CN102134302B - 一种防静电海绵 - Google Patents

一种防静电海绵 Download PDF

Info

Publication number
CN102134302B
CN102134302B CN2010100195410A CN201010019541A CN102134302B CN 102134302 B CN102134302 B CN 102134302B CN 2010100195410 A CN2010100195410 A CN 2010100195410A CN 201010019541 A CN201010019541 A CN 201010019541A CN 102134302 B CN102134302 B CN 102134302B
Authority
CN
China
Prior art keywords
parts
sponge
alkaline metal
static
electrostatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2010100195410A
Other languages
English (en)
Other versions
CN102134302A (zh
Inventor
卫建东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN SUNNY WORLD INDUSTRIAL Co Ltd
Original Assignee
DONGGUAN SUNNY WORLD INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN SUNNY WORLD INDUSTRIAL Co Ltd filed Critical DONGGUAN SUNNY WORLD INDUSTRIAL Co Ltd
Priority to CN2010100195410A priority Critical patent/CN102134302B/zh
Publication of CN102134302A publication Critical patent/CN102134302A/zh
Application granted granted Critical
Publication of CN102134302B publication Critical patent/CN102134302B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防静电海绵,由以下重量份的原料组成:聚醚多元醇800~110份、甲苯二异氰酸酯60~70份、聚氧硅烷1~5份、三乙烯二胺0.1~0.5份、辛酸亚锡0.1~1.0份、碱性金属盐2~8份、水4~5份,本发明通过在传统海绵发泡原料中加入防静电的碱性金属盐制成的防静电海绵,用于电子等产品的包装,使电子等产品运输过程中不产生静电,从而更好地保护电子产品,具有弹性高、防静电效果好、安全环保等优点。

Description

一种防静电海绵
技术领域
本发明属于海绵材料,更具体的说是一种防静电海绵。
背景技术
普通海绵作为包装材料时在货物的运输过程中与外围的包装物和所包装的物件会产生磨擦。在这种磨擦过程中会自然产生静电。这种静电虽然小,但对一些敏感的电子零件还是会产生影响甚至造成损坏。
目前市面上也有一些类似的防静电海绵在推广使用,如中国专利,申请号:03228523.X,专利名称为:一种防静电垫,该专利公开了一种具有防静电功能的台垫或地垫,其包括防静电层和导电层,防静电层和导电层之间有一层微孔结构的海绵型防静层,塑料防静电层、海绵型防静电层、塑料导电层三层层叠热压结合成一体,该专利产品手感柔软,平整度高,避免了因绉折产生导电率不均匀的问题,既保证了良好持久的防静电性能,又延长了产品使用寿命,其不足之处该专利产品结构复杂,使用大量的塑胶导致造价高,难以大范围推广使用。
防静电的包装材料除了防静电海绵外,还包括其他同类的产品,如中国专利申请号为:200610008067.5,专利名称为:一种防静电包装材料,公开了防静电包装材料,包含至少一层导电聚合物层,导电聚合物层由碳粉、聚氨酯、添加剂和溶剂组成,具有较好的防止静电的作用,但生产工艺比较复杂、防震效果差。
发明内容
本发明提供一种防静电海绵,有效解决了上述技术问题的不足,具有生产工艺简单、生产成本低、弹性高、防震效果好、防静电效果好的优点。
为了达到上述目的,通过下述方案实现:
一种防静电海绵,由下列重量份的原料组成:
聚醚多元醇        80~110份
甲苯二异氰酸酯    60~70份
聚氧硅烷          1~5份
三乙烯二胺        0.1~1.0份
辛酸亚锡          0.1~1.0份
碱性金属盐        2~8份
水                4~5份;
所述的碱性金属盐为碳酸钾、碳酸钠、乙酸钠的任意一种。
更优的,一种防静电海绵,由下列重量份的原料组成:
聚醚多元醇        90~100份
甲苯二异氰酸酯    65~70份
聚氧硅烷          1~5份
三乙烯二胺        0.1~0.5份
辛酸亚锡          0.1~0.6份
碱性金属盐        3~5份
水                4~5份。
一种防静电海绵,包括以下制备步骤:
A、依上述配方比例将聚醚多元醇、聚氧硅烷、三乙烯二胺、辛酸亚锡、碱性金属盐和水依次加入搅拌机内,转速为200~300转/分搅拌1~10分钟,让以上材料充分混合;
B、再将甲苯二异氰酸酯依配方比例加入搅拌机中,提速速度为1300~1500转/分钟,搅拌3~5秒;
C、将混合料倒入定型模具内成形,冷却至室温后移出,再进行切割加工,即得到防静电海绵。
本发明的有益效果在于:通过在传统海绵发泡原料中加入防静电的碱性金属盐制成的防静电海绵,用于电子等产品的包装,使电子等产品运输过程中不产生静电,从而更好地保护电子产品,因此,本发明具有生产工艺简单、生产成本低、弹性高、防震效果好、防静电效果好的优点。
具体实施方式
下面结合实例对本发明作进一步的描述,但本发明不仅限于此实例:
实施例一:
第一步:将聚醚多元醇90份、聚氧硅烷3份、三乙烯二胺0.5份、辛酸亚锡1份、碳酸钾2份和水4份依次加入搅拌机内,转速为200转/分搅拌8分钟,让以上材料充分混合;
第二步:再将甲苯二异氰酸酯60份加入搅拌机中,提速速度为1300转/分钟,搅拌3秒;
第三步:将混合料倒入定型模具内成形,冷却至室温后移出,再进行切割加工,即得到防静电海绵。
实施例二:
第一步:将聚醚多元醇100份、聚氧硅烷4份、三乙烯二胺0.5份、辛酸亚锡1份、碳酸钠3份和水4份依次加入搅拌机内,转速为250转/分搅拌6分钟,让以上材料充分混合;
第二步:再将甲苯二异氰酸酯65份加入搅拌机中,提速速度为1400转/分钟,搅拌3秒;
第三步:将混合料倒入定型模具内成形,冷却至室温后移出,再进行切割加工,即得到防静电海绵。
实施例三:
第一步:将聚醚多元醇110份、聚氧硅烷4份、三乙烯二胺0.5份、辛酸亚锡0.5份、乙酸钠5份和水4份依次加入搅拌机内,转速为300转/分搅拌5分钟,让以上材料充分混合;
第二步:再将甲苯二异氰酸酯70份加入搅拌机中,提速速度为1500转/分钟,搅拌5秒;
第三步:将混合料倒入定型模具内成形,冷却至室温后移出,再进行切割加工,即得到防静电海绵。
实施例一、实施例二、实施例三检测效果见下表:
  检测指标   实施例一   实施例二   实施例三
  硬度   40kpa   45kpa   50kpa
  回弹   36%   34%   32%
  电阻值   1012欧姆   1010欧姆   108欧姆
由上表可以看出,实施例一、实施例二、实施例三中硬度、回弹、欧姆值三个主要指标显示良好,具有较好的扩电性功能。
以上内容仅为本发明的较佳实施例,对于本领域的普通技术人员,依据本发明的思想,在具体实施方式及应用范围上均会有改变之处,本实施例内容不应理解为对本发明的限制。

Claims (1)

1.一种防静电海绵,其特征在于:由下列重量份的原料组成:
聚醚多元醇                 80~110份
甲苯二异氰酸酯           60~70份
聚氧硅烷                     1~5份
三乙烯二胺                  0.1~1.0份
辛酸亚锡                      0.1~1.0份
碱性金属盐                  2~8份
水                                 4~5份;
所述的碱性金属盐为碳酸钾、碳酸钠的任意一种;
所述的一种防静电海绵包括以下制备步骤:
A、依上述配方比例将聚醚多元醇、聚氧硅烷、三乙烯二胺、辛酸亚锡、碱性金属盐和水依次加入搅拌机内,转速为200~300转/分搅拌1~10分钟,让以上材料充分混合;
B、再将甲苯二异氰酸酯依配方比例加入搅拌机中,提速转速为1300~1500转/分钟,搅拌3~5秒;
C、将混合料倒入定型模具内成形,冷却至室温后移出,再进行切割加工,即得到防静电海绵。
CN2010100195410A 2010-01-21 2010-01-21 一种防静电海绵 Expired - Fee Related CN102134302B (zh)