CN102166806A - 一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺 - Google Patents

一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺 Download PDF

Info

Publication number
CN102166806A
CN102166806A CN2010106118329A CN201010611832A CN102166806A CN 102166806 A CN102166806 A CN 102166806A CN 2010106118329 A CN2010106118329 A CN 2010106118329A CN 201010611832 A CN201010611832 A CN 201010611832A CN 102166806 A CN102166806 A CN 102166806A
Authority
CN
China
Prior art keywords
resin
weatherability
glue
production technology
transmission rate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010106118329A
Other languages
English (en)
Other versions
CN102166806B (zh
Inventor
张书龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN NANYU RESIN HARDWARE Co Ltd
Original Assignee
DONGGUAN NANYU RESIN HARDWARE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN NANYU RESIN HARDWARE Co Ltd filed Critical DONGGUAN NANYU RESIN HARDWARE Co Ltd
Priority to CN201010611832.9A priority Critical patent/CN102166806B/zh
Publication of CN102166806A publication Critical patent/CN102166806A/zh
Application granted granted Critical
Publication of CN102166806B publication Critical patent/CN102166806B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，属于树脂加工技术领域，该方法是将优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；将专用的环氧树脂胶水A、B两组按A:B=1：1比例混合均匀，作为专用树脂胶水原料；用自动滴胶机或人工的方法将胶水注入硅胶模具腔内；固化，成品成型后即得成品；色彩的实现可通过喷底色、镀底色或者用胶水加色精的方法制得；采用该工艺制备的树脂透光率高达到90%以上，热变形温度达摄氏80度以上，邵氏硬度D达80以上，其耐候性好，不容易黄变。

Description

一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺
技术领域
本发明涉及一种树脂仿钻的生产工艺，特别涉及一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，属于树脂加工技术领域。
背景技术
钻石是人类最早利用的宝石材料之一，是地球上最硬的材料，由于其美丽、稀少、耐久、无害并且光彩熠熠，成为了最受欢迎的宝石，其颜色也无奇不有，所以人们的钻石的追求是孜孜不倦的，拥有它成为每个女性心中的梦想，但由于钻石稀少，价格比较昂贵，所以不是每个人都可以拥有，所以制造一种仿钻产品成为一些商家不断努力的方向。
基于人们对钻石不倦的崇尚与追求，全球饰品市场上仿钻的需求极度扩张，目前市场上有几种仿钻产品，但是最多见的要数玻璃水钻和亚克力仿钻产品，但是由于玻璃水钻存在着成本高，品质控制难，色彩难调，易碎等天生的缺陷，而亚克力仿钻则存在品质差，易缩水，有水口等缺陷，目前市面上用环氧树脂制成的产品透光率低、耐候性差、容易变黄，其仿钻效果不能满足市场的需要，因此以高品质环氧树脂为原材料生产的树脂钻，具有甚至高于玻璃仿钻的品质，必将引领潮流，赢得市场的认同。
发明内容
本发明的目的是克服原有的环氧树脂产品耐候性差、透光率低、容易变黄的的缺陷，提供一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，采用该工艺生产的树脂具备高耐候性，高透光率，高耐温，不易变黄。
本发明是通过以下途径来实现的：
一种高透光率、高耐候行抗黄变树脂仿钻的生产工艺，包括如下步骤：
（1）模具的准备：用优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；
（2）树脂胶水原料的准备：将液体环氧树脂（比如环氧值可以为50~54）,比如陶氏的331或331J树脂，或宏昌的128树脂等作为A组份，将甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成固化剂作为B组份，按1：1的比例混合均匀，制得专用树脂胶水原料；
（3）注模：将步骤（2）准备好的专用树脂胶水原料用自动滴胶机或人工的方法注入硅胶模具腔内；
（4）固化：将注好专用树脂胶水的硅胶模具送入烤箱中加温固化成型制得半成品；
（5）成品成型：从硅胶或塑胶模具中取出树脂仿钻作为成品，或再用塑料膜片固定方向后，或丝印后喷底，或送进真空电镀炉内镀底后即得成品；
（6）色彩的实现可通过喷底色、镀底色或者用胶水加色精的方法制得。
上述的所述的液体环氧树脂环氧值为0.38~0.55之间；为了改善专用胶水的流动性可加入稀释剂等。
所述专用树脂胶水原料中的紫外线吸收剂，这种紫外线吸收剂可以从多家公司有多种选择；所述的专用树脂胶水原料中有抗氧剂，这种抗氧剂可以从多家公司有多种选择。
采用本方法制备的高透光率、高耐候性抗黄变树脂透光率高达到90%以上，热变形温度达80度以上，邵氏硬度D达80以上，其耐候性好，不容易黄变。
所述的专用树脂胶水还可以在不改变主要性质的条件下加入其它树脂制备过程中需要的辅助原料。
本发明的突出效果是：
1.该树脂仿钻产品具有耐候性极好，不易黄变，参照ISO105 A02的标准为3级以上；
2.采用该种工艺制得的树脂仿钻产品透光率达到90%以上，热变形温度达80度以上，邵氏硬度D达80以上。
具体实施方式
下面通过实施例对本发明做进一步详细说明，这些实施例仅用来说明本发明，并不限制本发明的范围。
实施例1
将液体环氧树脂：陶氏的331树脂作为A组份，将甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成固化剂作为B组份，克服了环氧树脂原有的耐候性极差，易黄变等缺点，使用时按重量比A ：B = 1 ：1的比例混合均匀成为专用胶水；
用优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；
 将上述环氧树脂专用胶水作为原料用自动滴胶机或人工的方法，注入硅胶或塑胶模具腔内，然后送入烤箱加温固化成型制得半成品；
从硅胶或塑胶模具中取出树脂仿钻作为成品；或再用塑料膜片固定方向后，或丝印后喷底，或送进真空电镀炉内镀底后即得成品；
其色彩的实现可通过喷底色，方法达到。
实施例2
将液体环氧树脂：陶氏的331J树脂作为A组份，将甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成固化剂作为B组份，克服了环氧树脂原有的耐候性极差，易黄变等缺点，使用时按重量比A ：B = 1 ：1的比例混合均匀成为专用胶水；
用优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；
将上述环氧树脂专用胶水作为原料用自动滴胶机或人工的方法，注入硅胶或塑胶模具腔内，然后送入烤箱加温固化成型制得半成品；
从硅胶或塑胶模具中取出树脂仿钻作为成品；或再用塑料膜片固定方向后，或丝印后喷底，或送进真空电镀炉内镀底后即得成品；
其色彩的实现可通过喷底色，方法达到。
实施例3
将液体环氧树脂:宏昌的128树脂作为A组份，将甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成固化剂作为B组份，克服了环氧树脂原有的耐候性极差，易黄变等缺点，使用时按重量比A ：B = 1 ：1的比例混合均匀成为专用胶水；
用优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；
将上述环氧树脂专用胶水作为原料用自动滴胶机或人工的方法，注入硅胶或塑胶模具腔内，然后送入烤箱加温固化成型制得半成品；
从硅胶或塑胶模具中取出树脂仿钻作为成品；或再用塑料膜片固定方向后，或丝印后喷底，或送进真空电镀炉内镀底后即得成品。

Claims (6)

1.一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：包括如下步骤：
（1）模具的准备：用优质的玻璃水钻或锆石仿钻作为模种，粘接于玻璃或金属板面上，再覆盖上高品质的硅胶或塑胶固化制得产品模具；
（2）专用胶水原料的准备：将液体环氧树脂作为A组份，将甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成固化剂作为B组份，按A : B = 1 ：1比例混合均匀，制得专用树脂胶水原料备用； 
（3）注模：将步骤（2）准备好的专用树脂胶水原料用自动滴胶机或人工的方法注入硅胶模具腔内；
（4）固化：将注好专用树脂胶水的硅胶模具送入烤箱中加温固化成型制得半成品；
（5）成品成型：从硅胶或塑胶模具中取出树脂仿钻作为成品，或再用塑料膜片固定方向后，或丝印后喷底，或送进真空电镀炉内镀底后即得成品；
（6）色彩的实现可通过喷底色、镀底色或者用胶水加色精的方法制得。
2.根据权利要求1所述的一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：所述的液体环氧树脂环氧值为0.38~0.55之间。
3.根据权利要求1所述的一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：所述的固化剂为甲基六氢邻苯二甲酸酐配上适量的紫外线吸收剂和抗氧剂组成。
4.根据权利要求1所述的一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：为了改善专用胶水的流动性可加入稀释剂等。
5.根据权利要求1所述的一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：采用本方法制备的高透光率、高耐候性抗黄变树脂透光率高达到90%以上，热变形温度达80度以上，邵氏硬度D达80以上，其耐候性好，不容易黄变，参照ISO105 A02的标准为3级以上。
6.根据权利要求1所述的一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺，其特征在于：所述的专用树脂胶水还可以在不改变主要性质的条件下加入其它树脂制备过程中需要的辅助原料。
CN201010611832.9A 2010-12-29 2010-12-29 一种高透光率、高耐候性抗黄变树脂仿钻的生产工艺 Expired - Fee Related CN102166806B (zh)