CN102226049A - 可打印光盘用紫外光固化防水油墨 - Google Patents

可打印光盘用紫外光固化防水油墨 Download PDF

Info

Publication number
CN102226049A
CN102226049A CN2011101407134A CN201110140713A CN102226049A CN 102226049 A CN102226049 A CN 102226049A CN 2011101407134 A CN2011101407134 A CN 2011101407134A CN 201110140713 A CN201110140713 A CN 201110140713A CN 102226049 A CN102226049 A CN 102226049A
Authority
CN
China
Prior art keywords
acrylate
ultraviolet light
resin
hydrophobic
light polymerization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101407134A
Other languages
English (en)
Inventor
陈清煌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONG JOU CHEMICAL INDUSTRIAL (KUNSHAN) Co Ltd
Original Assignee
TONG JOU CHEMICAL INDUSTRIAL (KUNSHAN) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONG JOU CHEMICAL INDUSTRIAL (KUNSHAN) Co Ltd filed Critical TONG JOU CHEMICAL INDUSTRIAL (KUNSHAN) Co Ltd
Priority to CN2011101407134A priority Critical patent/CN102226049A/zh
Publication of CN102226049A publication Critical patent/CN102226049A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种紫外光固化防水油墨，以所述油墨的总重量为基准，其由如下组分组成：水溶性单体13％～16％；水溶性树脂15％～21％；疏水性单体21％～25％；疏水性树脂7％～12％；分散剂1％～3％；光引发剂5％～10％；添加剂22％～32％。本发明配方的亲水性和疏水性达成平衡，其中亲水性单体和亲水性树脂在经过UV交联固化后形成可吸收墨水的涂层；而同时疏水性单体和疏水性树脂经固化后形成疏水涂层，从而使得油墨具有防水功能。

Description

可打印光盘用紫外光固化防水油墨
技术领域
本发明涉及一种油墨组合物，特别是一种应用于可打印光盘的印刷油墨。
背景技术
可打印油墨就是用丝印方式在光盘面和其他的塑料面上印一层可以吸墨的涂层，涂层具有吸水性，这样就可以用打印机打印漂亮的盘面了。
现有技术中的光盘可打印油墨，主要是在水性UV光油中加入具有很好吸水性的白炭黑。该可打印油墨虽然具有较好的打印效果，但是却不防水。如此，在光盘的光盘面打印出的个性图案或纪念照片颜色在光盘面接触水滴或在受到饮料杯水不慎打翻的泼溅时，容易发生褪色、模糊。
发明内容
本发明所要解决的技术问题是为了克服现有技术的不足，提供一种可打印光盘用紫外光固化防水油墨。
为解决以上技术问题，本发明采取如下技术方案：
一种紫外光固化防水油墨，以所述油墨的总重量为基准，其由如下组分组成：水溶性单体13％～16％；水溶性树脂15％～21％；疏水性单体21％～25％；疏水性树脂7％～12％；分散剂1％～3％；光引发剂5％～10％；添加剂22％～32％。
根据本发明的一个优选实施方案中，所述水溶性单体为丙烯酸酯类单体，所述水溶性树脂为水性丙烯酸树脂。其中，水溶性单体可以为选自2(2-乙氧基乙氧基)乙基丙烯酸酯、乙氧化甲基丙烯酸羟乙酯、金属盐二丙烯酸酯、金属盐二甲基丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯中的一种或多种。水溶性树脂可以为选自甲氧基聚乙二醇单甲基丙烯酸酯、聚乙二醇二丙烯酸酯、聚乙二醇二甲基丙烯酸酯中的一种或多种。优选地，所述水溶性树脂中聚乙二醇的数均分子量在400～1000之间。
根据本发明的另一优选方案：所述疏水性单体为丙烯酸酯类单体，所述疏水性树脂为疏水丙烯酸树脂。所述的疏水性单体例如可以为辛基丙烯酸酯、癸基丙烯酸酯、丙烯酸十八烷基酯、乙氧化壬基苯酚丙烯酸酯、烷氧化壬基苯酚丙烯酸酯、丙烯酸十八烷基酯、丙烯酸月桂酯、2-苯氧基乙基丙烯酸酯、丙烯酸异癸酯、丙烯酸辛/癸酯、丙烯酸十三烷基酯、丙烯酸异冰片酯、甲基丙烯酸异癸酯、甲基丙烯酸月桂酯、甲基丙烯酸十八烷基酯、甲基丙烯酸异冰片酯；所述疏水性树脂可以为乙氧化双酚A二丙烯酸酯、1，6-己二醇二丙烯酸酯、乙氧化双酚A二丙烯酸酯、二丙二醇二丙烯酸酯、1，6-己二醇二甲基丙烯酸酯、三羟甲基丙烷三丙烯酸酯、三(2-羟乙基)异氰脲酸三丙烯酸酯、三(2-羟乙基)异氰脲酸三丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯、丙氧化丙三醇三丙烯酸酯、三羟甲基丙烷三甲基丙烯酸酯、季戊四醇四丙烯酸酯、二季戊四醇五/六丙烯酸酯、二季戊四醇五/六丙烯酸酯中的一种或多种。
根据本发明，所述的分散剂优选为BYK系列分散剂，例如BYK分散剂ANTI-U、BYK-W966、BYK-103、BYK-110、BYK-161、BYK-162、BYK-163、BYK-164、BYK-180、BYK-190、BYK-P104S等。
根据本发明的一个具体方面，所述添加剂为无机填充料，其可以选自二氧化硅、滑石粉、高岭土、碳酸钙、碳酸镁、硫化锌、硫酸钡、云母粉、硅藻土以及二氧化钛中的一种或多种。所述光引发剂可以为选自
Figure BSA00000505657300021
Figure BSA00000505657300022
819；369；
Figure BSA00000505657300024
2959；1173；
Figure BSA00000505657300026
184；
Figure BSA00000505657300027
Figure BSA00000505657300028
TPO
Figure BSA00000505657300029
784以及
Figure BSA000005056573000210
250中的一种。
由于采取以上技术方案，本发明与现有技术相比具有如下优点：
本发明配方的亲水性和疏水性达成平衡，其中亲水性单体和亲水性树脂在经过UV交联固化后形成可吸收墨水的涂层；而同时疏水性单体和疏水性树脂经固化后形成疏水涂层，从而使得油墨具有防水功能。本发明油墨适用做光盘可打印油墨。
具体实施方式
通常，油墨的耐水性与墨水吸墨性很难取得平衡。水溶性越好，吸墨越佳则耐水性越差；反之，如果水溶性不好，则吸墨性差但耐水性较好。此发明就是在平衡亲水性及疏水性上的重大发现。下面结合具体的实施例，对本发明进行进一步详细的说明。
实施例1
按照本实施例的防水油墨，由如下重量配比的组分搅拌均匀后，经三辊筒研磨分散得到：(5)乙氧化甲基丙烯酸羟乙酯14％、聚乙二醇二丙烯酸酯18％(其中聚乙二醇数均分子量为400)、乙氧化壬基苯酚丙烯酸酯23％、季戊四醇四丙烯酸酯10％、分散剂BYK-184 2％、光引发剂
Figure BSA00000505657300031
8198％以及碳酸钙25％。
实施例2
按照本实施例的防水油墨，由如下重量配比的组分搅拌均匀后，经三辊筒研磨分散得到：乙氧化三羟甲基丙烷三丙烯酸酯15％、聚乙二醇二丙烯酸酯15％(其中聚乙二醇数均分子量为800)、丙烯酸十八烷基酯25％、三(2-羟乙基)异氰脲酸三丙烯酸酯12％、分散剂BYK-110 2％、光引发剂
Figure BSA00000505657300032
Figure BSA00000505657300033
1173 7％以及滑石粉24％。
实施例3
按照本实施例的防水油墨，由如下重量配比的组分搅拌均匀后，经三辊筒研磨分散得到：2(2-乙氧基乙氧基)乙基丙烯酸酯15％、甲氧基聚乙二醇单甲基丙烯酸酯(其中聚乙二醇数均分子量为400)15％、丙烯酸十八烷基酯20％、三(2-羟乙基)异氰脲酸三丙烯酸酯12％、分散剂BYK-110 3％、光引发剂
Figure BSA00000505657300034
Figure BSA00000505657300035
1173 5％以及滑石粉30％。
对比例1
按照本对比例的防水油墨，由如下重量配比的组分搅拌均匀后，经三辊筒研磨分散得到：2(2-乙氧基乙氧基)乙基丙烯酸酯30％、甲氧基聚乙二醇单甲基丙烯酸酯(其中聚乙二醇数均分子量为400)30％、丙烯酸十八烷基酯5％、三(2-羟乙基)异氰脲酸三丙烯酸酯10％、分散剂BYK-110 0.5％、光引发剂
Figure BSA00000505657300036
1173 4.5％以及滑石粉20％。
对比例2
按照本对比例的防水油墨，由如下重量配比的组分搅拌均匀后，经三辊筒研磨分散得到：2(2-乙氧基乙氧基)乙基丙烯酸酯10％、甲氧基聚乙二醇单甲基丙烯酸酯(其中聚乙二醇数均分子量为400)10％、丙烯酸十八烷基酯20％、三(2-羟乙基)异氰脲酸三丙烯酸酯25％、分散剂BYK-110 0.5％、光引发剂
Figure BSA00000505657300037
1173 4.5％以及滑石粉20％。
对实施例1～3以及对比例1～2的防水油墨的吸墨性(CANON IP4300喷印)和耐水性进行了测试，实施例1～3的吸墨性能和耐水性能均表现良好；对比例1的吸墨性虽然较好，但是防水性能差；对比例2则不仅吸墨性较差，而且耐水性也不好。
综上，本发明在充分了解墨水的组成的基础之上，通过将亲水性预聚物与疏水性预聚合有机组合，一方面，利用亲水性预聚物固化后的高交联性将已吸附的墨水的不挥发成分牢牢的抓住从而使得油墨具有优良的吸墨性能；另一方面，利用疏水性聚合物来赋予油墨优良的防水性能。因而，使用本发明油墨进行光盘打印出的个性图案或纪念照片颜色在光盘面接触水滴或在受到饮料杯水不慎打翻的泼溅时，也不会发生褪色、模糊。
以上对本发明做了详尽的描述，其目的在于让熟悉此领域技术的人士能够了解本发明的内容并加以实施，并不能以此限制本发明的保护范围，凡根据本发明的精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围内。

Claims (9)

1.一种紫外光固化防水油墨，其特征在于：以所述油墨的总重量为基准，其由如下组分组成：水溶性单体13％～16％；水溶性树脂15％～21％；疏水性单体21％～25％；疏水性树脂7％～12％；分散剂1％～3％；光引发剂5％～10％；添加剂22％～32％。
2.根据权利要求1所述的紫外光固化防水油墨，其特征在于：所述水溶性单体为丙烯酸酯类单体，所述水溶性树脂为水性丙烯酸树脂。
3.根据权利要求2所述的紫外光固化防水油墨，其特征在于：所述水溶性单体为2(2-乙氧基乙氧基)乙基丙烯酸酯、乙氧化甲基丙烯酸羟乙酯、金属盐二丙烯酸酯、金属盐二甲基丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯中的一种或多种的混合物。
4.根据权利要求2所述的紫外光固化防水油墨，其特征在于：所述水溶性树脂为甲氧基聚乙二醇单甲基丙烯酸酯、聚乙二醇二丙烯酸酯、聚乙二醇二甲基丙烯酸酯中的一种或多种，其中树脂中聚乙二醇的数均分子量在400～1000之间。
5.根据权利要求1所述的紫外光固化防水油墨，其特征在于：所述疏水性单体为丙烯酸酯类单体，所述疏水性树脂为疏水丙烯酸树脂。
6.根据权利要求5所述的紫外光固化防水油墨，其特征在于：所述的疏水性单体为辛基丙烯酸酯、癸基丙烯酸酯、丙烯酸十八烷基酯、乙氧化壬基苯酚丙烯酸酯、烷氧化壬基苯酚丙烯酸酯、丙烯酸月桂酯、2-苯氧基乙基丙烯酸酯、丙烯酸异癸酯、丙烯酸辛/癸酯、丙烯酸十三烷基酯、丙烯酸异冰片酯、甲基丙烯酸异癸酯、甲基丙烯酸月桂酯、甲基丙烯酸十八烷基酯、甲基丙烯酸异冰片酯中的一种或多种的混合物。
7.根据权利要求5所述的紫外光固化防水油墨，其特征在于：所述的疏水性树脂为乙氧化双酚A二丙烯酸酯、1，6-己二醇二丙烯酸酯、乙氧化双酚A二丙烯酸酯、二丙二醇二丙烯酸酯、1，6-己二醇二甲基丙烯酸酯、三羟甲基丙烷三丙烯酸酯、三(2-羟乙基)异氰脲酸三丙烯酸酯、三(2-羟乙基)异氰脲酸三丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯、丙氧化丙三醇三丙烯酸酯、三羟甲基丙烷三甲基丙烯酸酯、季戊四醇四丙烯酸酯、二季戊四醇五/六丙烯酸酯以及二季戊四醇五/六丙烯酸酯中的一种或多种的混合物。
8.根据权利要求1至7中任一项所述的紫外光固化防水油墨，其特征在于：所述的分散剂为BYK系列分散剂。
9.根据权利要求1所述的紫外光固化防水油墨，其特征在于：所述的添加剂为无机填充料，其为选自二氧化硅、滑石粉、高岭土、碳酸钙、碳酸镁、硫化锌、硫酸钡、云母粉、硅藻土以及二氧化钛中的一种或多种。
CN2011101407134A 2011-05-27 2011-05-27 可打印光盘用紫外光固化防水油墨 Pending CN102226049A (zh)