CN102079900A - Polyetherdiol(PD) type alcohol soluble printing composite oil ink - Google Patents
Polyetherdiol(PD) type alcohol soluble printing composite oil ink Download PDFInfo
- Publication number
- CN102079900A CN102079900A CN2010105846441A CN201010584644A CN102079900A CN 102079900 A CN102079900 A CN 102079900A CN 2010105846441 A CN2010105846441 A CN 2010105846441A CN 201010584644 A CN201010584644 A CN 201010584644A CN 102079900 A CN102079900 A CN 102079900A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil ink
- type alcohol
- ethanol
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses PD type alcohol soluble printing composite oil ink, which comprises the following components in part by weight: 22 to 30 parts of polyurethane resin, 5 to 7 parts of ketonealdehyde resin, 24 to 32 parts of rutile type titanium dioxide, 0.1 to 0.4 part of fumed silicon dioxide, 4 to 6 parts of propylene glycol monoethyl ether, 14 to 16 parts of ethanol, 10 to 13 parts of isopropanol, 0.1 to 0.3 part of fluorescent brightener and 7 to 9 parts of butyl acetate. The oil ink disclosed by the invention has the advantages that: the oil ink does not contain benzene and ketone, contains less residual solvent, and meets national requirements on food sanitation; the color of the oil ink is bright; the dot repeatability is high; the levelling property is high; the oil ink is particularly suitable for chromaticity printing and can be printed on flexible boards; and printability of the oil ink is high.
Description
[technical field]
The present invention relates to printing ink, relate in particular to the molten printing compound oil ink of a kind of PD type alcohol.
[background technology]
Existing printing-ink generally all contains chemical substances such as benzene, ketone, pollutes easily in packages printing is produced, and especially is not suitable in the food product pack printing.
[summary of the invention]
The present invention is directed to the above-mentioned defective of prior art, a kind of environment-friendly ink that does not contain benzene, ketone be provided---the molten printing compound oil ink of PD type alcohol.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
The molten printing compound oil ink of a kind of PD type alcohol contains following component: 22-30 part urethane resin, 5-7 part aldehyde ketone resin, 24-32 part rutile titanium white powder, 0.1-0.4 part aerosil, 4-6 part propylene-glycol ethyl ether, 14-16 part ethanol, 10-13 part Virahol, 0.1-0.3 part white dyes, 7-9 part N-BUTYL ACETATE by weight percentage.
Preferably, the molten printing compound oil ink of PD type alcohol of the present invention contains following component by weight percentage: 25 parts of urethane resins, 6 parts of aldehyde ketone resins, 28 parts of rutile titanium white powder, 0.2 part of aerosil, 5 parts of propylene-glycol ethyl ethers, 15.8 parts of ethanol, 11.9 parts of Virahols, 0.1 part of white dyes, 8 parts of N-BUTYL ACETATEs.
Printing ink of the present invention has the following advantages:
1, the present invention closes printing ink for alcohol-soluble composite, does not contain benzene, ketone, and dissolvent residual is few, meets the state food hygienic requirements;
2, ink colors is bright-coloured, and the site circulation ratio is good, and good leveling property is particularly suitable for chromaticity printing;
3, can on flexographic plate, print, and can reach good printing effect;
4, printability is good, can adapt to the printing of all kinds of gravure printing presses friction-motion speeds.
[embodiment]
The present invention is further detailed explanation below in conjunction with embodiment.
Embodiment one: contain following component by weight percentage: 25 parts of urethane resins, 6 parts of aldehyde ketone resins, 28 parts of rutile titanium white powder, 0.2 part of aerosil, 5 parts of propylene-glycol ethyl ethers, 15.8 parts of ethanol, 11.9 parts of Virahols, 0.1 part of white dyes, 8 parts of N-BUTYL ACETATEs, mix this component and stir promptly obtaining the molten printing compound oil ink of PD type alcohol of the present invention.
Embodiment two: contain following component by weight percentage: 22 parts of urethane resins, 7 parts of aldehyde ketone resins, 30.6 parts of rutile titanium white powder, 0.3 part of aerosil, 5 parts of propylene-glycol ethyl ethers, 16 parts of ethanol, 11 parts of Virahols, 0.1 part of white dyes, 8 parts of N-BUTYL ACETATEs, mix this component and stir promptly obtaining the molten printing compound oil ink of PD type alcohol of the present invention.
Embodiment three: contain following component by weight percentage: 26.7 parts of urethane resins, 5 parts of aldehyde ketone resins, 26 parts of rutile titanium white powder, 0.1 part of aerosil, 6 parts of propylene-glycol ethyl ethers, 15 parts of ethanol, 12 parts of Virahols, 0.2 part of white dyes, 9 parts of N-BUTYL ACETATEs, mix this component and stir promptly obtaining the molten printing compound oil ink of PD type alcohol of the present invention.
Above-mentioned aerosil claims gas phase white carbon black again, English name: Silicon Dioxide, and molecular formula: SiO2 is the fluffy powder of white, porousness is nonpoisonous and tasteless pollution-free, high temperature resistant.Its unreactiveness that possesses and the special thixotropic property tensile strength of obviously improving rubber item simultaneously, tear strength and wear resistance, rubber improvement back intensity improves tens of times.The control of the rheological of liquid system, tackiness agent, polymkeric substance etc. and thixotropy, as the reinforcement of auxiliary agent, HCR and the RTV-2K silicone rubber of anti-heavy, thickening, sag prevention, can be used to regulate unrestricted flow and improve powder properties as anti-caking agent.Aerosil is one of ultra tiny inorganic novel material of extremely important high-tech, because its particle diameter is very little, therefore specific surface area is big, surface adsorption power is strong, surface energy is big, and aspect such as chemical purity height, dispersing property are good, thermal resistance, resistance has special performance, with its superior stability, reinforcement, thickening property and thixotropy, in numerous subjects and field, show unique characteristics, the effect of not replacing is arranged.
Above-mentioned printing ink can be selected different diluent formulations for use according to the rate of drying of user's needs:
Fast dry separation is with 20% ethyl ester, the thinner that 80% ethanol disposes;
In dry separation with 80% ethanol, the thinner that 20% Virahol disposes;
Slow curing is selected 50% ethanol for use, 40% Virahol, the thinner of 10% propylene glycol monomethyl ether configuration.
The present invention is mainly used in the packages printing of food such as desiccating food products, the cold spot heart, is applicable to poach.The base material of the applicable printing of this printing ink has PET film (processing degree 52 reach grace or more than), BOPP film (processing degree 38 reach grace or more than), nylon (processing degree 52 reach grace or more than).
The above embodiment has only expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to claim of the present invention.Should be pointed out that for the person of ordinary skill of the art without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (2)
1. the molten printing compound oil ink of PD type alcohol is characterized in that, contains following component by weight percentage:
22-30 part urethane resin, 5-7 part aldehyde ketone resin, 24-32 part rutile titanium white powder, 0.1-0.4 part aerosil, 4-6 part propylene-glycol ethyl ether, 14-16 part ethanol, 10-13 part Virahol, 0.1-0.3 part white dyes, 7-9 part N-BUTYL ACETATE.
2. the molten printing compound oil ink of PD type alcohol according to claim 1, it is characterized in that, contain following component by weight percentage: 25 parts of urethane resins, 6 parts of aldehyde ketone resins, 28 parts of rutile titanium white powder, 0.2 part of aerosil, 5 parts of propylene-glycol ethyl ethers, 15.8 parts of ethanol, 11.9 parts of Virahols, 0.1 part of white dyes, 8 parts of N-BUTYL ACETATEs.