CN102166655A - 一种纳米级锑粉的制备方法 - Google Patents

一种纳米级锑粉的制备方法 Download PDF

Info

Publication number
CN102166655A
CN102166655A CN 201110067225 CN201110067225A CN102166655A CN 102166655 A CN102166655 A CN 102166655A CN 201110067225 CN201110067225 CN 201110067225 CN 201110067225 A CN201110067225 A CN 201110067225A CN 102166655 A CN102166655 A CN 102166655A
Authority
CN
China
Prior art keywords
ball
antimony powder
preparation
powder
antimony
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110067225
Other languages
English (en)
Other versions
CN102166655B (zh
Inventor
徐建林
郭强
杨树华
康昭
席国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lanzhou University of Technology
Original Assignee
Lanzhou University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lanzhou University of Technology filed Critical Lanzhou University of Technology
Priority to CN2011100672255A priority Critical patent/CN102166655B/zh
Publication of CN102166655A publication Critical patent/CN102166655A/zh
Application granted granted Critical
Publication of CN102166655B publication Critical patent/CN102166655B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种纳米级锑粉的制备方法，其步骤为：将原料锑粉与液体添加剂混合后置于球磨机中，采用球径大小为4～20mm的GGr15金属球进行任意配比后用作磨球；球料质量比为20∶1～40∶1；球磨机转速为50～400r/min，球磨时间为10～40小时；液体添加剂的总添加量按锑粉质量，配比为：0.2ml/g～1ml/g。

Description

一种纳米级锑粉的制备方法
技术领域
本发明涉及纳米锑粉的制备。
背景技术
目前锑粉的制备方法分为三类：由锑的化合物提纯制备；由工业纯金属锑火法冶炼制备；由锑电解精炼制取。此类生产方法或工艺复杂，或环境污染大，或生产周期长、产品产量少、粒径大，而纳米级锑产品的制备方法则更少且工艺更复杂，对资源的依附及对环境的影响也更严重。
发明内容
本发明的目的是提供一种纳米级锑粉的制备方法。
本发明是一种纳米级锑粉的制备方法，其步骤为：
(1)将原料锑粉与液体添加剂混合后置于球磨机中，采用球径大小为4～20mm的GGr15金属球进行任意配比后用作磨球；球料质量比为20∶1～40∶1；球磨机转速为50～400r/min，球磨时间为10～40小时；
(2)球磨后将球磨粉料进行过滤，干燥获得产品，干燥温度为10℃～70℃，其中40℃～70℃需真空干燥，10℃～40℃真空干燥、非真空干燥均可。
本发明的有益效果为：所涉及的球磨制备方法具有工艺简单，生产周期短，产品产量大，无环境污染，适用于工业化生产等优点；制备出的锑粉粒径小，粒径范围为1～50nm。
具体实施方式
本发明是一种纳米级锑粉的制备方法，其步骤为：
(1)将原料锑粉与液体添加剂混合后置于球磨机中，采用球径大小为4～20mm的GGr15金属球进行任意配比后用作磨球；球料质量比为20∶1～40∶1；球磨机转速为50～400r/min，球磨时间为10～40小时；
(2)球磨后将球磨粉料进行过滤，干燥获得产品，干燥温度为10℃～70℃，其中40℃～70℃需真空干燥，10℃～40℃真空干燥、非真空干燥均可。
本发明的原料为100目～300目的金属锑粉，所用液体添加剂为：去离子水，或者烷基酚聚氧乙烯醚，或者聚氧乙烯山梨糖醇酐单油酸酯，上述添加剂可单一使用，也可任意配比复配使用；液体添加剂的总添加量按锑粉质量，配比为：0.2ml/g～1ml/g。
球磨法是一种利用球磨机的转动或振动，使硬球对原料进行强烈的撞击、研磨和搅拌，以粉碎与研磨为主要手段来实现粉末的纳米化与机械合金化的粉体制备方法。球磨法的工艺简单，效率高，环境污染小，能制备出常规方法难以获得的纳米材料。

Claims (2)

1.一种纳米级锑粉的制备方法，其步骤为：
(1)将原料锑粉与液体添加剂混合后置于球磨机中，采用球径大小为4～20mm的GGr15金属球进行任意配比后用作磨球；球料质量比为20∶1～40∶1；球磨机转速为50～400r/min，球磨时间为10～40小时；
(2)球磨后将球磨粉料进行过滤，干燥获得产品，干燥温度为10℃～70℃，其中40℃～70℃需真空干燥，10℃～40℃真空干燥、非真空干燥均可。
2.根据权利要求1所述的纳米级锑粉的制备方法，其特征在于原料为100目～300目的金属锑粉，所用液体添加剂为：去离子水，或者烷基酚聚氧乙烯醚，或者聚氧乙烯山梨糖醇酐单油酸酯，上述添加剂可单一使用，也可任意配比复配使用；液体添加剂的总添加量按锑粉质量，配比为：0.2ml/g～1ml/g。
CN2011100672255A 2011-03-17 2011-03-17 一种纳米级锑粉的制备方法 Expired - Fee Related CN102166655B (zh)