CN102154735A - 一种服装用聚酯阻燃纤维 - Google Patents
一种服装用聚酯阻燃纤维 Download PDFInfo
- Publication number
- CN102154735A CN102154735A CN 201110073982 CN201110073982A CN102154735A CN 102154735 A CN102154735 A CN 102154735A CN 201110073982 CN201110073982 CN 201110073982 CN 201110073982 A CN201110073982 A CN 201110073982A CN 102154735 A CN102154735 A CN 102154735A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire retardant
- clothes
- fire resistant
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种服装用聚酯阻燃纤维,包括聚对苯二甲酸丁二酯与阻燃剂,其组成成分及重量份比例为:聚对苯二甲酸丁二酯40–60,聚丙烯树脂5–15,玻璃纤维20–30,阻燃剂10–20,所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30–50,多磷酸铵10–20,羧乙基甲基磷酸20–40,柠檬酸10–20。本设计不仅韧性较高、耐高温性较强,而且生产成本较低。
Description
技术领域
本发明涉及一种阻燃纤维,尤其涉及一种服装用聚酯阻燃纤维,具体适用于制作高韧性、高耐温性的阻燃纤维。
背景技术
目前,纺织纤维可分为易燃纤维、可燃纤维、难燃纤维、不燃纤维四种。常见的纺织纤维大多数是可燃的,甚至是易燃的。因此,只有对纤维进行必要的处理,才能达到我们所需要的阻燃要求。一般的处理方法包括:提高成纤高聚物的热稳定性,将阻燃剂与成纤高聚物共混纺丝,用阻燃剂对纤维进行后处理,共聚、嵌段共聚,复合纺丝法,接枝改性以及后处理改性方法。
中国专利公开号为CN101104963A,公开日为2008年1月16日的发明专利公开了一种磷系聚酯阻燃纤维,包括纤维主体,阻燃纤维的主体是聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二醇酯、聚对苯二甲酸丁二醇酯或阳离子改性聚对苯二甲酸乙二醇酯;在阻燃纤维的主体中含有磷系阻燃剂,磷系阻燃剂是2-羧乙基苯磷酸、2-羧乙基甲基磷酸酯或2-羧乙基甲基磷酸,生产方法包括将形成阻燃纤维主体的聚酯加入磷系阻燃剂,进行熔融纺丝,制得阻燃纤维原丝,并进一步经卷绕拉伸、网络得到阻燃聚酯长丝,即磷系聚酯阻燃纤维。虽然该发明所涉及的阻燃丝具有较好的可纺性能与阻燃效果,但其韧性较低,使用时易发生破裂,而且原料价格较高,大大提高了生产成本。
发明内容
本发明的目的是克服现有技术中存在的韧性较低、生产成本较高的缺陷与问题,提供一种韧性较高、生产成本较低的聚酯阻燃纤维。
为实现以上目的,本发明的技术解决方案是:一种服装用聚酯阻燃纤维,包括聚对苯二甲酸丁二酯与阻燃剂,其组成成分及重量份比例为:聚对苯二甲酸丁二酯40–60,聚丙烯树脂5–15,玻璃纤维20–30,阻燃剂10–20。
一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯50,聚丙烯树脂10,玻璃纤维25,阻燃剂15。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30–50,多磷酸铵10–20,羧乙基甲基磷酸20–40,柠檬酸10–20。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯40,多磷酸铵15,羧乙基甲基磷酸30,柠檬酸15。
与现有技术相比,本发明的有益效果为:
1、由于本发明一种服装用聚酯阻燃纤维的组成成分及重量份比例为:聚对苯二甲酸丁二酯50,聚丙烯树脂10,玻璃纤维25,阻燃剂15,制作时,先对聚对苯二甲酸丁二酯、聚丙烯树脂、玻璃纤维共熔以形成纤维丝,再混入阻燃剂进行熔融,然后纺丝以得到聚酯阻燃纤维,由于混入了玻璃纤维,因而提高了纤维丝的弹性,同时,严格限制了玻璃纤维的混入量,确保了纤维丝的强度。因此本发明的韧性较高。
2、由于本发明一种服装用聚酯阻燃纤维中采用的阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30–50,多磷酸铵10–20,羧乙基甲基磷酸20–40,柠檬酸10–20,与现有技术相比,不仅具有较高的耐高温性,而且对于价格较贵的苯基二氯磷酸酯,仅仅采用一部分,而以价格便宜的多磷酸铵、羧乙基甲基磷酸、柠檬酸作为另一部分,从而节省了原料价格。因此本发明的生产成本较低。
具体实施方式
以下结合具体实施方式对发明作进一步详细的说明。
一种服装用聚酯阻燃纤维,包括聚对苯二甲酸丁二酯与阻燃剂,其组成成分及重量份比例为:聚对苯二甲酸丁二酯40–60,聚丙烯树脂5–15,玻璃纤维20–30,阻燃剂10–20。
一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯50,聚丙烯树脂10,玻璃纤维25,阻燃剂15。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30–50,多磷酸铵10–20,羧乙基甲基磷酸20–40,柠檬酸10–20。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯40,多磷酸铵15,羧乙基甲基磷酸30,柠檬酸15。
实施例1:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯58,聚丙烯树脂6,玻璃纤维20,阻燃剂20。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯28,多磷酸铵9,羧乙基甲基磷酸38,柠檬酸20。
实施例2:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯42,聚丙烯树脂14,玻璃纤维28,阻燃剂12。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30,多磷酸铵20,羧乙基甲基磷酸20,柠檬酸10。
实施例3:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯50,聚丙烯树脂10,玻璃纤维25,阻燃剂15。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯36,多磷酸铵18,羧乙基甲基磷酸22,柠檬酸18。
实施例4:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯52,聚丙烯树脂8,玻璃纤维26,阻燃剂14。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯42,多磷酸铵18,羧乙基甲基磷酸29,柠檬酸12。
实施例5:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯45,聚丙烯树脂12,玻璃纤维25,阻燃剂16。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯40,多磷酸铵15,羧乙基甲基磷酸30,柠檬酸15。
实施例6:一种服装用聚酯阻燃纤维,其组成成分及重量份比例为:聚对苯二甲酸丁二酯58,聚丙烯树脂12,玻璃纤维26,阻燃剂12。
所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯35,多磷酸铵18,羧乙基甲基磷酸25,柠檬酸16。
Claims (4)
1.一种服装用聚酯阻燃纤维,包括聚对苯二甲酸丁二酯与阻燃剂,其特征在于其组成成分及重量份比例为:聚对苯二甲酸丁二酯40–60,聚丙烯树脂5–15,玻璃纤维20–30,阻燃剂10–20。
2.根据权利要求1所述的一种服装用聚酯阻燃纤维,其特征在于其组成成分及重量份比例为:聚对苯二甲酸丁二酯50,聚丙烯树脂10,玻璃纤维25,阻燃剂15。
3.根据权利要求1或2所述的一种服装用聚酯阻燃纤维,其特征在于所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯30–50,多磷酸铵10–20,羧乙基甲基磷酸20–40,柠檬酸10–20。
4.根据权利要求3所述的一种服装用聚酯阻燃纤维,其特征在于所述阻燃剂的组成成分及重量份比例为:苯基二氯磷酸酯40,多磷酸铵15,羧乙基甲基磷酸30,柠檬酸15。