CN102229480A - 稀土保温材料 - Google Patents

稀土保温材料 Download PDF

Info

Publication number
CN102229480A
CN102229480A CN2010106214468A CN201010621446A CN102229480A CN 102229480 A CN102229480 A CN 102229480A CN 2010106214468 A CN2010106214468 A CN 2010106214468A CN 201010621446 A CN201010621446 A CN 201010621446A CN 102229480 A CN102229480 A CN 102229480A
Authority
CN
China
Prior art keywords
rare earth
percent
earth heat
preserving material
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010106214468A
Other languages
English (en)
Inventor
谭明佳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BAOTOU CITY YI LONG INDUSTRY AND TRADE CO LTD
Original Assignee
BAOTOU CITY YI LONG INDUSTRY AND TRADE CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAOTOU CITY YI LONG INDUSTRY AND TRADE CO LTD filed Critical BAOTOU CITY YI LONG INDUSTRY AND TRADE CO LTD
Priority to CN2010106214468A priority Critical patent/CN102229480A/zh
Publication of CN102229480A publication Critical patent/CN102229480A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种稀土保温材料，其特征是：稀土保温材料是由下述组分的原料复合而成的：珍珠岩35～41wt％、粉煤灰5～10wt％、硅酸铝纤维棉5～6wt％、岩棉5～6wt％、石棉绒15～17wt％、澎润土15～17wt％、聚丙烯酰胺3～4wt％、渗透剂5～6wt％、稀土添加剂0.03～0.3wt％。其优点是：耐高温、防腐、隔音、防老化、防裂性能好，导热系数低，干容量轻，最高温度为1000℃，最低温度为-30℃，特别是防火性能达到了A1级水平。

Description

稀土保温材料
一、技术领域
本发明涉及一种稀土保温材料，属于建筑材料领域，特别是保温涂料领域。
二、背景技术：
我国的保温涂料如：硅酸盐、硅酸镁等保温材料，近年来虽然有很大发展，但还是有不理想的地方，其缺陷在于：1.最高保温温度大多在800℃以内，长期在高温下使用，涂料会碳化，影响保温寿命及效果；2.硅酸盐、硅酸镁保温涂料干容量重、导热系数大。近年来，建筑中都是节能保温房，在建筑节能方面，我国还属于探索当中，虽然聚苯板是建筑节能的主要产品，但是聚苯板也有它的缺陷和不足之处：1.聚苯板在建筑上，内墙内保温外墙外保温的综合价格太高；2.聚苯板导热系数高、施工复杂、工期长。
三、发明内容：
本发明的本发明的目的是为了克服上述保温材料的不足，提供一种耐高温防火、防腐、隔音、防老化、防裂性能好，导热系数低，干容量轻，最高温度为100℃，最低温度为-30℃的稀土保温材料。
本发明的稀土保温材料是由下述组分的原料复合而成的：珍珠岩35～41wt％、粉煤灰5～10wt％、硅酸铝纤维棉5～6wt％、岩棉5～6wt％、石棉绒15～17wt％、澎润土15～17wt％、聚丙烯酰胺3～4wt％、渗透剂5～6wt％、稀土添加剂0.03～0.3wt％。
所述渗透剂为琥珀酸酯磺酸钠水溶剂；
所述稀土添加剂为硝酸镧。
制做本发明的稀土保温材料的工艺流程是：硅酸铝纤维棉+渗透剂+水→浸泡→+岩棉浸泡→搅拌+石棉绒→搅拌+澎润土→搅拌+聚丙烯酰胺→+稀土舔加剂→搅拌→+膨胀珍珠岩+粉煤灰→搅拌→取样检验。
本发明的用料采用用途相同、性质不同的材料使其不足之处得以互补，使材料聚众多优点为一体，其主要优点是：耐高温、防腐、隔音、防老化、防裂性能好，导热系数低，干容量轻，最高温度为1000℃，最低温度为-30℃，特别是防火性能达到了A1级水平。
四、具体实施方式：
实施例1：
先将5wt％硅酸铝纤维棉放入池内，取出5.7wt％渗透剂和水搅拌均匀后一起倒入池内(水漫过硅酸铝纤维棉为好)，渗透剂采用河间市泰丰石棉化工有限公司生产的OT渗透剂，其组成为琥珀酸酯磺酸钠，PH值6.0～7.5(水溶剂1％)，活性物含量≥75％，表面张力25～27NZ cm-6。待24小时后，再加入岩棉5wt％40～50℃浸泡4小时，将浸泡好的物质放入搅拌机内，加入适量的水进行搅拌，10～15分钟后加入15wt％的石棉绒，搅拌10～15分钟后加入15wt％的澎润土，搅拌8～12分钟后加入3wt％的聚丙烯酰胺，搅拌8～12分钟后加入0.3wt％的稀土添加剂硝酸镧(La(NO3)3·6H2O)，搅拌12分钟后加入41wt％的珍珠岩和10wt％粉煤灰，搅拌均匀后取样检验合格后出厂。
实施例2：
先将6wt％硅酸铝纤维棉放入池内，取出5.07wt％渗透剂和水搅拌均匀后一起倒入池内(水漫过硅酸铝纤维棉为好)，渗透剂同实施例1。待24小时后，再加入6wt％岩棉40～50℃浸泡4小时，将浸泡好的物质放入搅拌机内，加入适量的水进行搅拌，10～15分钟后加入17wt％的石棉绒，搅拌10～15分钟后加入16.9wt％的澎润土，搅拌8～12分钟后加入4wt％的聚丙烯酰胺，搅拌8～12分钟后加入0.03wt％的稀土添加剂硝酸镧(La(NO3)3·6H2O)，搅拌12分钟后加入40wt％的珍珠岩和5wt％粉煤灰，搅拌均匀后取样检验合格后出厂。

Claims (3)

1.一种稀土保温材料，其特征是：稀土保温材料是由下述组分的原料复合而成的：珍珠岩35～41wt％、粉煤灰5～10wt％、硅酸铝纤维棉5～6wt％、岩棉5～6wt％、石棉绒15～17wt％、澎润土15～17wt％、聚丙烯酰胺3～4wt％、渗透剂5～6wt％、稀土添加剂0.03～0.3wt％。
2.根据权利要求1所述的稀土保温材料，其特征是：所述渗透剂为琥珀酸酯磺酸钠水溶剂。
3.根据权利要求1所述的稀土保温材料，其特征是：所述稀土添加剂为硝酸镧。
CN2010106214468A 2010-12-22 2010-12-22 稀土保温材料 Pending CN102229480A (zh)