to the test method set forth in KS M-1701 Wood Preservative (1997), after the test for 3 weeks using brown fungi, fusiform fungi, and white fungi, cloud fungi, obtain the average mass reduction rate of the specimen. Table 7 shows. In KS, the average mass reduction rate is 3% or less.
상기 표 7에 나타난 바와 같이, 본 발명의 코팅제 조성물을 처리한 소나무는 방부성 시험에 모두 합격하였으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무는 방부성 시험에 모두 불합격하였다. 따라서 본 발명의 코팅제 조성물은 방부성 또한 우수함을 알 수 있다.As shown in Table 7, the pine treated with the coating composition of the present invention passed all preservative tests, but the pine without the coating composition of the present invention all failed the preservative test. Therefore, it can be seen that the coating composition of the present invention is also excellent antiseptic.
방충성 시험Insect repellent test
임업연구원 목재보존연구실 규격 제10호(1997)에 정하는 방법에 따라 일본 흰개미와 집흰개를 이용하여 3 주일간 시험한 후에 각 시편의 평균 질량 감소율 및 사충율을 구하여 그 결과를 하기 표 8에 나타내었다. 이 경우 평균 질량 감소율이 3% 이하가 되어야 방충효력이 있는 것으로 평가된다.According to the method of forestry researcher wood conservation laboratory standard No. 10 (1997), after testing for 3 weeks using Japanese termites and herd termites, the average mass loss rate and mortality rate of each specimen were obtained and the results are shown in Table 8 below. . In this case, the average mass reduction rate is 3% or less to evaluate the insect repellent effect.
상기 표 8에 나타난 바와 같이, 본 발명의 코팅제 조성물을 처리한 소나무는 방충성 시험에 모두 합격하였으나 본 발명의 코팅제 조성물을 처리하지 않은 소나무는 방충성 시험에 모두 불합격하였다. 따라서 본 발명의 코팅제 조성물은 방충성 또한 우수함을 알 수 있다.As shown in Table 8, the pine treated with the coating composition of the present invention passed all the insect repellent test, but the pine without the coating composition of the present invention all failed the insect repellent test. Therefore, it can be seen that the coating composition of the present invention is also excellent in insect repellent.
본 발명의 코팅제 조성물은 방수성, 발수성, 방염성, 방미성, 방부성, 방충성 및 목재, 콘크리트 등의 건축자재에 대한 접착성이 우수하고, 아름다운 색채를 나타내고, 코팅방법이 간단하고 코팅층의 두께를 자유로이 조절할 수 있고 환경친화적이다.The coating composition of the present invention is waterproof, water repellent, flame retardant, anti-fog, antiseptic, insect repellent and excellent adhesion to building materials, such as wood, concrete, exhibits a beautiful color, the coating method is simple and the thickness of the coating layer freely It is adjustable and environmentally friendly.
Claims (9)