CN102140025A - Alkali-resistant high-class ceramic tile sealant - Google Patents
Alkali-resistant high-class ceramic tile sealant Download PDFInfo
- Publication number
- CN102140025A CN102140025A CN2010101034596A CN201010103459A CN102140025A CN 102140025 A CN102140025 A CN 102140025A CN 2010101034596 A CN2010101034596 A CN 2010101034596A CN 201010103459 A CN201010103459 A CN 201010103459A CN 102140025 A CN102140025 A CN 102140025A
- Authority
- CN
- China
- Prior art keywords
- alkali
- ceramic tile
- sealant
- resistant high
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method of an alkali-resistant high-class ceramic tile sealant which has alkali-resistant property, mildew-resistant property, waterproof property and weather-resistant property. The alkali-resistant high-class ceramic tile sealant is mixed and packaged according to the weight ratio of various materials by using equipment in a plant and can be applied to construction by stirring with water according to the proportion of dry powder sealant to water of 1:(0.15-0.20) when in use. The alkali-resistant high-class ceramic tile sealant solves the industry problem of alkali return of the traditional cement-based ceramic tile sealant and achieves the purposes of perfectly reflecting the visual effect of buildings and effectively reducing potential safety hazards caused by ceramic tile falling.
Description
Technical field
The present invention relates to a kind of building dry-mixed mortar material, specifically a kind of preparation method with senior tile grout of alkali resistance.
Technical background
Ceramic tile has become one of important architectural coating finishing material in the buildings of China, is widely used in the Decorating Project at positions such as the interior exterior wall of buildings and ground.At present, the used spackling of tile decorative surface is to adopt Portland cement, building fine sand, mineral dye through hybrid packed mostly, temper during use as the packing material of ceramic tile seam, use the construction of this tile grout after finishing long time through wind, Exposure to Sunlight, drench with rain, under the influence of the factor of natural environment of freeze thawing etc., the large-area whiting of ceramic tile the metope accumulation of salt in the surface soil, shrinkage crack just can occur, go mouldy even ceramic tile quality problems and potential safety hazard such as come off.For the design effect that obtains and embody buildings effectively reduces potential safety hazard, it is just particularly important to prepare the high-quality tile grout of a kind of not accumulation of salt in the surface soil.
Summary of the invention
The object of the present invention is to provide a kind of preparation method with senior tile grout of alkali resistant type of alkali resistant, anti-mildew, waterproof, weather resistance.
The used starting material of the senior tile grout of alkali resistant type of the present invention mainly comprise: ordinary Portland cement, washed-out sand, flyash, dicalcium powder, pigment, organosilicon, water reducer, redispersable latex powder, Vltra tears, mould inhibitor, calcium formiate.Each raw-material weight percent of this spackling is respectively ordinary Portland cement 35%, washed-out sand 40.45%, flyash 15%, dicalcium powder 5%, mineral dye 2.5%, organosilicon 0.3%, water reducer 0.2%, redispersable latex powder 0.5%, Vltra tears 0.05%, mould inhibitor 0.5%, calcium formiate 0.5%.
Embodiment
The used hydraulic cementing materials of the present invention is a PO32.5 cement, and aggregate adopts the washed-out sand of 70-100 order, and active filler is the low calcium fly ash of secondary, and stopping composition adopts 325 order dicalcium powders, and pigment adopts inorganic oxide pigments, and hydrophobic, alkaline-resisting auxiliary agent adopt
Trade mark organosilicon, water reducer is selected for use
Trade mark colleges and universities water reducer, flexible tackify material selection 5044N redispersable latex powder, it is the HPMC40000S methylcellulose gum that water-holding agent is selected model for use, and mould inhibitor is selected the MB-P100 trade mark for use, and the calcium formiate model is BS32X21133-1.But will be understood that specific embodiment only is an illustrative, and should not provide constraints to protection scope of the present invention.
Embodiment
The senior tile grout specific embodiment of alkali resistant type of the present invention according to weight percent is:
PO32.5 cement 35%
70-100 order washed-out sand 40.45%
Second class powered coal ash 15%
325 order dicalcium powders 5%
Ferric oxide mineral dye 2.5%
Organosilicon 0.3%
High efficiency water reducing agent 0.2%
Redispersable latex powder 5044N 0.5%
Methylcellulose gum HPMC40000S 0.05%
MB-P100 mould inhibitor 0.5%
BS32X21133-1 calcium formiate 0.5%
Utilize the dry-mixed mortar whipping device to weigh in proportion according to above weight percent in factory, the bucket packing is divided in the back of mixing, stir, and promptly obtains the senior tile grout of alkali resistant type.During use in the dry powder spackling: the ratio of water=1: 0.15-0.20 adds water and stirs and get final product construction application.
The technical indicator of this spackling and the contrast of existing " ceramic wall and floor bricks spackling " JC/T1004-2006 index request are as follows:
The senior tile grout of alkali resistant type of the present invention preparation has alkali resistant, anti-mildew, waterproof, characteristics such as weather-proof, can be widely used in the filling in ceramic tile, stone material and other building materials slit at dry and moist position, has very high promotion and application value.
Claims (1)
1. the preparation method of the senior tile grout of alkali resistant type, the weight percent of its material is respectively ordinary Portland cement 35%, washed-out sand 40.45%, flyash 15%, dicalcium powder 5%, mineral dye 2.5%, organosilicon 0.3%, water reducer 0.2%, redispersable latex powder 0.5%, Vltra tears 0.05%, mould inhibitor 0.5%, calcium formiate 0.5%.