CN102212716A - 一种低成本的α+β型钛合金 - Google Patents
一种低成本的α+β型钛合金 Download PDFInfo
- Publication number
- CN102212716A CN102212716A CN 201110117624 CN201110117624A CN102212716A CN 102212716 A CN102212716 A CN 102212716A CN 201110117624 CN201110117624 CN 201110117624 CN 201110117624 A CN201110117624 A CN 201110117624A CN 102212716 A CN102212716 A CN 102212716A
- Authority
- CN
- China
- Prior art keywords
- percent
- alloy
- beta
- alpha
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于合金技术领域,涉及一种低成本的α+β型钛合金。其特征在于:该合金成分的重量百分比组成为:Al:3%~3.7%;Mo:2.5%~4%;Zr:2%~4%;Si:0%~0.35%;Cr:2.3%~3.3%或Fe:0.4%~1.2%;余量为Ti;合金中的杂质元素总量≤0.4%,且间隙杂质元素C≤0.04%;O≤0.15%;N≤0.04%;H≤0.015%。本发明α+β型钛合金用价格便宜的其他金属代替了昂贵的钒元素,从而降低了合金的生产成本。由于综合力学性能与Ti-6Al-4V合金相当,因而本发明α+β型钛合金具有更高的性价比,工程应用前景广阔。
Description
技术领域
本发明属于合金技术领域,涉及一种低成本的α+β型钛合金。
背景技术
钛及钛合金因具有高比强度、耐蚀性好等优点而被广泛应用于航空、航天、兵器、汽车等工业领域。到目前为止,国内外研制成功的钛合金已经多达几十种,其中应用最广泛的是Ti-6Al-4V合金。在航空、汽车、能源、舰船、化工、医疗器械及体育用品等所有钛合金应用领域中,Ti-6Al-4V合金的比重占到50%以上。由于Ti-6Al-4V合金中含有4%(重量百分比,下同)的价格昂贵的钒元素,导致Ti-6Al-4V合金的生产成本较高,因而限制了它在工业领域,特别是在民用领域的应用范围。Ti-6Al-4V合金不仅加工成本较高,而且难以加工形状很复杂的零件,因而限制了其在更大范围的应用。
发明内容
本发明的目的是:提出一种力学性能与Ti-6Al-4V合金相当,但具有更高性价比的α+β型钛合金。
本发明的技术方案是:一种低成本的α+β型钛合金,其特征在于:该合金成分的重量百分比组成为:Al:3%~3.7%;Mo:2.5%~4%;Zr:2%~4%;Si:0%~0.35%;Cr:2.3%~3.3%或Fe:0.4%~1.2%;余量为Ti;合金中的杂质元素总量≤0.4%,且间隙杂质元素C≤0.04%;O≤0.15%;N≤0.04%;H≤0.015%。
本发明的优点是:与Ti-6Al-4V合金相比,本发明α+β型钛合金用价格便宜的其他金属元素代替了昂贵的钒元素,从而降低了合金的生产成本。由于综合力学性能与Ti-6Al-4V合金相当,因而本发明α+β型钛合金具有更高的性价比,工程应用前景广阔。
具体实施方式
下面对本发明做进一步详细说明,种低成本的α+β型钛合金,其特征在于:该合金成分的重量百分比组成为:Al:3%~3.7%;Mo:2.5%~4%;Zr:2%~4%;Si:0%~0.35%;Cr:2.3%~3.3%或Fe:0.4%~1.2%;余量为Ti;合金中的杂质元素总量≤0.4%,且间隙杂质元素C≤0.04%;O≤0.15%;N≤0.04%;H≤0.015%。
本发明钛合金的制备过程是:按照上述成分范围的要求配比钛合金,原材料可以选用纯Al、Al-Mo中间合金、Ti-Mo中间合金、Ti-Fe中间合金、纯Cr、海绵锆、海绵钛等。按配比成分混料后压制成电极,在真空自耗电弧炉中熔炼两次或三次获得合金铸锭。铸锭扒皮、切去冒口和尾端后,经过开坯锻造、中间多火次变形、最终锻造或轧制成棒材、板材、锻件等本发明钛合金的各类半成品,经过合适热处理后的这些合金半成品可以用于制造工程零部件。开坯锻造加热温度为1050℃~1150℃,反复墩拔的加热温度为合金β转变温度以下30℃~80℃,即Tβ-30℃~80℃;最终成形温度可以根据需要的组织形态进行选择。
实施例1:
按名义成分Ti-3.5Al-2.5Mo-2Zr-2.3Cr(重量百分比,%)配制合金料,原材料使用Al-55%Mo中间合金、0级海绵钛、火器海绵锆、纯Al和纯Cr。混料后压制成电极,用真空自耗电弧炉熔炼三次获得合金铸锭。铸锭扒皮、切去冒口和尾端后,在1150℃开坯锻造,并在Tβ-30℃~80℃下进行多火次墩拔以细化组织,最后锻成Ф55mm的棒材。棒材经650℃/1h/AC热处理后获得的力学性能典型值为:屈服强度≥870MPa,断裂强度≥950Mpa,延伸率≥10%。
实施例2:
按名义成分Ti-3Al-2.5Mo-2Zr-2.8Cr(重量百分比,%)配制合金料,原材料使用Ti-32%Mo中间合金、0级海绵钛、火器海绵锆、纯Al和Ti-Fe中间合金。混料后压制成电极,用真空自耗电弧炉熔炼三次获得合金铸锭。铸锭扒皮、切去冒口和尾端后,在1150℃开坯锻造,并在Tβ-30℃~80℃下进行多火次墩拔以细化组织,最后轧制成Ф22mm的棒材。棒材经860℃/1h/WQ+650℃/2h/AC热处理后获得的力学性能典型值为:屈服强度≥910MPa,断裂强度≥980Mpa,延伸率≥13%。
实施例3~实施例16的合金名义成分参见表1。
表1实施例3~实施例16的合金名义成分
Al:3%~3.7%;Mo:2.5%~4%;Zr:2%~4%;Si:0%~0.35%;Cr:2.3%~3.3%或Fe:0.4%~1.2%
上述实施例合金制备过程与实施例1和2类似,它们被锻成Ф45mm的棒材,经Tβ-40℃/1h/WQ+Tβ-300℃/2h/AC热处理后获得的力学性能典型值为:屈服强度≥870MPa,断裂强度≥950MPa,延伸率≥6%。
Claims (1)
1.一种低成本的α+β型钛合金,其特征在于:该合金成分的重量百分比组成为:Al:3%~3.7%;Mo:2.5%~4%;Zr:2%~4%;Si:0%~0.35%;Cr:2.3%~3.3%或Fe:0.4%~1.2%;余量为Ti;合金中的杂质元素总量≤0.4%,且间隙杂质元素C≤0.04%;0≤0.15%;N≤0.04%;H≤0.015%。