CN102179668A - 锅炉和压力容器压制封头及制造方法 - Google Patents

锅炉和压力容器压制封头及制造方法 Download PDF

Info

Publication number
CN102179668A
CN102179668A CN2011100606338A CN201110060633A CN102179668A CN 102179668 A CN102179668 A CN 102179668A CN 2011100606338 A CN2011100606338 A CN 2011100606338A CN 201110060633 A CN201110060633 A CN 201110060633A CN 102179668 A CN102179668 A CN 102179668A
Authority
CN
China
Prior art keywords
end socket
steel plate
boiler
plate blank
sealing head
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011100606338A
Other languages
English (en)
Other versions
CN102179668B (zh
Inventor
袁承春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Boiler Co Ltd
Original Assignee
Harbin Boiler Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Boiler Co Ltd filed Critical Harbin Boiler Co Ltd
Priority to CN201110060633.8A priority Critical patent/CN102179668B/zh
Publication of CN102179668A publication Critical patent/CN102179668A/zh
Application granted granted Critical
Publication of CN102179668B publication Critical patent/CN102179668B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

锅炉和压力容器压制封头及制造方法。以往锅炉和压力容器产品球形或椭圆形封头除大直径薄壁封头采用旋压成型外，一般都是用钢板毛坯直接通过压制模具热压成型，每一种公称直径和厚度规格的封头都需要相应的冲头和拉环模具；公称直径相同而厚度不同时，需要的拉环模具也不同；往往厚度相差几毫米，也必须制作不同的拉环模具。一种锅炉和压力容器的压制封头，其组成包括：封头钢板毛坯（1），所述的封头钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层（2）。发明用于锅炉和压力容器制造企业单台、小批量产品制造。

Description

锅炉和压力容器压制封头及制造方法
技术领域：
发明属于锅炉和压力容器制造领域；具体涉及一种用于锅炉和压力容器压制封头及制造工艺方法。
背景技术：
以往锅炉和压力容器产品球形或椭圆形封头除大直径薄壁封头采用旋压成型外，一般都是用钢板毛坯直接通过压制模具热压成型，每一种公称直径和厚度规格的封头都需要相应的冲头和拉环模具；公称直径相同而厚度不同时，需要的拉环模具也不同；往往厚度相差几毫米，也必须制作不同的拉环模具。造成锅炉和压力容器制造企业封头拉环模具过多、模具成本高、严重影响经济效益。
发明内容：
发明的目的是提供一种锅炉和压力容器压制封头及制造方法，达到制造工艺进一步优化、提高现有拉环模具利用率、减少拉环模具数量、降低生产成本、缩短生产周期、提高经济效益的目的。
上述的目的通过以下的技术方案实现：
锅炉和压力容器的压制封头，其组成包括：封头钢板毛坯，所述的封头钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层。
所述的锅炉和压力容器的压制封头，所述的封头钢板毛坯为球形封头钢板毛坯、或椭圆形封头钢板毛坯。
一种锅炉和压力容器压制封头的制造方法，封头压制前在钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层；利用拉环模具进行封头压制过程中，调正工艺使得压制成型时堆焊层出现在封头端部外表面直段增厚部位。
所述的锅炉和压力容器压制封头的制造方法，所述的堆焊包括丝极埋弧自动焊、或带极埋弧自动焊、或手工焊条焊；所述的堆焊层在压制成型后加工去除或作为环焊缝过渡加工利用。
有益效果：
1.本发明有效地减少了过去锅炉和压力容器产品压制封头制作过程中，采用钢板毛坯直接热压成型、并且必须一一对应模具的单一制造工艺对模具的依赖和制约。
本发明在钢板毛坯表面边缘进行环形堆焊增厚的特殊制造工艺，在保证封头压制成型尺寸和质量的前提下，尺寸适应范围增大，可有效地提高锅炉和压力容器制造企业现有拉环模具利用率，减少模具数量，降低模具制造成本、缩短生产周期、提高经济效益。
本发明技术新颖、实用、先进、可靠，特别适用于锅炉和压力容器制造企业制作各种规格单台锅炉封头、小批量的产品封头、成品尺寸经常在一定范围内变化情况下的封头。
本发明通过不同厚度的堆焊，尺寸的适应程度明显增大，能够有效提高现有模具利用率、减少模具数量、缩短生产周期、降低生产成本、提高经济效益。技术新颖、实用、先进、可靠。
本发明节省拉环模具的制造成本，提高了制造企业的经济效益。
附图说明：
附图1是本产品的结构示意图。
附图2是附图1中堆焊后的封头钢板毛坯的俯视图。
附图3是附图1中堆焊后的封头钢板毛坯的剖视图。
附图4是附图3的A向局部放大图。
附图5是本产品的球形封头的结构示意图。
附图6是本产品的椭圆形封头的结构示意图。
具体实施方式：
实施例1：
一种锅炉和压力容器的压制封头，其组成包括：封头钢板毛坯1，所述的封头钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层2。
实施例2：
实施例1所述的锅炉和压力容器的压制封头，所述的封头钢板毛坯可以是球形封头钢板毛坯3，或椭圆形封头钢板毛坯4。
实施例3：
一种锅炉和压力容器压制封头的制造方法，封头压制前在钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层；利用拉环模具进行封头压制过程中，调正工艺使得压制成型时堆焊层出现在封头端部外表面直段增厚部位。
实施例4：
实施例3所述的锅炉和压力容器压制封头的制造方法，所述的堆焊包括丝极埋弧自动焊、或带极埋弧自动焊、或手工焊条焊，焊接方法可以是不同种类的组合，以形成一定的宽度和厚度符合工艺要求的堆焊层，适当地均匀增加钢板毛坯边缘厚度，便于利用现有的压制模具进行封头压制。
堆焊层在封头压制成型后加工去除，或作为环焊缝过渡加工利用。
实施例5：
实施例1或2或3或4所述的锅炉和压力容器压制封头的制造工艺方法，利用现有Dn700×60椭圆冲头和拉环模具压制Dn700×54椭圆封头4的工艺流程：    1）钢板毛坯气割下料，根据现有模具和椭圆封头数据确定堆焊层厚度和宽度，按焊接工艺规程进行堆焊并加工修整堆焊层符合压制要求；    2）压制前堆焊层方向向下放置，封头热压成型；    3）车加工封头环缝坡口时去除堆焊层；    4）封头形状和几何尺寸及探伤检查合格。
实施例7：
实施例1或2或3或4所述的锅炉和压力容器压制封头的制造工艺方法，利用现有SR350×60球形冲头和拉环模具压制SR350×54球形封头3的工艺流程：    1）钢板毛坯气割下料，根据现有模具和球形封头数据确定堆焊层厚度和宽度，按焊接工艺规程进行堆焊并加工修整堆焊层符合压制要求；    2）压制前堆焊层方向向下放置，封头热压成型；    3）车加工封头环缝坡口时去除堆焊层；    4）封头形状和几何尺寸及探伤检查合格。

Claims (4)

1.一种锅炉和压力容器的压制封头，其组成包括：封头钢板毛坯，其特征是：所述的封头钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层。
2.根据权利要求1所述的锅炉和压力容器的压制封头，其特征是：所述的封头钢板毛坯为球形封头钢板毛坯、或椭圆形封头钢板毛坯。
3.一种锅炉和压力容器压制封头的制造方法，其特征是：封头压制前在钢板毛坯的直边位置的表面堆焊环形局部增厚焊接层；利用拉环模具进行封头压制过程中，调正工艺使得压制成型时堆焊层出现在封头端部外表面直段增厚部位。
4.根据权利要求3所述的锅炉和压力容器压制封头的制造方法，其特征是：所述的堆焊包括丝极埋弧自动焊、或带极埋弧自动焊或手工焊条焊；所述的堆焊层在压制成型后加工去除或作为环焊缝过渡加工利用。
CN201110060633.8A 2011-03-14 2011-03-14 锅炉和压力容器压制封头及制造方法 Active CN102179668B (zh)