CN102161865A - 水乳型高聚物改性沥青防水涂料配方及制作工艺 - Google Patents
水乳型高聚物改性沥青防水涂料配方及制作工艺 Download PDFInfo
- Publication number
- CN102161865A CN102161865A CN2011100873521A CN201110087352A CN102161865A CN 102161865 A CN102161865 A CN 102161865A CN 2011100873521 A CN2011100873521 A CN 2011100873521A CN 201110087352 A CN201110087352 A CN 201110087352A CN 102161865 A CN102161865 A CN 102161865A
- Authority
- CN
- China
- Prior art keywords
- water
- waterproof paint
- type high
- polymer modified
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
水乳型高聚物改性沥青防水涂料配方及制作工艺,其特征在于:由以下质量百分比的成份组成,90#沥青40-45%,改性剂5-9%,水35-45%,乳化剂6-10%,凹土2-5%。首先用改性剂对沥青改性并加热至180℃,把水及乳化剂混合加热到80℃,并用酸把pH值调至1.5-2.5;将热沥青和混合好的乳化水按比例用专用乳化磨进行乳化;之后加凹土搅拌冷却灌装。本发明的有益效果:民用及工业建筑屋面的防水工程、厕浴间、厨房的防水防渗、地下室、水池、冷库的防水、防潮工程等,无毒、无污染、无气味、属环保型产品;且涂膜具有高强、坚韧、耐水、耐候、耐久性、性能优异等。
Description
技术领域
本发明涉及防水涂料,具体涉及一种水乳型高聚物改性沥青防水涂料配方及制作工艺。
背景技术
建筑防水涂料具有施工简便,对复杂结构适应性强的特点,在建筑施工中用量很大。防水涂料主要用于建筑物某些可能受到水侵蚀的结构部位的防水、防潮和防渗等。因此对防水涂料的耐高、低温性能、防腐性能有一定要求。现有的建筑防水涂料主要有聚氨酯防水涂料,聚合物水泥防水涂料,沥青类防水涂料和改性乳化沥青类防水涂料,聚合物沥青防水涂料,硅橡胶防水涂料等。其中改性乳化沥青类防水涂料,成膜后抗拉强度及断裂延伸率较低,易产生二次污染。以聚氨酯焦油为代表的非外露型双组分涂料,具有一定的毒性,施工基层面必须干燥,且双组分有一定的配比,施工要求严格。
发明内容
本发明需要解决技术问题是提供一种无毒,无污染、耐水、耐候、耐久性、性能优异的水乳型高聚物改性沥青防水涂料配方及制作工艺。
水乳型高聚物改性沥青防水涂料配方及制作工艺,其特征在于:由以下质量百分比的成份组成,
所述的填料为凹土。
水乳型高聚物改性沥青防水涂料制作工艺为,首先用改性剂对沥青改性并加热至180℃,把水及乳化剂混合加热到80℃,并用酸把PH值调至1.5-2.5;将热沥青和混合好的乳化水按比例用专用乳化磨进行乳化;之后加填料搅拌冷却灌装。
本发明的有益效果:民用及工业建筑屋面的防水工程、厕浴间、厨房的防水防渗、地下室、水池、冷库的防水、防潮工程等,无毒、无污染、无气味、属环保型产品;且涂膜具有高强、坚韧、耐水、耐候、耐久性、性能优异等。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
水乳型高聚物改性沥青防水涂料配方及制作工艺,由以下质量百分比的成份组成,
首先用改性剂对沥青改性并加热至180℃,把水及乳化剂混合加热到80℃,并用酸把PH值调至1.5-2.5;将热沥青和混合好的乳化水按比例用专用乳化磨进行乳化;之后加凹土搅拌冷却灌装。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.水乳型高聚物改性沥青防水涂料配方,其特征在于:由以下质量百分比的成份组成,
2.水乳型高聚物改性沥青防水涂料制作工艺,其特征在于:首先用改性剂对沥青改性并加热至180℃,把水及乳化剂混合加热到80℃,并用酸把PH值调至1.5-2.5;将热沥青和混合好的乳化水按比例用专用乳化磨进行乳化;之后加填料搅拌冷却灌装。
3.根据权利要求1所述的水乳型高聚物改性沥青防水涂料配方,其特征在于:所述的填料为凹土。