CN102151700A - 一种改善冷轧带钢冷轧平直度的方法 - Google Patents

一种改善冷轧带钢冷轧平直度的方法 Download PDF

Info

Publication number
CN102151700A
CN102151700A CN2010105754384A CN201010575438A CN102151700A CN 102151700 A CN102151700 A CN 102151700A CN 2010105754384 A CN2010105754384 A CN 2010105754384A CN 201010575438 A CN201010575438 A CN 201010575438A CN 102151700 A CN102151700 A CN 102151700A
Authority
CN
China
Prior art keywords
calender rolls
intermediate calender
convexity
row
cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010105754384A
Other languages
English (en)
Other versions
CN102151700B (zh
Inventor
杨东
刘素华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN201010575438A priority Critical patent/CN102151700B/zh
Publication of CN102151700A publication Critical patent/CN102151700A/zh
Application granted granted Critical
Publication of CN102151700B publication Critical patent/CN102151700B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种改善冷轧带钢冷轧平直度的方法，它是在轧制时，根据带钢宽度W，采用下述辊锥长L和锥度Y的第一列中间辊及凸度为H1的第二列下中间辊与凸度为H2的第二列上中间辊：I第一列中间辊的辊锥长L为L＝(1250-W)/2+230 单位mm；II第一列中间辊的辊锥的锥度Y为Y＝0.26％+(1250-W)×0.0001％；III第二列下中间辊的凸度H1为H1＝0.3+(1250-W)×0.001 单位mm；IV第二列上中间辊的凸度H2为H2＝H1-0.3 单位mm。本消除冷轧带钢冷轧平直度的方法轧制的带钢上下面均匀延伸，轧后板型平直，平直度达到10I以下。

Description

一种改善冷轧带钢冷轧平直度的方法
技术领域：
本发明涉及一种改善冷轧带钢冷轧平直度的方法，具体讲是一种消除冷轧带钢上下表面延伸不均的方法。
背景技术：
轧机在轧制带钢时，在轧制压力下，上辊系与下辊系之间的辊缝呈上下对称的鼓形，即辊缝的中部宽两边窄，轧制出的钢板中间厚两薄。现有的改善冷轧带钢冷轧平直度的方法，为了轧出良好的板型，在轧机上设计了多种板型控制机构，如上辊系与下辊系有一中间辊横向移动，用来控制带钢边部板型，AS-U凸度调整，用来控制带钢中部板型。对于AS-U凸度调整，现在轧机一般上下都有，执行对称控制。而对于早期的二十辊轧机，只有轧机上部设计有AS-U凸度调整，轧机在轧制带钢时，辊缝不再是上下对称的鼓形，上辊缝的鼓肚小于下辊缝的鼓肚，这样轧制时，带钢上下表面出现非对称延伸，下表面延伸多，上表面延伸少，轧制成的带钢的横截面呈向下弯的弧形，在经过退火酸洗工序时，易引起划伤，严重影响产品的质量。
发明内容
为了克服现有改善冷轧带钢冷轧平直度的方法的上述不足，本发明提供一种改善冷轧带钢冷轧平直度的方法，本发明轧制出的冷轧带钢板型平直度达到工艺要求，避免退火酸洗工序划伤。
本发明的技术方案是根据带钢的宽窄，在轧制带钢时，采用锥度不同的第一中间辊，并且采用第二中间自由辊凸度执行上下非对称设置。
本改善冷轧带钢冷轧平直度的方法是在轧制带钢时，它是在轧制时，根据带钢宽度W，采用下述辊锥长L和锥度Y的第一列中间辊及凸度为H1的第二列下中间辊与凸度为H2的第二列上中间辊，对第一列上下中间辊与第二列上中间辊和第二列下中间辊作了下述的设置：
I第一列上下中间辊的辊锥长L为
L＝(1250-W)/2+230单位mm；
II第一列上下中间辊的辊锥的锥度Y为
Y＝100％×(D1-d1)/2L＝0.26％+(1250-W)×0.0001％；
III第二列下中间辊的凸度H1为
H1＝DR2-dR2＝0.3+(1250-W)×0.001单位mm；
IV第二列上中间辊的凸度H2为
H2＝DH2-dH2＝H1-0.3单位mm。
第二列下中间辊的凸度比第二列上中间辊的凸度大。
根据上述的参数结合轧辊的直径或求出第一列上下中间辊的外形尺寸和第二列上下辊的外形尺寸。
本改善冷轧带钢冷轧平直度的方法，将第一列中间辊和第二列中间辊的辊形采取上述配置，使带钢轧制时轧机辊缝呈上下对称的鼓形，带钢上下面均匀延伸，轧后板型平直，平直度达到10I以下，可有效消除轧制时由于冷轧带钢上下表面延伸不均而形成的带钢弓形板型，避免了酸洗过程中划伤。
附图说明
图1是本改善冷轧带钢冷轧平直度的方法第一列中间辊轴向调节与第二列中间辊凸度调整原理图。
图2是第一列上中间辊外形图。
图3是第二列上中间辊外形图。
图4是第二列下中间辊外形图。
上述图中：
1-辊锥    2-第一列上中间辊  3-工作辊  4-带钢
5-工作辊  6-第二列上中间辊  7-鼓形面  8-辊锥
9-第一列下中间辊  10-第二列下中间辊  11-鼓形面
D1-第一列中间辊直径  d1-第一列中间辊的辊锥顶直径
L-第一列中间辊的辊锥长度  DH2-第二列上中间辊中部直径
dH2-第二列上中间辊两端的直径  DR2-第二列下中间辊中部直径
dR2-第二列下中间辊两端的直径
具体实施方式
下面结合实施例及其附图详细说明本发明的具体实施方式，但本发明的具体实施方式不局限于下述的实施例。
本发明在轧制宽度相同的带钢时，采用锥度相同的第一列上下中间辊，见图1与图2，并且采用凸度不同的第二列上中间辊6与第二列下中间辊10，第二列下中间辊10的凸度大于第二列上中间辊6的凸度，第二列上下中间辊的辊凸度为非对称设置。第二列上下中间辊的设置见图1，第二列上下中间辊的外形见图3与图4。轧制宽度不同的带钢时，采用锥度不同的第一列中间辊。下述三个实施例采用的是法国DMS公司的ZR22B52型号二十辊冷轧机。
实施例一
本实施例轧制的是不锈钢冷轧钢板，宽度为1050mm，厚度3.0mm。
I第一列(上下)中间辊的辊锥长L为
L＝(1250-W)/2+230＝(1250-1050)/2+230＝330mm；
II第一列(上下)中间辊的辊锥的锥度Y为
Y＝0.26％+(1250-W)×0.0001％＝0.26％+(1250-1050)×0.0001％＝0.28％；
III第二列下中间辊的凸度H1为
H1＝0.3+(1250-W)×0.001＝0.3+(1250-1050)×0.001＝0.5mm；
IV第二列上中间辊的凸度H2为
H2＝0.5-0.3＝0.2mm。
第二列下中间辊的凸度比第二列上中间辊的凸度大。
轧制出的带钢的平直度为9I。
实施例二
本实施例轧制的是不锈钢冷轧钢板，宽度为1250mm，厚度1.0mm。
I第一列(上下)中间辊的辊锥长L为
L＝(1250-W)/2+230＝(1250-1250)/2+230＝230mm；
II第一列(上下)中间辊的辊锥的锥度Y为
Y＝0.26％+(1250-W)×0.0001％＝0.26％+(1250-1250)×0.0001％＝0.26％；
III第二列下中间辊的凸度H1为
H1＝0.3+(1250-W)×0.001＝0.3+(1250-1250)×0.001＝0.3mm；
IV第二列上中间辊的凸度H2为
H2＝0.3-0.3＝0mm。
第二列下中间辊的凸度比第二列上中间辊的凸度大。
轧制出的带钢的平直度为8.5I。
实施例三
本实施例轧制的是不锈钢冷轧钢板，宽度为1180mm，厚度0.5mm。
I第一列(上下)中间辊的辊锥长L为
L＝(1250-W)/2+230＝(1250-1180)/2+230＝275mm；
II第一列(上下)中间辊的辊锥的锥度Y为
Y＝0.26％+(1250-W)×0.0001％＝0.26％+(1250-1180)×0.0001％＝0.267％；
III第二列下中间辊的凸度H1为
H1＝0.3+(1250-W)×0.001＝0.3+(1250-1180)×0.001＝0.37mm；
IV第二列上中间辊的凸度H2为
H2＝0.37-0.3＝0.07mm。
轧制出的带钢的平直度为9I。

Claims (1)

1.一种改善冷轧带钢冷轧平直度的方法，它是在轧制时，根据带钢宽度W，采用下述辊锥长L和锥度Y的第一列中间辊及凸度为H1的第二列下中间辊与凸度为H2的第二列上中间辊：
I第一列中间辊的辊锥长L为
L＝(1250-W)/2+230单位mm；
II第一列中间辊的辊锥的锥度Y为
Y＝0.26％+(1250-W)×0.0001％；
III第二列下中间辊的凸度H1为
H1＝0.3+(1250-W)×0.001单位mm；
IV第二列上中间辊的凸度H2为
H2＝H1-0.3单位mm。
CN201010575438A 2010-12-01 2010-12-01 一种改善冷轧带钢冷轧平直度的方法 Active CN102151700B (zh)