CN102219444A - 轻集料混凝土地面砖的配制方法 - Google Patents
轻集料混凝土地面砖的配制方法 Download PDFInfo
- Publication number
- CN102219444A CN102219444A CN 201110062235 CN201110062235A CN102219444A CN 102219444 A CN102219444 A CN 102219444A CN 201110062235 CN201110062235 CN 201110062235 CN 201110062235 A CN201110062235 A CN 201110062235A CN 102219444 A CN102219444 A CN 102219444A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- light aggregate
- cement
- floor tile
- concrete floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及节能环保领域中的一种利用粉煤灰和炉渣为轻集料生产轻集料混凝土地面砖的配制方法。技术方案:每一立方混凝土按2400公斤计算,其中包括以下原料及重量份:水泥360-370公斤,砂700-750公斤,石子1160-1170公斤,粉煤灰140-150公斤,水灰比0.25-0.30。所述的粉煤灰为II级灰,水泥为325等级。发明益果:本配方经高温养护28天,强度预计为10MPa,经试验证实3天强度平均可达6.8MPa,替代水泥后,在强度不变的情况下,成本大大降低,取得了较好的经济效益。
Description
技术领域
本发明涉及节能环保领域中的一种利用粉煤灰作轻集料生产轻集料混凝土地面砖的配制方法。
背景技术
粉煤灰是工业企业和热电厂排放的废料,长期排放,不仅占用大量土地,还严重污染环境,在此情况下,国家及各省市大量提倡对粉煤灰进行二次再利用,申请人从事地面砖生产多年,凭着多年的实践经验,利用粉煤灰生产轻集料混凝土地面砖,取得了较好的经济和社会效益。
发明内容
本发明的目的就是根据多年的实践经验,提供一种粉煤灰利用率高且地砖强度高的轻集料混凝土地面砖的配制方法。
技术方案:每一立方混凝土按2400公斤计算,其中包括以下原料及重量份:水泥360-370公斤,砂700-750公斤,石子1160-1170公斤,粉煤灰140-150公斤,水灰比0.25-0.30。
所述的粉煤灰为II级灰,水泥为325等级。
发明益果
本配方经高温养护28天,强度预计为10MPa,经试验证实3天强度平均可达6.8MPa,替代水泥后,在强度不变的情况下,成本大大降低,取得了较好的经济效益。
具体实施方式;
实施例1:每一立方混凝土按2400公斤计算,其中包括以下原料及重量份:水泥364公斤,砂727公斤,石子1164公斤,粉煤灰145公斤,水灰比0.28。经搅拌机搅均装模后,预养24小时后拆模,在湿度75±5%,温度12±5度的情况下养护,3天后测抗压强度不均值为6.85MPa。
Claims (2)
1.一种轻集料混凝土地面砖的配制方法,其特征在于:每一立方混凝土按2400公斤计算,其中包括以下原料及重量份:水泥360-370公斤,砂700-750公斤,石子1160-1170公斤,粉煤灰140-150公斤,水灰比0.25-0.30。
2.根据权利要求1所述的轻集料混凝土地面砖的配制方法,其特征在于:所述的粉煤灰为II级灰,水泥为325等级。