CN102113913B - 一种牙科用切割砂片 - Google Patents

一种牙科用切割砂片 Download PDF

Info

Publication number
CN102113913B
CN102113913B CN 201010510678 CN201010510678A CN102113913B CN 102113913 B CN102113913 B CN 102113913B CN 201010510678 CN201010510678 CN 201010510678 CN 201010510678 A CN201010510678 A CN 201010510678A CN 102113913 B CN102113913 B CN 102113913B
Authority
CN
China
Prior art keywords
disc
cutting
dentistry
particle size
colorant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201010510678
Other languages
English (en)
Other versions
CN102113913A (zh
Inventor
孙学义
孙秀云
雷复兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LUOYANG BEIYUAN SPECIAL CERAMICS CO Ltd
Original Assignee
LUOYANG BEIYUAN SPECIAL CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LUOYANG BEIYUAN SPECIAL CERAMICS CO Ltd filed Critical LUOYANG BEIYUAN SPECIAL CERAMICS CO Ltd
Priority to CN 201010510678 priority Critical patent/CN102113913B/zh
Publication of CN102113913A publication Critical patent/CN102113913A/zh
Application granted granted Critical
Publication of CN102113913B publication Critical patent/CN102113913B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开的一种牙科用切割砂片，各组分按重量百分比配比如下：刚玉砂、66~75%，碳化硅砂、8~15%，色料、0.5~1%，酚醛树脂液、13~16%，无水乙醇、2~3%；将各原料按比例称量并混炼均匀，再经挤压、切割成带中心孔的圆片，之后将圆片在50℃以下干燥10-20小时，再经230~250℃温度老化处理20小时即可制备出砂片，且所述砂片具备高抗弯强度，高韧性。

Description

一种牙科用切割砂片
技术领域
本发明涉及砂片技术领域，具体涉及一种以刚玉为主要成分，以高强高温酚醛树脂为结合剂的用于牙科修复义齿的切割砂片。
背景技术
本发明所涉及的砂片主要用于义齿加工过程中的切割、打磨，是义齿加工的常用工具之一。常用的牙科砂片的直径为15~38mm，厚度为0.1~2mm。由于其尺寸小而薄，因此要求砂片具有：1）高的抗弯强度；2）高的韧性；3）高的磨削锋利度；4）高的耐磨性；5）外形平整。
然而，国内产品存在的主要问题是强度低、韧性差，高速切割时容易破裂造成飞片，直接威胁操作者的人身安全。目前，国内使用的牙科砂片以台湾产品为主。
发明内容
     本发明所要解决的技术问题是提供一种具有高抗弯强度，高韧性牙科用切割砂片及其制造方法。
为实现上述发明目的，本发明采用如下技术方案：
本发明的牙科用切割砂片，各组分按重量百分比配比如下：
      刚玉砂        66~75%
      碳化硅砂      8~15%
      色料          0.5~1%
      酚醛树脂液    13~16%
      无水乙醇       2~3%
为更好的实施本发明创造，所述刚玉砂的最小粒度为350#，最大粒度为60#。
为更好的实施本发明创造，所述碳化硅砂的最小粒度为350#，最大粒度为150#。
为更好的实施本发明创造，所述色料选用红色时，用铁红；所述色料选用绿色时，用铬绿；所述色料选用黄色时，用钛黄；所述色料选用蓝色时，用钴蓝。
本发明的牙科用切割砂片经以下步骤制造而成：将原料按比例称量并混炼均匀，再经挤压、切割成带中心孔的圆片，之后将圆片在50℃以下干燥10-20小时，再经230~250℃温度老化处理20小时即可。
本发明中，无水乙醇的主要作用是调节成型时物料的粘度和提高气孔率，加入色料可以满足顾客对颜色的要求。
经过上述原料配比及制备方法生产的牙科用切割砂片，特别是采用了高强高温酚醛树脂作为结合剂大幅度的提高了砂片的抗弯强度。采用三点承载法对砂片的抗弯强度进行了对比试验，结果表明，国产砂片的承载力都小于800g，而本发明所制备的砂片的承载力都在1000g以上，达到了国外产品的性能。其中，本文采用的三点承载法实验时，结合图1，是将砂片置于呈120??均布的三处支架上，通过在承载台上增添砝码，将力通过与承载台设置为一体的杆传递至砂片；杆接近支架的一端设置为尖形，以便准确对准砂片中心孔。
附图说明
    图1为本发明砂片强度实验装置的结构示意图；  
    图中：1、承载台；2、砝码；3、砂片；4、支架。
具体实施方式：
1．配比：重量%
刚玉砂   碳化硅砂   色料   酚醛树脂液   无水乙醇   承载力g
A：  66         15       1         16           2      1050
B：  75         8        0.5       13.5          3      1020
C：  72         12       0.8        13          2.2     1000
D：  71         11       0.7        15          2.3     1020
E：  68         14       0.9        15          2.1     1010
2．制备方法：
各组分按重量百分比选配，称量后在混炼机中混炼均匀，将混炼后的物料用对辊机挤压到所需的厚度，将挤压后的料片用切割机切割成带中心孔的圆片，再将圆片在50℃以下干燥10-20小时，使无水乙醇蒸发，酚醛树脂固化；经230~250℃温度老化处理20小时即可。

Claims (1)

1.一种牙科用切割砂片，其特征在于：各组分按重量百分比配比如下：
      刚玉砂        66～75%
      碳化硅砂      8～15%
      色料          0. 5～1%
      高温高强酚醛树脂液    13～16%
      无水乙醇       2～3% ；
将各组分按比例称量并混炼均匀，再经挤压、切割成带中心孔的圆片，之后将圆片在50℃以下干燥10-20小时，再经230～250℃温度老化处理20小时即可。
2、根据权利要求1所述的牙科用切割砂片，其特征在于：所述刚玉砂的最小粒度为350#，最大粒度为60#。
3、根据权利要求1所述的牙科用切割砂片，其特征在于：所述碳化硅砂的最小粒度为350#，最大粒度为150#。
4、根据权利要求1所述的牙科用切割砂片，其特征在于：所述色料选用红色时，用铁红；所述色料选用绿色时，用铬绿；所述色料选用黄色时，用钛黄；所述色料选用蓝色时，用钴蓝。
CN 201010510678 2010-10-18 2010-10-18 一种牙科用切割砂片 Expired - Fee Related CN102113913B (zh)