Summary of the invention
The objective of the invention is to overcome deficiency of the prior art, a kind of lip pomade that also can " diaphoresis " in the time of 50 ± 1 ℃ is provided.
Second purpose of the present invention provides a kind of method for preparing of lip pomade.
Technical scheme of the present invention is summarized as follows:
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: wax 5-20%, octyl palmitate 6.5-10%, skin moistening oils and fats 13.5-25%, hydrophobic silica 2-12%, silicon are handled mica powder 9-10%, pearl essence 15-20%, vitamin E .1-5%, titanium dioxide 8-10%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 4-5 ℃ of mastic titre,, said silica gel mould is placed 0-2 ℃ environment cooling rapidly down being heated in 75 ℃-105 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Said wax is that paraffin, Cera Flava, microwax, Brazil wax, candelilla wax, Tissuemat E, Japan wax and Ka Naba wax are at least a.
Said skin moistening oils and fats is at least four kinds of squalane, glycerol three monooctyl esters, glycerol ester in three last of the ten Heavenly stems, glycerol three iso stearyl esters, glycerol three adipate esters, isopropyl palmitate, three benzenetricarboxylic acids, 13 esters, isononyl isononanoate, isostearic acid isopropyl ester, Oleum Ricini, octyldodecanol and oleyl alcohol.
The lip pomade of above-mentioned method for preparing preparation.
Advantage of the present invention is;
Lip pomade of the present invention has heat-stable characteristics; When temperature is elevated to 45 ± 1 ℃, even can " not perspire " during to 50 ± 1 ℃, solve the difficult problem of high temperature lip pomade " perspiration "; Make the skin moistening composition be locked in the structure of forming by wax, ester etc. the better protection lips firmly.Guarantee the quality of finished product, also be fit to the use of high temperature area consumer simultaneously.
The specific embodiment
Following embodiment can make those skilled in the art understand the present invention better, but does not limit the present invention in any way.
Below in conjunction with specific embodiment the present invention is further described.
Embodiment 1
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: wax 10% (wherein: Brazil wax 2%, Cera Flava 6%, Japan wax 1%, Tissuemat E 1%), octyl palmitate 10%, skin moistening oils and fats 18% (wherein: glycerol three monooctyl esters 3%, squalane 5%, isopropyl palmitate 4%, octyldodecanol 6%), hydrophobic silica 12%, silicon are handled mica powder 10%, pearl essence 20%, vitamin E 5%, titanium dioxide 10%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 5 ℃ of mastic titres,, said silica gel mould is placed 1 ℃ environment cooling rapidly down being heated in 85 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Embodiment 2
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: Brazil wax 5%, octyl palmitate 10%, skin moistening oils and fats 23% (wherein: three benzenetricarboxylic acids, 13 esters 9.5%, squalane 3%, isopropyl palmitate 4%, octyldodecanol 3.5%, Oleum Ricini 3%), hydrophobic silica 12%, silicon are handled mica powder 10%, pearl essence 20%, vitamin E 5%, titanium dioxide 10%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 4 ℃ of mastic titres,, said silica gel mould is placed 2 ℃ environment cooling rapidly down being heated in 75 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Embodiment 3
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: wax 20% (wherein: Brazil wax 3%, Ka Naba wax 4%, microwax 4%, Cera Flava 9%), octyl palmitate 10%, skin moistening oils and fats 25% (wherein: glycerol ester in three last of the ten Heavenly stems 7%, glycerol three iso stearyl esters 6%, glycerol three adipate esters 7%, isononyl isononanoate 5%), hydrophobic silica 2%, silicon are handled mica powder 10%, pearl essence 15%, vitamin E 5%, titanium dioxide 8%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 5 ℃ of mastic titres,, said silica gel mould is placed 0 ℃ environment cooling rapidly down being heated in 105 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Embodiment 4
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: wax 15% (wherein: candelilla wax 4%, paraffin 3%, Tissuemat E 2%, Cera Flava 6%), octyl palmitate 6.5%, skin moistening oils and fats 23.5% (wherein: three benzenetricarboxylic acids, 13 esters 4%, isostearic acid isopropyl ester 6.5%, isopropyl palmitate 7%, oleyl alcohol 6%), hydrophobic silica 10%, silicon are handled mica powder 9%, pearl essence 20%, vitamin e1 %, titanium dioxide 10%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 5 ℃ of mastic titres,, said silica gel mould is placed 2 ℃ environment cooling rapidly down being heated in 80 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Embodiment 5
A kind of method for preparing of lip pomade comprises the steps:
(1) take by weighing following raw material by mass percentage: wax 14.5% (wherein: candelilla wax 4%, paraffin 3%, Tissuemat E 2.5%, Cera Flava 5%), octyl palmitate 10%, skin moistening oils and fats 13.5% (wherein: three benzenetricarboxylic acids, 13 esters 1%, isostearic acid isopropyl ester 2.5%, isopropyl palmitate 5%, oleyl alcohol 5%), hydrophobic silica 12%, silicon are handled mica powder 10%, pearl essence 20%, vitamin E 5%, titanium dioxide 10%, pigment 3% and essence 2%;
(2) said pigment and titanium dioxide mixing are stirred, add octyl palmitate, mix homogeneously, subsequent use;
(3) said wax, skin moistening oils and fats, vitamin E are mixed, be heated to 85 ℃;
(4) material of step (2) acquisition and the material of step (3) acquisition are stirred, add said hydrophobic silica, silicon processing mica powder and pearl essence mix homogeneously;
(5) be cooled to 45 ℃ after, add essence;
(6) continue to be cooled to 40 ℃, discharging gets mastic;
(7) silica gel mould is preheated to is higher than 4 ℃ of mastic titres,, said silica gel mould is placed 0 ℃ environment cooling rapidly down being heated in 90 ℃ mastic fill to the said silica gel mould; Treating that the mastic temperature drops to is lower than dropping point; After the mastic molding, the vacuum demoulding, packing.
Test:
Each 10 of the lip pomades of embodiment 1-embodiment 5 preparations are placed within 24 hours at 50 ℃ respectively, " diaphoresis " phenomenon do not occurred.And this heat resistant test extended to 3 months, " diaphoresis " phenomenon also appears.
Every kind each 10 of the lip pomades of two kinds of certain commercially available domestic brands, wherein a kind of 50 ℃ of placements 24 hours, wherein 100% " diaphoresis " phenomenon occurs.Another kind of placement 24 hours, 50 ℃ of 100% appearance " diaphoresis " phenomenon.