CN102198502B - 高压开关用铸铝壳体的模具、制备铸铝壳体的方法 - Google Patents
高压开关用铸铝壳体的模具、制备铸铝壳体的方法 Download PDFInfo
- Publication number
- CN102198502B CN102198502B CN 201110128057 CN201110128057A CN102198502B CN 102198502 B CN102198502 B CN 102198502B CN 201110128057 CN201110128057 CN 201110128057 CN 201110128057 A CN201110128057 A CN 201110128057A CN 102198502 B CN102198502 B CN 102198502B
- Authority
- CN
- China
- Prior art keywords
- core
- stage
- die
- cast aluminum
- relative pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
高压开关用铸铝壳体的模具、制备铸铝壳体的方法，包括金属型模具和砂芯，其特征在于：底板上设有与坩埚升液管相连的导入口，与导入口相连的是砂芯底部的直浇道，直浇道上设有内浇道；砂芯外部包裹金属型模具，金属型模具的顶部设有冒口芯，冒口芯内侧与砂芯上部外侧组成冒口，砂芯侧面纵向安装有镶块。方法包括以下步骤：铝合金熔炼、装配模具、低压铸造、取出铸件。通过本发明所述技术方案的实施，方法操作简单，便于控制，产品表面质量高，工艺出品率高，气密性检查合格率高，生产成本低。
Description
技术领域
本发明涉及金属型成型方法，具体指一种制备高压开关用铸铝壳体的模具及制备铸铝壳体的方法。
背景技术
高压开关铸铝壳体，其内部要求充入SF6气体，年泄漏率小于0.5%，铸件水压破裂性试验强度值要高于3.75MPa。近年来多采用树脂砂型重力铸造，工艺出品率只有50 %，而且铸件针孔度、圆跳度和平面度等质量指标均超标，局部晶粒粗大，气密性检查一次性合格率较低；其次是生产效率低，生产成本高。因此，利用低压铸造金属型工艺取代砂型铸造，提高生产率和合格率。这就是本发明的宗旨。
发明内容
本发明提供一种制备高压开关铸铝壳体的模具及方法，其目的是提高工艺出品率、致密度、力学性能和生产率。
为实现上述目的，本发明采用如下技术方案：
高压开关用铸铝壳体的模具，包括金属型模具和砂芯，其特征在于：底板上设有与坩埚升液管相连的导入口，与导入口相连的是砂芯底部的直浇道，直浇道上设有内浇道；砂芯外部包裹金属型模具，金属型模具的顶部设有冒口芯，冒口芯内侧与砂芯上部外侧组成冒口，砂芯侧面纵向安装有镶块。
直浇道上设有4个均匀分布的内浇道。
砂芯侧面纵向阶梯分布有3个镶块。
铸铝壳体的制备方法，其特征在于：所述方法包括以下步骤：
（1）铝合金熔炼：先进行配料，然后进行熔炼，熔炼后的溶液经过除渣除气后，进行变质处理，得铝合金溶液备用；
（2）装配模具；
（3）低压铸造：将步骤（1）所得铝合金溶液通过导入口注入直浇道，铝合金熔液的注入压力逐步上升到0.112Mpa，然后降至0 Mpa，过程如下：
①升液阶段：升液阶段在前20秒内，相对压力从0MPa上升到0.04Mpa；
②充型阶段：充型阶段在第20-55秒内，相对压力从0.04MPa上升到0.08Mpa；
③结壳阶段：结壳阶段在第55-60秒内，相对压力从0.08MPa上升到0.085Mpa；
④增压阶段：增压阶段在第60-75秒内，相对压力从0.085MPa上升到0.112Mpa；
⑤保压结晶阶段：保压结晶阶段在第75-300秒内，相对压力保持在0.112Mpa；
⑥卸压阶段：卸压阶段在第300秒至400秒内，相对压力从0.112MPa降到0MPa。
（4）取出铸件。
通过本发明所述技术方案的实施，方法操作简单，便于控制，产品表面质量高，工艺出品率高，气密性检查合格率高，生产成本低。
附图说明：
图1为本发明生产工艺流程图；
图2为图1方法中模具主视剖面结构示意图；
图3为图2中模具左视剖面结构示意图；
图4为图1方法中操作步骤压力趋线图；
附图标记说明：
1.底板、2.砂芯、3.金属型模具、4.冒口芯、5.冒口、6.内浇道、7.直浇道、8.导入口、9.镶块。
具体实施方式：
下面结合附图对本发明进行详细说明。
图2为模具主视剖面结构示意图，图3为图2中模具左视剖面结构示意图，如图所示，底板1上设有与坩埚升液管相连的导入口8，与导入口8相连的是砂芯2底部的直浇道7，直浇道7上设有4个均匀分布的内浇道6；砂芯2外部包裹金属型模具3，金属型模具3的顶部设有冒口芯4，冒口芯4内侧与砂芯2上部外侧组成冒口5，砂芯2侧面纵向阶梯分布有3个镶块9。
图1为本发明生产工艺流程图，如图所示，包括以下步骤：
（1）铝合金熔炼：先进行配料，然后进行熔炼，熔炼后的溶液经过除渣除气后，进行变质处理，得铝合金溶液备用；
（2）装配模具；
（3）低压铸造：将步骤（1）所得铝合金溶液通过导入口8注入直浇道7，铝合金熔液的注入压力逐步上升到0.112Mpa，然后降至0 Mpa，过程如下：
①升液阶段：升液阶段在前20秒内，相对压力从0MPa上升到0.04Mpa；
②充型阶段：充型阶段在第20-55秒内，相对压力从0.04MPa上升到0.08Mpa；
③结壳阶段：结壳阶段在第55-60秒内，相对压力从0.08MPa上升到0.085Mpa；
④增压阶段：增压阶段在第60-75秒内，相对压力从0.085MPa上升到0.112Mpa；
⑤保压结晶阶段：保压结晶阶段在第75-300秒内，相对压力保持在0.112Mpa；
⑥卸压阶段：卸压阶段在第300秒至400秒内，相对压力从0.112MPa降到0MPa。
压力趋线图如图4所示。
（4）取出铸件。
Claims (1)
1.一种高压开关用铸铝壳体的制备方法，其特征在于：所述方法包括以下步骤：
（1）铝合金熔炼：先进行配料，然后进行熔炼，熔炼后的熔液经过除渣除气后，进行变质处理，得铝合金熔液备用；
（2）装配模具；
（3）低压铸造：将步骤（1）所得铝合金熔液通过导入口（8）注入直浇道（7），铝合金熔液的注入压力逐步上升到0.112Mpa，然后降至0 Mpa，过程如下：
①升液阶段：升液阶段在前20秒内，相对压力从0MPa上升到0.04Mpa；
②充型阶段：充型阶段在第20-55秒内，相对压力从0.04MPa上升到0.08Mpa；
③结壳阶段：结壳阶段在第55-60秒内，相对压力从0.08MPa上升到0.085Mpa；
④增压阶段：增压阶段在第60-75秒内，相对压力从0.085MPa上升到0.112Mpa；
⑤保压结晶阶段：保压结晶阶段在第75-300秒内，相对压力保持在0.112Mpa；
⑥卸压阶段：卸压阶段在第300秒至400秒内，相对压力从0.112MPa降到0Mpa；
（4）取出铸件；
其中，步骤（2）中所述模具包括金属型模具（3）和砂芯（2），其特征在于：底板（1）上设有与坩埚升液管相连的导入口（8），与导入口（8）相连的是砂芯（2）底部的直浇道（7），直浇道（7）上设有4个均匀分布的内浇道（6）；砂芯（2）外部包裹金属型模具（3），金属型模具（3）的顶部设有冒口芯（4），冒口芯（4）内侧与砂芯（2）上部外侧组成冒口（5），砂芯（2）侧面纵向阶梯安装有3个镶块（9）。