CN102153723A - 喷涂型聚氨酯组合料 - Google Patents
喷涂型聚氨酯组合料 Download PDFInfo
- Publication number
- CN102153723A CN102153723A CN201110054684XA CN201110054684A CN102153723A CN 102153723 A CN102153723 A CN 102153723A CN 201110054684X A CN201110054684X A CN 201110054684XA CN 201110054684 A CN201110054684 A CN 201110054684A CN 102153723 A CN102153723 A CN 102153723A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- composite material
- polyurethane composite
- type polyurethane
- spray painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种喷涂型聚氨酯组合料,由结构型阻燃聚醚多元醇、结构型阻燃聚酯多元醇、胺类催化剂、添加型阻燃剂、反应型阻燃剂、一氟二氯乙烷组成。本发明是一种用于外墙保温的高阻燃B1级聚氨酯组合料。该产品应用于建筑外墙体系,可在钢板面、水泥面、砖面、木材面以及其他基材上施工,材料粘结力强,尺寸稳定性好。该产品不但具有普通聚氨酯保温材料导热系数低、保温性能优良的特点、而且更具有很高的阻燃等级,达到B1级阻燃要求,远远超过了国家规定的B2级要求。属于一种高科技的新型节能阻燃建材,该材料既符合节能减排要求,又符合安全环保要求,产品可以大力推广。
Description
技术领域
本发明涉及一种喷涂型聚氨酯组合料。
背景技术
当今世界绿色经济和低碳经济已成为全人类共同奋斗目标,也是我国未来经济发展的主流。节能减排是实现绿色和低碳经济的重要手段。而在各国能源消耗中建筑能耗占全社会总能耗中比例最大。为此,建筑节能已成为国家实现节能减排和低碳经济长期坚持的重大国策。建筑节能新材料已列为国家六大战略型新兴产业中重要内容
聚氨酯保温材料是目前世界上公认的最理想的保温材料,所以聚氨酯保温节能材料将是国家实施建筑节能目标不可缺少的重要材料。其中聚氨酯喷涂材料的施工最为方便,因此应用最为广泛。尽管现在普通的聚氨酯外墙喷涂保温材料的保温性能比其他的一些有机或者无机材料好,但是由于普通聚氨酯材料的阻燃性能达不到国家阻燃B2级的要求,因此没有推广前景。
发明内容
本发明的目的在于提供一种阻燃效果好的喷涂型聚氨酯组合料。
本发明的技术解决方案是:
一种喷涂型聚氨酯组合料,其特征是:由下列重量百分比的成分组成:
结构型阻燃聚醚多元醇 30~40%
结构型阻燃聚酯多元醇 20~30%
胺类催化剂 3~5%
添加型阻燃剂 10~15%
反应型阻燃剂 10~15%
一氟二氯乙烷 15~20%。
所述胺类催化剂为三乙烯二胺、二甲基环己烷、二甲基乙醇中的至少混合物。
添加型阻燃剂为阻燃剂TCCP,反应型阻燃剂为阻燃剂DMMP。
本发明是一种用于外墙保温的高阻燃B1级聚氨酯组合料。该产品应用于建筑外墙体系,可在钢板面、水泥面、砖面、木材面以及其他基材上施工,材料粘结力强,尺寸稳定性好。该产品不但具有普通聚氨酯保温材料导热系数低、保温性能优良的特点、而且更具有很高的阻燃等级,达到B1级阻燃要求,远远超过了国家规定的B2级要求。属于一种高科技的新型节能阻燃建材,该材料既符合节能减排要求,又符合安全环保要求,产品可以大力推广。
本发明产品的一些典型性能
该产品与黑料PAPI经喷涂机发泡成型后泡沫典型性能
下面结合实施例对本发明作进一步说明。
具体实施方式
实施例1:
在1000ml的混合釜中加入350g结构型阻燃聚醚多元醇;250g结构型阻燃聚酯多元醇;40g胺类催化剂(33%三乙稀二胺20g、二甲基环己胺20g); 100g阻燃剂TCPP;100g阻燃剂DMMP;160g发泡剂141B;适量水及硅油搅拌30分钟,即可制得浅黄色透明B1级聚氨酯喷涂组合料,物料粘度(25℃)120 mpa.s,比重1.15。
实施例2:
本方法生产的B1级聚氨酯喷涂组合料经喷涂设备发泡成型后的泡沫性能:
将上述方法生产的B1级聚氨酯喷涂组合料与黑料PAPI分别加入聚氨酯喷涂设备的料罐中,控制物料温度25-30℃;黑白料比例为1∶1对墙面进行喷涂发泡,泡沫层厚3-5mm。
泡沫的反应特性:
物料温度:POL/IS0℃ | 26/25 |
乳白时间S | 3 |
纤维时间S | 7 |
不粘时间S | 10 |
自由发泡密度Kg/m3 | 35 |
物料比例:POL/ISO | 1/1 |
成型后检测泡沫的各项性能
通过以上结果可以证明:本发明的B1级聚氨酯喷涂组合料制成的泡沫保温效果好,尺寸稳定性好,阻燃等级高。可以大量推广使用。
实施例3:
一种喷涂型聚氨酯组合料,:由下列重量百分比的成分组成:
结构型阻燃聚醚多元醇30~40%(例30%、35%、40%)
结构型阻燃聚酯多元醇20~30%(例20%、25%、30%)
胺类催化剂 3~5%(例3%、4%、5%)
添加型阻燃剂 10~15%(例10%、12%、15%)
反应型阻燃剂 10~15%(例10%、12%、15%)
一氟二氯乙烷 15~20%(例15%、18%、20%)。
所述胺类催化剂为三乙烯二胺、二甲基环己烷、二甲基乙醇中的至少混合物。其余同实施例1。
Claims (3)
1.一种喷涂型聚氨酯组合料,其特征是:由下列重量百分比的成分组成:
结构型阻燃聚醚多元醇 30~40%
结构型阻燃聚酯多元醇 20~30%
胺类催化剂 3~5%
添加型阻燃剂 10~15%
反应型阻燃剂 10~15%
一氟二氯乙烷 15~20%。
2.根据权利要求1所述的喷涂型聚氨酯组合料,其特征是:所述胺类催化剂为三乙烯二胺、二甲基环己烷、二甲基乙醇中的至少混合物。
3.根据权利要求1所述的喷涂型聚氨酯组合料,其特征是:添加型阻燃剂为阻燃剂TCCP,反应型阻燃剂为阻燃剂DMMP。