CN102102147A - 链篦机回转窑生产镁质球团工艺 - Google Patents

链篦机回转窑生产镁质球团工艺 Download PDF

Info

Publication number
CN102102147A
CN102102147A CN2009102484802A CN200910248480A CN102102147A CN 102102147 A CN102102147 A CN 102102147A CN 2009102484802 A CN2009102484802 A CN 2009102484802A CN 200910248480 A CN200910248480 A CN 200910248480A CN 102102147 A CN102102147 A CN 102102147A
Authority
CN
China
Prior art keywords
grate
ball
pelletizing process
pellets
roasting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2009102484802A
Other languages
English (en)
Other versions
CN102102147B (zh
Inventor
姚强
王红艳
金忠伟
周征
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Group Mining Co Ltd
Original Assignee
Angang Group Mining Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Group Mining Co Ltd filed Critical Angang Group Mining Co Ltd
Priority to CN2009102484802A priority Critical patent/CN102102147B/zh
Publication of CN102102147A publication Critical patent/CN102102147A/zh
Application granted granted Critical
Publication of CN102102147B publication Critical patent/CN102102147B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于冶金原料矿物加工的破碎工艺技术领域，特别是涉及一种链篦机回转窑生产镁质球团工艺，包括下述步骤：按照下述组分的重量百分比配料：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，将此配料混匀，加水搅拌均匀，混合料送入造球盘造球形成生球，将筛分出合格的生球给入链篦机进行干燥、预热成预热球，将预热球给入回转窑焙烧成焙烧球，测试此焙烧球的性能，将焙烧球送入环冷机冷却后成为合格镁质球团矿，磁铁精矿水分为7.0～9.0％，菱镁石的用量为MgO＜2.5％。本发明能够提高球团矿在高炉原料的配比，提高入炉品位，改善炉料冶金性能，提高炼铁高炉的生产能力，能使炼铁获得较高的经济效益。

Description

链篦机回转窑生产镁质球团工艺
技术领域
本发明属于冶金原料矿物加工的破碎工艺技术领域，特别是涉及一种链篦机回转窑生产镁质球团工艺。
背景技术
随着钢铁工业的炼铁原料中酸性氧化球团矿产能的增加，高炉炉料结构中高碱度烧结矿与酸性球团矿的使用配比也发生变化。面对鞍钢酸性球团矿产能增加后高炉炉料结构问题，研究在现有原料条件下，探索生产熔剂性球团矿的可行性，提高球团矿碱度和增加MgO的含量，在保证炼铁高炉原料总体碱度指标不变的条件下，增加球团矿入炉配料比例，提高入炉品位，改善炉料冶金性能。
发明内容
本发明的目的是提供一种链篦机回转窑生产镁质球团工艺，可提高球团矿的还原度，有较高的软化和熔融温度，能降低高炉焦化，能提高高炉产量，改善炼铁技术经济指标。
本发明的目的是通过下述技术方案来实现的：
本发明的链篦机回转窑生产镁质球团工艺，其特征在于包括下述步骤：
1)按照下述组分的重量百分比配料：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，将此配料混合，加水搅拌均匀，加水量以使混合料湿润为准，
2)将湿润的混合料送入造球盘造球形成生球，并筛分出合格的生球，
3)将筛分出合格的生球给入链篦机进行鼓风干燥、抽风干燥、预热成预热球，测试此预热球的性能，
4)将预热球给入回转窑焙烧成焙烧球，测试此焙烧球的性能，
5)将焙烧球送入环冷机冷却后成为合格镁质球团矿，
所述的磁铁精矿水分为7.0～9.0％，
所述的菱镁石的用量为MgO＜2.5％。
所述的将湿润的混合料送入造球盘时的料层厚度为150～250mm。
所述的链篦机机速为3.0～3.4m/min。
所述的链篦机鼓风干燥的温度为200～250℃、风速为1.8～2.4m/s，
所述的链篦机抽风干燥的温度为350～400℃、抽风风速1.8～2.1m/s。
所述的链篦机预热的温度920～960℃、风速2.4～2.7m/s。
所述的回转窑焙烧的焙烧条件为：焙烧温度1250～1280℃，焙烧时间8～14min。
所述的测试预热球的性能包括测抗压强度、测AC转鼓指数、测粉末量。
所述的测试焙烧球的性能包括测抗压强度、测转鼓强度、测耐磨指数。
所述的组分的重量百分比配料为：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，石灰石0.5～1.0％。
按照本发明的链篦机回转窑生产镁质球团工艺生产的镁质球团矿，就是在球团矿配料中，添加含有大量MgO细磨物料，诸如菱镁石等。含MgO熔剂性球团矿有较高的还原度；有较高的软化和熔融温度；能降低高炉焦化；能提高高炉产量；改善炼铁技术经济指标。
通过添加少量的石灰石，提高成品球强度。在此条件下获得的球团，其冶金性能较好，还原度、还原膨胀性能及熔滴温度均要优于普通球团。
由于镁质球团矿还原度提高，使得高炉间接还原率较高，减少了熔剂熔解需要的热量，降低了焦(燃料)比；由于软熔带较窄的结果，使得高炉生产率提高；使得炉内软熔带位置较使用酸性球团时低，延长炉内耐火材料的寿命。
按照本发明生产镁质球团矿，能够提高球团矿在高炉原料的配比，提高入炉品位，改善炉料冶金性能，提高炼铁高炉的生产能力，能使炼铁获得较高的经济效益。
附图说明
图1为本发明的工艺流程图。
具体实施方式
下面结合实施例详细说明本发明的具体实施方式。
如图1所示，按照本发明的链篦机回转窑生产镁质球团工艺，其特征在于包括下述步骤：
1)按照下述组分的重量百分比配料：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，将此配料混匀，加水搅拌均匀，加水量以使混合料湿润为准，
2)将湿润的混合料送入造球盘造球，形成生球，并筛分出合格的生球，
3)将筛分出合格的生球给入链篦机干燥、预热，进行鼓风干燥、抽风干燥、预热成预热球，测试此预热球的性能，
4)将预热球给入回转窑焙烧成焙烧球，测试此焙烧球的性能，
5)将焙烧球送入环冷机冷却后成为合格的成品镁质球团矿，
所述的磁铁精矿水分为7.0～9.0％，
所述的菱镁石的用量为MgO＜2.5％。
所述的将湿润的混合料送入造球盘时的料层厚度为150～250mm。
所述的链篦机机速为3.0～3.4m/min。
所述的链篦机鼓风干燥的温度为200～250℃、风速为1.8～2.4m/s，
所述的链篦机抽风干燥的温度为350～400℃、抽风风速1.8～2.1m/s。
所述的链篦机预热的温度920～960℃、风速2.4～2.7m/s。
所述的回转窑焙烧的焙烧条件为：焙烧温度1250～1280℃，焙烧时间8～14min。
所述的测试预热球的性能包括测抗压强度、测AC转鼓指数、测粉末量。
所述的测试焙烧球的性能包括测抗压强度、测转鼓强度、测耐磨指数。
所述的组分的重量百分比配料为：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，石灰石0.5～1.0％。
按照本发明生产镁质球团矿，能够提高球团矿在高炉原料的配比，提高入炉品位，改善炉料冶金性能，提高炼铁高炉的生产能力，能使炼铁获得较高的经济效益。

Claims (10)

1.一种链篦机回转窑生产镁质球团工艺，其特征在于包括下述步骤：
1)按照下述组分的重量百分比配料：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，将此配料混匀，加水搅拌均匀，加水量以使混合料湿润为准，
2)将湿润的混合料送入造球盘造球形成生球，并筛分出合格的生球，
3)将筛分出合格的生球给入链篦机进行鼓风干燥、抽风干燥、预热成预热球，测试此预热球的性能，
4)将预热球给入回转窑焙烧成焙烧球，测试此焙烧球的性能，
5)将焙烧球送入环冷机冷却后成为合格镁质球团矿，
所述的磁铁精矿水分为7.0～9.0％，
所述的菱镁石的用量为MgO＜2.5％。
2.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的将湿润的混合料送入造球盘时的料层厚度为150～250mm。
3.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的链篦机机速为3.0～3.4m/min。
4.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的链篦机鼓风干燥的温度为200～250℃、风速为1.8～2.4m/s，
5.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的链篦机抽风干燥的温度为350～400℃、抽风风速1.8～2.1m/s。
6.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的链篦机预热的温度920～960℃、风速2.4～2.7m/s。
7.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的回转窑焙烧的焙烧条件为：焙烧温度1250～1280℃，焙烧时间8～14min。
8.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的测试预热球的性能包括测抗压强度、测AC转鼓指数、测粉末量。
9.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的测试焙烧球的性能包括测抗压强度、测转鼓强度、测耐磨指数。
10.根据权利要求1所述的链篦机回转窑生产镁质球团工艺，其特征在于所述的组分的重量百分比配料为：磁铁精矿92～96％，膨润土1.0～3.0％，菱镁矿3.0～4.5％，石灰石0.5～1.0％。
CN2009102484802A 2009-12-17 2009-12-17 链篦机回转窑生产镁质球团工艺 Active CN102102147B (zh)