- Active
Links
Abstract
本发明公开了一种无机防水材料,它是由原料硅酸盐水泥、细河沙、粉煤灰、硅粉、膨胀剂和减水剂按照下述重量份配比制备而成:硅酸盐水泥72份~76份,细河沙144份~152份,粉煤灰9份~11份,硅粉3份~5份,膨胀剂11份~13份和减水剂1份。该防水材料具有高抗渗性能、高强度和高抗裂性能,可提高混凝土或砂浆防水性能,减少渗漏所造成的危害。由于选取了廉价的工业原料和工业副产品作为该防水材料的原料,价格成本低廉;既可以配制成防水砂浆抹于结构物表面防水,还可以用作防水结构物的组成部分;使用时无需特殊养护,耐老化,使用寿命长,对环境无污染,施工工艺简单。
Description
技术领域
本发明涉及一种防水材料,尤其是涉及一种用于配制防水砂浆的无机防水材料。
背景技术
在建筑工程中,渗漏问题一直是困扰工程界的疑难杂症,是科研人员着力研究解决的重要课题。我国建筑物渗漏状况是十分惊人和严峻的,每年仅用于维修房屋等建筑工程防水渗漏的费用就高达20亿元以上。渗漏的危害轻则加速混凝土老化病害的发展,重则造成建筑物破坏甚至失事,损失将是不可估量的。
防水材料从最早的混凝土结构自防水(采用富砂浆、集料密实级配等方法,来提高混凝土或砂浆自身密实度、减少孔隙率以提高其防水能力)发展到上世纪初的外加剂防水混凝土或砂浆(主要通过在混凝土或砂浆中加入长链脂肪酸或无机盐等化合物,与水泥水化产物反应,生成不溶于水的胶体化合物或者络合物堵塞孔隙,增加密实度,来提高混凝土或砂浆的抗渗性能),进而在混凝土或砂浆中加入膨胀剂,使混凝土或砂浆产生适量膨胀,从而使混凝土或砂浆中产生约束膨胀,以提高其抗渗性能;到20世纪50年代,出现各种高分子合成防水材料,为现代化防水材料的发展提供了新材料、新技术,从此我国通过引进、借鉴国外先进设备与技术,在改性沥青防水卷材、合成高分子防水卷材以及其他先进防水材料方面得到迅速发展;目前,我国防水材料已由沥青纸胎油毡等有机材料一统天下的格局,发展成为今天的两大主要类别的防水材料:柔性材料和刚性材料,柔性材料主要利用高分子物质,通过聚合、改性等手段,在结构物表面形成一层憎水的保护层以阻止水的通过,是一种外防水技术,主要有防水卷材、防水涂料、柔性防水砂浆和柔性防水混凝土等;刚性防水材料则是以水泥、砂、石为原材料,掺加少量有机或无机外加剂,在混凝土和砂浆表面或内部形成致密的、有一定强度的、弥合混凝土和砂浆结构缺陷、增强混凝土和砂浆的防水层,是一种内防水技术,主要有防水砂浆、防水混凝土等。
刚性无机防水材料渗水的主要原因有两大方面,一是混凝土或砂浆内部的体积收缩裂缝,二是混凝土或砂浆内部的孔隙结构。而这些裂缝和孔隙又是混凝土组分的物理化学性质及结构缺陷造成的,是混凝土或砂浆自身无法克服的,从而渗漏也成为其自身难以解决的问题。
发明内容
本发明的目的在于提供一种能克服或减轻上述缺陷、提高混凝土或砂浆防水性能、减少渗漏所造成危害的无机防水材料。
为实现上述目的,本发明可采取下述技术方案:
本发明所述的无机防水材料,它是由原料硅酸盐水泥、细河沙、粉煤灰、硅粉、膨胀剂和减水剂按照下述重量份配比制备而成:
硅酸盐水泥72份~76份,细河沙144份~152份,粉煤灰9份~11份,硅粉3份~5份,膨胀剂11份~13份和减水剂1份。
所述膨胀剂包括FEA膨胀剂、UEA膨胀剂或MgO膨胀剂;所述减水剂包括FDN高效减水剂、UNF高效减水剂、ZF高效减水剂。
所述细河沙的细度模数为2.00~2.10。
使用时,取本发明的无机防水材料中的各种原料,拌合均匀,并加入适量水拌制,即可制作成防水砂浆,砂浆跳桌流动度控制在155mm~165mm,抹于结构物表面或用作防水结构物的组成部分,无需特殊的养护措施,使用方法简单,对环境无污染,施工工艺无特殊要求。
本发明的优点在于该防水材料具有高抗渗性能、高强度和高抗裂性能,可提高混凝土或砂浆防水性能,减少渗漏所造成的危害。由于选取了廉价的工业原料和工业副产品作为该防水材料的原料,价格成本低廉;不仅可以制作成防水砂浆抹于结构物表面防水,还可以用作防水结构物的组成部分;使用时无需特殊养护,耐老化,使用寿命长,对环境无污染,施工工艺简单。按照《砂浆、混凝土防水剂(JC474-2008)》标准,对本发明的无机防水材料的性能进行测试及相应单项评定表见表1:
表1 测试无机防水材料的基本性能与标准对比
从上表中可以看出, 按照国内现行砂浆、混凝土防水剂标准测试,本发明的无机防水材料的各项指标均达到或超过国内一等品要求。可用于水库、堤坝、沟渠、游泳池、水族设施、密封污水处理系统、地铁、隧道、坑道、地下仓库、屋面及地下室等建筑设施的防水。
具体实施方式
实施例1:
本发明所述的无机防水材料由原料42.5号普通硅酸盐水泥72重量份,细度模数2.00~2.10的细河沙144重量份,Ⅰ级粉煤灰9重量份,硅粉3重量份,MgO膨胀剂11重量份,ZF(如LRY-ZF、ZS-ZF等)高效减水剂1重量份混合均匀而得成品。
使用时,将上述原料拌合均匀,并加入适量水拌制,即制作成砂浆,砂浆跳桌流动度控制在155mm~165mm。此种防水砂浆比较适合用于地铁、隧道、坑道等的建筑物防水。
实施例2:
本发明所述的无机防水材料是由原料42.5号普通硅酸盐水泥76重量份,细度模数2.00~2.10的细河沙152重量份,Ⅰ级粉煤灰11重量份,硅粉5重量份,UEA膨胀剂13重量份,UNF(如UNF-MA、UNF-5等)减水剂1重量份混合均匀而得成品。
使用时,将上述原料拌合均匀,并加入适量水拌制,即制作成砂浆,砂浆跳桌流动度控制在155mm~165mm。此种防水砂浆比较适合用于水库、堤坝、沟渠、游泳池、水族设施等的建筑物防水。
实施例3:
本发明所述的无机防水材料是由原料42.5号普通硅酸盐水泥74重量份,细度模数2.00~2.10的细河沙148重量份,Ⅰ级粉煤灰10重量份,硅粉4重量份,FEA膨胀剂12重量份,FDN类高效减水剂1重量份混合均匀而得成品。
使用时,将上述原料拌合均匀,并加入适量水拌制,即制作成砂浆,砂浆跳桌流动度控制在155mm~165mm。此种防水砂浆比较适合用于地下仓库、地下室、屋面、密封污水处理系统等的建筑物防水。
Claims (3)
1.一种无机防水材料,其特征在于:它是由原料硅酸盐水泥、细河沙、粉煤灰、硅粉、膨胀剂和减水剂按照下述重量份配比制备而成:
硅酸盐水泥72份~76份,细河沙144份~152份,粉煤灰9份~11份,硅粉3份~5份,膨胀剂11份~13份和减水剂1份。
2.根据权利要求1所述的无机防水材料,其特征在于:所述膨胀剂包括FEA膨胀剂、UEA膨胀剂或MgO膨胀剂;所述减水剂包括FDN减水剂、UNF减水剂、ZF减水剂。
3.根据权利要求1所述的无机防水材料,其特征在于:所述细河沙的细度模数为2.00~2.10。
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN 201110045592 CN102173686B (zh) | 2011-02-25 | 2011-02-25 | 无机防水材料 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN 201110045592 CN102173686B (zh) | 2011-02-25 | 2011-02-25 | 无机防水材料 |
Publications (2)
Publication Number | Publication Date |
---|---|
CN102173686A CN102173686A (zh) | 2011-09-07 |
CN102173686B true CN102173686B (zh) | 2012-12-26 |
Family
ID=44516984
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN 201110045592 Active CN102173686B (zh) | 2011-02-25 | 2011-02-25 | 无机防水材料 |
Country Status (1)
Country | Link |
---|---|
CN (1) | CN102173686B (zh) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103951349B (zh) * | 2014-04-22 | 2016-02-17 | 黄河勘测规划设计有限公司 | 具有高抗渗性能的无机防水材料 |
CN111926646A (zh) * | 2020-08-11 | 2020-11-13 | 董星 | 一种高强轻质多孔混凝土及其制备方法 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1142523A (zh) * | 1996-06-11 | 1997-02-12 | 朴素 | 无机浸透式防水剂 |
CN1438291A (zh) * | 2003-03-17 | 2003-08-27 | 刘金生 | 无机浸透式防水剂 |
CN101492268A (zh) * | 2009-03-11 | 2009-07-29 | 朱炳喜 | 一种混凝土修补砂浆添加剂及修补砂浆的配制方法 |
-
2011
- 2011-02-25 CN CN 201110045592 patent/CN102173686B/zh active Active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1142523A (zh) * | 1996-06-11 | 1997-02-12 | 朴素 | 无机浸透式防水剂 |
CN1438291A (zh) * | 2003-03-17 | 2003-08-27 | 刘金生 | 无机浸透式防水剂 |
CN101492268A (zh) * | 2009-03-11 | 2009-07-29 | 朱炳喜 | 一种混凝土修补砂浆添加剂及修补砂浆的配制方法 |
Also Published As
Publication number | Publication date |
---|---|
CN102173686A (zh) | 2011-09-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN105948617B (zh) | 一种抗裂、抗渗砂浆及其制备方法 | |
CN102718455B (zh) | 一种水泥基渗透结晶型高性能防水粉料及其应用 | |
CN102504670A (zh) | 混凝土用渗透环氧树脂防水涂料 | |
CN106082871B (zh) | 一种混凝土挡浪块 | |
CN104478374A (zh) | 一种水泥基自流平砂浆 | |
CN104261749A (zh) | 一种高膨胀性能的水泥基材料及其应用 | |
CN104761205A (zh) | 一种聚合物防水砂浆 | |
CN103553408B (zh) | 一种柔性防水粉及制备方法 | |
CN110746166A (zh) | 一种自身结晶抗渗防潮砂浆及其生产方法 | |
CN110395931A (zh) | 一种早强速凝剂和耐高温抗裂防水堵漏材料及其制备方法和施工料 | |
CN103951349B (zh) | 具有高抗渗性能的无机防水材料 | |
CN101717222B (zh) | 渗晶催化络合剂 | |
CN102173686B (zh) | 无机防水材料 | |
CN103755213A (zh) | 一种多功能高效混凝土防水剂的制备方法 | |
CN101362641A (zh) | 一种防水砂浆 | |
CN110835249A (zh) | 一种海洋工程阻锈防裂砂浆及其制备与使用方法 | |
CN204254073U (zh) | 一种预应力钢筒活性粉末混凝土管材 | |
CN113429173A (zh) | 一种工程渣土免烧波形瓦及其制备工艺 | |
CN110451840B (zh) | 一种复合式密实剂 | |
CN104197129A (zh) | 一种新型钢筋混凝土排水管材及其制造方法 | |
CN105801060A (zh) | 一种超早强水泥基灌浆料 | |
CN101786827A (zh) | 一种抗渗剂 | |
CN115093184A (zh) | 一种低氯离子迁移系数的水泥基材料的制备方法 | |
CN204626470U (zh) | 一种冬季施工桩头防水装置 | |
CN112851281A (zh) | 一种聚合物快干早强抗腐蚀砂浆的制作方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
C14 | Grant of patent or utility model | ||
GR01 | Patent grant | ||
CP01 | Change in the name or title of a patent holder |
Address after: 450003 Jinshui Road 109, Zhengzhou City, Henan Province Patentee after: Yellow River Survey Planning and Design Research Institute Co., Ltd. Address before: 450003 Jinshui Road 109, Zhengzhou City, Henan Province Patentee before: Yellow River Engineering Consulting Co., Ltd. |
|
CP01 | Change in the name or title of a patent holder |