CN102121279B - 挤塑聚苯板外墙外保温系统及其制作工艺 - Google Patents

挤塑聚苯板外墙外保温系统及其制作工艺 Download PDF

Info

Publication number
CN102121279B
CN102121279B CN2011100213790A CN201110021379A CN102121279B CN 102121279 B CN102121279 B CN 102121279B CN 2011100213790 A CN2011100213790 A CN 2011100213790A CN 201110021379 A CN201110021379 A CN 201110021379A CN 102121279 B CN102121279 B CN 102121279B
Authority
CN
China
Prior art keywords
layer
anticracking grout
extruded polystyrene
heat preservation
external heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2011100213790A
Other languages
English (en)
Other versions
CN102121279A (zh
Inventor
李月英
杨升辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIMEN BIWEI INTELLECTUAL PROPERTY SERVICE Co.,Ltd.
Original Assignee
BEIJING SOLID BUILDING ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING SOLID BUILDING ENGINEERING Co Ltd filed Critical BEIJING SOLID BUILDING ENGINEERING Co Ltd
Priority to CN2011100213790A priority Critical patent/CN102121279B/zh
Publication of CN102121279A publication Critical patent/CN102121279A/zh
Application granted granted Critical
Publication of CN102121279B publication Critical patent/CN102121279B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种挤塑聚苯板外墙外保温系统,包括粘结层、保温层、抗裂防护层和饰面层,所述粘结层与基层墙体相邻,所述保温层位于所述粘结层与所述抗裂防护层之间,所述抗裂防护层位于所述保温层与所述饰面层之间。本发明挤塑聚苯板外墙外保温系统的制作工艺包括如下步骤:(a)在基层墙体上刷粘结砂浆构成粘结层;(b)在粘结层上粘贴挤塑聚苯保温板构成保温层;(c)在所述保温层上抹一层抗裂砂浆,并在抗裂砂浆层上压上耐碱玻纤网格布或热镀锌钢丝网,构成抗裂防护层;(d)在抗裂防护层上铺贴饰面层。本发明的挤塑聚苯板外墙外保温系统强度很大,并且表面的粘贴性好,可以粘贴面砖等;非常适于作为建筑物的装饰材料。

Description

挤塑聚苯板外墙外保温系统及其制作工艺
技术领域
本发明涉及一种建筑物外墙外保温系统及其制作工艺,特别涉及挤塑聚苯板外墙外保温系统及其制作工艺。 
背景技术
在现有技术中,挤塑板具有一定的脆性,并且表面比较光滑导致粘贴性及附着性比较差,虽然其具有较好的保温性能,但是其并不适合作为建筑物的装饰材料。 
发明内容
针对现有技术中存在的不足,本发明的目的在于提供一种适合于建筑物的装饰材料的挤塑聚苯板外墙外保温系统及所述挤塑聚苯板外墙外保温系统的制作工艺。 
本发明的技术方案是这样实现的:挤塑聚苯板外墙外保温系统,包括粘结层、保温层、抗裂防护层和饰面层,所述粘结层与基层墙体相邻,所述保温层位于所述粘结层与所述抗裂防护层之间,所述抗裂防护层位于所述保温层与所述饰面层之间;所述抗裂防护层包括第一抗裂砂浆层、第二抗裂砂浆层和位于所述第一抗裂砂浆层与所述第二抗裂砂浆层之间的热镀锌钢丝网层,所述第一抗裂砂浆层位于所述保温层与所述热镀锌钢丝网层之间,所述第二抗裂砂浆层位于所述饰面层与所述热镀锌钢丝网层之间。 
上述挤塑聚苯板外墙外保温系统,所述抗裂防护层包括抗裂砂浆层和耐 碱玻纤网格布层,所述抗裂砂浆层位于所述耐碱玻纤网格布层与所述保温层之间,所述耐碱玻纤网格布层位于所述抗裂砂浆层与所述饰面层之间。 
上述挤塑聚苯板外墙外保温系统,所述饰面层包括柔性耐水腻子层和涂料层,所述柔性耐水腻子层位于所述耐碱玻纤网格布层与所述涂料层之间。 
上述挤塑聚苯板外墙外保温系统,所述饰面层包括粘结砂浆层和面砖层,所述粘结砂浆层位于所述面砖层与所述第二抗裂砂浆层之间。 
上述挤塑聚苯板外墙外保温系统,相邻所述面砖之间有勾缝料。 
上述挤塑聚苯板外墙外保温系统,所述粘结层为粘结砂浆,所述保温层为挤塑聚苯保温板。 
上述挤塑聚苯板外墙外保温系统的制作工艺,包括如下步骤: 
(a)按照粘结砂浆干粉料与水的质量之比为4∶1配制粘结砂浆,在基层墙体上刷一层粘结砂浆,粘结砂浆层即为所述粘结层; 
(b)在所述粘结层上粘贴挤塑聚苯保温板,挤塑聚苯保温板层即为所述保温层; 
(c)按照抗裂砂浆干粉料与水的质量比为4∶1配制抗裂砂浆,先加入抗裂砂浆干粉料再加入水并搅拌均匀,在所述保温层上抹一层抗裂砂浆、厚度为2-3毫米,并在抗裂砂浆层上压上耐碱玻纤网格布,抗裂砂浆层与耐碱玻纤网格布构成所述抗裂防护层; 
(d)在所述抗裂防护层上刷一层柔性耐水腻子,并在柔性耐水腻子层上刷一层涂料,柔性耐水腻子层与涂料层构成所述饰面层。 
上述挤塑聚苯板外墙外保温系统的制作工艺,包括如下步骤: 
上述挤塑聚苯板外墙外保温系统的制作工艺,包括如下步骤: 
(a)按照粘结砂浆干粉料与水的质量之比为4∶1配制粘结砂浆,在基层墙体上刷一层粘结砂浆构成所述粘结层; 
(b)在所述粘结层上粘贴挤塑聚苯保温板,挤塑聚苯保温板层即为所述保温层; 
(c)按照抗裂砂浆干粉料与水的质量比为4∶1配制抗裂砂浆,先加入抗裂砂浆干粉料再加入水并搅拌均匀,即得抗裂砂浆; 
(d)在所述保温层上抹一层步骤(c)中制得的抗裂砂浆、厚度为2-3毫米,形成第一抗裂砂浆层;然后在所述第一抗裂砂浆层上铺贴上热镀锌钢丝网,再在所述热镀锌钢丝网上抹上一层步骤(c)中制得的抗裂砂浆、厚度为1-2毫米,形成第二抗裂砂浆层,所述第一抗裂砂浆层、所述第二抗裂砂浆层以及所述热镀锌钢丝网层构成所述抗裂防护层; 
(e)在所述第二抗裂砂浆层上抹一层粘结砂浆,并在粘结砂浆层上铺贴面砖,所述粘结砂浆层和所述面砖层构成所述饰面层; 
(f)用勾缝料勾缝。 
本发明的有益效果是:利用本发明的挤塑聚苯板外墙外保温系统的制作工艺制作的挤塑聚苯板外墙外保温系统强度很大,并且表面的粘贴性好,可以粘贴面砖等;非常适于作为建筑物的装饰材料。 
附图说明
图1为本发明的挤塑聚苯板外墙外保温系统的结构示意图。 
图中:1-基层墙体,2-粘结层,3-保温层,4-抗裂防护层,5-饰面层。 
具体实施方式
结合附图对本发明做进一步的说明: 
实施例1 
如图1所示,本实施例的挤塑聚苯板外墙外保温系统包括粘结层2、保温层3、抗裂防护层4和饰面层5,所述粘结层2与基层墙体1相邻,所述保温层3位于所述粘结层2与所述抗裂防护层4之间,所述抗裂防护层4位于所述保温层3与所述饰面层5之间。所述抗裂防护层4包括抗裂砂浆层和耐碱玻纤网格布层,所述抗裂砂浆层位于所述耐碱玻纤网格布层与所述保温层3之间,所述耐碱玻纤网格布层位于所述抗裂砂浆层与所述饰面层5之间。所述饰面层5包括柔性耐水腻子层和涂料层,所述柔性耐水腻子层位于所述耐碱玻纤网格布层与所述涂料层之间。所述粘结层2为粘结砂浆,所述保温层3为挤塑聚苯保温板。所述基层墙体1可以是混凝土墙及各种砌体墙。 
本实施例挤塑聚苯板外墙外保温系统的制作工艺包括如下步骤: 
(a)弹控制线:根据建筑立面设计和外墙外保温技术要求,在墙面弹出外门窗水平、垂直控制线及伸缩缝线、装饰缝线等;挂基准线:在建筑外墙大角(阳角、阴角)及其它必要处挂垂直基准钢线,每个楼层适当位置挂水平线,以控制挤塑聚苯板的垂直度和平整度;按照粘结砂浆干粉料与水的质量之比为4∶1配制粘结砂浆(粘结砂浆的配制最好专人负责、严格计量、机械搅拌并确保搅拌均匀,拌好的胶浆在静停20分后最好经二次搅拌再投入使用,配好的料注意防晒避风,以免水分蒸发过快,一次配制量应在可操作时间45分钟内用完),在基层墙体1上刷一层粘结砂浆,粘结砂浆层即为所述粘结层2; 
(b)在所述粘结层2上粘贴挤塑聚苯保温板,挤塑聚苯保温板可以选择标准尺寸,例如:600mm×900mm、600mm×1200mm,非标准尺寸或局部不 规则处可现场裁切,但必须注意切口与板面垂直;整块墙面的边角应用最小尺寸超过300mm的挤塑聚苯保温板,挤塑聚苯保温板的拼缝不得正好留在门窗口的四角处;当采用粘贴方式固定挤塑聚苯保温板时,粘贴方式有点框法和条粘法;点框法适用于平整度较差的墙面,应保证粘结面积不小于50%;条粘法适用于平整度较好的墙面;不得在挤塑聚苯保温板侧面涂抹胶粘剂;排板时按水平顺序排列,上下错缝粘结,阴阳角应做错茬处理;粘挤塑聚苯保温板应用专用工具轻揉、均匀挤压挤塑聚苯保温板,随时用2m靠尺和托线板检查平整度和垂直度;粘挤塑聚苯保温板时应注意清除板边溢出的胶粘剂,使板与板之间无“碰头灰”;板缝拼严,缝宽超出2mm时用相应厚度的挤塑板片填塞;拼缝高差不大于1.5mm,否则应用砂纸或专用打磨机具打磨平整;挤塑聚苯保温板层即为所述保温层3,凡在粘贴的挤塑聚苯保温板侧边外露处(如伸缩缝、建筑沉降缝、温度缝等缝线两侧、门窗口处,都应做网格布翻包处理;为增加附着的强度,可以采用锚固件固定挤塑聚苯保温板,采用锚固件固定挤塑聚苯保温板时,锚固件安装应至少在胶粘剂使用24h后进行,用电锤(冲击钻)在挤塑聚苯保温板表面向内打孔,孔径视锚固件直径而定,拧入或敲入锚固钉,钉头和园盘不得超出板面; 
(c)按照抗裂砂浆干粉料与水的质量比为4∶1配制抗裂砂浆,先加入抗裂砂浆干粉料再加入水并搅拌均匀(抗裂砂浆配制好之后不得任意加水,最好在2小时内用完),在所述保温层3上抹一层抗裂砂浆、厚度为2-3毫米,并在抗裂砂浆层上压上耐碱玻纤网格布(将耐碱玻纤网格布绷紧后贴于底层抗裂砂浆上,用抹子由中间向四周把耐碱玻纤网格布压入抗裂砂浆的表层,要平整压实,严禁网格布皱褶;耐碱玻纤网格布不得压入过深,表面必须在 底层砂浆之外;单张耐碱玻纤网格布长度不宜大于3m;铺贴遇有搭接时,必须满足横向100mm、纵向80mm的搭接长度要求),抗裂砂浆层与耐碱玻纤网格布构成所述抗裂防护层4; 
(d)在所述抗裂防护层4上刷一层柔性耐水腻子,并在柔性耐水腻子层上刷一层涂料,柔性耐水腻子层与涂料层构成所述饰面层5。 
为了提高抗冲击强度,可以增加一层所述抗裂防护层4作为增强防护层,所述增强防护层的厚度为3毫米-7毫米。 
考虑首层与其它需加强部位的抗冲击要求,在标准外保温做法基础上加铺一层网格布,并再抹一道抗裂砂浆抹面,以提高抗冲击强度。在这种双层网格布做法中,底层网格布可以是标准网格布,也可以是质量更大、强度更高的增强网格布,以满足设计要求的抗冲击强度为原则。加强部位抗裂砂浆总厚度宜为5-7mm。 
利用本实施例的挤塑聚苯板外墙外保温系统的制作工艺制作的挤塑聚苯板外墙外保温系统强度很大,并且表面的粘贴性好,可以粘贴面砖等;非常适于作为建筑物的装饰材料。 
实施例2 
如图1所示,本实施例的挤塑聚苯板外墙外保温系统包括粘结层2、保温层3、抗裂防护层4和饰面层5,所述粘结层2与基层墙体1相邻,所述保温层3位于所述粘结层2与所述抗裂防护层4之间,所述抗裂防护层4位于所述保温层3与所述饰面层5之间。所述抗裂防护层4包括第一抗裂砂浆层、第二抗裂砂浆层和位于所述第一抗裂砂浆层与所述第二抗裂砂浆层之间的热镀锌钢丝网层,所述第一抗裂砂浆层位于所述保温层3与所述热镀锌钢丝网 层之间,所述第二抗裂砂浆层位于所述饰面层5与所述热镀锌钢丝网层之间。所述饰面层5包括粘结砂浆层和面砖层,所述粘结砂浆层位于所述面砖层与所述第二抗裂砂浆层之间。所述粘结层2为粘结砂浆,所述保温层3为挤塑聚苯保温板;相邻所述面砖之间有勾缝料。所述基层墙体1可以是混凝土墙及各种砌体墙。 
为了提高抗冲击强度,可以增加一层所述抗裂防护层4作为增强防护层,所述增强防护层的厚度为8毫米-10毫米。 
本实施例挤塑聚苯板外墙外保温系统的制作工艺包括如下步骤: 
(a)弹控制线:根据建筑立面设计和外墙外保温技术要求,在墙面弹出外门窗水平、垂直控制线及伸缩缝线、装饰缝线等;挂基准线:在建筑外墙大角(阳角、阴角)及其它必要处挂垂直基准钢线,每个楼层适当位置挂水平线,以控制挤塑聚苯板的垂直度和平整度;按照粘结砂浆干粉料与水的质量之比为4∶1配制粘结砂浆(粘结砂浆的配制最好专人负责、严格计量、机械搅拌并确保搅拌均匀,拌好的胶浆在静停20分后最好经二次搅拌再投入使用,配好的料注意防晒避风,以免水分蒸发过快,一次配制量应在可操作时间45分钟内用完),在基层墙体1上刷一层粘结砂浆构成所述粘结层2; 
(b)在所述粘结层2上粘贴挤塑聚苯保温板,挤塑聚苯保温板可以选择标准尺寸,例如:600mm×900mm、600mm×1200mm,非标准尺寸或局部不规则处可现场裁切,但必须注意切口与板面垂直;整块墙面的边角应用最小尺寸超过300mm的挤塑聚苯保温板,挤塑聚苯保温板的拼缝不得正好留在门窗口的四角处;当采用粘贴方式固定挤塑聚苯保温板时,粘贴方式有点框法和条粘法;点框法适用于平整度较差的墙面,应保证粘结面积不小于50%; 条粘法适用于平整度较好的墙面;不得在挤塑聚苯保温板侧面涂抹胶粘剂;排板时按水平顺序排列,上下错缝粘结,阴阳角应做错茬处理;粘挤塑聚苯保温板应用专用工具轻揉、均匀挤压挤塑聚苯保温板,随时用2m靠尺和托线板检查平整度和垂直度;粘挤塑聚苯保温板时应注意清除板边溢出的胶粘剂,使板与板之间无“碰头灰”;板缝拼严,缝宽超出2mm时用相应厚度的挤塑板片填塞;拼缝高差不大于1.5mm,否则应用砂纸或专用打磨机具打磨平整;挤塑聚苯保温板层即为所述保温层3,凡在粘贴的挤塑聚苯保温板侧边外露处(如伸缩缝、建筑沉降缝、温度缝等缝线两侧、门窗口处,都应做网格布翻包处理;为增加附着的强度,可以采用锚固件固定挤塑聚苯保温板,采用锚固件固定挤塑聚苯保温板时,锚固件安装应至少在胶粘剂使用24h后进行,用电锤(冲击钻)在挤塑聚苯保温板表面向内打孔,孔径视锚固件直径而定,拧入或敲入锚固钉,钉头和园盘不得超出板面; 
(c)按照抗裂砂浆干粉料与水的质量比为4∶1配制抗裂砂浆,先加入抗裂砂浆干粉料再加入水并搅拌均匀(抗裂砂浆配制好之后不得任意加水,最好在2小时内用完),即得抗裂砂浆; 
(d)在所述保温层3上抹一层步骤(c)中制得的抗裂砂浆、厚度为2-3毫米,形成第一抗裂砂浆层;然后在所述第一抗裂砂浆层上铺贴上热镀锌钢丝网(将热镀锌钢丝网绷紧后贴于底层第一抗裂砂浆上,用抹子由中间向四周把热镀锌钢丝网压入第一抗裂砂浆的表层,要平整压实,严禁热镀锌钢丝网皱褶,不平之处用12#镀锌铁丝做成的U型卡子固定;热镀锌钢丝网上不得压入过深,表面必须在底层第一抗裂砂浆之外;单张热镀锌钢丝网长度不宜大于3m,铺贴遇有搭接时,搭接长度不得小于40mm;为增加附着的强度, 采用机械锚固件固定镀锌钢丝网和挤塑聚苯保温板,锚固件安装在挤塑聚苯保温板粘贴24小时后进行,用电锤在挤塑聚苯保温板表面向内打孔,孔径8mm,进墙深度不小于50mm,拧入或敲入锚固钉,钉头和园盘不得超出底层第一抗裂砂浆,铺贴热镀锌钢丝网后,打入加钢垫片锚钉),在第一抗裂砂浆凝结前再在所述热镀锌钢丝网上抹上一层步骤(c)中制得的抗裂砂浆、厚度为1-2毫米,形成第二抗裂砂浆层,所述第一抗裂砂浆层、所述第二抗裂砂浆层以及所述热镀锌钢丝网层构成所述抗裂防护层4; 
(e)在所述第二抗裂砂浆层上抹一层粘结砂浆,并在粘结砂浆层上铺贴面砖,所述粘结砂浆层和所述面砖层构成所述饰面层5; 
(f)用勾缝料勾缝。 
利用本实施例的挤塑聚苯板外墙外保温系统的制作工艺制作的挤塑聚苯板外墙外保温系统强度很大,并且表面的粘贴性好,可以粘贴面砖等;非常适于作为建筑物的装饰材料。 
在上述实施例1和实施例2中,主要配套材料的性能指标如下: 
1、粘结砂浆的主要性能指标如表1所示: 
Figure BSA00000421787000091
5~30℃条件下贮存,贮存期为6个月。 
2、挤塑板的主要性能指针如表2所示: 
Figure BSA00000421787000101
3、抗裂砂浆的主要技术性能指标如表3所示: 
Figure BSA00000421787000102
4、锚栓的主要性能指标如表4所示: 
上述实施例1和实施例2中的挤塑聚苯板外保温系统性能指标如表5所 示: 

Claims (7)

1.挤塑聚苯板外墙外保温系统,其特征在于,包括粘结层(2)、保温层(3)、抗裂防护层(4)和饰面层(5),所述粘结层(2)与基层墙体(1)相邻,所述保温层(3)位于所述粘结层(2)与所述抗裂防护层(4)之间,所述抗裂防护层(4)位于所述保温层(3)与所述饰面层(5)之间;所述抗裂防护层(4)包括第一抗裂砂浆层、第二抗裂砂浆层和位于所述第一抗裂砂浆层与所述第二抗裂砂浆层之间的热镀锌钢丝网层,所述第一抗裂砂浆层位于所述保温层(3)与所述热镀锌钢丝网层之间,所述第二抗裂砂浆层位于所述饰面层(5)与所述热镀锌钢丝网层之间。
2.根据权利要求1所述的挤塑聚苯板外墙外保温系统,其特征在于,所述抗裂防护层(4)包括抗裂砂浆层和耐碱玻纤网格布层,所述抗裂砂浆层位于所述耐碱玻纤网格布层与所述保温层(3)之间,所述耐碱玻纤网格布层位于所述抗裂砂浆层与所述饰面层(5)之间。
3.根据权利要求2所述的挤塑聚苯板外墙外保温系统,其特征在于,所述饰面层(5)包括柔性耐水腻子层和涂料层,所述柔性耐水腻子层位于所述耐碱玻纤网格布层与所述涂料层之间。
4.根据权利要求1所述的挤塑聚苯板外墙外保温系统,其特征在于,所述饰面层(5)包括粘结砂浆层和面砖层,所述粘结砂浆层位于所述面砖层与所述第二抗裂砂浆层之间。
5.根据权利要求4所述的挤塑聚苯板外墙外保温系统,其特征在于,相邻所述面砖之间有勾缝料。
6.根据权利要求1-5任一所述的挤塑聚苯板外墙外保温系统,其特征在于, 所述粘结层(2)为粘结砂浆,所述保温层(3)为挤塑聚苯保温板。
7.权利要求1-5任一所述挤塑聚苯板外墙外保温系统的制作工艺,其特征在于,包括如下步骤:
(a)按照粘结砂浆干粉料与水的质量之比为4∶1配制粘结砂浆,在基层墙体(1)上刷一层粘结砂浆构成所述粘结层(2);
(b)在所述粘结层(2)上粘贴挤塑聚苯保温板,挤塑聚苯保温板层即为所述保温层(3);
(c)按照抗裂砂浆干粉料与水的质量比为4∶1配制抗裂砂浆,先加入抗裂砂浆干粉料再加入水并搅拌均匀,即得抗裂砂浆;
(d)在所述保温层(3)上抹一层步骤(c)中制得的抗裂砂浆、厚度为2-3毫米,形成第一抗裂砂浆层;然后在所述第一抗裂砂浆层上铺贴上热镀锌钢丝网,再在所述热镀锌钢丝网上抹上一层步骤(c)中制得的抗裂砂浆、厚度为1-2毫米,形成第二抗裂砂浆层,所述第一抗裂砂浆层、所述第二抗裂砂浆层以及所述热镀锌钢丝网层构成所述抗裂防护层(4);
(e)在所述第二抗裂砂浆层上抹一层粘结砂浆,并在粘结砂浆层上铺贴面砖,所述粘结砂浆层和所述面砖层构成所述饰面层(5);
(f)用勾缝料勾缝。 
CN2011100213790A 2011-01-19 2011-01-19 挤塑聚苯板外墙外保温系统及其制作工艺 Active CN102121279B (zh)