CN110092619A - A kind of tile grout and its construction method - Google Patents
A kind of tile grout and its construction method Download PDFInfo
- Publication number
- CN110092619A CN110092619A CN201910501647.5A CN201910501647A CN110092619A CN 110092619 A CN110092619 A CN 110092619A CN 201910501647 A CN201910501647 A CN 201910501647A CN 110092619 A CN110092619 A CN 110092619A
- Authority
- CN
- China
- Prior art keywords
- parts
- tile
- water
- tile grout
- grout
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of tile grouts, belong to gap filler technical field, including below according to the raw material of parts by weight: 200-400 parts of cement, 400-500 parts of quartz sand, 100-255 parts of coarse whiting, 10-50 parts of redispersable latex powder, 0.1-0.6 parts of methylcellulose, 1-15 parts of bentonite, 5-15 parts of white lime, 0.1-1 parts of water-reducing agent；Tile grout produced by the present invention has good wearability and adhesiveness, while also having enough non-deformabilities and high tenacity；With the solving wall hidden danger of sweat, and have beautification effect, and facilitate the cleaning to ceramic tile.
Description
Technical field
The present invention relates to gap filler technical field, specifically a kind of tile grout and its construction method.
Background technique
Gap filler is also referred to as caulking agent, jointing agent, for filling up between the ceramic tile or natural stone being attached on wall or floor
Joint filler.Cement base tile grout appropriate is matched suitable for indoor and outdoors.With the ornament materials phase such as ceramic tile, stone material
Cooperation provides bonding, antiseepage etc. between beautiful surface and tapestry brick, and good tile grout can also reduce entire wall
Stress in wall or floor covering protects tile base layer material from mechanical failure and water penetration into whole building institute band
The negative effect come.
Ceramic tile is one of most common ornament materials, when previous ceramic tile joint filling multi-purpose white cement powder.These are put on ceramic tile seam
The white cement on surface is simultaneously uncured, and cohesive force and waterproofness are poor, and after dehydration or chance cold shrinkage and thermal expansion will be cracked, causes outer
The infiltration of the Wall or floor tiles such as wall, bathroom.In recent years, gradually goed deep into design, a large amount of building exterior wall and interior decoration paving
It is increasingly particular about, just necessarily becomes the integrated beauty of prominent outdoor tile using color tile grout or the preferred of lines sense produces
Product.
The cement mo(u)ld product of dry powder-shaped, the joint filling toner being made of cement, fine sand and polymeric additive, coloration is high, matter
Sense is fine and smooth, and there are many colors can enhance the decorative effect of plane materiel, part suitable for the ceramic tile and stone material seam of most of type
Premium quality product and have the function of water proof anti-seepage and antifungi, after it and water mixed construction, with certain flexibility and impervious
Ability can enhance the cohesive force between ceramic tile and basal plane, ceramic tile and ceramic tile, and can prevent ground and brick, stone from waiting for is not specification
To extend the service life of facing, the unit area of tile grout takes swell-shrinking deformation between the big brick of size, stone
It is high with lower cost performance, it is one of the material that can be more early widely accepted with apply in dry powder and mortar；Existing gap filler is wear-resisting
Property is poor, causes to be easy to appear loosening between ceramic tile, therefore, it is proposed that a kind of tile grout and its construction method.
Summary of the invention
The purpose of the present invention is to provide a kind of tile grout and its construction methods, to solve to mention in above-mentioned background technique
Out the problem of.
To achieve the above object, the invention provides the following technical scheme:
A kind of tile grout, including below according to the raw material of parts by weight: 200-400 parts of cement, quartz sand 400-500
Part, 100-255 parts of coarse whiting, 10-50 parts of redispersable latex powder, 0.1-0.6 parts of methylcellulose, 1-15 parts of bentonite, ripe stone
It is 5-15 parts grey, 0.1-1 parts of water-reducing agent.
As a further solution of the present invention: including below according to the raw material of parts by weight: 350 parts of cement, quartz sand 454.5
Part, 150 parts of coarse whiting, 25 parts of redispersable latex powder, 0.3 part of methylcellulose, 10 parts of bentonite, 10 parts of white lime, water-reducing agent
0.3 part.
As further scheme of the invention: water-reducing agent is MF10 water-reducing agent.
The preparation method of the tile grout, steps are as follows:
S1, it is carried out afterwards for 24 hours in tile laying completion, first cleaning ceramic tile gap, dust, the ceramic tile for removing ceramic tile surface are viscous
Tie agent and grease stain；
S2, tile grout is taken, be put into blender, then added water and stirred into blender, the rate of blender is
500-1500r/min, stirring stands 5min to without blocks of solid, blender is then shut off in blender, spare；
S3, the gap filler being stirred is inserted in ceramic tile gap with rubber chincing iron, is turned by diagonal or with annular
Tile grout is filled up gap by flowing mode, and solidifies preceding wet sponge or wet cloth wiping ceramic tile surface, rubber in tile grout
It should be rinsed immediately with clear water after glue chincing iron use；
After S4, tile grout solidification, the tile grout of surface dusting is wiped with dry cloth, is then carried out with water
Last cleaning.
Compared with prior art, the beneficial effects of the present invention are: tile grout produced by the present invention is with good resistance to
Mill property and adhesiveness, while also there is enough non-deformabilities and high tenacity；With the solving wall hidden danger of sweat, and have beauty
Change effect, and facilitates the cleaning to ceramic tile.
Specific embodiment
Technical solution of the present invention is described in more detail With reference to embodiment, it is clear that described
Embodiment be only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ability
Domain those of ordinary skill every other embodiment obtained without making creative work, belongs to guarantor of the present invention
The range of shield.
Embodiment 1
A kind of tile grout, including below according to the raw material of parts by weight: including below according to the raw material of parts by weight: cement
350 parts, 454.5 parts of quartz sand, 150 parts of coarse whiting, 25 parts of redispersable latex powder, 0.3 part of methylcellulose, 10 parts of bentonite,
10 parts of white lime, 0.3 part of water-reducing agent.
Water-reducing agent is MF10 water-reducing agent
In the present embodiment, the preparation method of the tile grout, steps are as follows:
S1, it is carried out afterwards for 24 hours in tile laying completion, first cleaning ceramic tile gap, dust, the ceramic tile for removing ceramic tile surface are viscous
Tie agent and grease stain；
S2, tile grout is taken, be put into blender, then added water and stirred into blender, the rate of blender is
1500r/min, stirring stands 5min to without blocks of solid, blender is then shut off in blender, spare；
S3, the gap filler being stirred is inserted in ceramic tile gap with rubber chincing iron, is turned by diagonal or with annular
Tile grout is filled up gap by flowing mode, and wipes ceramic tile surface, rubber joint filling with wet sponge before tile grout solidification
It should be rinsed immediately with clear water after knife use；
After S4, tile grout solidification, the tile grout of surface dusting is wiped with dry cloth, is then carried out with water
Last cleaning.
Embodiment 2
A kind of tile grout, including below according to the raw material of parts by weight: 200 parts of cement, 400 parts of quartz sand, coarse whiting 100
Part, 10 parts of redispersable latex powder, 0.1 part of methylcellulose, 1 part of bentonite, 5 parts of white lime, 0.1 part of water-reducing agent.
Water-reducing agent is MF10 water-reducing agent
In the present embodiment, the preparation method of the tile grout, steps are as follows:
S1, it is carried out afterwards for 24 hours in tile laying completion, first cleaning ceramic tile gap, dust, the ceramic tile for removing ceramic tile surface are viscous
Tie agent and grease stain；
S2, tile grout is taken, be put into blender, then added water and stirred into blender, the rate of blender is
1500r/min, stirring stands 5min to without blocks of solid, blender is then shut off in blender, spare；
S3, the gap filler being stirred is inserted in ceramic tile gap with rubber chincing iron, is turned by diagonal or with annular
Tile grout is filled up gap by flowing mode, and wipes ceramic tile surface, rubber chincing iron with wet cloth before tile grout solidification
It should be rinsed immediately with clear water after use；
After S4, tile grout solidification, the tile grout of surface dusting is wiped with dry cloth, is then carried out with water
Last cleaning.
Embodiment 3
A kind of tile grout, including below according to the raw material of parts by weight: 400 parts of cement, 500 parts of quartz sand, coarse whiting 255
Part, 50 parts of redispersable latex powder, 0.6 part of methylcellulose, 15 parts of bentonite, 15 parts of white lime, 1 part of water-reducing agent.
Water-reducing agent is MF10 water-reducing agent
In the present embodiment, the preparation method of the tile grout, steps are as follows:
S1, it is carried out afterwards for 24 hours in tile laying completion, first cleaning ceramic tile gap, dust, the ceramic tile for removing ceramic tile surface are viscous
Tie agent and grease stain；
S2, tile grout is taken, be put into blender, then added water and stirred into blender, the rate of blender is
1000r/min, stirring stands 5min to without blocks of solid, blender is then shut off in blender, spare；
S3, the gap filler being stirred is inserted in ceramic tile gap with rubber chincing iron, is turned by diagonal or with annular
Tile grout is filled up gap by flowing mode, and wipes ceramic tile surface, rubber joint filling with wet sponge before tile grout solidification
It should be rinsed immediately with clear water after knife use；
After S4, tile grout solidification, the tile grout of surface dusting is wiped with dry cloth, is then carried out with water
Last cleaning.
Comparative example 1
Methylcellulose is free of in raw material, other are same as Example 3.
Comparative example 2
Redispersable latex powder is free of in raw material, other are same as Example 3.
Comparative example 3
Redispersable latex powder and methylcellulose are free of in raw material, other are same as Example 5.
Tile grout prepared by 1-3 of the embodiment of the present invention and comparative example 1-3 is tested for the property, test result is such as
Table 1, obtained test result is as follows, and (wherein, wearability test standard is JC/T1004-2017-7.2, flexural strength and anti-
Compressive Strength testing standard is JC/T1004-2017-7.3, and the testing standard of shrinkage value is JC/T1004-2017-7.4, water absorption
Testing standard be JC/T1004-2017-7.5).
1 performance test table of table
In conclusion tile grout produced by the present invention has good wearability and adhesiveness, while also there is foot
Enough non-deformabilities and high tenacity；With the solving wall hidden danger of sweat, and have beautification effect, and facilitate to the clear of ceramic tile
It washes.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of tile grout, which is characterized in that including below according to the raw material of parts by weight: 200-400 parts of cement, quartz sand
400-500 parts, 100-255 parts of coarse whiting, 10-50 parts of redispersable latex powder, 0.1-0.6 parts of methylcellulose, bentonite 1-15
Part, 5-15 parts of white lime, 0.1-1 parts of water-reducing agent.
2. tile grout according to claim 1, which is characterized in that including below according to the raw material of parts by weight: cement
350 parts, 454.5 parts of quartz sand, 150 parts of coarse whiting, 25 parts of redispersable latex powder, 0.3 part of methylcellulose, 10 parts of bentonite,
10 parts of white lime, 0.3 part of water-reducing agent.
3. tile grout according to claim 2, which is characterized in that water-reducing agent is MF10 water-reducing agent.
4. a kind of construction method of tile grout a method according to any one of claims 1-3, which is characterized in that steps are as follows:
S1, it is carried out afterwards for 24 hours in tile laying completion, first cleaning ceramic tile gap, removes dust, the ceramic tile bond of ceramic tile surface
And grease stain；
S2, tile grout is taken, be put into blender, then added water and stirred into blender, without block in stirring to blender
Shape solid is then shut off blender, stands, spare；
S3, the gap filler being stirred is inserted in ceramic tile gap with rubber chincing iron, by diagonal or with annular rotation side
Tile grout is filled up gap by formula, and ceramic tile surface is wiped before tile grout solidifies, and rubber chincing iron uses rear Ying Li
Rinsed with clear water；
After S4, tile grout solidification, the tile grout of surface dusting is wiped with dry cloth, is then carried out finally with water
Cleaning.
5. the construction method of tile grout according to claim 4, which is characterized in that in step S2, the speed of blender
Rate is 500-1500r/min.
6. the construction method of tile grout according to claim 5, which is characterized in that in step S2, time of repose is
5min。
7. the construction method of tile grout according to claim 4, which is characterized in that in step S3, with wet sponge or
Wet cloth wipes ceramic tile surface.