CN1021972C - 混凝土脱模剂及其制备工艺 - Google Patents
混凝土脱模剂及其制备工艺 Download PDFInfo
- Publication number
- CN1021972C CN1021972C CN 92100897 CN92100897A CN1021972C CN 1021972 C CN1021972 C CN 1021972C CN 92100897 CN92100897 CN 92100897 CN 92100897 A CN92100897 A CN 92100897A CN 1021972 C CN1021972 C CN 1021972C
- Authority
- CN
- China
- Prior art keywords
- oil
- water
- concrete
- release agent
- releasing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
混凝土脱模剂及其制备工艺,脱模剂是由脱模油、再生机油或废机油、食用植物油脚皂、水配制成的水性制剂。制备工艺是先将油脚皂、脱模油、机油混合加热熔融,再加水乳化为产品,制备工艺简单。本脱模剂用化工废料,再生料为原料,生产成本低,使用费用低。本剂无毒,油感强,滑性好,涂刷一次,可连续脱模2-3次,模件表面光滑、气孔少、模板沾灰少。涂层干燥后能耐水冲刷、围水浸泡。本剂特别适于在难脱模地方使用。
Description
本发明属于用于建筑材料的辅助剂类,具体地是用于混凝土浇注的脱模剂。
混凝土脱模剂是可以减少或防止混凝土与模板表面粘着的制剂。在混凝土浇注中,制品与模板相粘,不仅容易损坏制品,而且造成拆模和清模困难,劳动强度大,生产效率低。因此,脱模剂的使用在混凝土施工中至关重要。随着混凝土和模板材料品种的增加,脱模剂的品种越来越多,它们大多为脂肪酸皂类,植物油脚皂类、乳化油类,不仅成本高、售价高,如W-15脱模剂每吨售价890元,而且涂一次,只能脱模一次,易沾灰,而且脱模剂涂层不能耐水冲刷。
为了满足装配式钢筋混凝土浇注的需要和外露构件及装饰面对混凝土外表的要求,国内外已十分重视水剂脱模剂的研究,但其基本上采用化工原料配制而成,生产成本高、使用费用高,脱模效果差,涂层不耐水冲刷。
本发明的目的旨在研制一种用化工废料或再生料为主要原料制备的水剂脱模剂。脱模剂无毒,对模板的附着力强,对混凝土的粘附力小,成膜干燥快,涂层能耐水冲刷。喷涂一次,可连续脱模2-3次。设计的制备工艺简单。
本发明的目的是以下述方式实现的,混凝土脱模剂是由再生润滑油的轻油馏分(俗称脱模油)、再生机油或废机油、食用植物油脚皂、水配制而成的水性制剂,其重量配比为:
脱模油 再生机油或废机油 食用植物油脚皂 水
160 64~88 72~104 加至浓度为30%~35%
脱模剂外观:黄色或深黄色乳状液
粘度(涂-4杯)12~13秒 有效物含量30~35%
离心稳定度(分离%)3000转/分离心分离15分钟,分层≤8%。
贮存稳定性:自然存放半年~一年不破乳
涂模表干时间(分)20分钟~30分钟
混凝土脱模剂的制备工艺为:将脱模油、再生机油或废机油、油脚皂混合均匀,边加热,边搅拌,待油脚皂熔融成糊状后,于75-80℃下分次加入溶介水,使油脚皂全部溶解,再于70℃左右加入乳化水,保温乳化40分钟后得乳化液,然后降温搅拌至40℃,出料即为产品。
本发明所采用的原料为:
先选用:中性油含量70%以上(干基),脂肪酸总量50%以上,皂化价120-150的食用植物油脚按常规方法皂化制取食用植物油脚皂。
烧碱 固体碱或液体碱 工业级
脱模油 再生润滑油的轻油馏分
再生机油或废机油 20号左右
水 自来水或软水
为检测本脱模剂的性能我们作了以下试验:
在国内尚无评定脱模性能的试验标准情况下,我们以截头水泥砂浆锥体对模板的粘附力,脱模件表面的气孔率、模板的沾灰量等测定其性能。
截头水泥砂浆锥体对模板的粘附力的测定方法为:截头圆锥体,底面直径和高分别为10cm,顶面直径为6cm,顶端装有脱模起吊用吊环。测定时,将脱模剂涂于15×15厘米的金属板上,园锥体放于其上,使其成型为水泥砂浆锥体,再在20℃温度下放置24小
时,用测力计测定水泥砂浆锥体对金属模板的脱除力,并与其他的产品(武汉化工二厂的W-15、山西万荣的RH)进行对比,其结果列于表1。
混凝土构件浇注中,成型面上经常出现较多的孔泡,俗称麻面。这些孔泡的产生,是由于模板、混凝土界面上截留有水泡、气泡之故、脱模剂涂层的界面状况是直接影响表面孔泡形成的原因之一,因此测定脱模面的表面孔泡率,可评定脱模剂的优劣。我们参照美国水泥和混凝土协会提出的方法进行测定。采取的方法为:在所选择面积范围内,先测出孔泡个数和孔泡直径,再计算出孔泡面积及孔泡的面积率。具体作法是:将涂有脱模剂的20×20×4cm的金属试模成型混凝土薄板,待脱模后观测混凝土板面2mm以上的孔泡数及直径,计算出孔泡率,并称取模板表面粘附的灰浆量,其试验对比结果见表1:
脱模剂 本脱模剂 W-15 RH 机油
试验项目
粘附力(kg) 10.4 21.5 12.9 9.7
孔泡数及其直径 2.5/1 8.5/1 7.7/1 5.2/1 7.3/1 8.5/1 6.0/1
mm/个 2/1 5.0/3 4.5/2 4.2/2 5.5/2 4.5/1 4.3/1
4/2 3.5/1 3.2/1 4.0/4 3.7/2 3.5/6
3.0/6 2.7/3 2.5/2 3.0/5 2.5/13 2/23
2/5
孔泡率% 0.01 0.4 0.6
模板沾灰量(g) 0.1 0.2 0.43
从表1可见,本脱模剂粘附力的测定量和机油相近,比其他的脱模剂小,可见脱模效果好,润滑减阻性能好,因而也防止或减少了混凝土表面孔泡的形成。模板表面的粘灰量比其他脱模剂也少。
众所周知,高层建筑需要使用大量立面和侧面的钢模,这些模板粘灰多,脱模难度大,因此需要采用脱模效能好的脱模剂。一冶筑炉公司承建的南京大胜观高压线过江塔,塔高248米,塔体结构复杂,外模采用直升模板,内模为翻转模板,施工难度大。一冶筑炉公司采用本脱模剂,作了有关涂药量,脱模次数、模板粘灰量等方面的试验。试验方法为:选用4块0.5×0.2米毫无光洁度的粗糙钢模板,拼接成竖直的立方体,脱模面积0.4米2,涂刷脱模剂后,浇注混凝土,再脱模,其测试结果见表2。
表2
脱模剂 本脱模剂(1∶2稀释液) 煤油石蜡脱模剂
试验项目
涂药量g/m 75 75
涂药一次连续脱模次数 2-3 1
模板累积粘灰量g/m 9.5
脱模试件外观 外形完整,表面光滑,
气孔少
涂刷于混凝土底模或金属模板上的本脱模剂涂层,用水冲刷或于水中浸泡48小时后,成型0.4×0.2×0.05米混凝土板,易脱模,板面光滑,粘灰少。
湖北省建筑总公司构件厂将本脱模剂喷涂于混凝土地坪上,附着力强,脱除混凝土空心楼板,喷涂一次可连续脱模2次,脱模效果好。汉阳预制构件厂,用本脱模剂涂刷6×0.35×0.35米混凝土胎模,浇注的混凝土方桩起吊时无粘连现象,胎模完好无损。交通部二航工程局九江预制厂浇注钢筋混凝土空心板和钢筋混凝土方桩,在金属模板上,涂刷本脱模剂后,脱模构件易起吊,外形完整、表面光滑、气孔少。
本脱模剂是主要用化工废料和再生料制成的水剂试剂,原料来源广泛,生产成本低,使用费用低,每平方米模板的脱模费不到2分。本脱模剂无毒、油感强,滑性好,对模板的附着力强,对混凝土的粘附力小,涂刷一次,可连续脱模2-3次,脱模构件外形完整、表面光滑、气孔少,模板沾灰少,涂层能耐雨水冲刷、围水浸泡。本脱模剂适于金属模、木模、混凝土地模,胎模及一切难于脱模的地方使用。
下面举出本发明的实施例:
例1,将100克再生润滑油的轻油馏分,55克废机油,50克油脚皂混合加热,不断搅拌,融成糊状,于75℃将100ml水分次加入其中,搅拌至油脚皂全部溶融后,缓慢加入乳化水,于73-75℃乳化30分钟,然后自然降温搅拌至40℃出料,得产品585克,有效物含量35%。
例2,将160克再生润滑油的轻油馏分,80克再生机油(20号),95克油脚皂混合均匀,在不断搅拌下,于水浴中加热,使油脚皂与油料熔融成糊状,于76℃加入约40ml溶介水,温度降至70℃,反应物由稠→稀→稠,搅拌3-5分钟后,继续分次加入120ml溶介水,至油脚皂全部溶融后,缓慢加入约1000ml热水,于70℃左右乳化40分钟,冷水回流冷却搅拌至40℃加入10克甲醛出料,得产品1000克,有效物含量33.5%。
例3,将10克再生润滑油的轻油馏分,5克再生机油,6.5克油脚皂在不断搅拌下,加热混合熔融成糊状,于77℃加溶介水10ml,搅拌,再分二次各加入10ml溶介水,温度降至70℃,加余水乳化30分钟得产品70克,有效物含量30%。
Claims (3)
1、混凝土脱模剂,其特征在于它是由脱模油,再生机油或废机油、食用植物油脚皂、水配制而成的水性制剂,其重量配比为:
脱模油 再生机油或废机油 食用植物油脚皂 水
160 64~88 72~104 加至浓度为30%~35%
2、根据权利要求1所述的脱模剂,其特征在于脱模油采用石油再生炼油厂的轻油馏分。
3、混凝土建材脱模剂的制备工艺,其特征在于将脱模油、再生机油或废机油、油脚皂混合均匀,边加热、边搅拌,待油脚皂熔融成糊状后,于75-80℃下分次加入溶介水,使油脚皂全部溶解,再于70℃左右加入乳化水,保温乳化40分钟后得乳化液,然后降温搅拌至40℃,出料即为产品。