CN102140023A - 纤维水泥外墙板通体着色工艺 - Google Patents
纤维水泥外墙板通体着色工艺 Download PDFInfo
- Publication number
- CN102140023A CN102140023A CN 201010103243 CN201010103243A CN102140023A CN 102140023 A CN102140023 A CN 102140023A CN 201010103243 CN201010103243 CN 201010103243 CN 201010103243 A CN201010103243 A CN 201010103243A CN 102140023 A CN102140023 A CN 102140023A
- Authority
- CN
- China
- Prior art keywords
- wall panel
- external wall
- fiber cement
- product
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种纤维水泥外墙板通体着色工艺，包括如下步骤：1)在生产纤维水泥外墙板的原材料粉料中掺加调配好的无机颜料，并通过高速搅拌让其吸附在其它颗粒表面，从而达到充分分散的目的，然后再加水搅拌；2)原材料经过捏合和混练工序，进入挤出机挤出成型；3)在蒸压釜中对产品进行蒸汽常压养护和压蒸养护，以加快并提高产品强度；4)最后对产品表面进行处理，并喷涂无色清水漆。本发明通过把无机颜料加入到纤维水泥外墙板中，采用针对性的生产和养护工艺，使得纤维水泥外墙板通体一色，色泽鲜艳，美观大方，且能经受高温不褪色，解决了传统使用涂料着色的外墙板表面涂层易老化、褪色和剥离的问题。
Description
技术领域
本发明涉及一种纤维水泥外墙板通体着色工艺。
背景技术
纤维水泥外墙板在生产的过程中需要着色，目前的处理通常是通过涂料着色来进行处理，由于涂料属于有机物，其耐久性较差，使用时间一长外墙板就容易出现表面涂层老化、褪色和剥离的问题。而且纤维水泥外墙板的使用寿命为50年，而普通涂料的寿命仅为8-10年，高档涂料的使用寿命也超不过20年，在纤维水泥外墙板的使用寿命内，至少需要3-5次修补涂装，造成了后期维护成本过高。
发明内容
本发明要解决的技术问题是提供一种纤维水泥外墙板通体着色工艺，经过本发明处理的外墙板表面涂层不会出现老化、褪色或是剥离。
为了解决上述问题，本发明提供了一种纤维水泥外墙板通体着色工艺包括如下步骤：
1)在生产纤维水泥外墙板的原材料粉料中掺加调配好的耐高温、耐碱的无机颜料，并通过高速搅拌让其吸附在其它颗粒表面，从而达到充分分散的目的，然后再加水搅拌。此处搅拌机转速应在750转/分钟以上；原材料粉料的颗粒大小应在200目-400目左右，含水率应在5％以下；否则会导致无机颜料分散不均，产生色差。
2)接下来原材料经过捏合和混练工序，使颜料与原材料进一步充分融合，避免出现颜色不均的问题，然后进入挤出机挤出成型；
3)在蒸压釜中对产品进行蒸汽常压养护和压蒸养护，以加快并提高产品强度；
4)最后对产品表面进行处理，并喷涂无色清水漆。
优选地，在通过所述步骤3)进行蒸汽常压养护时，湿度应控制在90％以下，以免产品表面水分过多导致内外层颜色不一致；进行压蒸养护时，先排尽所述蒸压釜中空气后再升压，否则易在产品表面产生杂色。
优选地，在通过所述步骤4)中表面喷涂的无色清水漆需具有高渗透性，且在产品表面不形成涂层(否则颜色失真)，同时能对产品表层毛细管进行有效封闭。经无色清水漆涂装过的产品表面，水的浸润角小于30度。
本发明通过把无机颜料加入到纤维水泥外墙板中，采用针对性的生产和养护工艺，使得纤维水泥外墙板通体一色，色泽鲜艳，美观大方，且能经受高温不褪色。因其为通体着色，且为无机材料，其颜色可持续产品的整个使用寿命。解决了传统使用涂料着色的外墙板表面涂层寿命短、易老化、褪色、剥离和需要多次修补涂装的问题。
具体实施方式
本发明的一种纤维水泥外墙板通体着色工艺具体包括如下工艺步骤：
首先，在生产纤维水泥外墙板的原材料粉料中掺加调配好的无机颜料，并通过高速搅拌让其吸附在粉料颗粒表面，从而达到是无机颜料充分分散的目的，然后再加水搅拌。
然后将充分混合了无机颜料的原材料经过捏合和混练工序，进入挤出机挤出成型。
接下来再在蒸压釜中对挤压成型的产品进行蒸汽常压养护和压蒸养护来加快成型时间并提高产品强度。在压蒸养护时，应先排尽蒸压釜中空气后再升压。
最后对产品表面进行处理，并喷涂无色清水漆。
上述蒸汽常压养护和压蒸养护通过如下步骤来进行：
首先，在纤维水泥外墙板挤出成型后，在20-30℃下对纤维水泥外墙板进行10-20小时的低温蒸汽养护，养护湿度控制在60-80％，待纤维水泥外墙板中水泥终凝后，再进入下一养护阶段；
2)在60-90℃下进行5-15小时的高温蒸汽养护，养护湿度控制在70-90％，以避免湿度过大造成纤维水泥外墙板吸水饱和影响强度。
本发明通过把无机颜料加入到纤维水泥外墙板中，采用针对性的生产和养护工艺，使得纤维水泥外墙板通体一色，色泽鲜艳，美观大方，且能经受高温不褪色，解决了传统使用涂料着色的外墙板表面涂层易老化、褪色和剥离的问题。
综上所述，以上仅为本发明的较佳实施例而已，并非用于限定本发明的保护范围，因此，凡在本发明的精神和原则之内所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种纤维水泥外墙板通体着色工艺，包括如下步骤：
1)在生产纤维水泥外墙板的原材料粉料中掺加调配好的无机颜料，并通过高速搅拌让其吸附在其它颗粒表面，从而达到充分分散的目的，然后再加水搅拌；
2)原材料经过捏合和混练工序，进入挤出机挤出成型；
3)在蒸压釜中对产品进行蒸汽常压养护和压蒸养护，已加快并提高产品强度；
4)最后对产品表面进行处理，并喷涂无色清水漆。
2.如权利要求1所述的工艺，其特征在于，在通过所述步骤3)进行压蒸养护时，先排尽所述蒸压釜中空气后再升压。