CN102114583B - 一种新型的耐磨堆焊焊条 - Google Patents

一种新型的耐磨堆焊焊条 Download PDF

Info

Publication number
CN102114583B
CN102114583B CN 201010597724 CN201010597724A CN102114583B CN 102114583 B CN102114583 B CN 102114583B CN 201010597724 CN201010597724 CN 201010597724 CN 201010597724 A CN201010597724 A CN 201010597724A CN 102114583 B CN102114583 B CN 102114583B
Authority
CN
China
Prior art keywords
hardfacing electrode
percent
coating
novel
novel hardfacing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201010597724
Other languages
English (en)
Other versions
CN102114583A (zh
Inventor
张东博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU ATHENA TECHNOLOGY Co Ltd
Original Assignee
SUZHOU ATHENA TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU ATHENA TECHNOLOGY Co Ltd filed Critical SUZHOU ATHENA TECHNOLOGY Co Ltd
Priority to CN 201010597724 priority Critical patent/CN102114583B/zh
Publication of CN102114583A publication Critical patent/CN102114583A/zh
Application granted granted Critical
Publication of CN102114583B publication Critical patent/CN102114583B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种新型的耐磨堆焊焊条，属于耐磨损防护领域。一种新型的耐磨堆焊焊条，包括焊芯和药皮，所述药皮含有成分的质量百分比为：C：0.5-1.5％，Cr：7-11％，Si：0.5-1.5％，Mo：1-4％，V：2-4％，Re：0.5-2％。其应用如下：利用手工电弧焊的方法，将新型的耐磨堆焊焊条在金属基体表面制备一层Fe-C-Si-Mo-Cr-V-Re系涂层，所述Fe-C-Si-Mo-Cr-V-Re系涂层的厚度为0.5mm。本发明具有加工方便、性能稳定和成本较低等特点，使用本发明后的基材和未经处理的基材相比，具有明显的耐磨性能，可以大幅度的提高基体材料的使用寿命，具有较大的经济及社会效益。

Description

一种新型的耐磨堆焊焊条
技术领域
本发明涉及一种新型的耐磨堆焊焊条，属于耐磨损防护领域。
背景技术
在全球每年由于材料的磨损而造成的直接损失多达300亿美元以上，这种损失不仅浪费很多材料，同都会造成大量的间接损失。因此近年来随着节能减排的需要，导致了绿色再制造产业的兴起，此产业的核心就是以表面工程为基础的产业，由于大多数的零件失效发生在表面，在失效的零件表面上制备一层新的涂层，既能保证表面的需要，又能够使继续使用芯部等部分，这样可以节省大量的材料费及加工费，因此，表面工程是节能减排的很好的范例，使用表面堆焊技术是提高工件耐磨性的方法之一，所谓的堆焊是焊接领域的一个分支，它是焊接的方法在零件表面堆敷一层具有一定性能材料的工艺过程，其目的不是为了连接零件，而是在于使零件表面获得具有耐磨、耐热和耐蚀等特殊性能的熔敷金属，或是为了恢复或增加尺寸而进行的焊接过程。
发明内容
本发明的目的在于提供一种新型的耐磨堆焊焊条，其具有加工方便、性能稳定和成本较低等特点，适合用于电厂、钢厂、军用设施和工厂等的防护等场合，对国防和民用都有着重要意义。
本发明解决其技术问题所采取的技术方案是：一种新型的耐磨堆焊焊条，包括焊芯和药皮，所述药皮含有成分的质量百分比为：C：0.5-1.5％，Cr：7-11％，Si：0.5-1.5％，Mo：1-4％，V：2-4％，Re：0.5-2％。
上述新型的耐磨堆焊焊条的应用如下：利用手工电弧焊的方法，将新型的耐磨堆焊焊条在金属基体表面制备一层Fe-C-Si-Mo-Cr-V-Re系涂层。
所述Fe-C-Si-Mo-Cr-V-Re系涂层的厚度为0.5mm。
本发明具有加工方便、性能稳定和成本较低等特点，使用本发明后的基材和未经处理的基材相比，具有明显的耐磨性能，可以大幅度的提高基体材料的使用寿命，具有较大的经济及社会效益。
附图说明
图1为使用本发明后金属基体的结构示意图。
图中：1、Fe-C-Si-Mo-Cr-V-Re系涂层；2、金属基体。
具体实施方式
一种新型的耐磨堆焊焊条，包括焊芯和药皮，所述焊芯选用H08A焊芯，所述药皮含有成分的质量百分比为：C：0.5-1.5％，Cr：7-11％，Si：0.5-1.5％，Mo：1-4％，V：2-4％，Re：0.5-2％。
采用Si、Mo、Cr、V为添加元素，使得使用了该新型的耐磨堆焊焊条的金属基体的耐磨性能得到提高，其中Cr能提高涂层的强度和硬度，同时使塑性和韧性降低不大，Mo可以细化晶粒，并可防止回火脆性，还可以增加红硬性，降低产生裂纹倾向，并能提高抗冲击破坏性能。V可以细化及共晶组织，改善碳化物的分布，同时可抑制焊接热裂纹的产生，Si能够提高钢的热强性，同时提高耐热疲劳性，Re可以细化晶粒，净化晶界，消除有害杂质，净化堆焊层。
下面给出本发明的两个应用实例(结合图1所示)。
1.样品基材304不锈钢/其他金属材料。采用手工电弧焊工艺，将新型的耐磨堆焊焊条在金属基体2表面制备一层0.5mm厚度的Fe-C-Si-Mo-Cr-V-Re系涂层1，其新型的耐磨堆焊焊条药皮成分为：C：0.5％，Cr：7％，Si：1％，Mo：2％，V：2.5％，Re：0.5％。堆焊时的焊接工艺参数为：直流反接，焊接电流为：180A，焊接电压为：22V，焊后空冷。焊后通过合适的表面处理。和未经处理的基材相比，具有明显的耐磨性能，可以大幅度的提高基体材料的使用寿命，具有较大的经济及社会效益。
2.样品基材304不锈钢/其他金属材料。采用手工电弧焊工艺，将新型的耐磨堆焊焊条在金属基体2表面制备一层0.5mm厚度的Fe-C-Si-Mo-Cr-V-Re系涂层1，其新型的耐磨堆焊焊条药皮成分为：C：0.7％，Cr：10％，Si：1.5％，Mo：4％，V：4％，Re：2％。堆焊时的焊接工艺参数为：直流反接，焊接电流为：175A，焊接电压为：20V，焊后空冷。焊后通过合适的表面处理。和未经处理的基材相比，具有明显的耐磨性能，可以大幅度的提高基体材料的使用寿命，具有较大的经济及社会效益。
为了能够更好的利用本体系涂层的性能，可以根据不同的要求制备不同厚度的Fe-C-Si-Mo-Cr-V-Re系涂层1，以使其能够达到工业使用效果。

Claims (3)

1.一种新型的耐磨堆焊焊条，包括焊芯和药皮，其特征是：所述新型的耐磨堆焊焊条的药皮含有成分的质量百分比为：C：0.5-1.5％，Cr：7-11％，Si：0.5-1.5％，Mo：1-4％，V：2-4％，Re：0.5-2％。
2.一种根据权利要求1所述的新型的耐磨堆焊焊条的应用，其特征是：利用手工电弧焊的方法，将新型的耐磨堆焊焊条在金属基体(2)表面制备一层Fe-C-Si-Mo-Cr-V-Re系涂层(1)。
3.根据权利要求2所述的新型的耐磨堆焊焊条的应用，其特征是：所述Fe-C-Si-Mo-Cr-V-Re系涂层(1)的厚度为0.5mm。
CN 201010597724 2010-12-21 2010-12-21 一种新型的耐磨堆焊焊条 Expired - Fee Related CN102114583B (zh)